Hydroxyapatite Whisker Reinforced 63s Glass Scaffolds for Bone Tissue Engineering

Bioactive glass (BG) is widely used for bone tissue engineering. However, poor mechanical properties are the major shortcomings. In the study, hydroxyapatite nanowhisker (HANw) was used as a reinforcement to improve the mechanical properties. 63s glass/HANw scaffolds were successfully fabricated by selective laser sintering (SLS). It was found that the optimal compressive strength and fracture toughness were achieved when 10 wt.% HANw was added. This led to 36% increase in compressive strength and 83% increase in fracture toughness, respectively, compared with pure 63s glass scaffolds. Different reinforcement mechanisms were analyzed based on the microstructure investigation. Whisker bridging and whisker pulling-out were efficient in absorbing crack propagating energy, resulting in the improvement of the mechanical properties. Moreover, bioactivity and biocompatibility of the scaffolds were evaluated in vitro. The results showed that composite scaffolds with 10 wt.% HANw exhibited good apatite-forming ability and cellular affinity.

Download Full-text

In vitro degradation and bioactivity of poly(propylene fumarate)/bioactive glass sintered microsphere scaffolds for bone tissue engineering

Science and Engineering of Composite Materials ◽

10.1515/secm-2014-0116 ◽

2016 ◽

Vol 23 (3) ◽

pp. 245-256 ◽

Cited By ~ 2

Author(s):

Sima Shahabi ◽

Yashar Rezaei ◽

Fathollah Moztarzadeh ◽

Farhood Najafi

Keyword(s):

Tissue Engineering ◽

Bioactive Glass ◽

Bone Tissue Engineering ◽

Bone Tissue ◽

P Uptake ◽

Surface Reactivity ◽

Ion Concentration ◽

Composite Scaffolds ◽

Poly Propylene

AbstractWe developed degradable poly(propylene fumarate)/bioactive glass (PPF/BG) composite scaffolds based on a sintered microsphere technique and investigated the effects of BG content on the characteristics of these composite scaffolds. Immersion in a simulated body fluid (SBF) was used to evaluate the surface reactivity of composite scaffolds. The surface of composite scaffolds was covered with hydroxycarbonate apatite layer after 7 days of immersion. Ion concentration analyses revealed a decrease in P concentration and an increase in Si, Ca, and Sr concentrations in SBF immersed with composite scaffolds during the 3-week period. The Ca and P uptake rates decreased after 4 days of incubation. This coincided with the decrease of the Si release rate. These data lend support to the suggestion that the Si released from the BG content of scaffolds present in the polymer matrix was involved in the formation of the Ca-P layer. The evaluation of the in vitro degradation of composite microspheres revealed that the weight of scaffolds remained relatively constant during the first 3 weeks and then started to decrease slowly, losing 10.5% of their initial mass by week 12. Our results support the concept that these new bioactive, degradable composite scaffolds may be used for bone tissue engineering applications.

Download Full-text

Binary bioactive glass composite scaffolds for bone tissue engineering—Structure and mechanical properties in micro and nano scale. A preliminary study

Micron ◽

10.1016/j.micron.2018.12.006 ◽

2019 ◽

Vol 119 ◽

pp. 64-71 ◽

Cited By ~ 7

Author(s):

Michał J. Woźniak ◽

Adrian Chlanda ◽

Przemysław Oberbek ◽

Marcin Heljak ◽

Katarzyna Czarnecka ◽

...

Keyword(s):

Mechanical Properties ◽

Tissue Engineering ◽

Bioactive Glass ◽

Bone Tissue Engineering ◽

Bone Tissue ◽

Glass Composite ◽

Composite Scaffolds ◽

Engineering Structure ◽

Nano Scale ◽

Preliminary Study

Download Full-text

Fabrication and in-vitro evaluation of copper doped bioactive glass/polymer composite scaffolds for bone tissue engineering

Research on Engineering Structures and Materials ◽

10.17515/resm2019.107ma0131 ◽

2019 ◽

Author(s):

Ahsen Ünal ◽

◽

Işıl Özer ◽

Melek Erol Taygun ◽

Sadriye Küçükbayrak ◽

...

Keyword(s):

Tissue Engineering ◽

Bioactive Glass ◽

Bone Tissue Engineering ◽

Bone Tissue ◽

Polymer Composite ◽

Composite Scaffolds ◽

In Vitro Evaluation

Download Full-text

Development of Biopolymeric Hybrid Scaffold-Based on AAc/GO/nHAp/TiO2 Nanocomposite for Bone Tissue Engineering: In-Vitro Analysis

Nanomaterials ◽

10.3390/nano11051319 ◽

2021 ◽

Vol 11 (5) ◽

pp. 1319

Author(s):

Muhammad Umar Aslam Khan ◽

Wafa Shamsan Al-Arjan ◽

Mona Saad Binkadem ◽

Hassan Mehboob ◽

Adnan Haider ◽

...

Keyword(s):

Mechanical Properties ◽

Tissue Engineering ◽

Bone Tissue Engineering ◽

Bone Tissue ◽

Guar Gum ◽

Porous Scaffolds ◽

Vitro Assay ◽

Vitro Analysis ◽

Nanocomposite Scaffolds

Bone tissue engineering is an advanced field for treatment of fractured bones to restore/regulate biological functions. Biopolymeric/bioceramic-based hybrid nanocomposite scaffolds are potential biomaterials for bone tissue because of biodegradable and biocompatible characteristics. We report synthesis of nanocomposite based on acrylic acid (AAc)/guar gum (GG), nano-hydroxyapatite (HAp NPs), titanium nanoparticles (TiO2 NPs), and optimum graphene oxide (GO) amount via free radical polymerization method. Porous scaffolds were fabricated through freeze-drying technique and coated with silver sulphadiazine. Different techniques were used to investigate functional group, crystal structural properties, morphology/elemental properties, porosity, and mechanical properties of fabricated scaffolds. Results show that increasing amount of TiO2 in combination with optimized GO has improved physicochemical and microstructural properties, mechanical properties (compressive strength (2.96 to 13.31 MPa) and Young’s modulus (39.56 to 300.81 MPa)), and porous properties (pore size (256.11 to 107.42 μm) and porosity (79.97 to 44.32%)). After 150 min, silver sulfadiazine release was found to be ~94.1%. In vitro assay of scaffolds also exhibited promising results against mouse pre-osteoblast (MC3T3-E1) cell lines. Hence, these fabricated scaffolds would be potential biomaterials for bone tissue engineering in biomedical engineering.

Download Full-text

Three-dimensionally printed polycaprolactone/multicomponent bioactive glass scaffolds for potential application in bone tissue engineering

Biomedical glasses ◽

10.1515/bglass-2020-0006 ◽

2020 ◽

Vol 6 (1) ◽

pp. 57-69

Author(s):

Amirhosein Fathi ◽

Farzad Kermani ◽

Aliasghar Behnamghader ◽

Sara Banijamali ◽

Masoud Mozafari ◽

...

Keyword(s):

Tissue Engineering ◽

3D Printing ◽

Bone Tissue Engineering ◽

Bone Tissue ◽

Three Dimensional ◽

Layer By Layer ◽

Composite Scaffolds ◽

3D Printed ◽

Co Doped

AbstractOver the last years, three-dimensional (3D) printing has been successfully applied to produce suitable substitutes for treating bone defects. In this work, 3D printed composite scaffolds of polycaprolactone (PCL) and strontium (Sr)- and cobalt (Co)-doped multi-component melt-derived bioactive glasses (BGs) were prepared for bone tissue engineering strategies. For this purpose, 30% of as-prepared BG particles (size <38 μm) were incorporated into PCL, and then the obtained composite mix was introduced into a 3D printing machine to fabricate layer-by-layer porous structures with the size of 12 × 12 × 2 mm3.The scaffolds were fully characterized through a series of physico-chemical and biological assays. Adding the BGs to PCL led to an improvement in the compressive strength of the fabricated scaffolds and increased their hydrophilicity. Furthermore, the PCL/BG scaffolds showed apatite-forming ability (i.e., bioactivity behavior) after being immersed in simulated body fluid (SBF). The in vitro cellular examinations revealed the cytocompatibility of the scaffolds and confirmed them as suitable substrates for the adhesion and proliferation of MG-63 osteosarcoma cells. In conclusion, 3D printed composite scaffolds made of PCL and Sr- and Co-doped BGs might be potentially-beneficial bone replacements, and the achieved results motivate further research on these materials.

Download Full-text