P-type single-crystalline ZnO films obtained by (N,O) dual implantation through dynamic annealing process

2016 ◽  
Vol 100 ◽  
pp. 468-473 ◽  
Author(s):  
Zhiyuan Zhang ◽  
Jingyun Huang ◽  
Shanshan Chen ◽  
Xinhua Pan ◽  
Lingxiang Chen ◽  
...  
2017 ◽  
Vol 28 (21) ◽  
pp. 16215-16219 ◽  
Author(s):  
Zhiyuan Zhang ◽  
Jingyun Huang ◽  
Shanshan Chen ◽  
Xinhua Pan ◽  
Lingxiang Chen ◽  
...  

2018 ◽  
Vol 483 ◽  
pp. 236-240 ◽  
Author(s):  
Zhiyuan Zhang ◽  
Jingyun Huang ◽  
Shanshan Chen ◽  
Xinhua Pan ◽  
Lingxiang Chen ◽  
...  

2018 ◽  
Vol 48 (2) ◽  
pp. 780-786 ◽  
Author(s):  
Zhiyuan Zhang ◽  
Jingyun Huang ◽  
Shanshan Chen ◽  
Xinhua Pan ◽  
Lingxiang Chen ◽  
...  

Carbon ◽  
2004 ◽  
Vol 42 (2) ◽  
pp. 317-321 ◽  
Author(s):  
C.X. Wang ◽  
G.W. Yang ◽  
C.X. Gao ◽  
H.W. Liu ◽  
Y.H. Han ◽  
...  

2013 ◽  
Vol 1494 ◽  
pp. 77-82
Author(s):  
T. N. Oder ◽  
A. Smith ◽  
M. Freeman ◽  
M. McMaster ◽  
B. Cai ◽  
...  

ABSTRACTThin films of ZnO co-doped with lithium and phosphorus were deposited on sapphire substrates by RF magnetron sputtering. The films were sequentially deposited from ultra pure ZnO and Li3PO4 solid targets. Post deposition annealing was carried using a rapid thermal processor in O2 and N2 at temperatures ranging from 500 °C to 1000 °C for 3 min. Analyses performed using low temperature photoluminescence spectroscopy measurements reveal luminescence peaks at 3.359, 3.306, 3.245 eV for the co-doped samples. The x-ray diffraction 2θ-scans for all the films showed a single peak at about 34.4° with full width at half maximum of about 0.17°. Hall Effect measurements revealed conductivities that change from p-type to n-type over time.


2014 ◽  
Vol 104 (11) ◽  
pp. 111905 ◽  
Author(s):  
Hoang-Phuong Phan ◽  
Dzung Viet Dao ◽  
Philip Tanner ◽  
Li Wang ◽  
Nam-Trung Nguyen ◽  
...  
Keyword(s):  

2012 ◽  
Vol 101 (11) ◽  
pp. 112101 ◽  
Author(s):  
M. A. Myers ◽  
M. T. Myers ◽  
M. J. General ◽  
J. H. Lee ◽  
L. Shao ◽  
...  

2008 ◽  
Vol 25 (9) ◽  
pp. 3400-3402 ◽  
Author(s):  
Wang Jing-Wei ◽  
Bian Ji-Ming ◽  
Liang Hong-Wei ◽  
Sun Jing-Chang ◽  
Zhao Jian-Ze ◽  
...  

Sign in / Sign up

Export Citation Format

Share Document