Ultrasonic Pulse Method - Influence of Internal Compressive Stress on Results of Testing Calcium Silicate Bricks

2016 ◽  
Vol 722 ◽  
pp. 260-266
Author(s):  
Jiří Brožovský
Keyword(s):  
Compressive Strength ◽  
Calcium Silicate ◽  
Pulse Method ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Ultimate Compressive Strength ◽  
Technical Literature ◽  
Theoretical Assumptions ◽  
Inner Tension

Measuring with ultrasonic pulse method is influenced by various factors, like loading in particular inner tension when material built in a construction is tested. The paper researches influence of inner tension (load) on testing of calcium silicate bricks with ultrasonic pulse method. Calcium silicate bricks were loaded with force corresponding to 0 % (unloaded test specimens), 10 %, 20 %, 50 %, 60 % of ultimate compressive strength with various content of humidity (dried samples, w=2 %, w=8 % and samples saturated with water). It was found that ultrasonic pulse velocity is not considerably influenced at load of 10% and 20% of ultimate strength of bricks. However, ultrasonic pulse velocity considerably decreases after loading at 50% and 60% of ultimate compressive strength. Most of theoretical assumptions concerning mentioned concrete stated in technical literature were confirmed, however, particular values were different because of differences between concrete and calcium silicate bricks.

Analysis of Relations for Determination of Parameters of Various Types of Concrete Based on Ultrasonic Pulse Method Measurement

2014 ◽  
Vol 923 ◽  
pp. 99-107
Author(s):  
Jiří Brožovský ◽  
Jiří Bydžovský
Keyword(s):  
High Performance ◽  
Pulse Propagation ◽  
Pulse Method ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Normal Weight ◽  
Technical Literature ◽  
Determination Of Parameters

It is often necessary to determine strength of concrete (Normal-weight, High-performance and Light-Weight) in the structure. To determine strength, ultrasonic pulse method is used. However, the basic condition of its effective use is existence of relations between velocity of ultrasonic pulse propagation and strength. These relations are elaborated for normal weight concrete in great extent. However, for other types of concrete, relations for determination of strength on the basis of ultrasonic pulse velocity are stated in technical literature and their practical applicability could be questioned. The paper gives analysis of such relations from the point of view of practical applicability for determination of parameters of concrete built in a structure.

PENGKAJIAN KEKUATAN BETON STRUKTUR JEMBATAN PASCA KEBAKARAN

2013 ◽  
Vol 12 (3) ◽  
Author(s):  
Sudarmadi Sudarmadi
Keyword(s):  
Compressive Strength ◽  
Concrete Strength ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Test Results ◽  
Concrete Compressive Strength ◽  
Strength Assessment ◽  
Concrete Testing

In this paper a case study about concrete strength assessment of bridge structure experiencing fire is discussed. Assessment methods include activities of visual inspection, concrete testing by Hammer Test, Ultrasonic Pulse Velocity Test, and Core Test. Then, test results are compared with the requirement of RSNI T-12-2004. Test results show that surface concrete at the location of fire deteriorates so that its quality is decreased into the category of Very Poor with ultrasonic pulse velocity ranges between 1,14 – 1,74 km/s. From test results also it can be known that concrete compressive strength of inner part of bridge pier ranges about 267 – 274 kg/cm2 and concrete compressive strength of beam and plate experiencing fire directly is about 173 kg/cm2 and 159 kg/cm2. It can be concluded that surface concrete strength at the location of fire does not meet the requirement of RSNI T-12-2004. So, repair on surface concrete of pier, beam, and plate at the location of fire is required.

scholarly journals The Hydration, Mechanical, Autogenous Shrinkage, Durability, and Sustainability Properties of Cement–Limestone–Slag Ternary Composites

2021 ◽  
Vol 13 (4) ◽  
pp. 1881
Author(s):  
Mei-Yu Xuan ◽  
Yi Han ◽  
Xiao-Yong Wang
Keyword(s):  
Compressive Strength ◽  
Electrical Resistivity ◽  
Experimental Studies ◽  
Autogenous Shrinkage ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Hydration Heat ◽  
Granulated Blast Furnace Slag ◽  
Binder Ratio

This study examines the hydration–mechanical–autogenous shrinkage–durability–sustainability properties of ternary composites with limestone filler (LF) and ground-granulated blast furnace slag (BFS). Four mixtures were prepared with a water/binder ratio of 0.3 and different replacement ratios varying from 0 to 45%. Multiple experimental studies were performed at various ages. The experimental results are summarized as follows: (1) As the replacement levels increased, compressive strength and autogenous shrinkage (AS) decreased, and this relationship was linear. (2) As the replacement levels increased, cumulative hydration heat decreased. At the age of 3 and 7 days, there was a linear relationship between compressive strength and cumulative hydration heat. (3) Out of all mixtures, the ultrasonic pulse velocity (UPV) and electrical resistivity exhibited a rapid increase in the early stages and tended to slow down in the latter stages. There was a crossover of UPV among various specimens. In the later stages, the electrical resistivity of ternary composite specimens was higher than plain specimens. (4) X-ray diffraction (XRD) results showed that LF and BFS have a synergistic effect. (5) With increasing replacement ratios, the CO2 emissions per unit strength reduced, indicating the sustainability of ternary composites.

Estimation of Compressive Strength of Recycled Aggregate High Strength Concrete Using Ultrasonic Pulse Velocity

2014 ◽  
Vol 605 ◽  
pp. 147-150
Author(s):  
Seong Uk Hong ◽  
Seung Hun Kim ◽  
Yong Taeg Lee
Keyword(s):  
Compressive Strength ◽  
High Strength Concrete ◽  
Coarse Aggregate ◽  
High Strength ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Recycled Aggregate ◽  
Strength Concrete ◽  
Recycled Coarse Aggregate

This study used the ultrasonic pulse velocity method, one of the non-destructive test methods that does not damage the building for maintenance of to-be-constructed concrete structures using recycled aggregates in order to estimate the compressive strength of high strength concrete structure using recycled coarse aggregate and provide elementary resources for technological establishment of ultrasonic pulse velocity method. 200 test pieces of high strength concrete 40, 50MPa using recycled coarse aggregate were manufactured by replacement rates (0, 30, 50, 100%) and age (1, 7, 28, 180days), and air curing was executed to measure compressive strength and wave velocity. As the result of compressive strength measurement, the one with age of 180day and design strength of 40MPa was 43.69MPa, recycled coarse aggregate replacement rate of 30% 50% 100% were 42.82, 41.22, 37.35MPa, and 50MPa was 52.50MPa, recycled coarse aggregate replacement rate of 30% 50% 100% were 49.02, 46.66, 45.30MPa, and while it could be seen that the test piece substituted with recycled aggregate was found to have lower strength than the test piece with natural aggregate only, but it still reached the design strength to a degree. The correlation of compressive strength and ultrasonic pulse velocity was found and regression analysis was conducted. The estimation formula for compressive strength of high strength concrete using recycled coarse aggregate was found to be Fc=0.069Vp4.05, R2=0.66

scholarly journals Performance Evaluation of Concrete using Marble Mining Waste

2016 ◽  
Vol 11 (2) ◽  
pp. 53-66 ◽  
Author(s):  
Sudarshan Dattatraya Kore ◽  
A. K. Vyas
Keyword(s):  
Compressive Strength ◽  
Coarse Aggregate ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Mining Waste ◽  
Partial Replacement ◽  
Infrastructure Development ◽  
The Impact ◽  
Marble Waste

Abstract A huge amount waste (approximately 60%) is generated during mining and processing in marble industries. Such waste can be best utilized in infrastructure development works. Coarse aggregate 75% by weight was replaced by aggregate obtained from marble mining waste. The impact of marble waste as a partial replacement for conventional coarse aggregate on the properties of concrete mixes such as workability, compressive strength, permeability, abrasion, etc. was evaluated. The test results revealed that the compressive strength was comparable to that of control concrete. Other properties such as workability of concrete increased, water absorption reduced by 17%, and resistance to abrasion was marginally increased by 2% as compared to that of control concrete. Ultrasonic pulse velocity and FTIR results show improvement in quality of concrete with crushed marble waste. From the TGA analysis it was confirmed that, aggregate produced from marble waste shows better performance under elevated temperature than that of conventional aggregates.

scholarly journals Assessment of Concrete Compressive Strength by Ultrasonic Non-Destructive Test

2021 ◽  
Vol 318 ◽  
pp. 03004
Author(s):  
AbdulMuttalib I. Said ◽  
Baqer Abdul Hussein Ali
Keyword(s):  
Compressive Strength ◽  
Salt Content ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Experimental Program ◽  
Concrete Compressive Strength ◽  
Statistical Program ◽  
Non Destructive ◽  
Accurate Relation

This paper has carried out an experimental program to establish a relatively accurate relation between the ultrasonic pulse velocity (UPV) and the concrete compressive strength. The program involved testing concrete cubes of (100) mm and prisms of (100×100×300) cast with specified test variables. The samples are tested by using ultrasonic test equipment with two methods, direct ultrasonic pulse (DUPV) and surface (indirect) ultrasonic pulse (SUPV) for each sample. The obtained results were used as input data in the statistical program (SPSS) to predict the best equation representing the relation between the compressive strength and the ultrasonic pulse velocity. In this research 383 specimens were tested, and an exponential equation is proposed for this purpose. The statistical program has been used to prove which type of UPV is more suitable, the (SUPV) test or the (DUPV) test, to represent the relation between the ultrasonic pulse velocity and the concrete compressive strength. In this paper, the effect of salt content on the connection between the ultrasonic pulse velocity and the concrete compressive strength has also been studied.