Microstructures and mechanical properties of TiAl alloy fabricated by spark plasma sintering

2019 ◽  
Vol 34 (01n03) ◽  
pp. 2040036
Author(s):  
Yongjun Su ◽  
Yunfeng Lin ◽  
Na Zhang ◽  
Deliang Zhang
Keyword(s):  
Mechanical Properties ◽  
Spark Plasma Sintering ◽  
Alloy Powder ◽  
Room Temperature ◽  
Tial Alloy ◽  
Sintering Temperature ◽  
Tensile Tests ◽  
Alloyed Powder ◽  
Plasma Sintering ◽  
Spark Plasma

This work deals with the consolidation of a TiAl alloy powder by spark plasma sintering (SPS). Pre-alloyed powder with a composition of Ti–48Al–2Cr–2Nb (at.%) was consolidated in a SPS furnace at temperatures between 1200[Formula: see text]C and 1325[Formula: see text]C and with a pressure of 50 MPa. The microstructures obtained after SPS depend on the sintering temperature. Tensile tests at room temperature were performed. The alloy SPSed at temperatures not less than 1250[Formula: see text]C exhibits good properties at room temperature.

Microstructures and Mechanical Properties of Ti-43Al-5V-4Nb-Y Alloy Consolidated by Spark Plasma Sintering

2016 ◽  
Vol 704 ◽  
pp. 183-189
Author(s):  
Yong Jun Su ◽  
Yi Feng Zheng ◽  
De Liang Zhang ◽  
Fan Tao Kong
Keyword(s):  
Mechanical Properties ◽  
Spark Plasma Sintering ◽  
Tial Alloy ◽  
Tensile Tests ◽  
X Ray Diffraction ◽  
X Ray ◽  
Plasma Sintering ◽  
Short Period ◽  
Spark Plasma ◽  
Fully Lamellar

TiAl alloy with a composition of Ti-43Al-5V-4Nb-Y (at.%) was prepared by spark plasma sintering (SPS). The TiAl powders were sintered between 650°C and 1300°C for 5 min under different loads. With the increasing of the temperature, the diffusion of the elements can be observed. Full compaction is achieved in a short period of time and the overall processing duration does not exceed 30 min. A fully lamellar structure was seen in the TiAl alloy after heat treatment. The microstructures of the samples were determined by X-ray diffraction and scanning electron microscopy. Their mechanical properties were evaluated by tensile tests performed at room temperature

First Investigations on a TNM TiAl Alloy Processed by Spark Plasma Sintering

2012 ◽  
Vol 1516 ◽  
pp. 17-22 ◽  
Author(s):  
Thomas Voisin ◽  
Jean-Philippe Monchoux ◽  
Helmut Clemens ◽  
Alain Couret
Keyword(s):  
Phase Diagram ◽  
Spark Plasma Sintering ◽  
Room Temperature ◽  
Tial Alloy ◽  
Tensile Tests ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
First Time

ABSTRACTThe processing of a TNM powder (Ti-43.9Al-4Nb-0.95Mo-0.1B, in at.%) by Spark Plasma Sintering (SPS) was investigated for the first time. SPS experiments were performed at varying temperatures. The microstructures of the products were analyzed and interpreted in reference to the available phase diagram. Results of tensile tests conducted at room temperature are also presented.

Spark Plasma Sintering of Ti-4.5Al-3V-2Fe-2Mo (SP-700)

2010 ◽  
Vol 654-656 ◽  
pp. 819-822
Author(s):  
Genki Kikuchi ◽  
Hiroshi Izui ◽  
Yuya Takahashi ◽  
Shota Fujino
Keyword(s):  
Spark Plasma Sintering ◽  
Room Temperature ◽  
Volume Fraction ◽  
Titanium Boride ◽  
Tensile Tests ◽  
X Ray Diffraction ◽  
X Ray ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
Tib2 Particles

In this study, we focused on the sintering performance of Ti-4.5Al-3V-2Mo-2Fe (SP-700) and mechanical properties of SP-700 reinforced with titanium boride (TiB/SP-700) fabricated by spark plasma sintering (SPS). TiB whiskers formed in titanium by a solid-state reaction of titanium and TiB2 particles were analyzed with scanning electron microscopy and X-ray diffraction. The TiB/SP-700 was sintered at temperatures of 1073, 1173, and 1273 K and a pressure of 70 MPa for 10, 30, and 50 min. The volume fraction of TiB ranged from 1.7 vol.% to 19.9 vol.%. Tensile tests of TiB/SP-700 were conducted at room temperature, and the effect of TiB volume fraction on the tensile properties was investigated.

Microstructure and Mechanical Properties of Spark-Plasma-Sintered SiC-TiC Composites

2005 ◽  
Vol 287 ◽  
pp. 335-339 ◽  
Author(s):  
Kyeong Sik Cho ◽  
Kwang Soon Lee
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Heating Rate ◽  
Spark Plasma Sintering ◽  
Sintering Temperature ◽  
Applied Pressure ◽  
Argon Atmosphere ◽  
Full Density ◽  
Plasma Sintering ◽  
Spark Plasma

Rapid densification of the SiC-10, 20, 30, 40wt% TiC powder with Al, B and C additives was carried out by spark plasma sintering (SPS). In the present SPS process, the heating rate and applied pressure were kept at 100°C/min and at 40 MPa, while the sintering temperature varied from 1600-1800°C in an argon atmosphere. The full density of SiC-TiC composites was achieved at a temperature above 1800°C by spark plasma sintering. The 3C phase of SiC in the composites was transformed to 6H and 4H by increasing the process temperature and the TiC content. By tailoring the microstructure of the spark-plasma-sintered SiC-TiC composites, their toughness could be maintained without a notable reduction in strength. The strength of 720 MPa and the fracture toughness of 6.3 MPa·m1/2 were obtained in the SiC-40wt% TiC composite prepared at 1800°C for 20 min.

Fabrication of MgO/Graphene Composites by Combustion Synthesis and Spark Plasma Sintering

2018 ◽  
Vol 281 ◽  
pp. 125-130
Author(s):  
Nan Lu ◽  
Jia Xi Liu ◽  
Gang He ◽  
Jiang Tao Li
Keyword(s):  
Mechanical Properties ◽  
Combustion Synthesis ◽  
Spark Plasma Sintering ◽  
Sintering Temperature ◽  
Ceramic Composites ◽  
Combustion Reaction ◽  
Sintering Additive ◽  
Microstructure And Mechanical Properties ◽  
Plasma Sintering ◽  
Spark Plasma

MgO/Graphene ceramic composites were fabricated by combining combustion synthesis with spark plasma sintering. MgO/Graphene mixture powders were prepared by the combustion reaction between Mg powders and CO2 gas. Dense MgO/Graphene composites were fabricated by spark plasma sintering (SPS) using LiF as the sintering additive. The effect of the sintering temperature on microstructure and mechanical properties of the prepared MgO/Graphene ceramics was discussed. The sintering temperature of the MgO/Graphene mixture powders increased from 900°C to 1300°C. The highest density of 3.43g/cm3 and hardness of 2133MPa were obtained at 1100°C. Compared with monolithic MgO ceramics, the hardness of MgO/Graphene ceramics at the same sintering temperature was increased from 840MPa to 2133MPa.

Spark Plasma Sintering TiAl Alloy from Mechanically Activated Powders

2011 ◽  
Vol 250-253 ◽  
pp. 3309-3312 ◽  
Author(s):  
Zhi Wei Wang ◽  
Hong Cheng ◽  
Hui Ming Cheng
Keyword(s):  
Spark Plasma Sintering ◽  
Tial Alloy ◽  
Sintering Temperature ◽  
Al Alloy ◽  
Tial Alloys ◽  
Fine Grained ◽  
Plasma Sintering ◽  
Short Period ◽  
Spark Plasma ◽  
Higher Temperature

Powder of Ti-46at%Al alloy was synthesized through mechanical activation (MA) and then sintered and concurrently consolidated in a short sintering time of 900 s by using spark plasma sintering (SPS) process. The XRD and SEM profiles show that the microstructures of TiAl alloys contained γ TiAl and small amount α-2 Ti3Al phase, whose amount can be controlled by the sintering temperature. The compacts retained the original fine-grained fully densified bodies by avoiding an excessively high sintering temperature. The alloys sintered at higher temperature with this process showed a coarser microstructure. So it is possible to produce dense nanostructured TiAl alloys by mechanically activated spark plasma sintering (MASPS) within a very short period of time.