Resistance Spot Welding in Non-Combustible Magnesium Alloy

2020 ◽  
Author(s):  
Xuanyi Shao ◽  
Yukio Miyashita ◽  
Duriyathep Panwised ◽  
Rattana Borrisutthekul
Keyword(s):  
Magnesium Alloy ◽  
Resistance Spot Welding ◽  
Spot Welding ◽  
Shear Test ◽  
Dissimilar Materials ◽  
Maximum Load ◽  
Tensile Shear ◽  
Similar Material ◽  
Resistance Spot ◽  
Surface Polishing

Abstract Resistance spot welding (RSW) was applied to non-combustible magnesium alloy, AX41 (Mg-4%Al-1%Ca) to investigate its weldability. The similar material joint of AX41 and dissimilar materials joint between AX41 and aluminum alloy, AA6061 were welded. Tensile shear test was carried out to evaluate joining strength in the similar and dissimilar materials RSW joints. In case of similar material joints, the maximum load obtained with tensile shear test in AX41 similar material joint was higher than that obtained in AA6061 similar material joint. Moreover, higher maximum load was obtained in a similar material joint without surface polishing compared to joint welded with surface polishing in AX41. In case of the dissimilar materials joint, the maximum load obtained was almost comparable with AX41 similar material joint, however scatter in joint strength was large. Weldability of the dissimilar materials joint became poor by applying surface polishing.

Properties of Light Metal Joint Welded by Thermal Compensation Resistance Spot Welding

2011 ◽  
Vol 230-232 ◽  
pp. 1084-1088
Author(s):  
Yi Min Tu ◽  
Ran Feng Qiu ◽  
Hong Xin Shi ◽  
Hua Yu ◽  
Ke Ke Zhang
Keyword(s):  
Aluminum Alloy ◽  
Magnesium Alloy ◽  
Resistance Spot Welding ◽  
Spot Welding ◽  
Light Metal ◽  
Welding Parameters ◽  
Shear Load ◽  
Thermal Compensation ◽  
Tensile Shear ◽  
Resistance Spot

A new technique of thermal compensation resistance spot welding was used to weld light metal such as aluminum alloy sheet and magnesium alloy. The effects of welding parameters on the tensile shear strength of joint and nugget diameter were investigated. The tensile shear load and nugget of the joint increased with the increasing of welding time, whereas that of the joint decreased with the increasing of electrode force. The joint with the maximum tensile shear load of approximately 5 kN was obtained at the condition of 12 kA and 11 kA welding current for aluminum alloy and magnesium alloy, respectively. The results reveal that the thermal compensation resistance spot welding is a feasible method to weld aluminum alloy and magnesium alloy..

scholarly journals Resistance Spot Welding Optimization Based on Artificial Neural Network

2014 ◽  
Vol 2014 ◽  
pp. 1-6 ◽  
Author(s):  
Thongchai Arunchai ◽  
Kawin Sonthipermpoon ◽  
Phisut Apichayakul ◽  
Kreangsak Tamee
Keyword(s):  
Neural Network ◽  
Artificial Neural Network ◽  
Shear Strength ◽  
Aluminum Alloy ◽  
Parameter Optimization ◽  
Resistance Spot Welding ◽  
Spot Welding ◽  
Tensile Shear Strength ◽  
Tensile Shear ◽  
Resistance Spot

Resistance Spot Welding (RSW) is processed by using aluminum alloy used in the automotive industry. The difficulty of RSW parameter setting leads to inconsistent quality between welds. The important RSW parameters are the welding current, electrode force, and welding time. An additional RSW parameter, that is, the electrical resistance of the aluminum alloy, which varies depending on the thickness of the material, is considered to be a necessary parameter. The parameters applied to the RSW process, with aluminum alloy, are sensitive to exact measurement. Parameter prediction by the use of an artificial neural network (ANN) as a tool in finding the parameter optimization was investigated. The ANN was designed and tested for predictive weld quality by using the input and output data in parameters and tensile shear strength of the aluminum alloy, respectively. The results of the tensile shear strength testing and the estimated parameter optimization are applied to the RSW process. The achieved results of the tensile shear strength output were mean squared error (MSE) and accuracy equal to 0.054 and 95%, respectively. This indicates that that the application of the ANN in welding machine control is highly successful in setting the welding parameters.

EVOLUTION OF INTERFACIAL MICROSTRUCTURE DURING RESISTANCE SPOT WELDING OF CU AND AL WITH AND NI-P COATING

2021 ◽  
pp. 1-12
Author(s):  
Nannan Chen ◽  
Hongliang Wang ◽  
Jingjing Li ◽  
Vic Liu ◽  
James Schroth
Keyword(s):  
Heat Input ◽  
Resistance Spot Welding ◽  
Spot Welding ◽  
Dissimilar Materials ◽  
Kirkendall Effect ◽  
Interfacial Microstructure ◽  
Formation Mechanisms ◽  
Elemental Distribution ◽  
Resistance Spot ◽  
State Diffusion

Abstract Dissimilar materials of copper (Cu) to aluminum (Al) with nickel-phosphorus (Ni-P) coatings were joined using resistance spot welding. The Ni-P coatings were electroless plated on the Al surfaces to eliminate the formation of brittle Cu-Al intermetallic compounds (IMCs) at the faying interface of Cu to Al. Three welding schedules with various heat input were employed to produce different interfacial microstructure. The evolution of interfaces in terms of phase constitution, elemental distribution and defects (gaps and voids) was characterized and the formation mechanisms were elucidated. During the welding, the bonding between Cu and Ni-P form through solid-state diffusion, while the faster diffusion rate of Cu relative to Ni and P atoms promotes the generation of sub-micro voids. As the heat input increases, gaps at the Cu/Ni-P interface diminishes accompanied by increase of sub-micro voids. A moderate schedule helps to remove the gaps and inhibit the voids formation. An Al3Ni layer and nanovoids were found around the interface of Ni-P/Al. The increased heat input decreases the grain size of Al3Ni at the interface by eutectic remelting and increases the nanovoids by enhanced nanoscale Kirkendall effect.

Dissimilar resistance spot welding of AISI 304 to AISI 409 stainless steels: mechanical properties and microstructural evolutions

2018 ◽  
Vol 115 (6) ◽  
pp. 610 ◽  
Author(s):  
Mehdi Safari ◽  
Hossein Mostaan ◽  
Abdoreza Ghaderi
Keyword(s):  
Stainless Steels ◽  
Resistance Spot Welding ◽  
Spot Welding ◽  
Steel Sheet ◽  
Welding Current ◽  
Stainless Steel Sheet ◽  
Tensile Shear ◽  
Aisi 304 ◽  
Resistance Spot ◽  
Electrode Force

In this work, dissimilar resistance spot welding of austenitic stainless steel sheet (304 grade) and ferritic stainless steel sheet (409 grade) is studied experimentally. For this purpose, the effects of process parameters such as welding current, welding time and electrode force on tensile-shear strength of resistance spot welded joints are investigated with response surface methodology (RSM). Also, microstructural evolutions during resistance spot welding process of AISI 409 and AISI 304 stainless steels are evaluated by optical microscopy. It is concluded from results that the tensile-shear strength of spot welds is increased with increasing the welding current, welding time and electrode force. It is shown that widmanstatten ferrites have been grown in the weld metal of dissimilar resistance spot welds of AISI 304 and AISI 409 stainless steels.

Sign in / Sign up

Export Citation Format

Share Document