scholarly journals Preparation ofZincOxide Nanoparticles by UV-IrradiationMethod in Two Different Media

2021 ◽  
Vol 2114 (1) ◽  
pp. 012079
Author(s):  
Noor AlhudaMahammed Noori ◽  
Mahdi A. Mohammed
Keyword(s):  
Polyvinyl Alcohol ◽  
Aqueous Medium ◽  
Zinc Acetate ◽  
Deionized Water ◽  
Ease Of Use ◽  
Ultraviolet Rays ◽  
Zno Nps ◽  
Uv Visible ◽  
Polymeric Medium

Abstract The zinc oxidenanoparticles(ZnO NPs) were prepared in two media. The first one was in an aqueous medium resulting from the reaction of urea with zinc acetate at 0.3M concentration in both of them in deionized water. The second medium is a polymeric solution which is a dissolving of 4% polyvinyl alcohol (PVA)in deionized water with zinc acetate. The nanoparticles were obtained after the two media were irradiated with ultraviolet rays for 30 min. According to the characterization of the XRD, FESEM, and UV-visible, the polymeric medium gives a less granular size in addition to its ease of use and handling.

scholarly journals Antimicrobial Efficacy and Cell Adhesion Inhibition of In Situ Synthesized ZnO Nanoparticles/Polyvinyl Alcohol Nanofibrous Membranes

2016 ◽  
Vol 2016 ◽  
pp. 1-9 ◽  
Author(s):  
Jian Li ◽  
Qun Zhang ◽  
Minjing Xu ◽  
Changzhu Wu ◽  
Ping Li
Keyword(s):  
Cell Adhesion ◽  
Polyvinyl Alcohol ◽  
Zno Nanoparticles ◽  
Zinc Acetate ◽  
Membrane Damage ◽  
Antimicrobial Activities ◽  
Zno Nps ◽  
Adhesion Inhibition ◽  
Nanofibrous Membranes

Nanoparticle metal oxides are emerging as a new class of important materials in medical, agricultural, and industrial applications. In this context, free zinc oxide (ZnO) nanoparticles (NPs) have been increasingly shown with broad antimicrobial activities. However, biological properties of immobilized ZnO NPs on matrixes like nanofibrous membranes are still limited. In this study, in situ synthesized ZnO NPs/polyvinyl alcohol (PVA) nanofibrous membranes were fabricated by electrospinning with different zinc acetate concentrations. Characterization results indicated that, with 5 mM zinc acetate, uniform size ZnO NPs (~40 nm) were formed and evenly distributed on the membrane surface. The surfaces became more hydrophobic with higher concentration of zinc acetate. ZnO NPs/PVA nanofibrous membranes showed a broad spectrum of antimicrobial activities and cell adhesion inhibiting effects against four microorganisms including Gram-positive Staphylococcus aureus, Gram-negative Escherichia coli, fungi Candida albicans, and spores of Aspergillus niger. Our data revealed that the major antimicrobial mechanism could be attributed to cell membrane damage and cellular internalization of ZnO NPs, while the hydrophobic surface of the membrane primarily contributed to the cell adhesion inhibition. This study suggests that ZnO NPs/PVA nanofibrous membranes could potentially be used as an effective antimicrobial agent to maintain agricultural and food safety.

scholarly journals Synthesis and Characterization of Aluminum Doped Zinc Oxide Nanostructures by Nd:YAG Laser in Liquid

2020 ◽  
pp. 2590-2598
Author(s):  
Khawla S. Khashan ◽  
Ghassan M. Sulaiman ◽  
Sura A. Hussain
Keyword(s):  
Zinc Oxide ◽  
Visible Region ◽  
Laser Pulses ◽  
Deionized Water ◽  
Zinc Oxide Nanostructures ◽  
Zno Nps ◽  
Sem Images ◽  
Oxide Nanostructures ◽  
Aluminum Doped Zinc Oxide

Aluminum doped zinc oxide nanoparticles (AZO) with different doping concentrations were prepared by Nd-YAG laser ablation of target in deionized water. The characterization of these nanoparticles was performed using Fourier transform infrared (FTIR)  spectroscopy,  scanning electron microscopy (SEM) and photoluminance spectroscopy (PL).  FTIR spectra confirmed the formation  of vibrational bonds for ZnO NPs and AZO NPs. SEM images illustrated that the size and shape of the NPs changed with changing the number of laser pulses. Photoluminescence peaks exhibited two emission peaks, one at the UV region and the second in the visible region, which were modified as the number of laser pulses and doping concentration were changed.

scholarly journals Zinc Oxide and Silver Nanoparticle Effects on Intestinal Bacteria

Materials ◽  
2021 ◽  
Vol 14 (10) ◽  
pp. 2489
Author(s):  
Ami Yoo ◽  
Mengshi Lin ◽  
Azlin Mustapha
Keyword(s):  
Electron Microscopy ◽  
Zinc Oxide ◽  
Morphological Changes ◽  
Intestinal Bacteria ◽  
Bacterial Cells ◽  
Ag Nps ◽  
Zno Nps ◽  
Bifidobacterium Animalis ◽  
Transmission Electron

The application of nanoparticles (NPs) for food safety is increasingly being explored. Zinc oxide (ZnO) and silver (Ag) NPs are inorganic chemicals with antimicrobial and bioactive characteristics and have been widely used in the food industry. However, not much is known about the behavior of these NPs upon ingestion and whether they inhibit natural gut microflora. The objective of this study was to investigate the effects of ZnO and Ag NPs on the intestinal bacteria, namely Escherichia coli, Lactobacillus acidophilus, and Bifidobacterium animalis. Cells were inoculated into tryptic soy broth or Lactobacilli MRS broth containing 1% of NP-free solution, 0, 12, 16, 20 mM of ZnO NPs or 0, 1.8, 2.7, 4.6 mM Ag NPs, and incubated at 37 °C for 24 h. The presence and characterization of the NPs on bacterial cells were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy-dispersive X-ray spectroscopy (EDS). Membrane leakage and cell viability were assessed using a UV-visible spectrophotometer and confocal electron microscope, respectively. Numbers of treated cells were within 1 log CFU/mL less than those of the controls for up to 12 h of incubation. Cellular morphological changes were observed, but many cells remained in normal shapes. Only a small amount of internal cellular contents was leaked due to the NP treatments, and more live than dead cells were observed after exposure to the NPs. Based on these results, we conclude that ZnO and Ag NPs have mild inhibitory effects on intestinal bacteria.

Biofabrication and characterization of cyanobacteria derived ZnO NPs for their bioactivity comparison with commercial chemically synthesized nanoparticles

2021 ◽  
pp. 104999
Author(s):  
Nida Asif ◽  
Samreen Fatima ◽  
Md. Nafe Aziz ◽  
Shehzadi ◽  
Almaz Zaki ◽  
...  
Keyword(s):  
Zno Nps

Chemical, Physical and Engineering Characterization Of Candidate Backfill Clays and Clay Admixtures for a Nuclear Waste Respository-Part I

1981 ◽  
Vol 6 ◽  
Author(s):  
Sudesh K. Singh
Keyword(s):  
Nuclear Waste ◽  
Morphological Changes ◽  
Deionized Water ◽  
Engineering Properties ◽  
Nuclear Waste Repository ◽  
Exchange Cation ◽  
Mineral Components ◽  
Waste Repository ◽  
Mineralogical Compositions

ABSTRACTFourteen Canadian clays and clay admixtures were subjected to simulated nuclear waste repository environments. The present work is concerned with the montmorillonite-dominant materials only. The montmorillonite-dominant samples showed significant leaching on interaction with deionized water. On heating the samples at 200°C for 500 hours, montmorillomites lost intermicellar water completely and acquired cusp-like to cylindrical morphologies. The loss of water and the morphological changes in montmorillonites significantly altered the engineering characteristics. Permeability, shrinkage limits, compactability and shear strength varied in response to the dominant exchange cation in the structure of montmorillonites and the presence of other mineral components in the materials. The synthetic granite water reacted with montmorillonites and led to changes in chemical and mineralogical compositions, crystalline state and engineering properties.

Synthesis and Characterization of Tris(trimethyltin) Thiophosphate (Me3Sn)3PO3S

1993 ◽  
Vol 48 (12) ◽  
pp. 1781-1783 ◽  
Author(s):  
Abdel-Fattah Shihada
Keyword(s):  
Aqueous Medium ◽  
Raman Spectra ◽  
Mass Spectra ◽  
Ir And Raman Spectra ◽  
Synthesis And Characterization ◽  
Polymeric Structure ◽  
Ir And Raman

(Me3Sn)3PO3S has been prepared from the reaction of Me3SnCl with Na3PO3S • 12 H2O under cooling in aqueous medium. Its IR and Raman spectra are found to be consistent with a polymeric structure with tetra- and penta-coordinated tin atoms. The 31P NMR and mass spectra of (Me3Sn)3PO3S are reported and discussed.

pH Influences on Optical Absorption of Anthocyanin from Black Rice as Sensitizer for Dye Sensitized Solar Cell TiO2 Nanoparticles

2016 ◽  
Vol 864 ◽  
pp. 154-158
Author(s):  
Mariya Al Qibtiya ◽  
Eka Cahya Prima ◽  
Brian Yuliarto ◽  
Suyatman
Keyword(s):  
Solar Cell ◽  
Optical Absorption ◽  
Dye Sensitized Solar Cell ◽  
Black Rice ◽  
X Ray ◽  
Dye Sensitized ◽  
Current Voltage ◽  
Average Grain Size ◽  
Uv Visible

Natural dyes extracted from black rice are used as sensitizer for dye sensitized solar cell. The anthocyanin extracted with various pH in acidic and neutral coditions. Preparation of fotolectrode TiO2 film using doctor blade method and resulting average grain size 33,9 nm using X-Ray Diffractometer. Characterization of morphology and cross-section film TiO2 is confirmed by Scanning Electron microscopy (SEM). Optical absorption using UV-Visible Spectroscopy to obtain spectrum absorbance of anthocyanin in various pH. The current-voltage (J-V) characterization shows the performance DSSC have a match relation to the optical absorption. The best absorption of anthocyanin obtained at pH 6 as well as conversion efficiency reaches 2.26% at this pH condition.

Designing Soft Reactive Adhesives by Controlling Polymer Chemistry

MRS Bulletin ◽  
2003 ◽  
Vol 28 (6) ◽  
pp. 424-427 ◽  
Author(s):  
Agnès Aymonier ◽  
Eric Papon
Keyword(s):  
Automotive Industry ◽  
Ease Of Use ◽  
Large Strains ◽  
Structural Adhesives ◽  
Wide Range ◽  
Step Growth ◽  
Visible Irradiation ◽  
Step Growth Polymerization ◽  
Uv Visible ◽  
Activation Heat

AbstractSoft reactive adhesives (SRAs) are polymer-based materials (e.g., polyurethanes, polysiloxanes, polydienes) designed to be further vulcanized or slightly cross-linked through external activation (heat, moisture, oxygen, UV–visible irradiation, etc.), either at the time of their application or within a subsequent predefined period. They are used mainly as mastics, or sealing compounds, in a wide range of industrial and commercial fields such as construction, footwear, and the automotive industry. Generally deposited as thick films, SRAs behave as structural adhesives; their low elastic moduli accommodate large strains between the bonded parts without incurring permanent damage. Other outstanding attributes of SRAs are their resistance to solvents, their ability to withstand aggressive environments, and their ease of use. This article discusses examples of SRAs and, more specifically, shows how the cross-linking chemistry, mainly through step-growth polymerization, provides their primary advantages.

Sign in / Sign up

Export Citation Format

Share Document