Microstructure and mechanical properties of novel ternary electroconductive ceramics

2004 ◽  
Vol 19 (11) ◽  
pp. 3343-3352 ◽  
Author(s):  
Diletta Sciti ◽  
Stefano Guicciardi
Keyword(s):  
Mechanical Properties ◽  
High Temperature ◽  
Oxidation Resistance ◽  
Hot Pressing ◽  
Room Temperature ◽  
Matrix Material ◽  
Ceramic Composites ◽  
Microstructure And Mechanical Properties ◽  
Electrical Conductors ◽  
Poor Oxidation Resistance

Electroconductive ceramic composites, constituted of an insulating matrix (a composite AlN-SiC) containing 30 vol% of an electroconductive phase (MoSi2, ZrB2, or ZrC), were densified through hot-pressing. Microstructure and mechanical properties were compared to those of the AlN-SiC matrix material. All the ternary composites are good electrical conductors, with resistivities in the range 0.3 × 10-3to 4 × 10-3Ω·cm. Room temperature properties are improved by the addition of the electroconductive particles. Strength and toughness measurements at high temperature show that MoSi2-containing composite is stable up to 1300 °C (strength 611 MPa, toughness 3.7 MPa·m1/2), whereas ZrB2-containing composite is stable up to 1000 °C. ZrC-containing composite is not suitable for high-temperature applications due to poor oxidation resistance.

Microstructure and Mechanical Properties of SiC Whisker-Reinforced ZrB2 Ultra-High Temperature Ceramic

2008 ◽  
Vol 368-372 ◽  
pp. 1730-1732 ◽  
Author(s):  
Ping Hu ◽  
Xing Hong Zhang ◽  
Jie Cai Han ◽  
Song He Meng ◽  
Bao Lin Wang
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
High Temperature ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Room Temperature ◽  
Pressing Temperature ◽  
Sintering Time ◽  
Microstructure And Mechanical Properties ◽  
Ultra High Temperature

SiC whisker-reinforced ZrB2 matrix ultra-high temperature ceramic were prepared at 2000°C for 1 h under 30MPa by hot pressing and the effects of whisker on flexural strength and fracture toughness of the composites was examined. The flexural strength and fracture toughness are 510±25MPa and 4.05±0.20MPa⋅m1/2 at room temperature, respectively. Comparing with the SiC particles-reinforced ZrB2 ceramic, no significant increase in both strength and toughness was observed. The microstructure of the composite showed that the SiC whisker was destroyed because the SiC whisker degraded due to rapid atom diffusivity at high temperature. The results suggested that some related parameters such as the lower hot-pressing temperature, a short sintering time should be controlled in order to obtain SiC whiskerreinforced ZrB2 composite with high properties.

Effect of Hot Processing on Mircrostructure and Properties of Flat Billets of TA15 Titanium Alloy

2021 ◽  
Vol 1016 ◽  
pp. 906-910
Author(s):  
Xin Hua Min ◽  
Cheng Jin
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Titanium Alloy ◽  
High Temperature ◽  
Room Temperature ◽  
High Strength ◽  
Slow Cooling ◽  
Microstructure And Mechanical Properties ◽  
Ta15 Titanium Alloy ◽  
The Ideal

In this paper,effect of the different forging processes on the microstructure and mechanical properties of the flat flat billets of TA15 titanium alloy was investigated.The flat billiets of 80 mm×150 mm×L sizes of TA15 titanium alloy are produced by four different forging processes.Then the different microstrure and properties of the flat billiets were obtained by heat treatment of 800 °C~850 °C×1 h~4h.The results show that, adopting the first forging temperature at T1 °C、slow cooling and the second forging temperature at T2°C 、quick cooling, the primary αphases content is just 10%, and there are lots of thin aciculate phases on the base. This microstructure has both high strength at room temperature and high temperature, while the properties between the cross and lengthwise directions are just the same. So the hot processing of the first forging temperature at T1 °C、slow cooling and the second forging temperature at T2°C 、quick cooling is choosed as the ideal processing for production of aircraft frame parts.

Microstructure and Mechanical Properties of Hot Pressed ZrC-SiC-ZrB2 Composites

2010 ◽  
Vol 434-435 ◽  
pp. 173-177 ◽  
Author(s):  
Bao Xia Ma ◽  
Wen Bo Han ◽  
Xing Hong Zhang
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Grain Size ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Ceramic Composites ◽  
Strong Function ◽  
Slight Tendency ◽  
Microstructure And Mechanical Properties

Ternary ZrC-SiC-ZrB2 ceramic composites were prepared by hot pressing at 1900 °C for 60 min under a pressure of 30 MPa in argon. The influence of ZrB2 content on the microstructure and mechanical properties of ZrC-SiC-ZrB2 composites was investigated. Examination of SEM showed that the microstructure of the composites consisted of the equiaxed ZrB2, ZrC and SiC grains, and there was a slight tendency of reduction for grain size in ZrC with increasing ZrB2 content. The hardness increased considerably from 23.3 GPa for the ZS material to 26.4 GPa for the ZS20B material. Flexural strength was a strong function of ZrB2 content, increasing from 407 MPa without ZrB2 addition to 627 MPa when the ZrB2 content was 20vol.%. However, the addition of ZrB2 has little influence on the fracture toughness, ranging between 5.5 and 5.7 MPam1/2.

Effects of Carbon Black on Microstructure and Mechanical Properties of Hot Pressed ZrB2-SiC Ceramics

2010 ◽  
Vol 434-435 ◽  
pp. 185-188 ◽  
Author(s):  
Xin Sun ◽  
Xing Hong Zhang ◽  
Zhi Wang ◽  
Wen Bo Han ◽  
Chang Qing Hong
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
High Temperature ◽  
Carbon Black ◽  
Potential Method ◽  
Ceramic Composites ◽  
Grain Refining ◽  
Ultra High Temperature Ceramics ◽  
Sic Ceramics ◽  
Microstructure And Mechanical Properties

Abstract. ZrB2-SiC ultra-high temperature ceramics (UHTCs) was hot-pressed at a temperature of 1900°C with the addition of carbon black as a reinforcing phase. Microstructure and mechanical properties were investigated. Analysis revealed that the amount of carbon black had a significant influence on the sinterability and mechanical properties of ZrB2-SiC ceramics. When a small amount ( < 10 vol.%) of carbon black was introduced, it may react with oxide impurities (i.e. ZrO2, B2O3 and SiO2) present on the surface of the starting powder, thus promote the densification and grain refining of ZrB2-SiC ceramics. As a result, the mechanical properties including flexural strength and fracture toughness were improved. However, with the further adoption of carbon black, mechanical properties were not improved much, which could be attributed to the redundant phase at grain boundaries. The results presented here point to a potential method for improving densification, microstructure and mechanical properties of ZrB2-based ceramic composites.

Microstructure and Mechanical Properties of a Novel Ti-6.5Al-2Sn-4Zr-1.5Mo-2Nb-0.25Fe-0.2Si High-Temperature Titanium Alloy

2020 ◽  
Vol 993 ◽  
pp. 351-357
Author(s):  
Ming Yu Zhao ◽  
Xiao Yun Song ◽  
Wen Jing Zhang ◽  
Yu Wei Diao ◽  
Wen Jun Ye ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
High Temperature ◽  
Room Temperature ◽  
Annealing Treatment ◽  
Tensile Tests ◽  
Electron Backscattered Diffraction ◽  
Two Phase ◽  
Bimodal Structure ◽  
Α Phase ◽  
Microstructure And Mechanical Properties

The Ti-6.5Al-2Sn-4Zr-1.5Mo-2Nb-0.25Fe-0.2Si (wt%) alloy is a novel two-phase high temperature alloy for short-term application. The effects of different heat treatments on the microstructure and mechanical properties were investigated through electron probe microanalysis (EPMA), optical microcopy (OM), scanning electron microscope (SEM), electron backscattered diffraction (EBSD) and tensile tests at room temperature and 650°C. Subjected to the annealing treatment at α+β region (1010 °C/2 h, FC to 990 °C+990 °C/2 h, AC), the microstructure was composed of bimodal structure, which consists of equiaxed primary α (αp) phase and lamellar transformed β (βt) structure. As a strong β stabilizer, the content of Fe in α phase is much less than that in β phase. Annealing at β region (1040 °C/2 h, AC) resulted in the formation of widmannstatten structure, consisting of coarse raw β grain and secondary α phase precipitated on the β grain. With respect to the tensile property, different heat-treated alloys obtained similar strength. However, widmannstatten structure was characterized by lower plasticity, with the elongation only half that of bimodal structure. The fracture characteristics at room temperature for the alloy with bimodal structure and widmannstatten structure are dominated by ductile fracture and cleavage fracture, respectively.

Processing, mechanical properties and oxidation behavior of TaC and HfC composites containing 15 vol% TaSi2 or MoSi2

2009 ◽  
Vol 24 (6) ◽  
pp. 2056-2065 ◽  
Author(s):  
Diletta Sciti ◽  
Laura Silvestroni ◽  
Stefano Guicciardi ◽  
Daniele Dalle Fabbriche ◽  
Alida Bellosi
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
High Temperature ◽  
Mechanical Strength ◽  
Hot Pressing ◽  
Room Temperature ◽  
Oxidation Behavior ◽  
Temperature Stability ◽  
High Temperature Stability ◽  
Better Than

Fully dense HfC and TaC-based composites containing 15 vol% TaSi2 or MoSi2 were produced by hot pressing at 1750–1900 °C. TaSi2 enhanced the sinterability of the composites and nearly fully dense materials were obtained at lower temperatures than in the case of MoSi2-containing ones. The TaC-based composites performed better than HfC composites at room temperature, showing values of mechanical strength up to 900 MPa and a fracture toughness of 4.7 MPa·m1/2. However, preliminary oxidation tests carried out in air at 1600 °C revealed that HfC-based composites have a superior high temperature stability compared to TaC-based materials.