scholarly journals Effects of synthesised polyaniline (PAni) contents on the anti-static properties of PAni-based polylactic acid (PLA) films

RSC Advances ◽  
2020 ◽  
Vol 10 (65) ◽  
pp. 39693-39699
Author(s):  
Pei-Yi Wong ◽  
Sook-Wai Phang ◽  
Azizah Baharum
Keyword(s):  
Lactic Acid ◽  
Polymer Film ◽  
Polylactic Acid ◽  
Poly Lactic Acid ◽  
Static Properties ◽  
Biodegradable Poly

An anti-static polymer film was prepared using biodegradable poly(lactic acid) as a matrix and polyaniline (PAni) as an anti-static agent to eliminate accumulated static charges.

Antifungal and plasticization effects of carvacrol in biodegradable poly(lactic acid) and poly(butylene adipate terephthalate) blend films for bakery packaging

LWT ◽  
2021 ◽  
pp. 112356
Author(s):  
Phatthranit Klinmalai ◽  
Atcharawan Srisa ◽  
Yeyen Laorenza ◽  
Wattinee Katekhong ◽  
Nathdanai Harnkarnsujarit
Keyword(s):  
Lactic Acid ◽  
Poly Lactic Acid ◽  
Blend Films ◽  
Biodegradable Poly

DGEBA-Based Epoxy Resin as Compatibilizer for Biodegradable Poly (lactic acid)/Poly(butylene adipate-co-terephthalate) Blends

2018 ◽  
Vol 381 (1) ◽  
pp. 1800133 ◽  
Author(s):  
Elaine C. Lopes Pereira ◽  
Bluma G. Soares ◽  
Rayan B. Jesus ◽  
Alex S. Sirqueira
Keyword(s):  
Lactic Acid ◽  
Epoxy Resin ◽  
Poly Lactic Acid ◽  
Biodegradable Poly

scholarly journals The combined plasticization of jute and tung oil anhydride for jute fiber reinforced poly(lactic acid) composites

2021 ◽  
pp. 096739112110576
Author(s):  
Ying Zhou ◽  
Can Chen ◽  
Lan Xie ◽  
Xiaolang Chen ◽  
Guangqiang Xiao ◽  
...  
Keyword(s):  
Lactic Acid ◽  
Physical And Mechanical Properties ◽  
Complex Viscosity ◽  
Poly Lactic Acid ◽  
Melt Blending ◽  
Sem Images ◽  
Pseudoplastic Fluid ◽  
Tung Oil ◽  
Biodegradable Poly ◽  
The Impact

In this work, novel plasticizing biodegradable poly (lactic acid) (PLA) composites were prepared by melt blending of jute and tung oil anhydride (TOA), and the physical and mechanical properties of PLA/jute/TOA composites were tested and characterized. The impact strength of PLA/jute/TOA composites significantly increases with increasing the content of TOA. The SEM images of fracture surface of PLA/jute/TOA composites become rough after the incorporation of TOA. In addition, TOA changes the crystallization temperature and decomposition process of PLA/jute/TOA composites. With increasing the amount of TOA, the value of storage modulus (E′) of PLA/jute/TOA composites gradually increases. The complex viscosity (η*) values for all samples reduce obviously with increasing the frequency, which means that the pure PLA and PLA/jute/TOA composites is typical pseudoplastic fluid. This is attributed to the formation of crosslinking, which restricts the deformation of the composites.

scholarly journals Impact Toughness and Ductility Enhancement of Biodegradable Poly(lactic acid)/Poly(ε-caprolactone) Blends via Addition of Glycidyl Methacrylate

2013 ◽  
Vol 2013 ◽  
pp. 1-8 ◽  
Author(s):  
Wei Kit Chee ◽  
Nor Azowa Ibrahim ◽  
Norhazlin Zainuddin ◽  
Mohd Faizal Abd Rahman ◽  
Buong Woei Chieng
Keyword(s):  
Lactic Acid ◽  
Impact Strength ◽  
Glycidyl Methacrylate ◽  
Interfacial Adhesion ◽  
Tensile Modulus ◽  
Sem Analysis ◽  
Poly Lactic Acid ◽  
Biodegradable Poly ◽  
Interfacial Compatibility ◽  
The Impact

Poly(lactic acid) (PLA)/poly(ε-caprolactone) (PCL) blends were prepared via melt blending technique. Glycidyl methacrylate (GMA) was added as reactive compatibilizer to improve the interfacial adhesion between immiscible phases of PLA and PCL matrices. Tensile test revealed that optimum in elongation at break of approximately 327% achieved when GMA loading was up to 3wt%. Slight drop in tensile strength and tensile modulus at optimum ratio suggested that the blends were tuned to be deformable. Flexural studies showed slight drop in flexural strength and modulus when GMA wt% increases as a result of improved flexibility by finer dispersion of PCL in PLA matrix. Besides, incorporation of GMA in the blends remarkably improved the impact strength. Highest impact strength was achieved (160% compared to pure PLA/PCL blend) when GMA loading was up to 3 wt%. SEM analysis revealed improved interfacial adhesion between PLA/PCL blends in the presence of GMA. Finer dispersion and smooth surface of the specimens were noted as GMA loading increases, indicating that addition of GMA eventually improved the interfacial compatibility of the nonmiscible blend.

scholarly journals Morphology, Thermal, Mechanical Properties and Rheological Behavior of Biodegradable Poly(butylene succinate)/poly(lactic acid) In-Situ Submicrofibrillar Composites

Materials ◽  
2018 ◽  
Vol 11 (12) ◽  
pp. 2422 ◽  
Author(s):  
Zhiwen Zhu ◽  
Hezhi He ◽  
Bin Xue ◽  
Zhiming Zhan ◽  
Guozhen Wang ◽  
...  
Keyword(s):  
Lactic Acid ◽  
Cold Drawing ◽  
Mechanical Analysis ◽  
Poly Lactic Acid ◽  
Fiber Morphology ◽  
Molding Process ◽  
Butylene Succinate ◽  
Low Frequencies ◽  
Biodegradable Poly

In this study, biodegradable poly(butylene succinate)/poly(lactic acid) (PBS/PLA) in-situ submicrofibrillar composites with various PLA content were successfully produced by a triple-screw extruder followed by a hot stretching−cold drawing−compression molding process. This study aimed to investigate the effects of dispersed PLA submicro-fibrils on the thermal, mechanical and rheological properties of PBS/PLA composites. Morphological observations demonstrated that the PLA phases are fibrillated to submicro-fibrils in the PBS/PLA composites, and all the PLA submicro-fibrils produced seem to have a uniform diameter of about 200nm. As rheological measurements revealed, at low frequencies, the storage modulus (G’) of PBS/PLA composites has been increased by more than four orders of magnitude with the inclusion of high concentrations (15 wt % and 20 wt %) of PLA submicro-fibrils, which indicates a significant improvement in the elastic responses of PBS melt. Dynamic Mechanical Analysis (DMA) results showed that the glass transition temperature (Tg) of PBS phase slightly shifted to the higher temperature after the inclusion of PLA. DSC experiments proved that fiber morphology of PLA has obvious heterogeneous nucleation effect on the crystallization of PBS. The tensile properties of the PBS/PLA in-situ submicrofibrillar composites are also improved compared to neat PBS.