Mechanical Properties of High Performance Concrete Subjected to High Temperature as a Function of Fly-Ash and Fiber Addition

2014 ◽  
Vol 912-914 ◽  
pp. 227-230 ◽  
Author(s):  
Seung Jo Lee
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Weight Reduction ◽  
High Performance ◽  
Mechanical Characteristics ◽  
High Performance Concrete ◽  
Reduction Ratio ◽  
Crack Control ◽  
Residual Compressive Strength ◽  
Heating Up

The purpose of this study is to have a better understanding of the mechanical characteristics of high performance concrete which is produced by mixing reinforcing fiber controlled by high temperatures with fly ash. After heating up the concrete, its appearance, demolition mode, residual compressive strength, weight reduction ratio and other mechanical characteristics were measured. To improve the mechanical characteristics of concrete, it was mixed with nylon, polypropylene, steel fiber and fly ash. The specimen was exposed to 100 ~ 800°C and its crack control, spalling prevention and other mechanical characteristics were reviewed. When the high performance concrete was exposed to 600°C or higher, its residual compressive strength dropped but its weight reduction ratio was significantly higher than it was heated before.

Contribution of Reinforcing Fiber Types on the Mechanical Properties of High Performance Concrete Subjected to High Temperature

2013 ◽  
Vol 368-370 ◽  
pp. 1052-1055
Author(s):  
Seung Jo Lee ◽  
Jung Min Park
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
High Temperature ◽  
Weight Reduction ◽  
High Performance ◽  
High Performance Concrete ◽  
Reduction Ratio ◽  
Fiber Types ◽  
Residual Compressive Strength ◽  
Reinforcing Fiber

The aim of the study is to improve the understanding of the influence of reinforcing fiber types on the mechanical properties of high performance concretes (HPC) subjected to high temperature. The mechanical properties measured include residual compressive strength, weight reduction ratio, outward appearance property, and failure mode. Nylon, polypropylene, and steel fiber were added to enhance mechanical property of the concretes. After exposure to high temperatures ranged from 100 to 800°C, mechanical properties of fiber-toughened HPC were investigated. For HPC, although residual compressive strength was decreased by exposure to high temperature over 500°C, weight reduction ratio was significantly higher than that before heating temperature.

scholarly journals Ultra-high-performance concrete with local high unburned carbon fly ash

DYNA ◽  
2021 ◽  
Vol 88 (216) ◽  
pp. 38-47
Author(s):  
Joaquín Abellán García ◽  
Nancy Torres Castellanos ◽  
Jaime Antonio Fernandez Gomez ◽  
Andres Mauricio Nuñez Lopez
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
High Performance ◽  
High Performance Concrete ◽  
Unburned Carbon ◽  
High Tech ◽  
Ultra High Performance Concrete ◽  
Conventional Concrete ◽  
The Cost

Ultra-high-performance concrete (UHPC) is a kind of high-tech cementitious material with superb mechanical and durability properties compared to other types of concrete. However, due to the high content of cement and silica fume used, the cost and environmental impact of UHPC is considerably higher than conventional concrete. For this reason, several efforts around the world have been made to develop UHPC with greener and less expensive local pozzolans. This study aimed to design and produce UHPC using local fly ash available in Colombia. A numerical optimization, based on Design of Experiments (DoE) and multi-objective criteria, was performed to obtain a mixture with the proper flow and highest compressive strength, while simultaneously having the minimum content of cement. The results showed that, despite the low quality of local fly ashes in Colombia, compressive strength values of 150 MPa without any heat treatment can be achieved.

Macroscopic and Microscopic Properties of High Performance Concrete with Partial Replacement of Cement by Fly Ash

2019 ◽  
Vol 292 ◽  
pp. 108-113 ◽  
Author(s):  
Josef Fládr ◽  
Petr Bílý ◽  
Roman Chylík ◽  
Zdeněk Prošek
Keyword(s):  
Compressive Strength ◽  
Elastic Modulus ◽  
Fly Ash ◽  
High Performance ◽  
High Performance Concrete ◽  
Partial Replacement ◽  
Experimental Program ◽  
Second Phase ◽  
Depth Of Penetration ◽  
Cement Replacement

The paper describes an experimental program focused on the research of high performance concrete with partial replacement of cement by fly ash. Four mixtures were investigated: reference mixture and mixtures with 10 %, 20 % and 30 % cement weight replaced by fly ash. In the first stage, the effect of cement replacement was observed. The second phase aimed at the influence of homogenization process for the selected 30% replacement on concrete properties. The analysis of macroscopic properties followed compressive strength, elastic modulus and depth of penetration of water under pressure. Microscopic analysis concentrated on the study of elastic modulus, porosity and mineralogical composition of cement matrix using scanning electron microscopy, spectral analysis and nanoindentation. The macroscopic results showed that the replacement of cement by fly ash notably improved compressive strength of concrete and significantly decreased the depth of penetration of water under pressure, while the improvement rate increased with increasing cement replacement (strength improved by 18 %, depth of penetration by 95 % at 30% replacement). Static elastic modulus was practically unaffected. Microscopic investigation showed impact of fly ash on both structure and phase mechanical performance of the material.

scholarly journals Effect of Mineral Aggregates and Chemical Admixtures as Internal Curing Agents on the Mechanical Properties and Durability of High-Performance Concrete

Materials ◽  
2020 ◽  
Vol 13 (9) ◽  
pp. 2090 ◽  
Author(s):  
Francisco Javier Vázquez-Rodríguez ◽  
Nora Elizondo-Villareal ◽  
Luz Hypatia Verástegui ◽  
Ana Maria Arato Tovar ◽  
Jesus Fernando López-Perales ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
High Performance ◽  
High Performance Concrete ◽  
Chloride Ions ◽  
Internal Curing ◽  
Fine Aggregate ◽  
Pumice Stone ◽  
Chemical Admixtures ◽  
Mineral Aggregates

In the present work, the effect of mineral aggregates (pumice stone and expanded clay aggregates) and chemical admixtures (superplasticizers and shrinkage reducing additives) as an alternative internal curing technique was investigated, to improve the properties of high-performance concrete. In the fresh and hardened state, concretes with partial replacements of Portland cement (CPC30R and OPC40C) by pulverized fly ash in combination with the addition of mineral aggregates and chemical admixtures were studied. The physical, mechanical, and durability properties in terms of slump, density, porosity, compressive strength, and permeability to chloride ions were respectively determined. The microstructural analysis was carried out by scanning electronic microscopy. The results highlight the effect of the addition of expanded clay aggregate on the internal curing of the concrete, which allowed developing the maximum compressive strength at 28 days (61 MPa). Meanwhile, the replacement of fine aggregate by 20% of pumice stone allowed developing the maximum compressive strength (52 MPa) in an OPC-based concrete at 180 days. The effectiveness of internal curing to develop higher strength is attributed to control in the porosity and a high water release at a later age. Finally, the lowest permeability value at 90 days (945 C) was found by the substitutions of fine aggregate by 20% of pumice stone saturated with shrinkage reducing admixture into pores and OPC40C by 15% of pulverized fly ash. It might be due to impeded diffusion of chloride ions into cement paste in the vicinity of pulverized fly ash, where the pozzolanic reaction has occurred. The proposed internal curing technology can be considered a real alternative to achieve the expected performance of a high-performance concrete since a concrete with a compressive strength range from 45 to 67 MPa, density range from 2130 to 2310 kg/m3, and exceptional durability (< 2000 C) was effectively developed.

Experimental Study on Workability and Strength of Green High Performance Concrete with High Volume Fly Ash

2013 ◽  
Vol 859 ◽  
pp. 52-55 ◽  
Author(s):  
Yong Qiang Ma
Keyword(s):  
Tensile Strength ◽  
Compressive Strength ◽  
Fly Ash ◽  
High Performance ◽  
High Performance Concrete ◽  
High Volume ◽  
Ash Content ◽  
Splitting Tensile Strength ◽  
Binder Ratio ◽  
Water Binder Ratio

A great deal of experiments have been carried out in this study to reveal the effect of the water-binder ratio and fly ash content on the workability and strengths of GHPC (green high performance concrete). The workability of GHPC was evaluated by slump and slump flow. The strengths include compressive strength and splitting tensile strength. The results indicate that the increase of water-binder ratio can improve the workability of GHPC, however the strengths of GHPC were decreased with the increase of water-binder ratio. When the fly ash content is lower than 40%, the increase in fly ash content has positive effect on workability of GHPC, while the workability begins to decrease after the fly ash content is more than 40%. The addition of fly ash in GHPC has adverse effect on the strengths, and there is a tendency of decrease in the compressive strength and splitting tensile strength of GHPC with the increase of fly ash content.

Effects of Fly Ash Particle Sizes on the Compressive Strength and Fracture Toughness of High Performance Concrete

2011 ◽  
Vol 284-286 ◽  
pp. 984-988
Author(s):  
An Shun Cheng ◽  
Yue Lin Huang ◽  
Chung Ho Huang ◽  
Tsong Yen
Keyword(s):  
Fracture Toughness ◽  
Particle Size ◽  
Compressive Strength ◽  
Fly Ash ◽  
High Performance ◽  
High Performance Concrete ◽  
Concrete Strength ◽  
Bending Test ◽  
Strength Development ◽  
Particle Sizes

The study aims to research the effect of the particle size of fly ash on the compressive strength and fracture toughness of high performance concrete (HPC). In all HPC mixtures, the water-to-binder ratio selected is 0.35; the cement replacement ratios includes 0%, 10% and 20%; the particle sizes of fly ash have three types of passing through sieves No. 175, No. 250 and No. 325. Three-point-bending test was adopted to measure the load-deflection relations and the maximum loads to determine the fracture energy (GF) and the critical stress intensity factor (KSIC). Test results show that adding fly ash in HPC apparently enhances the late age strengths of HPC either for replacement ratio of 10% or 20%, in which the concrete with 10% fly ash shows the higher effect. In addition, the smaller the particle size is the better the late age concrete strength will be. The HPC with the finer fly ash can have higher strength development and the values of GF and KSIC due to the facts of better filling effect and pozzolanic reaction. At late age, the GF and KSIC values of concrete with 10% fly ash are all higher than those with 20% fly ash.

Size Effect on Compressive Strength and Modulus of Elasticity in High Performance Concrete

2013 ◽  
Vol 634-638 ◽  
pp. 2742-2745 ◽  
Author(s):  
Jeong Eun Kim ◽  
Wan Shin Park ◽  
Nam Yong Eom ◽  
Do Gyeum Kim ◽  
Jea Myoung Noh
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Size Effect ◽  
Modulus Of Elasticity ◽  
High Performance ◽  
High Performance Concrete ◽  
Type A ◽  
Type B ◽  
Replacement Ratio ◽  
Curing Age

This study undertook the research of size effect on compressive strength and modulus of elasticity, respectively. The parameters of this study are curing age and fly ash replacement ratio to investigate size effect of Type A (100mm x 200mm) and Type B (150mm x 300mm) specimens in high performance concrete. On this study, high performance concrete was fabricated with different FA contents of 10%, 20% and 30%. The measurements were performed on days 28 and 91.