Consistency of Performance of Concretes With and Without Fly Ash

1986 ◽  
Vol 86 ◽  
Author(s):  
Weston T. Hester
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Fresh Concrete ◽  
High Strength ◽  
High Compressive Strength ◽  
Measures Of Performance ◽  
Construction Practice ◽  
Design And Construction

ABSTRACTFly ash and other pozzolans are increasingly used in concretes that must consistently achieve high compressive strength and other measures of performance. In contemporary design and construction practice, however, there is some concern as to whether or not use of commercial fly ash materials contribute to or reduce variations observed in field compressive strengths and properties of the fresh concrete. Regardless of its potential for improving the performance of the concrete, if the daily ongoing use of commercial fly ash will decrease the consistency of the concrete produced, the use of fly ash will be curtailed. In this paper, the experiences of geographically diverse, specific concrete suppliers using their respective sources of fly ash are summarized in detail. The nominal compressive strength of concretes, made with and without fly ash, are analyzed statistically. Special attention is given to moderate- and high-strength concretes. In conclusion, it is shown that concretes made with fly ash may not be more consistent than concretes with only portland cement.

scholarly journals Kajian Karakteristik Beton Memadat Sendiri yang Menggunakan Serat Ijuk (Hal. 54-65)

2018 ◽  
Vol 4 (4) ◽  
pp. 54
Author(s):  
Iis Nurjamilah ◽  
Abinhot Sihotang
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Coarse Aggregate ◽  
Fresh Concrete ◽  
High Strength ◽  
Self Compacting Concrete ◽  
Palm Fiber ◽  
Fiber Concrete ◽  
Dilute Mixture

ABSTRAKKajian karakteristik beton memadat sendiri yang menggunakan serat ijuk merupakan sebuah kajian yang dilakukan untuk mengetahui pengaruh penambahan serat ijuk terhadap karakteristik beton memadat sendiri (SCC). Beton memadat sendiri yang menggunakan serat ijuk (PFSCC) didesain memiliki campuran yang encer, bermutu tinggi (= 40 MPa) dan memiliki persentase kekuatan lentur yang lebih baik. PFSCC  didapatkan dari hasil pencampuran antara semen sebanyak 85%, fly ash 15%, superplastizicer 1,5%, serat ijuk 0%, 0,5%; 1%; 1,5%; 2% dan 3% dari berat binder (semen + fly ash), kadar air 190 kg/m3, agregat kasar 552,47 kg/m3 dan pasir 1.063 kg/m3. Semakin banyak persentase penambahan serat ijuk ke dalam campuran berdampak terhadap menurunnya workability beton segar. Penambahan serat ijuk yang paling baik adalah sebanyak 1%, penambahan tersebut dapat meningkatkan kekuatan tekan beton sebesar 13% dan lentur sebesar 1,8%.Kata kunci: beton memadat sendiri (SCC), beton berserat, beton memadat sendiri yang menggunakan serat ijuk (PFSCC), serat ijuk ABSTRACTThe study of characteristics self compacting concrete using palm fibers is a study conducted to determine the effect of adding palm fibers to characteristics of self compacting concrete (SCC). palm fibers self compacting concrete (PFSCC) is designed to have a dilute mixture, high strength (= 40 MPa), and have better precentage flexural strength. PFSCC was obtained from mixing of 85% cement, 15% fly ash, 1.5% superplastizicer, 0%, 0.5%, 1%, 1.5%, 2% and 3% palm fibers from the weight of binder  (cement + fly ash), water content 190 kg/m3, coarse aggregate 552.47 kg/m3 and sand 1,063 kg/m3. The more persentage palm fibers content added to the mixture makes workability of fresh concrete decreases. The best addition of palm fiber is 1%, this addition can increases the compressive strength 13% and flexural strength 1.8%.Keywords: self compacting concrete (SCC), fiber concrete, Palm fiber self compacting concrete (PFSCC), palm fiber

scholarly journals Influence of Temperature on Workability and Compressive Strength of Ordinary Concrete with High Calcium Fly Ash

2017 ◽  
Vol 17 (1) ◽  
pp. 37-44 ◽  
Author(s):  
Jacek Gołaszewski ◽  
Tomasz Ponikiewski ◽  
Grzegorz Cygan
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Fresh Concrete ◽  
Influence Of Temperature ◽  
Ordinary Concrete ◽  
Concrete Mixtures ◽  
High Calcium ◽  
High Calcium Fly Ash ◽  
Influence Of Temperature On

Abstract The rheological properties of fresh ordinary concrete are closely affected by temperature and time. The paper presents the study of consistency of fresh concrete mixtures made with Portland cement and cement with calcareous fly ash. Two types of admixtures were used. It was proven that the temperature has a clear effect on workability and compressive strength concrete. Influence on workability can be reduced by selecting the appropriate superplasticizer and cement.

Study of Performance on Reduce Fragility and Increase the Toughness of Fly Ash Ceramsite Concrete

2014 ◽  
Vol 977 ◽  
pp. 120-123 ◽  
Author(s):  
Rui Li ◽  
Xiao Hua Zhang ◽  
Yun Fang Meng
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Carbon Fiber ◽  
Compression Ratio ◽  
High Strength ◽  
Orthogonal Test ◽  
Low Density ◽  
High Compressive Strength

High strength fly ash ceramsite concrete has the advantages of low density, high compressive strength, but the brittleness is too large, limiting its application in engineering. In order to solve this problem, we used Carbon fiber in the orthogonal test. The results show that Carbon fiber can obviously improve the tension compression ratio of fly ash ceramisite concrete, improve the strength of fly ash ceramsite concrete brittleness.

COMPRESSIVE STRENGTH AND THERMAL CONDUCTIVITY OF WATER AND AIR CURED PORTLAND CEMENT-FLY ASH-SILICA FUME MORTARS

2018 ◽  
Vol 17 (9) ◽  
pp. 2023-2030
Author(s):  
Arnon Chaipanich ◽  
Chalermphan Narattha ◽  
Watcharapong Wongkeo ◽  
Pailyn Thongsanitgarn
Keyword(s):  
Thermal Conductivity ◽  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Silica Fume

Investigation on a New Hydraulic Cementitious Binder Made from Phosphogypsum

2013 ◽  
Vol 864-867 ◽  
pp. 1923-1928
Author(s):  
Yue Xu ◽  
Jian Xi Li ◽  
Li Li Kan
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Active Carbon ◽  
High Strength ◽  
Tricalcium Silicate ◽  
Dicalcium Silicate ◽  
Cementitious Material ◽  
Saturation Ratio ◽  
Tricalcium Aluminate ◽  
Cementitious Binder

A new kind of high strength cementitious material is made from phosphogypsum (PG), active carbon and fly-ash. Through the orthogonal research, it was showed that the calcination temperature, retention time, dosage of active carbon and fly ash on the compressive strength of cementitious binder are the most important. The result also showed that, in the conditions of temperature 1200°C, time retention 30 min, dosage of active carbon 10%, dosage of fly ash 5%, the compressive strength of the cementitious material for 3d and 28d could reach to 46.35MPa and 92.70MPa, the content of sulfur trioxide was 11.60% accordingly. A lot of active mineral materials, such as dicalcium silicate, tricalcium silicate, tricalcium aluminate were formed in the calcination. The C-S-H gel, calcium hydroxide and ettringite were found in 3d and 28d hydrates. It is found that the lime saturation ratio and silica modulus need to be control between 0.40~0.65 and 4~8 in order to produce high strength cementitious material.

Effect of Chopped Basalt Fiber on the Fresh and Hardened Properties of Fly Ash High Strength Concrete

2014 ◽  
Vol 567 ◽  
pp. 381-386 ◽  
Author(s):  
Nasir Shafiq ◽  
Muhd Fadhil Nuruddin ◽  
Ali Elheber Ahmed Elshekh ◽  
Ahmed Fathi Mohamed Salih
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
High Strength Concrete ◽  
Basalt Fiber ◽  
High Strength ◽  
Progressive Increase ◽  
Test Results ◽  
Strength Concrete ◽  
Hardened Properties ◽  
Chopped Basalt Fiber

In order to improve the mechanical properties of high strength concrete, HSC, several studies have been conducted using fly ash, FA. Researchers have made it possible to achieve 100-150MPa high strength concrete. Despite the popularity of this FAHSC, there is a major shortcoming in that it becomes more brittle, resulting in less than 0.1% tensile strain. The main objective of this work was to evaluate the fresh and hardened properties of FAHSC utilizing chopped basalt fiber stands, CBFS, as an internal strengthening addition material. This was achieved through a series of experimental works using a 20% replacement of cement by FA together with various contents of CBFS. Test results of concrete mixes in the fresh state showed no segregation, homogeneousness during the mixing period and workability ranging from 60 to 110 mm. Early and long terms of compressive strength did not show any improvement by using CBFS; in fact, it decreased. This was partially substituted by the effect of FA. Whereas, the split and flexural strengths of FASHC were significantly improved with increasing the content of CBFS as well as the percentage of the split and flexural tensile strength to the compressive strength. Also, test results showed a progressive increase in the areas under the stress-strain curves of the FAHSC strains after the CBFS addition. Therefore, the brittleness and toughness of the FAHSC were enhanced and the pattern of failure moved from brittle failure to ductile collapse using CBFS. It can be considered that the CBFS is a suitable strengthening material to produce ductile FAHSC.

scholarly journals Hydration study of mechanically activated mixtures of Portland cement and fly ash

2007 ◽  
Vol 72 (6) ◽  
pp. 591-604 ◽  
Author(s):  
Gordana Stefanovic ◽  
Ljubica Cojbasic ◽  
Zivko Sekulic ◽  
Srdjan Matijasevic
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Mechanical Activation ◽  
Early Period ◽  
Negative Effects ◽  
Early Hydration ◽  
Cement Pastes ◽  
Dta And Tg ◽  
Low Activity

Fly ash (FA) can be used in cement mixtures with certain limitations. The problem of the mentioned mixtures lies in the insufficient activity of the particles of FA in the reactions which are important for the establishment of the mechanical characteristics of cement. This is particularly true for the hydration reactions. As a result of this, cement pastes formed by mixing ash and clinker have worse characteristics compared to those of pure Portland cement (PC), especially in the early period of setting. As is well known, FA can be a good solution for the neutralization of the negative effects generated due to the creation of free Ca(OH)2 during the hydration of PC, provided that the problems with the low activity of FAare overcome. For the experiments in this study, a mixture of Portland cement and fly ash was used, the content of ash in the mixture being 30 % and 50 %. Mechanical activation was performed in a vibrating ring mill. The goal of this study was to demonstrate, through experimental results, that during the mechanical activation of a PC and FA mixture, the components in the mixture which mostly affect the direction, rate and range of hydration reactions occurring in the mixture had been activated. The values of the compressive strength of the activated and non-activated mixtures and the changes of their specific surface area proved that during the grinding process, the mixture PC+FA had been mechanically activated. The highest increase of compressive strength was achieved in the early period of setting, which indicates an improvement in the early hydration of the mixture. XRD, DTA and TG analyses showed that the alite (C3S) and belite (C2S) from the PC and a part of the fly ash were activated. .