Synthesis of CuFeO2 Powder by Sol-Gel Method

2008 ◽  
Vol 368-372 ◽  
pp. 663-665
Author(s):  
Rui Fen Wu ◽  
Wei Pan ◽  
Shan Liu ◽  
Jian Li
Keyword(s):  
Heat Treatment ◽  
Thermal Analysis ◽  
Sol Gel ◽  
Nitrogen Atmosphere ◽  
Gel Method ◽  
Sol Gel Method ◽  
Powder Precursor ◽  
Treatment Conditions ◽  
Heat Treated

Sol-gel method has been adopted to synthesize CuFeO2 powder. Precursor solutions and heat treatment conditions were studied using thermal analysis and XRD. Pure CuFeO2 was obtained using the prepared sol-gel precursor that heat treated at 950°C for 5 h under nitrogen atmosphere.

The Process of Sol-Gel Method Prepared Bi-2212 Superconductors Tapes

2013 ◽  
Vol 275-277 ◽  
pp. 2300-2303
Author(s):  
Gen Zong Song ◽  
Duo Zhang
Keyword(s):  
Heat Treatment ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Ni Substrate ◽  
Treatment Conditions ◽  
Drying Conditions ◽  
And Control

In this dissertation, Bi-2212 superconducting tapes was prepared by sol-gel method, in addition we mainly studied heat treatment conditions and sintering material drying conditions of the NiO/Ni substrate, and gived a optimization to the process. The heat treatment process of the NiO/Ni substrate had been researched.Based on previous experience, we explored the temperature of heat treatment and improved the process.Afterheattreatment,the samples was analyzed by metallographic microscope and X-ray diffraction,and we analysed these data. It’s concluded that the dense uniform oxide film can be sintered in 800°C with a 3 hours’ heat treatment.We further explored the conditions of the Bi-2212 superconducting materials.During the preparation. We mainly studied the drying temperature and sintering temperature ,because they would affect the gel phase transition and control components. It has a very important effect on high-quality superconducting strip preparation. Experiments results showed that drying the sample at 510 °C in temperature is best. all the samples was analyzed by X-ray diffraction. We summed up the data derived from experiments , it showed that sintering the sample at 850°C,we can obtain the mixed phase of Bi-2201 and Bi-2212.

Effect of heat treatment conditions on the growth of MgAl2O4 nanoparticles obtained by sol-gel method

2017 ◽  
Vol 43 (17) ◽  
pp. 15246-15253 ◽  
Author(s):  
Yubin Wen ◽  
Xinhong Liu ◽  
Xiaoyu Chen ◽  
Quanli Jia ◽  
Renhong Yu ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Sol Gel ◽  
Gel Method ◽  
Sol Gel Method ◽  
Treatment Conditions

scholarly journals Monoclinic Li2TiO3 Nano-particles via sol-gel method: Structure and impedance spectroscopy

2019 ◽  
Vol 8 (3) ◽  
pp. 209
Author(s):  
Fatima Zahra Krimech ◽  
Salaheddine Sayouri ◽  
Taj-Edine Lamcharfi ◽  
Fatima Zahra Ahjyaje
Keyword(s):  
Impedance Spectroscopy ◽  
Sol Gel ◽  
Low Frequency ◽  
Transport Processes ◽  
Nano Particles ◽  
Secondary Phases ◽  
Conventional Solid State Reaction ◽  
Gel Method ◽  
Sol Gel Method ◽  
Heat Treated

<p>Pure phase Li<sub>2</sub>TiO<sub>3 </sub>nano-particles were synthesized by the sol-gel method and the structural properties were examined with X-ray diffraction (XRD) technique. The latter showed that these materials, heat treated at relatively low temperature 900°C during 4h compared to the conventional solid-state reaction which calcination temperature is about 900–1100°C for 10 h; crystallize in the monoclinic phase without the presence of secondary phases. The microstructure of the LT ceramic (sintered at 1100°C) were determined by SEM and a good crystalline nature was observed with an average of granular size 2 μm. Moreover, the impedance spectroscopy showed at a higher temperature of 500°C the low-frequency arc due either to the grain boundary or sample-electrode charge transport processes.</p>

Preparation of La0.75Sr0.25Cr0.5Mn0.5O3-δ Nanometer Powders by Sol-Gel Method and Research about its Electrochemical Performance

2013 ◽  
Vol 712-715 ◽  
pp. 257-261
Author(s):  
Yin Lin Wu ◽  
Qing Hui Wang ◽  
Ling Wang ◽  
Hai Yan Zhao
Keyword(s):  
Heat Treatment ◽  
Particle Size ◽  
Electrochemical Performance ◽  
Heat Treatment Temperature ◽  
Sol Gel ◽  
Treatment Temperature ◽  
Preparation Process ◽  
Gel Method ◽  
Sol Gel Method ◽  
Ft Ir

The La0.75Sr0.25Cr0.5Mn0.5O3-δnanometer powders were prepared by citric acid sol-gel method.The samples were characterized by DTA, FT-IR, XRD, TEM techniques. The preparation process, morphology of synthesized powders, the best heat-treatment temperature and the electrochemical performance had been studied. The results show that the spherical nanometer powders can be obtained and the best heat-treatment temperature is 800°C. The particle size is about 30nm and Ea is 0.071 eV.

Synthesis and characterization of macroporous europium-doped Ca12Al14O33 (C12A7:Eu3+) and its application in metal ion detection

2019 ◽  
Vol 43 (21) ◽  
pp. 8315-8324
Author(s):  
Hui Yang ◽  
Rui Wang ◽  
Yaozu Wang ◽  
Jianzhong Jiang ◽  
Xingzhong Guo
Keyword(s):  
Heat Treatment ◽  
Metal Ion ◽  
Sol Gel ◽  
Synthesis And Characterization ◽  
Practical Application ◽  
Ion Detection ◽  
Gel Method ◽  
Sol Gel Method ◽  
Metal Ion Detection

Macroporous europium-doped Ca12Al14O33 (C12A7:Eu3+) was prepared via a sol–gel method followed by heat-treatment, and the resultant macroporous C12A7:Eu3+ shows potential for practical application in metal ion detection and has a good response to Pb2+ ions.

Preparation and Morphology of Mullite Whiskers by Sol-Gel Method

2007 ◽  
Vol 336-338 ◽  
pp. 1313-1315 ◽  
Author(s):  
Zhou Fu Wang ◽  
Chun Tian Du ◽  
Xi Tang Wang ◽  
Bao Guo Zhang
Keyword(s):  
Thermal Analysis ◽  
Aspect Ratio ◽  
High Aspect Ratio ◽  
Sol Gel ◽  
Gel Method ◽  
Sol Gel Method ◽  
Mullite Whiskers

Mullite whiskers were prepared by sol-gel method. The preparing conditions, the morphology and crystallite phase of the mullite whiskers were studied by Thermal analysis, XRD and SEM. The results demonstrate that the uniform mullite whiskers with high aspect ratio were obtained in properly preparing conditions and appropriate amount of fluorides.

Fabrication of Bi-2223 Powders Using Sol-Gel Method

2011 ◽  
Vol 412 ◽  
pp. 125-128 ◽  
Author(s):  
Ming Ya Li ◽  
Xiao Yan Wang ◽  
Cheng Li Ye ◽  
Feng Lin Xue
Keyword(s):  
Heat Treatment ◽  
Sol Gel ◽  
Chelating Agent ◽  
Experimental Results ◽  
Main Phase ◽  
Gel Method ◽  
Sol Gel Method ◽  
Dwelling Time ◽  
Metal Nitrates ◽  
Gel Technique

The Bi-2223 powders were fabricated by the sol-gel technique. Metal nitrates were used as starting materials, and ethylenediamineteracetic acid was used as chelating agent. The solution was heated until it turns to gel. Then the organic was removed at a temperature of 240°C, and the nitrite was removed at 500°C. The powder was calcined at different temperature, varying the dwelling time. Experimental results show that the main phase of samples after heat treatment is Bi-2212 phase.

The effect of thermal treatment conditions employed in sol-gel method on the structure of ZnO thin films

2009 ◽  
Vol 206 (9) ◽  
pp. 2139-2142 ◽  
Author(s):  
Takashi Ehara ◽  
Takafumi Otsuki ◽  
Junya Abe ◽  
Takaaki Ueno ◽  
Masahiro Ito ◽  
...  
Keyword(s):  
Thin Films ◽  
Thermal Treatment ◽  
Sol Gel ◽  
Zno Thin Films ◽  
Gel Method ◽  
Sol Gel Method ◽  
Treatment Conditions

Effects of Calcination Parameters on the Microstructure and Morphology of PZT Nanoparticles Prepared by Modified Sol–Gel Method

2012 ◽  
Vol 576 ◽  
pp. 326-329 ◽  
Author(s):  
Amid Shakeri ◽  
Hossein Abdizadeh ◽  
Mohammad Reza Golobostanfard
Keyword(s):  
Lead Zirconate Titanate ◽  
Sol Gel ◽  
Lead Zirconate ◽  
X Ray Diffraction ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Treatment Conditions ◽  
Perovskite Type ◽  
Perovskite Type Structure

Lead zirconate titanate nanopowder Pb(Zr0.53Ti0.47)O3 (PZT) was prepared by modified sol-gel method with 1-propanol as solvent and acetylacetone as stabilizer. The microstructure and particle size measurements at different heat treatment conditions were characterized by field emission scanning electron microscopy and x-ray diffraction analysis. It was found that the PZT nanoparticles calcinated at 600 °C showed mean diameter of 75-125 nm with high crystallinity of perovskite-type structure.

Sign in / Sign up

Export Citation Format

Share Document