Experimental analysis of constant-amplitude fatigue properties in 6156 (Al-Mg-Si) sheet aluminum alloy

2018 ◽  
Vol 53 (8) ◽  
pp. 676-686
Author(s):  
Nikolaos D Alexopoulos ◽  
Evangelos Migklis ◽  
Dimitrios Myriounis
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Aluminum Alloys ◽  
Work Hardening ◽  
Endurance Limit ◽  
Fatigue Tests ◽  
Fatigue Properties ◽  
Constant Amplitude ◽  
The Matrix ◽  
Fatigue Endurance

Fatigue mechanical behavior of wrought aluminum alloy (Al-Mg-Si) 6156 at T4 temper is experimentally investigated. Constant-amplitude fatigue tests, at fixed stress ratio R = 0.1, were carried out, and the respective stress–life diagram was constructed and compared against the competitive 6xxx aluminum alloys, for example, 6082 and 6061. Fatigue endurance limit of AA6156 was found to be approximately 155 ± 5 MPa, that is, almost 30% below yield stress Rp of the material. AA6156 presents almost 50% higher fatigue life in the high-cycle fatigue area and approximately 20% higher fatigue endurance limit, when compared with other 6xxx series aluminum alloys. Significant work hardening was induced due to fatigue and was experimentally validated by the measurements of residual stiffness of fatigue loops as well as of absorbed energy per fatigue loop. Work-hardening exponent was essentially decreased by almost 25% from the first fatigue cycles and up to 10% of fatigue life. Fracture surfaces of specimens loaded at applied stresses close to fatigue endurance limit exhibited signs of coarse voids due to the formed precipitates at the matrix. The fracture mechanism was a mixture of transgranunal and intergranular fracture for the fatigue specimens tested at higher applied fatigue loadings.

scholarly journals Effects of Actual Marine Atmospheric Pre-Corrosion and Pre-Fatigue on the Fatigue Property of 7085 Aluminum Alloy

Metals ◽  
2022 ◽  
Vol 12 (1) ◽  
pp. 81
Author(s):  
Laixin Shi ◽  
Lin Xiang ◽  
Jianquan Tao ◽  
Jun Liu ◽  
Qiang Chen ◽  
...  
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Pitting Corrosion ◽  
Atmospheric Corrosion ◽  
Fatigue Property ◽  
Outdoor Exposure ◽  
Fatigue Tests ◽  
Constant Amplitude ◽  
Fatigue Fractography ◽  
Corrosion Mode

Effects of actual marine atmospheric precorrosion and prefatigue on the fatigue property of 7085-T7452 aluminum alloy were investigated by using the methods of marine atmospheric outdoor exposure tests and constant amplitude axial fatigue tests. Marine atmospheric corrosion morphologies, fatigue life, and fatigue fractography were analyzed. After three months of outdoor exposure, both pitting corrosion and intergranular corrosion (IGC) occurred, while the latter was the dominant marine atmospheric corrosion mode. Marine atmospheric precorrosion could result in a dramatical decrease in the fatigue life of the as-received 7085-T7452 aluminum alloy, while selective prefatigue can improve the total fatigue life of the precorroded specimen. The mechanism of the actual marine atmospheric corrosion and its effects on the fatigue life of the 7085-T7452 aluminum alloy were also discussed.

The Effects of Periodic High Loads on Fretting Fatigue

1981 ◽  
Vol 103 (3) ◽  
pp. 223-228 ◽  
Author(s):  
A. Kantimathi ◽  
J. A. Alic
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Growth Retardation ◽  
Fretting Fatigue ◽  
Fatigue Tests ◽  
Constant Amplitude ◽  
Axial Loads ◽  
Prolonged Fatigue ◽  
Stress Ratios ◽  
Crack Growth Retardation

Fretting fatigue tests have been conducted on 7075-T7351 aluminum alloy coupons with fretting pads of the same material. Three different stress ratios were used, the otherwise constant amplitude axial loads being interrupted every 1000 cycles by either tensile overloads to 400 MPa or compressive underloads to −200 MPa. Tensile overloads greatly prolonged fatigue life for low stresses where the overload ratios were 1.6 and above; compressive underloads had comparatively little effect. The results are discussed in terms of crack growth retardation phenomena.

Fatigue Tests on Specimens Containing Skew Holes

1976 ◽  
Vol 18 (6) ◽  
pp. 287-291 ◽  
Author(s):  
I. Ficenec ◽  
G. Craggs ◽  
B. N. Cole
Keyword(s):  
Fatigue Life ◽  
Endurance Limit ◽  
Fatigue Crack Initiation ◽  
Major Axis ◽  
Fatigue Tests ◽  
Minor Axis ◽  
Skew Angle ◽  
Cross Sectional ◽  
Skew Angles ◽  
Fatigue Endurance

The fatigue life of uniaxial fatigue specimens containing a skew hole is investigated. Contrary to expectation, fatigue life and fatigue endurance limit show no discernible change for vertical skew angles up to 45 when stress is calculated using the gross cross-sectional area. The point of fatigue crack initiation moves from the tip of the minor axis of the ellipse towards the tip of the major axis as skew angle increases.

scholarly journals The Effect of Laser Peening without Coating on the Fatigue of a 6082-T6 Aluminum Alloy with a Curved Notch

Metals ◽  
2019 ◽  
Vol 9 (7) ◽  
pp. 728 ◽  
Author(s):  
Enrico Troiani ◽  
Nicola Zavatta
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Residual Stresses ◽  
Fatigue Behavior ◽  
Surface Hardness ◽  
Element Model ◽  
Fatigue Tests ◽  
Fatigue Properties ◽  
Laser Peening ◽  
Laser Peening Without Coating

Laser shock peening has established itself as an effective surface treatment to enhance the fatigue properties of metallic materials. Although a number of works have dealt with the formation of residual stresses, and their consequent effects on the fatigue behavior, the influence of material geometry on the peening process has not been widely addressed. In this paper, Laser Peening without Coating (LPwC) is applied at the surface of a notch in specimens made of a 6082-T6 aluminum alloy. The treated specimens are tested by three-point bending fatigue tests, and their fatigue life is compared to that of untreated samples with an identical geometry. The fatigue life of the treated specimens is found to be 1.7 to 3.3 times longer. Brinell hardness measurements evidence an increase in the surface hardness of about 50%, following the treatment. The material response to peening is modelled by a finite element model, and the compressive residual stresses are computed accordingly. Stresses as high as −210 MPa are present at the notch. The ratio between the notch curvature and the laser spot radius is proposed as a parameter to evaluate the influence of the notch.

Fatigue Endurance under Torsion Testing: 6061-T6 and 6063-T5 Aluminum Alloys

2019 ◽  
Author(s):  
Jorge L. Avila Ambriz ◽  
Erasmo Correa Gómez ◽  
Julio C. Verduzco Juárez ◽  
Gonzalo M. Dominguez Almaraz ◽  
Aymeric E. Dominguez
Keyword(s):  
Fatigue Life ◽  
Aluminum Alloys ◽  
Load Ratio ◽  
Fatigue Tests ◽  
General Description ◽  
Fatigue Load ◽  
Industrial Property ◽  
Torsion Testing ◽  
Research Article ◽  
Fatigue Endurance

This article deals with torsion fatigue tests carried out on the aluminum alloys: AISI 6061-T6 and 6063-T5, under two load ratios: R = −1 and R = 0, both of them at 10 Hz of frequency. The tests were obtained at room temperature (23°C) and with environmental humidity comprised between 35% and 45%. Results reveal a noticeable fatigue endurance reduction on tests with R = 0 against tests at R = −1 for both aluminum alloys. The load ratio was fixed by imposing the initial angle before the testing starting. A new torsion fatigue machine has been developed by two of the authors (under patent consideration before the Mexican Institute of Industrial Property), which has the versatility of torsion tests at different frequencies and load ratios; a general description of this machine is presented in the article. The torsion fatigue life and the fracture surfaces were analyzed for the two aluminum alloys and both torsion fatigue load ratios, leading to drawing up the conclusions related to this research article.

Fatigue Behavior of Aerospace Al-Cu, Al-Li and Al-Mg-Si Sheet Alloys

2015 ◽  
Vol 1099 ◽  
pp. 1-8
Author(s):  
Nikolaos D. Alexopoulos ◽  
Vangelis Migklis ◽  
Stavros K. Kourkoulis ◽  
Zaira Marioli-Riga
Keyword(s):  
Mechanical Properties ◽  
Experimental Study ◽  
Fatigue Life ◽  
High Cycle Fatigue ◽  
Endurance Limit ◽  
Fatigue Behavior ◽  
Cycle Fatigue ◽  
Constant Amplitude ◽  
6Xxx Series ◽  
Fatigue Endurance

In the present work, an experimental study was performed to characterize and analyze the tensile and constant amplitude fatigue mechanical behavior of several aluminum alloys, namely 2024 (Al-Cu), 2198 (Al-Li) and 6156 (Al-Mg-Si). Al-Li alloy was found to be superior of 2024 in the high cycle fatigue and fatigue endurance limit regimes, especially when considering specific mechanical properties. Alloy 6156 was found to have superior constant amplitude fatigue performance that the respective 6xxx series alloys; more than 15% higher endurance limit was noticed against 6061 and almost 30% higher than 6082. Alloy 6156 presented only a marginal increase in fatigue life for the HCF regime.

Effect of Pre-Strain and Roller Working on Torsional Fatigue Properties of a Structural Steel

2011 ◽  
Vol 295-297 ◽  
pp. 2227-2230
Author(s):  
Cong Ling Zhou
Keyword(s):  
Residual Stress ◽  
Fatigue Limit ◽  
Work Hardening ◽  
Compressive Residual Stress ◽  
Strain Ratio ◽  
Fatigue Tests ◽  
The Other ◽  
Fatigue Properties ◽  
Torsional Fatigue ◽  
Stress Work

In this study, fatigue tests have been performed using two kinds of specimens made of 25 steel. One is pre-strained specimen with pre-strain ratio changing from 2% to 8% by tension, the other is roller worked with deformation of 0.5 mm and 1.0 mm in diameter direction. In the case of pre-strained specimen, the fatigue limit increases according to increase of tensile pre-strain, the fatigue limit of 8% pre-strained specimen is 25% higher than that of non-pre-strained one; in the case of roller worked specimen, the fatigue limit of R05 and R10 is 126% and 143% to that of non-roller worked specimen, respectively. These remarkable improvements of fatigue limit would be caused by the existence of compressive residual stress, work-hardening and the elongated microscopic structures.

Cyclic Mechanical Properties of 16MnR Welded Joint under Constant

2011 ◽  
Vol 197-198 ◽  
pp. 1658-1661
Author(s):  
Ying Xiong ◽  
Han Ying Zheng
Keyword(s):  
Mechanical Properties ◽  
Weld Metal ◽  
Endurance Limit ◽  
Welded Joint ◽  
Cyclic Softening ◽  
Fatigue Tests ◽  
Test Results ◽  
Control Test ◽  
Strain Control ◽  
Fatigue Endurance

Fatigue tests are carried out for 16MnR welded joint under constant strain control. Test results reveal that 16MnR weld metal exhibits characteristic of cyclic softening and non-masing obviously. The strain–life curve can be best described by the three-parameter equation. It shows the fatigue endurance limit in the heat-affecting zone (HAZ) of welded joint is lower than that in the weld metal.

scholarly journals Development in mechanical and fatigue properties of AA6061/AL2O3 nanocomposites under stirring temperature (ST)

2021 ◽  
Vol 4 (12(112)) ◽  
pp. 47-52
Author(s):  
Raad Mohammed Abed ◽  
Ali Yousuf Khenyab ◽  
Hussain Jasim M. Alalkawi
Keyword(s):  
Mechanical Properties ◽  
Cost Effective ◽  
Fatigue Tests ◽  
Core Material ◽  
Fatigue Properties ◽  
Uniform Distributions ◽  
Al2o3 Composite ◽  
Structural Applications ◽  
The Matrix ◽  
High Fatigue

Aluminum is expected to remain the core material for many critical applications such as aircraft and automobiles. This is due to the high resistance to different environmental conditions, desired and manageable mechanical properties, as well as high fatigue resistance. Aluminum nanocomposites such as AA6061/Al2O3 can be made in many ways using a liquid metallurgy method. The main challenges for this method in the production of nanocomposites are the difficulties of achieving a uniform distribution of reinforcing materials and possible chemical reactions between the reinforcing material and the matrix. For structural applications exclusive to aerospace sectors. The growing cost-effective nanocomposites mass production technology with essential operational and geometric flexibility is a big challenge all the time. Each method of preparing AA6061/Al2O3 nanocomposites can provide different mechanical properties. In the present study, nine nanocomposites were prepared at three stirring temperatures (800, 850, and 900 °C) with the level of Al2O3 addition of 0, 5, 7, and 9 wt %. The results of tensile, hardness and fatigue tests revealed that the composite including 9 wt % Al2O3 with 850 °C stirring temperatures has the best properties. It was also revealed that the 850 °C stirring temperature (ST) with 9 wt % Al2O3 composite provide an increase in tensile strength, VHN and reduction in ductility by 20 %, 16 % and 36.8 % respectively, compared to zero-nano. Also, the fatigue life at the 90 MPa stress level increased by 17.4 % in comparison with 9 wt % nanocomposite at 800 °C (ST). Uniform distributions were observed for all nine microstructure compositions.

scholarly journals Evaluation of Fatigue Characteristics of Aluminum Alloys and Mechanical Components Using Extreme Value Statistics and C-specimens

Metals ◽  
2021 ◽  
Vol 11 (12) ◽  
pp. 1915
Author(s):  
Jungsub Lee ◽  
Sang-Youn Park ◽  
Byoung-Ho Choi
Keyword(s):  
Aluminum Alloys ◽  
Fem Analysis ◽  
Extreme Value ◽  
Fatigue Tests ◽  
Extreme Value Statistics ◽  
Fatigue Properties ◽  
Chemical Compositions ◽  
Cross Sectional ◽  
Fatigue Characteristics ◽  
Mechanical Components

In this study, the fatigue characteristics of aluminum alloys and mechanical components were investigated. To evaluate the effect of forging, fatigue specimens with the same chemical compositions were prepared from billets and forged mechanical components. To evaluate the cleanliness of the aluminum alloys, the cross-sectional area of specimens was observed, and the maximum inclusion sizes were obtained using extreme value statistics. Rotary bending fatigue tests were performed, and the fracture surfaces of the specimens were analyzed. The results show that the forging process not only elevated the fatigue strength but also reduced the scatter of the fatigue life of aluminum alloys. The fatigue characteristics of C-specimens were obtained to develop finite-element method (FEM) models. With the intrinsic fatigue properties and strain–life approach, the FEM analysis results agreed well with the test results.

Sign in / Sign up

Export Citation Format

Share Document