Woodallite, a new chromium analogue of iowaite from the Mount Keith nickel deposit, Western Australia

2001 ◽  
Vol 65 (3) ◽  
pp. 427-435 ◽  
Author(s):  
B. A. Grguric ◽  
I. C. Madsen ◽  
A. Pring
Keyword(s):  
Weight Loss ◽  
Western Australia ◽  
New Mineral ◽  
Low Grade ◽  
Interlayer Water ◽  
Nickel Deposit ◽  
X Ray ◽  
Mount Keith ◽  
Mohs Hardness ◽  
Hydroxide Water

AbstractWoodallite is a new Cr-rich member of the hydrotalcite group from the large, low-grade Mount Keith nickel deposit, in the northeastern Goldfields district of Western Australia. Woodallite occurs as whorls and clusters of minute platelets up to 6 mm across in lizardite+brucite-altered dunite. Individual platelets are typically 10–100 µm in maximum dimension and are often curved. Associated minerals include chromite, lizardite, iowaite, pentlandite, magnetite, tochilinite and brucite. Electron microprobe analysis gave: Mg 25.90 wt.%; Cr 10.81; Fe 4.86; Al 0.68; Cl 9.89; S 0.03; Si 0.01; Ni 0.01; Na 0.01, yielding (after correction for loss of volatiles) an empirical formula of Mg6.19(Cr1.21Fe0.51Al0.15)∑1.87(OH)16[Cl1.62(CO3)0.17(SO4)0.01]·4H2O, by analogy with the hydrotalcite group. The simplified formula is Mg6Cr2(OH)16Cl2·4H2O. Combined thermogravimetric analysis and mass spectroscopy showed a two-stage weight loss of 12.7% and 27.3% occurring over the ranges 25–300°C and 300–660°C, respectively. The first weight loss is attributed to loss of interlayer water, chlorine-bearing species (e.g. HCl) and some CO2, the second to loss of hydroxide water, remaining CO2 and Cl species. The mineral is deep magenta to purple in colour, transparent, with a resinous to waxy lustre, and a perfect basal {0001} cleavage. Woodallite has a Mohs hardness of 1.5–2, and a pale-pink to white streak. The strongest lines in the X-ray powder pattern are [dobs (Iobs) (hkl)] 8.037 (100) (003); 4.021 (48) (006); 2.679 (1) (009); 2.624 (3) (012); 2.349 (5) (015); 2.007 (6) (0,0,12); 1.698 (2) (0,1,11); 1.524 (2) (21̄3). These lines were indexed on a hexagonal cell with a = 3.103(2), c = 24.111(24)Å, V = 201.14 Å3 and Z = 3/8. The new mineral is isostructural with the hydrotalcite group and has space group R3̄m. The measured density is 2.062 gm/cm3. Woodallite is uniaxial negative with ω = 1.555 and ε = 1.535 (white light); pleochroism is distinct from violet to pinkish lilac. Woodallite forms as a result of hydrothermal alteration of primary magmatic chromite by Clrich solutions at temperatures <320°C. Relict chromite fragments are frequently present in the whorls, and associated magnetite is altered extensively to iowaite. The mineral is named after Roy Woodall, eminent Australian industry geologist.

Putnisite, SrCa4Cr83+ (CO3)8SO4(OH)16·25H2O, a new mineral from Western Australia: description and crystal structure

2014 ◽  
Vol 78 (1) ◽  
pp. 131-144 ◽  
Author(s):  
P. Elliott ◽  
G. Giester ◽  
R. Rowe ◽  
A. Pring
Keyword(s):  
Crystal Structure ◽  
Single Crystal ◽  
Western Australia ◽  
Empirical Formula ◽  
New Mineral ◽  
Orthorhombic Space Group ◽  
Calculated Density ◽  
X Ray ◽  
Area Detector ◽  
Mohs Hardness

AbstractPutnisite, SrCa4Cr83+ (CO7)8SO4(OH)16·25H2O, is a new mineral from the Polar Bear peninsula, Southern Lake Cowan, Western Australia, Australia. The mineral forms isolated pseudocubic crystals up to 0.5 mm in size in a matrix composed of quartz and a near amorphous Cr silicate. Putnisite is translucent, with a pink streak and vitreous lustre. It is brittle and shows one excellent and two good cleavages parallel to {100}, {010} and {001}. The fracture is uneven and the Mohs hardness 1½−2. The measured density is 2.20(3) g/cm3 and the calculated density based on the empirical formula is 2.23 g/cm3. Optically, putnisite is biaxial negative, with α = 1.552(3), β = 1.583(3) and γ = 1.599(3) (measured in white light). The optical orientation is uncertain and pleochroism is distinct: X pale bluish grey, Y pale purple, Z pale purple. Putnisite is orthorhombic, space group Pnma, with a = 15.351(3), b = 20.421(4) Å, c = 18.270(4) Å, V = 5727(2) Å3 (single-crystal data), and Z = 4. The strongest five lines in the X-ray powder diffraction pattern are [d(Å)(I)(hkl)]: 13.577 (100) (011), 7.659 (80) (200), 6.667 (43) (211), 5.084 (19) (222, 230), 3.689 (16) (411). Electron microprobe analysis (EMPA) gave (wt.%): Na2O 0.17, MgO 0.08, CaO 10.81, SrO 5.72, BaO 0.12, CuO 0.29, Cr2O3 31.13, SO3 3.95, SiO2 0.08, Cl− 0.28, CO2calc 17.94, H2Ocalc 30.30, O=Cl−0.06, total 100.81. The empirical formula, based on O + Cl = 69, is: Cr8.023+Ca3.78Sr1.08Na0.11Cu0.072+Mg0.04Ba0.02[(SO4)0.96(SiO4)0.03]0.99 (CO3)7.98(OH)16.19Cl0.15·24.84H2O. The crystal structure was determined from single-crystal X-ray diffraction data (MoKα, CCD area detector and refined to R1 = 5.84% for 3181 reflections with F0 > 4σF. Cr(OH)4O2 octahedra link by edge-sharing to form an eight-membered ring. A 10-coordinated Sr2+ cation lies at the centre of each ring. The rings are decorated by CO3 triangles, each of which links by corner-sharing to two Cr(OH)4O2 octahedra. Rings are linked by Ca(H2O)4O4 polyhedra to form a sheet parallel to (100). Adjacent sheets are joined along [100] by corner-sharing SO4 tetrahedra. H2O molecules occupy channels that run along [100] and interstices between slabs. Moderate to weak hydrogen bonding provides additional linkage between slabs.

Hingganite-(Nd), Nd2□Be2Si2O8(OH)2, a new gadolinite-supergroup mineral from Zagi Mountain, Pakistan

2020 ◽  
Vol 58 (5) ◽  
pp. 549-562
Author(s):  
Anatoly V. Kasatkin ◽  
Fabrizio Nestola ◽  
Radek Škoda ◽  
Nikita V. Chukanov ◽  
Atali A. Agakhanov ◽  
...  
Keyword(s):  
New Mineral ◽  
Monoclinic Space Group ◽  
X Ray Diffraction ◽  
Average Chemical Composition ◽  
X Ray ◽  
Conchoidal Fracture ◽  
Icp Ms ◽  
Optical Axes ◽  
Mohs Hardness ◽  
Khyber Pakhtunkhwa Province

ABSTRACT Hingganite-(Nd), ideally Nd2□Be2Si2O8(OH)2, is a new gadolinite group, gadolinite supergroup mineral discovered at Zagi Mountain, near Kafoor Dheri, about 4 km S of Warsak and 30 km NW of Peshawar, Khyber Pakhtunkhwa Province, Pakistan. The new mineral forms zones measuring up to 1 × 1 mm2 in loose prismatic crystals up to 0.7 cm long, where it is intergrown with hingganite-(Y). Other associated minerals include aegirine, microcline, fergusonite-(Y), and zircon. Hingganite-(Nd) is dark greenish-brown, transparent, has vitreous luster and a white streak. It is brittle and has a conchoidal fracture. No cleavage or parting are observed. Mohs hardness is 5½–6. Dcalc. = 4.690 g/cm3. Hingganite-(Nd) is non-pleochroic, optically biaxial (+), α = 1.746(5), β = 1.766(5), γ = 1.792(6) (589 nm). 2Vmeas. = 80(7)°; 2Vcalc. = 84°. Dispersion of optical axes was not observed. The average chemical composition of hingganite-(Nd) is as follows (wt.%; electron microprobe, BeO, B2O3, and Lu2O3 content measured by LA-ICP-MS; H2O calculated by stoichiometry): BeO 9.64, CaO 0.45, MnO 0.10, FeO 3.03, B2O3 0.42, Y2O3 8.75, La2O3 1.63, Ce2O3 12.89, Pr2O3 3.09, Nd2O3 16.90, Sm2O3 5.97, Eu2O3 1.08, Gd2O3 5.15, Tb2O3 0.50, Dy2O3 2.50, Ho2O3 0.33, Er2O3 0.84, Tm2O3 0.10, Yb2O3 0.44, Lu2O3 0.04, ThO2 0.13, SiO2 23.55, H2O 2.72, total 100.25. The empirical formula calculated on the basis of 2 Si apfu is (Nd0.513Ce0.401Y0.395Sm0.175Gd0.145Pr0.096Dy0.068La0.051Ca0.041Eu0.031Er0.022Tb0.014Yb0.011Ho0.009Tm0.003Th0.003Lu0.001)Σ1.979(□0.778Fe2+0.215Mn0.007)Σ1.000(Be1.967B0.062)Σ2.029Si2O8.46(OH)1.54. Hingganite-(Nd) is monoclinic, space group P21/c with a = 4.77193(15), b = 7.6422(2), c = 9.9299(2) Å, β = 89.851(2)°, V = 362.123(14) Å3, and Z = 2. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 6.105 (95) (011), 4.959 (56) (002), 4.773 (100) (100), 3.462 (58) (102), 3.122 , 3.028 (61) (013), 2.864 (87) (121), 2.573 (89) (113). The crystal structure of hingganite-(Nd) was refined from single-crystal X-ray diffraction data to R = 0.034 for 2007 unique reflections with I &gt; 2σ(I). The new mineral is named as an analogue of hingganite-(Y), hingganite-(Yb), and hingganite-(Ce), but with Nd dominant among the rare earth elements.

Dalnegroite, Tl5–xPb2x(As,Sb)2l–xS34, a new thallium sulphosalt from Lengenbach quarry, Binntal, Switzerland

2009 ◽  
Vol 73 (6) ◽  
pp. 1027-1032 ◽  
Author(s):  
F. Nestola ◽  
A. Guastoni ◽  
L. Bindi ◽  
L. Secco
Keyword(s):  
Polarized Light ◽  
New Mineral ◽  
X Ray Diffraction ◽  
X Ray ◽  
Elemental Concentrations ◽  
Reflected Light ◽  
Mohs Hardness ◽  
The Mean ◽  
The University ◽  
Probable Space

AbstractDalnegroite, ideally Tl4Pb2(As12Sb8)Σ20S34, is a new mineral from Lengenbach, Binntal, Switzerland. It occurs as anhedral to subhedral grains up to 200 μm across, closely associated with realgar, pyrite, Sb-rich seligmanite in a gangue of dolomite. Dalnegroite is opaque with a submetallic lustre and shows a brownish-red streak. It is brittle; the Vickers hardness (VHN25) is 87 kg mm-2(range: 69—101) (Mohs hardness ∼3—3½). In reflected light, dalnegroite is highly bireflectant and weakly pleochroic, from white to a slightly greenish-grey. In cross-polarized light, it is highly anisotropic with bluish to green rotation tints and red internal reflections.According to chemical and X-ray diffraction data, dalnegroite appears to be isotypic with chabournéite, Tl5-xPb2x(Sb,As)21-xS34. It is triclinic, probable space groupP1, witha= 16.217(7) Å,b= 42.544(9) Å,c= 8.557(4) Å, α = 95.72(4)°, β = 90.25(4)°, γ = 96.78(4)°,V= 5832(4) Å3,Z= 4.The nine strongest powder-diffraction lines [d(Å) (I/I0) (hkl)] are: 3.927 (100) (10 0); 3.775 (45) (22); 3.685 (45) (60); 3.620 (50) (440); 3.124 (50) (2); 2.929 (60) (42); 2.850 (70) (42); 2.579 (45) (02); 2.097 (60) (024). The mean of 11 electron microprobe analyses gave elemental concentrations as follows: Pb 10.09(1) wt.%, Tl 20.36(1), Sb 23.95(1), As 21.33(8), S 26.16(8), totalling 101.95 wt.%, corresponding to Tl4.15Pb2.03(As11.86Sb8.20)S34. The new mineral is named for Alberto Dal Negro, Professor in Mineralogy and Crystallography at the University of Padova since 1976.

Hrabákite, Ni9PbSbS8, a new member of the hauchecornite group from Příbram, Czech Republic

2021 ◽  
pp. 1-8
Author(s):  
Jiří Sejkora ◽  
Pavel Škácha ◽  
Jakub Plášil ◽  
Zdeněk Dolníček ◽  
Jana Ulmanová
Keyword(s):  
Czech Republic ◽  
Diffraction Data ◽  
New Mineral ◽  
X Ray Diffraction ◽  
Calculated Density ◽  
X Ray ◽  
Reflected Light ◽  
Mohs Hardness ◽  
Cation Sites ◽  
The Ideal

Abstract The new mineral hrabákite (IMA2020-034) was found in siderite–sphalerite gangue with minor dolomite–ankerite at the dump of shaft No. 9, one of the mines in the abandoned Příbram uranium and base-metal district, central Bohemia, Czech Republic. Hrabákite is associated with Pb-rich tučekite, Hg-rich silver, stephanite, nickeline, millerite, gersdorffite, sphalerite and galena. The new mineral occurs as rare prismatic crystals up to 120 μm in size and allotriomorphic grains. Hrabákite is grey with a brownish tint. Mohs hardness is ca. 5–6; the calculated density is 6.37 g.cm–3. In reflected light, hrabákite is grey with a brown hue. Bireflectance is weak and pleochroism was not observed. Anisotropy under crossed polars is very weak (brownish tints) to absent. Internal reflections were not observed. Reflectance values of hrabákite in air (Rmin–Rmax, %) are: 39.6–42.5 at 470 nm, 45.0–47.5 at 546 nm, 46.9–49.2 at 589 nm and 48.9–51.2 at 650 nm). The empirical formula for hrabákite, based on electron-microprobe analyses (n = 11), is (Ni8.91Co0.09Fe0.03)9.03(Pb0.94Hg0.04)0.98(Sb0.91As0.08)0.99S7.99. The ideal formula is Ni9PbSbS8, which requires Ni 47.44, Pb 18.60, Sb 10.93 and S 23.03, total of 100.00 wt.%. Hrabákite is tetragonal, P4/mmm, a = 7.3085(4), c = 5.3969(3) Å, with V = 288.27(3) Å3 and Z = 1. The strongest reflections of the calculated powder X-ray diffraction pattern [d, Å (I)(hkl)] are: 3.6543(57)(200); 3.2685(68)(210); 2.7957(100)(211); 2.3920(87)(112); 2.3112(78)(310); 1.8663(74)(222); and 1.8083(71)(302). According to the single-crystal X-ray diffraction data (Rint = 0.0218), the unit cell of hrabákite is undoubtedly similar to the cell reported for tučekite. The structure contains four metal cation sites, two Sb (Sb1 dominated by Pb2+) and two Ni (with minor Co2+ content) sites. The close similarity in metrics between hrabákite and tučekite is due to similar bond lengths of Pb–S and Sb–S pairs. Hrabákite is named after Josef Hrabák, the former professor of the Příbram Mining College.

scholarly journals Parisite-(La), ideally CaLa2(CO3)3F2, a new mineral from Novo Horizonte, Bahia, Brazil

2018 ◽  
Vol 82 (1) ◽  
pp. 133-144 ◽  
Author(s):  
Luiz A. D. Menezes Filho ◽  
Mario L. S. C. Chaves ◽  
Nikita V. Chukanov ◽  
Daniel Atencio ◽  
Ricardo Scholz ◽  
...  
Keyword(s):  
Single Crystal ◽  
Ir Spectrum ◽  
Empirical Formula ◽  
New Mineral ◽  
Formula Unit ◽  
Calculated Density ◽  
Oh Groups ◽  
Space Group ◽  
X Ray ◽  
Mohs Hardness

ABSTRACTParisite-(La) (IMA2016-031), ideally CaLa2(CO3)3F2, occurs in a hydrothermal vein crosscutting a metarhyolite of the Rio dos Remédios Group, at the Mula mine, Tapera village, Novo Horizonte county, Bahia, Brazil, associated with hematite, rutile, almeidaite, fluocerite-(Ce), brockite, monazite-(La), rhabdophane-(La) and bastnäsite-(La). Parisite-(La) occurs as residual nuclei (up to 5 mm) in steep doubly-terminated pseudo-hexagonal pyramidal crystals (up to 8.2 cm). Parisite-(La) is transparent, yellow-green to white, with a white streak and displays a vitreous (when yellow-green) to dull (when white) lustre. Cleavage is distinct on pseudo-{001}; fracture is laminated, conchoidal, or uneven. The Mohs hardness is 4 to 5, and it is brittle. Calculated density is 4.273 g cm−3. Parisite-(La) is pseudo-uniaxial (+), ω = 1.670(2) and ε = 1.782(5) (589 nm). The empirical formula normalized on the basis of 11 (O + F) atoms per formula unit (apfu) is Ca0.98(La0.83Nd0.51Ce0.37Pr0.16Sm0.04Y0.03)Σ1.94C3.03O8.91F2.09. The IR spectrum confirms the absence of OH groups. Single-crystal X-ray studies gave the following results: monoclinic (pseudo-trigonal), space group: C2, Cm, or C2/m, a = 12.356(1) Å, b = 7.1368(7) Å, c = 28.299(3) Å, β = 98.342(4)°, V = 2469.1(4) Å3 and Z = 12. Parisite-(La) is the La-dominant analogue of parisite-(Ce).

Sergevanite, Na15(Ca3Mn3)(Na2Fe)Zr3Si26O72(OH)3·H2O, a new eudialyte-group mineral from the Lovozero alkaline massif, Kola Peninsula

2020 ◽  
Vol 58 (4) ◽  
pp. 421-436 ◽  
Author(s):  
Nikita V. Chukanov ◽  
Sergey M. Aksenov ◽  
Igor V. Pekov ◽  
Dmitriy I. Belakovskiy ◽  
Svetlana A. Vozchikova ◽  
...  
Keyword(s):  
Kola Peninsula ◽  
Structural Data ◽  
New Mineral ◽  
X Ray Diffraction ◽  
Calculated Density ◽  
Eudialyte Group ◽  
Group Mineral ◽  
X Ray ◽  
Mohs Hardness ◽  
Alkaline Massif

ABSTRACT The new eudialyte-group mineral sergevanite, ideally Na15(Ca3Mn3)(Na2Fe)Zr3Si26O72(OH)3·H2O, was discovered in highly agpaitic foyaite from the Karnasurt Mountain, Lovozero alkaline massif, Kola Peninsula, Russia. The associated minerals are microcline, albite, nepheline, arfvedsonite, aegirine, lamprophyllite, fluorapatite, steenstrupine-(Ce), ilmenite, and sphalerite. Sergevanite forms yellow to orange-yellow anhedral grains up to 1.5 mm across and the outer zones of some grains of associated eudialyte. Its luster is vitreous, and the streak is white. No cleavage is observed. The Mohs' hardness is 5. Density measured by equilibration in heavy liquids is 2.90(1) g/cm3. Calculated density is equal to 2.906 g/cm3. Sergevanite is nonpleochroic, optically uniaxial, positive, with ω = 1.604(2) and ε = 1.607(2) (λ = 589 nm). The infrared spectrum is given. The chemical composition of sergevanite is (wt.%; electron microprobe, H2O determined by HCN analysis): Na2O 13.69, K2O 1.40, CaO 7.66, La2O3 0.90, Ce2O3 1.41, Pr2O3 0.33, Nd2O3 0.64, Sm2O3 0.14, MnO 4.15, FeO 1.34, TiO2 1.19, ZrO2 10.67, HfO2 0.29, Nb2O5 1.63, SiO2 49.61, SO3 0.77, Cl 0.23, H2O 4.22, –O=Cl –0.05, total 100.22. The empirical formula (based on 25.5 Si atoms pfu, in accordance with structural data) is H14.46Na13.64K0.92Ca4.22Ce0.27La0.17Nd0.12Pr0.06Sm0.02Mn1.81Fe2+0.58Ti0.46Zr2.67Hf0.04Nb0.38Si25.5S0.30Cl0.20O81.35. The crystal structure was determined using single-crystal X-ray diffraction data. The new mineral is trigonal, space group R3, with a = 14.2179(1) Å, c = 30.3492(3) Å, V = 5313.11(7) Å3, and Z = 3. In the structure of sergevanite, Ca and Mn are ordered in the six-membered ring of octahedra (at the sites M11 and M12), and Na dominates over Fe2+ at the M2 site. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 7.12 (70) (110), 5.711 (43) (202), 4.321 (72) (205), 3.806 (39) (033), 3.551 (39) (220, 027), 3.398 (39) (313), 2.978 (95) (), 2.855 (100) (404). Sergevanite is named after the Sergevan' River, which is near the discovery locality.

Pseudomeisserite-(NH4), a new mineral with a novel uranyl-sulfate linkage from the Blue Lizard mine, San Juan County, Utah, USA

2020 ◽  
Vol 84 (3) ◽  
pp. 435-443
Author(s):  
Anthony R. Kampf ◽  
Travis A. Olds ◽  
Jakub Plášil ◽  
Barbara P. Nash ◽  
Joe Marty
Keyword(s):  
New Mineral ◽  
San Juan ◽  
Optical Orientation ◽  
Uranyl Sulfate ◽  
X Ray ◽  
Pale Yellow ◽  
Light Yellow ◽  
Perfect Cleavage ◽  
Mohs Hardness ◽  
San Juan County

AbstractThe new mineral pseudomeisserite-(NH4) (IMA2018-166), (NH4,K)2Na4[(UO2)2(SO4)5]⋅4H2O, was found in the Blue Lizard mine, San Juan County, Utah, USA, where it occurs as light yellow prisms in a secondary assemblage with belakovskiite, blödite, changoite, ferrinatrite, gypsum, ivsite, metavoltine and tamarugite. The streak is very pale yellow and the fluorescence is bright lime green under 405 nm ultraviolet light. Crystals are transparent with vitreous lustre. The tenacity is brittle, the Mohs hardness is 2½, the fracture is curved or conchoidal and there is one perfect cleavage on {100}. The mineral is easily soluble in H2O and has a measured density of 3.22(2) g⋅cm–3. Pseudomeisserite-(NH4) is optically biaxial (–) with α = 1.536(2), β = 1.559(2) and γ = 1.565(2) (white light); 2Vmeas. = 53(1)°; dispersion is r > v, distinct; pleochroism: X colourless, Y light yellow and Z pale yellow (X < Z < Y); optical orientation: Z = b, Y ∧ c = 33° in obtuse β). Electron microprobe analyses (WDS mode) provided (NH4)1.49K0.60Na3.87U2.00S5.04O28H7.78. The five strongest X-ray powder diffraction lines are [dobs, Å(I)(hkl)]: 12.69(76)(100), 6.83(84)(012,102), 6.01(100)($\bar{2}$02), 3.959(67)($\bar{2}$21,$\bar{2}$14,$\bar{1}$23) and 3.135(76)($\bar{2}$06,223,$\bar{1}$16). Pseudomeisserite-(NH4) is monoclinic, P21/c, a = 13.1010(3), b = 10.0948(2), c = 19.4945(14) Å, β = 104.285(7)°, V = 2498.5(2) Å3 and Z = 4. The structural unit in the structure (R1 = 0.0254 for 3837 I > 2σI reflections) is a novel [(UO2)2(SO4)5]6– uranyl-sulfate band.

Bassoite, SrV3O7·4H2O, a new mineral from Molinello mine, Val Graveglia, eastern Liguria, Italy

2011 ◽  
Vol 75 (5) ◽  
pp. 2677-2686 ◽  
Author(s):  
L. Bindi ◽  
C. Carbone ◽  
R. Cabella ◽  
G. Lucchetti
Keyword(s):  
Structure Refinement ◽  
Full Professor ◽  
New Mineral ◽  
Monoclinic Space Group ◽  
Calculated Density ◽  
X Ray ◽  
Cell Parameters ◽  
Mohs Hardness ◽  
Dark Green ◽  
The University

AbstractBassoite, ideally SrV3O7·4H2O, is a new mineral from the Molinello manganese mine, Val Graveglia. eastern Liguria, northern Apennines, Italy. It occurs as black euhedral to subhedral grains up to 400 urn across, closely associated with rhodonite, quartz and braunite. Bassoite is opaque with a sub-metallic lustre and a black streak. It is brittle and neither fracture nor cleavage was observed; the Vickers micro-hardness (VHN100) is 150 kg/mm (range 142—165; corresponding to a Mohs hardness of 4—41/2). The calculated density is 2.940 g/cm3 (on the basis of the empirical formula and X-ray single-crystal data). Bassoite is weakly bireflectant and very weakly pleochroic from grey to a dark green. Internal reflections are absent. The mineral is anisotropic, without characteristic rotation tints. Reflectance percentages (Rmin and Rmax) for the four standard COM wavelengths are 18.5%, 19.0% (471.1 nm); 17.2%, 17.8% (548.3 nm); 16.8%, 17.5% (586.6 nm) and 16.2%, 16.8% (652.3 nm), respectively.Bassoite is monoclinic, space group P21/m, with unit-cell parameters: a = 5.313(3) Å, b = 10.495(3) Å, c = 8.568(4) Å, β = 91.14(5)°, V= 477.7(4) Å3, a:b:c = 0.506:1:0.816, and Z = 2. The crystal structure was refined to R1 = 0.0209 for 1148 reflections with Fo > 4σ(Fo) and it consists of layers of VO5 pyramids (with vanadium in the tetravalent state) pointing up and down alternately with Sr between the layers (in nine-fold coordination). The nine most intense X-ray powder-diffraction lines [d in Å (I/I0) (hkt)] are: 8.5663 (100) (001); 6.6363 (14) (011); 3.4399 (14) (1̄21); 3.4049 (17) (121); 2.8339 (15) (1̄22); 2.7949 (11) (122); 2.6550 (15) (200); 2.6237 (11) (040) and 1.8666 (15) (240). Electron microprobe analyses produce a chemical formula (Sr0.97Ca0.02Na0.01)V3.00O74H20, on the basis of 2(Sr+Ca+Na) = 1, taking the results of the structure refinement into account. The presence of water molecules was confirmed by micro-Raman spectroscopy. The name honours Riccardo Basso (b. 1947), full professor of Mineralogy and Crystallography at the University of Genova. The new mineral and mineral name have been approved by the Commission on New Minerals, Nomenclature and Classification, IMA (2011-028).

scholarly journals Fogoite-(Y), Na3Ca2Y2Ti(Si2O7)2OF3, a Group I TS-block mineral from the Lagoa do Fogo, the Fogo volcano, São Miguel Island, the Azores: Description and crystal structure

2017 ◽  
Vol 81 (2) ◽  
pp. 369-381 ◽  
Author(s):  
F. Cámara ◽  
E. Sokolova ◽  
Y. A. Abdu ◽  
F. C. Hawthorne ◽  
T. Charrier ◽  
...  
Keyword(s):  
Crystal Structure ◽  
New Mineral ◽  
X Ray Diffraction ◽  
Titanium Silicate ◽  
Triclinic Space Group ◽  
X Ray ◽  
Group I ◽  
Mohs Hardness ◽  
Fogo Volcano ◽  
The Ideal

AbstractFogoite-(Y), Na3Ca2Y2Ti(Si2O7)2OF3, is a new mineral from the Lagoa do Fogo, São Miguel Island, the Azores. It occurs in cavities as highly elongated (on [001]) prisms, up to 2000 μm long and 50 μm× 50 μm in cross-section, associated with sanidine, astrophyllite, fluornatropyrochlore, ferrokentbrooksite, quartz and ferro-katophorite. Crystals are generally transparent and colourless, with vitreous lustre, occasionally creamy white. Fogoite-(Y) has a white streak, splintery fracture and very good {100} cleavage. Mohs hardness is ∼5. Dcalc. = 3.523 g/cm3. It is biaxial (+) with refractive indices (λ = 590 nm) α = 1.686(2), β = 1.690(2), γ = 1.702(5); 2Vmeas. = 57(1)° and 2Vcalc. = 60°. It is nonpleochroic. Fogoite-(Y) is triclinic, space group P1, a = 9.575(6), b = 5.685(4), c = 7.279(5) Å, α = 89.985(6), β = 100.933(4), γ = 101.300(5)°, V = 381.2 (7) Å3. The six strongest reflections in the powder X-ray diffraction data [d (Å), I, (hkl)] are: 2.954, 100, (1̄1̄2, 3̄10); 3.069, 42, (300, 01̄2); 2.486, 24, (310, 21̄2); 3.960, 23, (1̄1̄1, 2̄10); 2.626, 21, (2̄20); 1.820, 20, (1̄04). Electron microprobe analysis gave the following empirical formula calculated on 18 (O + F) (Na2.74Mn0.15)∑2.89Ca2[Y1.21(La0.01Ce0.03Nd0.03Sm0.02Gd0.08Dy0.08Er0.05Yb0.04Lu0.01)∑0.35Mn0.16Zr0.11Na0.09Fe0.072+Ca0.01]∑2(Ti0.76Nb0.23Ta0.01)∑1(Si4.03O14)O1.12F2.88, Z = 1. The crystal structure was refined on a twinnedcrystal to R1 = 2.81% on the basis of 2157 unique reflections (Fo > 4σFo) and is a framework of TS (Titanium Silicate) blocks, which consist of HOH sheets (H – heteropolyhedral, O – octahedral) parallel to (100). In the O sheet, the the [6]MO(1) site is occupied mainly by Ti, <MO(1)–ϕ> = 1.980 Å, and the [6]MO(2) and [6]MO(3) sites are occupied by Na and Na plus minor Mn, <MO(2)–ϕ>= 2.490 Å and <MO(3)–ϕ> = 2.378 Å. In the H sheet, the two [4]Si sites are occupied by Si, with <Si–O> = 1.623 Å; the [6]MH site is occupied by Y and rare-earth elements (Y > REE), with minor Mn, Zr, Na, Fe2+ and Ca, <MH–ϕ> = 2.271 Å and the [6]AP site is occupied by Ca, <AP–ϕ> = 2.416 Å. The MH and AP octahedra and Si2O7 groups constitute the H sheet. The ideal compositions of the O and two H sheets are Na3Ti(OF)F2 and Y2Ca2(Si2O7)2 apfu. Fogoite-(Y) is isostructural with götzenite and hainite. The mineral is named after the type locality, the Fogo volcano in the Azores.

Natropharmacoalumite, NaAl4[(OH)4(AsO4)3].4H2O, a new mineral of the pharmacosiderite supergroup and the renaming of aluminopharmacosiderite to pharmacoalumite

2010 ◽  
Vol 74 (5) ◽  
pp. 929-936 ◽  
Author(s):  
M. S. Rumsey ◽  
S. J. Mills ◽  
J. Spratt
Keyword(s):  
Empirical Formula ◽  
Direct Methods ◽  
Structure Type ◽  
New Mineral ◽  
Gold Mine ◽  
Nomenclature System ◽  
Cubic Crystals ◽  
X Ray ◽  
Mohs Hardness ◽  
Dominant Cation

AbstractNatropharmacoalumite, ideally NaAl4[(OH)4(AsO4)3]·4H2O, is a new mineral from the Maria Josefa Gold mine, Rodalquilar, Andalusia region, Spain. It occurs as colourless, intergrown cubic crystals with chenevixite, kaolinite, jarosite and indeterminable mixtures of Fe and Sb oxyhydroxides. Individual crystals are up to 0.5 mm on edge, although crystals are more commonly ˜0.25 mm across and occur in patchy aggregates several millimetres across. The mineral is transparent with a vitreous to adamantine lustre. It is brittle with an imperfect cleavage, irregular fracture and a white streak. The Mohs hardness is ˜2.5 with a calculated densityof 2.56 g cm–3 for the empirical formula. Electron microprobe analyses yielded Na2O 2.52%, K2O 1.49%, Al2O3 29.50%, As2O5 48.84% and H2O was calculated in line with the structural analysis as 16.28% totalling 98.63%. The empirical formula, based upon 20.21 oxygen atoms, is [Na0.57K0.22(H3O)0.21]Σ1.00Al4.05(As2.97O12)(OH)4·4H2O. The five strongest lines in the X-ray powder diffraction pattern are [dobs(Å), Iobs,(hkl)]: 7.759,100,(100); 4.473,40,(111); 3.870,50,(200); 2.446,9,(301); 2.331,12,(311). Natropharmacoalumite is cubic, space group with a = 7.7280(3) Å, V = 461.53(3) Å3 and Z = 1. The crystal structure was solved by direct methods and refined to R1 = 0.063 for 295 reflections with F>4σ(F). The structure conforms broadly to that of the general pharmacosiderite structure type, with Na as the dominant cation in cavities of strongly distorted Al octahedra and As tetrahedra. A new group nomenclature system for minerals with the pharmacosiderite structure has been established, including the renaming of aluminopharmacosiderite to pharmacoalumite.

Sign in / Sign up

Export Citation Format

Share Document