Synthesis of Fe-rich Fe–Al nanocrystalline solid solutions using ball milling

1999 ◽  
Vol 14 (5) ◽  
pp. 1760-1770 ◽  
Author(s):  
H. G. Jiang ◽  
H. M. Hu ◽  
E. J. Lavernia
Keyword(s):  
Heat Treatment ◽  
Activation Energy ◽  
Thermal Stability ◽  
Intermetallic Compound ◽  
Ball Milling ◽  
Microstructural Evolution ◽  
Solid Solutions ◽  
Al Alloys ◽  
Time Intervals ◽  
Thermal Stability Of

The synthesis of nanocrystalline Fe, Fe–4 wt% Al, and Fe–10 wt% Al solid solutions by SPEX ball milling has been studied. The microstructural evolution during ball milling, as well as subsequent heat treatment, has been characterized. The results demonstrate that ball milling promotes the formation of αFe–4 wt% Al and αFe–10 wt% Al solid solutions by reducing the activation energy of these alloys and generating thermal energy during this process. For Fe–10 wt% Al powders milled for various time intervals up to approximately 20 min, the FeAl intermetallic compound is formed. For alloys annealed at temperatures ranging from 600 to 1000 °C, the addition of 10 wt% Al to Fe significantly enhances the thermal stability of the nanocrystalline Fe–Al alloys. Interestingly, the addition of Al within the range of 4–10 wt% seems to have little effect on the thermal stability of these alloys annealed under the same conditions. Also, the thermal stability improves for alloys milled in air as opposed to those processed using Ar.

Thermal stability of phase-separated nanograin structure during heat treatment

2021 ◽  
Vol 875 ◽  
pp. 160055
Author(s):  
Hua Guo ◽  
Fawei Tang ◽  
Yong Liu ◽  
Zhi Zhao ◽  
Hao Lu ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Thermal Stability ◽  
Thermal Stability Of

scholarly journals Effect of alloying elements on thermal stability of nanocrystalline Al alloys

2021 ◽  
Vol 31 (1) ◽  
pp. 11-23
Author(s):  
Hany Rizk AMMAR ◽  
Muneer BAIG ◽  
Asiful Hossain SEIKH ◽  
Jabair Ali MOHAMMED
Keyword(s):  
Thermal Stability ◽  
Al Alloys ◽  
Alloying Elements ◽  
Thermal Stability Of ◽  
Effect Of Alloying

Synthesis and Thermal Stability of Aluminum Titanate Solid Solutions

1987 ◽  
Vol 70 (2) ◽  
pp. 69-71 ◽  
Author(s):  
MASAYUKI ISHITSUKA ◽  
TSUGIO SATO ◽  
TADASHI ENDO ◽  
MASAHIKO SHIMADA
Keyword(s):  
Thermal Stability ◽  
Solid Solutions ◽  
Aluminum Titanate ◽  
Thermal Stability Of

Meyer-Neldel Rule on thermal stability parameters (trap depth and frequency factor) of luminescence signals in quartz

2021 ◽  
Author(s):  
Zuzanna Kabacińska ◽  
Alida Timar-Gabor ◽  
Benny Guralnik
Keyword(s):  
Activation Energy ◽  
Thermal Stability ◽  
Hydrogen Diffusion ◽  
Dose Range ◽  
Accurate Determination ◽  
Frequency Factor ◽  
Proton Conduction ◽  
High Dose ◽  
Compensation Law ◽  
Thermal Stability Of

<p>Thermally activated processes can be described mathematically by the Arrhenius equation. The Meyer-Neldel Rule (MNR), or compensation law, linearly relates the pre-exponent term to the logarithm of the excitation enthalpy for processes that are thermally driven in an Arrhenian manner. This empirical rule was observed in many areas of materials science, in physics, chemistry, and biology. In geosciences it was found to uphold in hydrogen diffusion (Jones 2014a) and proton conduction (Jones 2014b) in minerals.</p><p>Trapped charge dating methods that use electron spin resonance (ESR) or optically or thermally stimulated luminescence (OSL and TL) are based on the dose-dependent accumulation of defects in minerals such as quartz and feldspar. The thermal stability of these defects in the age range investigated is a major prerequisite for accurate dating, while the accurate determination of the values of the trap depths and frequency factors play a major role in thermochronometry applications. </p><p>The correlation of kinetic parameters for diffusion has been very recently established for irradiated oxides (Kotomin et al. 2018). A correlation between the activation energy and the frequency factor that satisfied the Meyer–Neldel rule was reported when the thermal stability of [AlO<sub>4</sub>/h<sup>+</sup>]<sup>0</sup> and [TiO<sub>4</sub>/M<sup>+</sup>]<sup>0</sup> ESR signals in quartz was studied as function of dose (Benzid and Timar-Gabor 2020). Here we compiled the optically stimulated luminescence (OSL) data published so far in this regard, and investigated experimentally the thermal stability of OSL signals for doses ranging from 10 to 10000 Gy in sedimentary quartz samples. We report a linear relationship between the natural logarithm of the preexponent term (the frequency factor) and the activation energy E, corresponding to a Meyer-Neldel energy of 45 meV, and a deviation from first order kinetics in the high dose range accompanied by an apparent decrease in thermal stability. The implications of these observations and the atomic and physical mechanisms are currently studied.</p><p> </p><p><strong>References</strong></p><p>Benzid, K., Timar Gabor, A. 2020. The compensation effect (Meyer–Neldel rule) on [AlO<sub>4</sub>/h<sup>+</sup>]<sup>0</sup> and [TiO<sub>4</sub>/M<sup>+</sup>]<sup>0</sup> paramagnetic centers in irradiated sedimentary quartz. <em>AIP Advance</em>s 10, 075114.</p><p>Kotomin, E., Kuzovkov, V., Popov, A. I., Maier, J., and Vila, R. 2018. Anomalous kinetics of diffusion-controlled defect annealing in irradiated ionic solids. <em>J. Phys. Chem. A</em> 122(1), 28–32</p><p>Jones, A. G. (2014a), Compensation of the Meyer-Neldel Compensation Law for H diffusion in minerals, <em>Geochem. Geophys. Geosyst.</em>, 15, 2616–2631</p><p>Jones, A. G. (2014b), Reconciling different equations for proton conduction using the Meyer-Neldel compensation rule, <em>Geochem. Geophys. Geosyst</em>., 15, 337–349</p>

scholarly journals Thermal Stability of Solid Solutions Formed by Ultrasonic Milling of Cu–Co and Cu–Fe Powder Mixtures

2017 ◽  
Vol 62 (8) ◽  
pp. 685-691
Author(s):  
V.M. Nadutov ◽  
◽  
A.Ye. Perekos ◽  
V.Z. Voinash ◽  
V.P. Zalutskiy ◽  
...  
Keyword(s):  
Thermal Stability ◽  
Solid Solutions ◽  
Powder Mixtures ◽  
Fe Powder ◽  
Ultrasonic Milling ◽  
Thermal Stability Of

Effect of Pre-Strain Rolling on Annealing Behavior of Friction-Stir Welded AA6061-T6 Aluminum Alloy

2018 ◽  
Vol 385 ◽  
pp. 355-358 ◽  
Author(s):  
Sergey Mironov ◽  
Sergey Malopheyev ◽  
Igor Vysotskiy ◽  
Daria Zhemchuzhnikova ◽  
Rustam Kaibyshev
Keyword(s):  
Heat Treatment ◽  
Thermal Stability ◽  
Aluminum Alloy ◽  
Cold Rolling ◽  
Grain Growth ◽  
Rolling Schedule ◽  
Annealing Behavior ◽  
Friction Stir ◽  
Welding Direction ◽  
Thermal Stability Of

In this work, the effect of pre-strain cold rolling on thermal stability of friction-stir welded AA6061-T6 alloy was studied. The pre-strain rolling was found to be very effective in suppression of abnormal grain growth during standard post-weld T6 heat treatment. It was also shown that the efficiency of this approach essentially depends on rolling path and the rolling along welding direction was the most effective rolling schedule.

Thermal Stability of Ultrafine-Grained Pure Titanium Processed by High-Pressure Torsion

2021 ◽  
Vol 1016 ◽  
pp. 338-344
Author(s):  
Wan Ji Chen ◽  
Jie Xu ◽  
De Tong Liu ◽  
De Bin Shan ◽  
Bin Guo ◽  
...  
Keyword(s):  
Activation Energy ◽  
Thermal Stability ◽  
Grain Size ◽  
High Pressure ◽  
Annealing Temperature ◽  
High Pressure Torsion ◽  
Stored Energy ◽  
Ultrafine Grained ◽  
Average Grain Size ◽  
Thermal Stability Of

High-pressure torsion (HPT) was conducted under 6.0 GPa on commercial purity titanium up to 10 turns. An ultrafine-grained (UFG) pure Ti with an average grain size of ~96 nm was obtained. The thermal properties of these samples were studied by using differential scanning calorimeter (DSC) which allowed the quantitative determination of the evolution of stored energy, the recrystallization temperatures, the activation energy involved in the recrystallization of the material and the evolution of the recrystallized fraction with temperature. The results show that the stored energy increases, beyond which the stored energy seems to level off to a saturated value with increase of HPT up to 5 turns. An average activation energy of about 101 kJ/mol for the recrystallization of 5 turns samples was determined. Also, the thermal stability of the grains of the 5 turns samples with subsequent heat treatments were investigated by microstructural analysis and Vickers microhardness measurements. It is shown that the average grain size remains below 246 nm when the annealing temperature is below 500 °C, and the size of the grains increases significantly for samples at the annealing temperature of 600 °C.

Sign in / Sign up

Export Citation Format

Share Document