Application of MIL-53(Fe) metal-organic framework material in catalytic wet oxidation of phenol

In the present study, MIL-53(Fe) metal-organic framework material was applied as catalyst for phenol oxidation reaction in aqueous solution with H2O2 under UV radiation. The materials were characterized using X-ray diffraction (XRD), and fourier transform infrared spectroscopy (FT-IR). The effects of reaction time, initial phenol concentration, and initial pH of the solution on phenol oxidation reactions were investigated. The results indicated that MIL-53(Fe) could work effectively in the wide pH range from 2 to 10. Phenol was quickly oxidized to form simple organic acids, including acetic acid, formic acid and oxalic acid.

Supercritical water oxidation of phenol and process enhancement with in situ formed Fe2O3 nano catalyst

During the past few decades, the treatment of hazardous waste and toxic phenolic compounds has become a major issue in the pharmaceutical, gas/oil, dying, and chemical industries. Considering polymerization and oxidation of phenolic compounds, supercritical water oxidation (SCWO) has gained special attention. The present study objective was to synthesize a novel in situ Fe2O3nano-catalyst in a counter-current mixing reactor by supercritical water oxidation (SCWO) method to evaluate the phenol oxidation and COD reduction at different operation conditions like oxidant ratios and concentrations. Synthesized nano-catalyst was characterized by powder X-ray diffraction (XRD) and transmission electron microscope (TEM). TEM results revealed the maximum average particle size of 26.18 and 16.20 nm for preheated and non-preheated oxidant configuration, respectively. XRD showed the clear peaks of hematite at a 2θ value of 24, 33, 35.5, 49.5, 54, 62, and 64 for both catalysts treated preheated and non-preheated oxidant configurations. The maximum COD reduction and phenol oxidation of about 93.5% and 99.9% were observed at an oxidant ratio of 1.5, 0.75 s, 25 MPa, and 380 °C with a non-preheated H2O2 oxidant, while in situ formed Fe2O3nano-catalyst showed the maximum phenol oxidation of 99.9% at 0.75 s, 1.5 oxidant ratio, 25 MPa, and 380 °C. Similarly, in situ formed Fe2O3 catalyst presented the highest COD reduction of 97.8% at 40 mM phenol concentration, 1.0 oxidant ratio, 0.75 s residence time, 380 °C, and 25 MPa. It is concluded and recommended that SCWO is a feasible and cost-effective alternative method for the destruction of contaminants in water which showed the complete conversion of phenol within less than 1 s and 1.5 oxidant ratio.