scholarly journals Evaluation of the Impact of Residual Stresses in Crack Initiation with the Application of the Crack Compliance Method Part II, Experimental Analysis

2010 ◽  
Vol 24-25 ◽  
pp. 261-266
Author(s):  
G. Urriolagoitia-Sosa ◽  
B. Romero-Ángeles ◽  
Luis Héctor Hernández-Gómez ◽  
G. Urriolagoitia-Calderón ◽  
Juan Alfonso Beltrán-Fernández ◽  
...  
Keyword(s):  
Residual Stress ◽  
Stress Field ◽  
Crack Initiation ◽  
Residual Stresses ◽  
Experimental Analysis ◽  
Previous History ◽  
Numerical Procedure ◽  
Tensile Specimen ◽  
Residual Stress Field ◽  
The Impact

The present work is based on a previous numerical simulation used for the introduction of a residual stress field in a modified compact tensile specimen. The main objective in that paper was to evaluate the effect that previous history has in crack initiation and to establish the new loading conditions needed to propagate a fracture. The experimental analysis presented in this paper was performed to compare and validate the numerical procedure. Several modified compact tensile specimens from a biocompatible material (AISI 316L) were manufactured to estimate the beneficial effect of a residual stress field. The specimens were separated in four batches; an initial group of uncracked specimens was used to establish an evaluation of the induction of a residual stress field produced by an overload; the remaining specimens were separated into three groups where a crack was introduced in each specimen (1 mm, 5 mm and 10 mm respectively) and the residual stress field caused by the application of an overload was determined. The assessment of all the residual stress fields introduced into the specimens was done by the application of the crack compliance method (CCM). The results obtained have provided useful information on the correlation between the numerical and experimental procedures. Furthermore, data concerning the understanding of diverse factors related to crack initiation are discussed in this paper. Finally, the beneficial aspects of the residual stresses are discussed.

scholarly journals Evaluation of the Impact of Residual Stresses in Crack Initiation with the Application of the Crack Compliance Method Part I, Numerical Analysis

2010 ◽  
Vol 24-25 ◽  
pp. 253-259 ◽  
Author(s):  
G. Urriolagoitia-Sosa ◽  
B. Romero-Ángeles ◽  
Luis Héctor Hernández-Gómez ◽  
G. Urriolagoitia-Calderón ◽  
Juan Alfonso Beltrán-Fernández ◽  
...  
Keyword(s):  
Numerical Simulation ◽  
Residual Stress ◽  
Numerical Analysis ◽  
Stress Field ◽  
Crack Initiation ◽  
Residual Stresses ◽  
Main Concern ◽  
Residual Stress Field ◽  
Set Up ◽  
The Impact

The understanding of how materials fail is still today a fundamental research problem for scientist and engineers. The main concern is the assessment of the necessary conditions to propagate a crack that will eventually lead to failure. Nevertheless, this kind of analysis tends to be more complicated, when a prior history in the material is taken into consideration and it will be extremely important to recognize all the factors involved in this process. In this work, a numerical simulation of the introduction of residual stresses, which change the crack initiation conditions, in a modified compact tensile specimen to change the condition of crack initiation is presented. Four numerical analyses were carried out; an initial evaluation was performed in a specimen without a crack and it was used for the estimation of a residual stress field produced by an overload; three more cases were simulated and a crack was introduced in each specimen (1 mm, 5 mm and 10 mm, respectively). The overload was then applied to set up a residual stress field into the component; furthermore, in each case the crack compliance method (CCM) was applied to measure the induced residual stress field. By performing this numerical simulation, the accuracy of the crack compliance method can be evaluated. On the other hand, elastic-plastic finite element analysis was utilized for the residual stress estimation. The numerical analysis was based on the mechanical properties of a biocompatible material (AISI 316L). The obtained results provided significant data about diverse factors, like; the manner in which a residual stress field could modify the crack initiation conditions, the convenient set up for induction of a beneficial residual stresses field, as well as useful information that can be applied for the experimental implementation of this research.

scholarly journals Impact of the Process Parameters, the Measurement Conditions and the Pre-Machining on the Residual Stress State of Deep Rolled Specimens

2019 ◽  
Vol 3 (3) ◽  
pp. 56 ◽  
Author(s):  
Nataliya Lyubenova ◽  
Dirk Bähre ◽  
Lukas Krupp ◽  
Julie Fouquet ◽  
Titouan Cronier ◽  
...  
Keyword(s):  
Residual Stress ◽  
Stress State ◽  
Stress Field ◽  
Residual Stresses ◽  
Process Parameters ◽  
Polished Surface ◽  
Deep Rolling ◽  
Residual Stress Field ◽  
The Impact ◽  
Compressive Residual Stresses

Mechanical surface treatments, e.g., deep rolling, are widely spread finishing processes due to their ability to enhance the fatigue strength of the treated materials with means of cold working and inducement of favorable compressive residual stresses. Despite of the clear advantages of deep rolling, the controlled generation of compressive residual stresses is still a challenging task, as the process can be influenced by the pre-machining stress state of the treated material. Additionally, the exact characterization of the induced residual stress field is impacted by the specific characteristics of the applied measurement technique. Therefore, this paper is focused on the X-ray diffraction residual stress analysis of deep rolled specimens, pre-machined to achieve rough or polished surface. The deep rolling process was realized as a single-trace to avoid the influence of the other process parameters and the resulted residual stress field on the surface and in depth was investigated. Additionally, the surface residual stress profiles were determined using two different measuring devices to analyze the impact of the different measurement conditions.

scholarly journals Residual stresses in thermite welded rails: significance of additional forging

2020 ◽  
Vol 64 (7) ◽  
pp. 1195-1212
Author(s):  
B. Lennart Josefson ◽  
R. Bisschop ◽  
M. Messaadi ◽  
J. Hantusch
Keyword(s):  
Residual Stress ◽  
Stress Field ◽  
Residual Stresses ◽  
Weld Metal ◽  
Welding Process ◽  
Surface Zone ◽  
Fe Model ◽  
Uneven Surface ◽  
Residual Stress Field ◽  
High Dynamic

Abstract The aluminothermic welding (ATW) process is the most commonly used welding process for welding rails (track) in the field. The large amount of weld metal added in the ATW process may result in a wide uneven surface zone on the rail head, which may, in rare cases, lead to irregularities in wear and plastic deformation due to high dynamic wheel-rail forces as wheels pass. The present paper studies the introduction of additional forging to the ATW process, intended to reduce the width of the zone affected by the heat input, while not creating a more detrimental residual stress field. Simulations using a novel thermo-mechanical FE model of the ATW process show that addition of a forging pressure leads to a somewhat smaller width of the zone affected by heat. This is also found in a metallurgical examination, showing that this zone (weld metal and heat-affected zone) is fully pearlitic. Only marginal differences are found in the residual stress field when additional forging is applied. In both cases, large tensile residual stresses are found in the rail web at the weld. Additional forging may increase the risk of hot cracking due to an increase in plastic strains within the welded area.

Temperature and Residual Stress Fields in an Austenitic Circumferential Pipe Weld

2002 ◽  
Author(s):  
Ruthard Bonn ◽  
Klaus Metzner ◽  
H. Kockelmann ◽  
E. Roos ◽  
L. Stumpfrock
Keyword(s):  
Residual Stress ◽  
Numerical Calculation ◽  
Stress Field ◽  
Quantitative Determination ◽  
Welding Residual Stress ◽  
Stress Fields ◽  
Residual Stress Field ◽  
Circumferential Welds ◽  
The Impact

The main target of a research programme “experimental and numerical analyses on the residual stress field in the area of circumferential welds in austenitic pipe welds”, sponsored by Technische Vereinigung der Großkraftwerksbetreiber e. V. (VGB) and carried out at MPA Stuttgart, was the validation of the numerical calculation for the quantitative determination of residual stress fields in austenitic circumferential pipe welds. In addition, the influence of operational stresses as well as the impact of the pressure test on the residual stress state had to be examined. By using the TIG orbital welding technique, circumferential welds (Material X 10 CrNiNb 18 9 (1.4550, corresponding to TP 347) were produced (geometric dimensions 255.4 mm I.D. × 8.8 mm wall) with welding boundary conditions and weld parameters (number of weld layers and weld built-up, seam volume, heat input) which are representative for pipings in power plants. Deformation and temperature measurements accompanying the welding, as well as the experimentally determined (X-ray diffraction) welding residual stress distribution, served as the basis for the verification of numeric temperature and residual stress field calculations. The material model on which the calculations were founded was developed by experimental weld simulations in the thermo-mechanical test rig GLEEBLE 2000 for the determination of the material behaviour at different temperatures and elasto-plastic deformation. The numeric calculations were carried out with the Finite Element program ABAQUS. The comparison of the calculation results with the experimental findings confirms the proven validation of the developed numerical calculation models for the quantitative determination of residual stresses in austenitic circumferential pipings. The investigation gives a well-founded insight into the complex thermo-mechanical processes during welding, not known to this extent from literature previously.

The Effects of Loadings on Welding Residual Stresses and Assessment of Fracture Parameters in a Welding Residual Stress Field

2011 ◽  
Author(s):  
Liwu Wei ◽  
Weijing He ◽  
Simon Smith
Keyword(s):  
Residual Stress ◽  
Stress Field ◽  
Residual Stresses ◽  
Path Dependence ◽  
Welding Residual Stress ◽  
Assessment Procedure ◽  
Fe Model ◽  
J Integral ◽  
Residual Stress Field ◽  
Growing Crack

The level of welding residual stress is an important consideration in the ECA of a structure or component such as a pipeline girth weld. Such a consideration is further complicated by their variation under load and the complexity involved in the proper assessment of fracture mechanics parameters in a welding residual stress field. In this work, 2D axi-symmetric FEA models for simulation of welding residual stresses in pipe girth welds were first developed. The modelling method was validated using experimental measurements from a 19-pass girth weld. The modeling method was used on a 3-pass pipe girth weld to predict the residual stresses and variation under various static and fatigue loadings. The predicted relaxation in welding residual stress is compared to the solutions recommended in the defect assessment procedure BS 7910. Fully circumferential internal cracks of different sizes were introduced into the FE model of the three-pass girth weld. Two methods were used to introduce a crack. In one method the crack was introduced instantaneously and the other method introduced the crack progressively. Physically, the instantaneously introduced crack represents a crack originated from manufacturing or fabrication processes, while the progressively growing crack simulates a fatigue crack induced during service. The J-integral values for the various cracks in the welding residual stress field were assessed and compared. This analysis was conducted for a welding residual stress field as a result of a welding simulation rather than for a residual stress field due to a prescribed temperature distribution as considered by the majority of previous investigations. The validation with the 19-pass welded pipe demonstrated that the welding residual stress in a pipe girth weld can be predicted reasonably well. The relaxation and redistribution of welding residual stresses in the three-pass weld were found to be significantly affected by the magnitude of applied loads and the strain hardening models. The number of cycles in fatigue loading was shown to have little effect on relaxation of residual stresses, but the range and maximum load together governed the relaxation effect. A significant reduction in residual stresses was induced after first cycle but subsequent cycles had no marked effect. The method of introducing a crack in a FE model, progressively or instantaneously, has a significant effect on J-integral, with a lower value of J obtained for a progressively growing crack. The path-dependence of the J-integral in a welding residual stress field is discussed.

A Numerical Study on the Redistribution of Residual Stress After Machining

2017 ◽  
Author(s):  
Kunyang Lin ◽  
Wenhu Wang ◽  
Ruisong Jiang ◽  
Yifeng Xiong
Keyword(s):  
Residual Stress ◽  
Stress Field ◽  
Residual Stresses ◽  
Numerical Study ◽  
Cutting Speed ◽  
Machining Process ◽  
Stress Profile ◽  
Residual Stress Field ◽  
Machining Processes ◽  
Residual Stress Profile

Machining induced residual stresses have an important effect on the surface integrity. Effects of various factors on the distribution of residual stress profiles induced by different machining processes have been investigated by many researchers. However, the initial residual, as one of the important factor that affect the residual stress profile, is always been ignored. In this paper, the residual stress field induced by the quenching process is simulated by the FEM software as the initial condition. Then the initial residual stress field is used to study the residual stress redistribution after the machining process. The influence of initial stress on the stress formation is carried out illustrating with the mechanical and thermal loads during machining processes. The effects of cutting speed on the distribution of residual stress profile are also discussed. These results are helpful to understand how initial residual stresses are redistributed during machining better. Furthermore, the results in the numerical study can be used to explain the machining distortion problem caused by residual stress in the further work.

The Effect of Residual Stresses on the Fracture Resistance of Ductile Steels

2002 ◽  
Author(s):  
Noel P. O’Dowd ◽  
Yuebao Lei
Keyword(s):  
Residual Stress ◽  
Stress Field ◽  
Residual Stresses ◽  
Crack Opening ◽  
Stress Distributions ◽  
Residual Stress Field ◽  
Element Analysis ◽  
Fatigue And Fracture ◽  
Negative Effect ◽  
Fracture Performance

Tensile residual stresses, such as those generated by welding, act as crack opening stresses and can have a negative effect on the fatigue and fracture performance of a component. In this work the effect of representative residual stress distributions on the fracture behaviour of a ferritic steel has been examined using finite element analysis. A Gurson-type void growth model is used to model the effect of ductile tearing ahead of a crack. For the cases examined it is seen that a tensile residual stress field may lead to a reduction in the toughness of the material (as represented by the J-resistance curve). The observed difference in toughness can be linked to the different constraint levels in the specimens due to the introduction of the residual stress field and can be rationalised through the use of a two parameter, J–Q approach.

Determination of the Residual Stress Field around Scratches Using Synchrotron X-Rays and Nanoindentation

2010 ◽  
Vol 652 ◽  
pp. 25-30
Author(s):  
M.K. Khan ◽  
Michael E. Fitzpatrick ◽  
L.E. Edwards ◽  
S.V. Hainsworth
Keyword(s):  
Residual Stress ◽  
Stress Field ◽  
Residual Stresses ◽  
Small Scale ◽  
X Rays ◽  
X Ray Diffraction ◽  
Residual Stress Field ◽  
Fine Grained ◽  
Load Displacement

The residual strain field around the scratches of 125µm depth and 5µm root radius have been measured from the Synchrotron X-ray diffraction. Scratches were produced using different tools in fine-grained aluminium alloy AA 5091. Residual stresses up to +1700 micro-strains were measured at the scratch tip for one tool but remained up to only +1000 micro-strains for the other tool scratch. The load-displacement curves obtained from nanoindentation were used to determine the residual stresses around the scratches. It was found that the load-displacement curves are sensitive to any local residual stress field present and behave according to the type of residual stresses. This combination of nanoindentation and synchrotron X-rays has been proved highly effective for the study of small-scale residual stresses around the features such as scratches.

Numerical Calculation of Residual Stress Corrected J-Integral Using ABAQUS

2014 ◽  
Author(s):  
Xian-Kui Zhu
Keyword(s):  
Residual Stress ◽  
Finite Element ◽  
Stress Field ◽  
Residual Stresses ◽  
Stress Effect ◽  
J Integral ◽  
Residual Stress Field ◽  
Path Independence ◽  
Residual Stress Effect ◽  
Senb Specimen

Residual stresses exist in welded structures due to thermal stresses. Without temperature change, large plastic deformation can result in “cold” residual stresses in a wrinkle or dent in a metallic pipe. For a crack in residual stress field, residual stresses might have strong effect on fracture parameter, the J-integral. In order to ensure its path-independence, different correction methods have been developed in consideration of residual stress effect. Recently, the finite element commercial software ABAQUS adopted one of the correction methods, and is able to calculate the residual stress corrected J-integral. A brief review is first given to the J-integral definition, the conditions of path-independence or path-dependence, and the modifications to consider the residual stress effect. A modified single edge-notched bend (SENB) specimen is then used, and a numerical procedure is developed for ABAQUS to evaluate the path-independence of the residual stress corrected J-integral. Detailed elastic-plastic finite element analyses are performed for the SENB specimen in three-point bending. The residual stress field, crack-tip stress field, and J-integral with and without consideration of residual stresses are discussed.