scholarly journals Evaluation the Mechanical Properties of Kaolin Particulate Reinforced Epoxy Composites

2018 ◽  
Vol 14 (1) ◽  
pp. 29-38
Author(s):  
Jabbar Hussein Mohmmed
Keyword(s):  
Mechanical Properties ◽  
Particle Size ◽  
Epoxy Resin ◽  
Flexural Modulus ◽  
Epoxy Composites ◽  
Elongation At Break ◽  
Crack Propagation Resistance ◽  
Brittle Behavior ◽  
Accuracy Of Prediction ◽  
Particulate Reinforced

Epoxy resin has many chemical features and mechanical properties, but it has a small elongation at break, low impact strength and crack propagation resistance, i.e. it exhibits a brittle behavior. In the current study, the influence of adding kaolin with variable particle size on the mechanical properties (flexural modulus E, toughness Gc, fracture toughness Kc, hardness HB, and Wear rate WR) of epoxy resin was evaluated. Composites of epoxy with varying concentrations (0, 10, 20, 30, 40 weights %) of kaolin were prepared by hand-out method. The composites showed improved (E, Gc, Kc, HB, and WR) properties with the addition of filler. Also, similar results were observed with the decrease in particle size. In addition, in this study, multiple regression models were developed by utilizing (SPSS) package to predict the properties of kaolin reinforced epoxy composites. Good agreement was obtained between the predicted and the experimental results. The accuracy of prediction was (89.71%, 80.58%, 85.82%, 92.27%, and 94.49%) for E, Gc, Kc, HB, and WR, respectively.    

scholarly journals The Structure and Mechanical Properties of Hemp Fibers-Reinforced Poly(ε-Caprolactone) Composites Modified by Electron Beam Irradiation

2021 ◽  
Vol 11 (12) ◽  
pp. 5317
Author(s):  
Rafał Malinowski ◽  
Aneta Raszkowska-Kaczor ◽  
Krzysztof Moraczewski ◽  
Wojciech Głuszewski ◽  
Volodymyr Krasinskyi ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Electron Beam ◽  
Impact Strength ◽  
Flexural Modulus ◽  
Natural Fibers ◽  
High Energy ◽  
Electron Radiation ◽  
Elongation At Break ◽  
Hemp Fibers

The need for the development of new biodegradable materials and modification of the properties the current ones possess has essentially increased in recent years. The aim of this study was the comparison of changes occurring in poly(ε-caprolactone) (PCL) due to its modification by high-energy electron beam derived from a linear electron accelerator, as well as the addition of natural fibers in the form of cut hemp fibers. Changes to the fibers structure in the obtained composites and the geometrical surface structure of sample fractures with the use of scanning electron microscopy were investigated. Moreover, the mechanical properties were examined, including tensile strength, elongation at break, flexural modulus and impact strength of the modified PCL. It was found that PCL, modified with hemp fibers and/or electron radiation, exhibited enhanced flexural modulus but the elongation at break and impact strength decreased. Depending on the electron radiation dose and the hemp fibers content, tensile strength decreased or increased. It was also found that hemp fibers caused greater changes to the mechanical properties of PCL than electron radiation. The prepared composites exhibited uniform distribution of the dispersed phase in the polymer matrix and adequate adhesion at the interface between the two components.

scholarly journals Improving the mechanical properties of polypropylene composites with coconut shell particles

2021 ◽  
Vol 30 ◽  
pp. 263498332110074
Author(s):  
Henry C Obasi ◽  
Uchechi C Mark ◽  
Udochukwu Mark
Keyword(s):  
Mechanical Properties ◽  
Particle Size ◽  
Flexural Modulus ◽  
Filler Particle ◽  
Tensile Modulus ◽  
Coconut Shell ◽  
Polypropylene Composites ◽  
Increase With Increase ◽  
Pp Composites ◽  
Shell Particles

Conventional inorganic fillers are widely used as fillers for polymer-based composites. Though, their processing difficulties and cost have demanded the quest for credible alternatives of organic origin like coconut shell fillers. Dried shells of coconut were burnt, ground, and sifted to sizes of 63, 150, 300, and 425 µm. The ground coconut shell particles (CSP) were used as a filler to prepare polypropylene (PP) composites at filler contents of 0% to 40% via injection melt blending process to produce PP composite sheets. The effect of the filler particle size on the mechanical properties was investigated. The decrease in the size of filler (CSP) was found to improve the yield strength, tensile strength, tensile modulus, flexural strength, flexural modulus, and hardness of PP by 8.5 MPa, 15.75 MPa, 1.72 GPa, 7.5 MPa, 100 MPa, and 10.5 HR for 63 µm at 40%, respectively. However, the elongation at break and modulus of resilience of the PP composites were seen to increase with increase in the filler size. Scanning electron microscope analysis showed that fillers with 63 µm particle size had the best distribution and interaction with the PP matrix resulting in enhanced properties.

scholarly journals Assessing the Flexural Properties of Epoxy Composites with Extremely Low Addition of Cellulose Nanofiber Content

2020 ◽  
Vol 10 (3) ◽  
pp. 1159 ◽  
Author(s):  
Yingmei Xie ◽  
Hiroki Kurita ◽  
Ryugo Ishigami ◽  
Fumio Narita
Keyword(s):  
Mechanical Properties ◽  
Epoxy Resin ◽  
Flexural Modulus ◽  
Strengthening Mechanism ◽  
Short Fiber ◽  
Cellulose Nanofiber ◽  
Resin Matrix ◽  
Element Analysis ◽  
Epoxy Resin Matrix ◽  
The Matrix

Epoxy resins are a widely used common polymer due to their excellent mechanical properties. On the other hand, cellulose nanofiber (CNF) is one of the new generation of fibers, and recent test results show that CNF reinforced polymers have high mechanical properties. It has also been reported that an extremely low CNF addition increases the mechanical properties of the matrix resin. In this study, we prepared extremely-low CNF (~1 wt.%) reinforced epoxy resin matrix (epoxy-CNF) composites, and tried to understand the strengthening mechanism of the epoxy-CNF composite through the three-point flexural test, finite element analysis (FEA), and discussion based on organic chemistry. The flexural modulus and strength were significantly increased by the extremely low CNF addition (less than 0.2 wt.%), although the theories for short-fiber-reinforced composites cannot explain the strengthening mechanism of the epoxy-CNF composite. Hence, we propose the possibility that CNF behaves as an auxiliary agent to enhance the structure of the epoxy molecule, and not as a reinforcing fiber in the epoxy resin matrix.

Graphite/Bio-Based Epoxy Composites: The Mechanical Properties Interface

2015 ◽  
Vol 799-800 ◽  
pp. 115-119 ◽  
Author(s):  
Anika Zafiah M. Rus ◽  
Nur Munirah Abdullah ◽  
M.F.L. Abdullah ◽  
M. Izzul Faiz Idris
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Elastic Modulus ◽  
Filler Content ◽  
Weight Percent ◽  
Epoxy Composites ◽  
Elongation At Break ◽  
Graphite Content ◽  
Dispersion Condition ◽  
Strong Interfacial Bonding

Graphite reinforced bio-based epoxy composites with different particulate fractions of graphite were investigated for mechanical properties such as tensile strength, elastic modulus and elongation at break. The graphite content was varied from 5 wt.%, 10 wt.%, 15 wt.%, 20 wt.%, 25 wt.%, 30 wt.% by weight percent in the composites. The results showed that the mechanical properties of the composites mainly depend on dispersion condition of the treated graphite filler, aggregate structure and strong interfacial bonding between treated graphite in the bio-based epoxy matrix. The composites showed improved tensile strength and elastic modulus with increase treated graphite weight loading. This also revealed the composites with increasing filler content was decreasing the elongation at break.

scholarly journals A Study Regarding the Mechanical Properties of a Hybrid Matrix with Various Volume Proportions of Dammar

2020 ◽  
Vol 57 (1) ◽  
pp. 133-140
Author(s):  
Dumitru Bolcu ◽  
Marius Marinel Stanescu ◽  
Ion Ciuca ◽  
Cosmin Mihai Miritoiu ◽  
Alin Dinita ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Epoxy Resin ◽  
Vibration Mode ◽  
Vibration Damping ◽  
The Other ◽  
Damping Properties ◽  
Elongation At Break ◽  
Hybrid Resin ◽  
Natural Resin ◽  
Volume Proportion

This paper studies the influence of the volume proportion between components on the mechanical behaviour of a hybrid resin obtained by combining the natural resin Dammar and epoxy resin. We analyse three sets of hybrid resin samples, in which we used a Dammar volume proportion of 60%, 70%, and 80% respectively and epoxy resin (employed together with its associated reinforcement in order to generate a quick process of polymerization). Following the tensile test we found the characteristic curves, the tensile strength and the elongation at break for each of the three types of resins. We also looked into the vibration damping properties of bars made of this resin. We experimentally determined the frequency and the damping coefficient of the first particular vibration mode for one bar taken out of each set of resins, with one end fixed and the other free. On the basis of the results, we calculated the loss coefficient for each type of resin.

Study on Electron Beam Curing of APTES Functionalized MWNTs/ Epoxy Composites

2011 ◽  
Vol 194-196 ◽  
pp. 1607-1610
Author(s):  
Yan Yan Lu ◽  
Hua Li ◽  
He Zhou Liu
Keyword(s):  
Mechanical Properties ◽  
Electron Beam ◽  
Epoxy Resin ◽  
Conversion Rate ◽  
Epoxy Composites ◽  
Pure Epoxy ◽  
Gel Content ◽  
Electron Beam Curing ◽  
Irradiation Process

In this study, we prepared the 3-aminopropyltriethoxysilane (APTES) functionalized MWNTs/epoxy composites by electron beam (EB) irradiation process. The modified MWNTs were characterized with SEM-EDS and FTIR. The gel content and conversion rate of epoxide groups of the EB cured pure epoxy resin and the APTES functionalized MWNTs/epoxy composites were measured and discussed. And the mechanical properties of the EB cured composites were also characterized. With addition of 0.25wt% APTES functionalized MWNTs, the Vicker’s hardness of the EB cured composite increased 100.02% compared with pure epoxy.

Research on Structure and Mechanical Properties of Epoxy Resin/Clay Nanocomposites by Shock Wave Method

2012 ◽  
Vol 501 ◽  
pp. 366-371 ◽  
Author(s):  
Guang Yi Lin ◽  
Xue Chen Mu ◽  
Dian Wei Qu
Keyword(s):  
Mechanical Properties ◽  
Mechanical Property ◽  
Shock Wave ◽  
Epoxy Resin ◽  
Process Condition ◽  
Interlayer Spacing ◽  
Clay Nanocomposites ◽  
Wave Method ◽  
Optimal Process ◽  
Elongation At Break

Epoxy resin / clay nanocomposites prepared by shock wave method. The structure and mechanical properties including hardness, stress, strain and elongation at break were investigated. XRD was used to observe the interlayer spacing of the OMMT and SEM was used to survey the morphology of nanocomposites system. The results indicated that nano-montmorillonite can effectively increase the mechanical property of the material. The nano-montmorillonite was well dispersed in the epoxy matrix. The optimal process condition is that shock time 5min, nano-MMT content of 5%, duty cycle 1:3, shock depth 3cm.

scholarly journals Study the effect of fiber loading and alkali treatment on the mechanical and water absorption properties of wheat straw fiber-reinforced epoxy composites

2017 ◽  
Vol 24 (5) ◽  
pp. 731-738 ◽  
Author(s):  
Varun Mittal ◽  
Shishir Sinha
Keyword(s):  
Mechanical Properties ◽  
Water Absorption ◽  
Epoxy Resin ◽  
Wheat Straw ◽  
Alkali Treatment ◽  
Fiber Composites ◽  
Epoxy Composites ◽  
Absorption Properties ◽  
Fiber Loading ◽  
Treated Fiber

AbstractThe aim of this research was to study the feasibility of using wheat straw fiber with epoxy resin for developing natural fiber-polymer composites. For this purpose, the epoxy resin was reinforced with 5, 10, 15, 20, and 25 wt.% of the wheat straw fiber with the help of the hand lay-up technique. Further, in order to improve the composite characteristic, wheat straw fibers were treated with three different concentrations of alkali (1%, 3%, and 5%). The mechanical and water absorption properties of the treated fiber composites were characterized and compared with those of untreated fiber-filled epoxy composites. It was observed that the mechanical properties and water resistance were reduced with the increase in wheat straw fiber loading from 5 to 25 wt.%. Among the three levels of alkali treatment, the composite made with 3% alkali-treated fiber exhibited superior mechanical properties than the other untreated and treated fiber composites, which pointed to an efficient fiber-matrix adhesion. The scanning electron microscope was used to observe the surface features of the wheat straw fiber.

Carbon Fiber Powder Reinforced Epoxy Composites used for Rapid Tooling

2011 ◽  
Vol 287-290 ◽  
pp. 197-200
Author(s):  
Hai Qing Hu ◽  
Li Zhao ◽  
Jia Qiang Liu ◽  
Shi Bao Wen ◽  
Yong Jiang Gu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Carbon Fiber ◽  
Glass Fiber ◽  
Epoxy Resin ◽  
Epoxy Matrix ◽  
Rapid Tooling ◽  
Epoxy Composites ◽  
Waste Materials ◽  
Ultrasonic Time ◽  
Good For

Carbon fiber powder (CFP) instead of the traditional glass fiber (cloth) was used to reinforce epoxy resin for rapid tooling. There are two obvious advantages: one is to utilize the waste materials, which is good for the protection of the environment; another is to simplify the producing process by cast molding. The filling amount and dispersing process of CFP was studied in this paper. The results show that when the amount of CFP was 10 wt%, and the ultrasonic time is more than 15 min, the CFP can be dispersed in the epoxy matrix uniformly, and the mechanical properties can meet the requirement of epoxy molding.

Sign in / Sign up

Export Citation Format

Share Document