scholarly journals Temperature-Induced Precipitation of V2O5 in Vanadium Flow Batteries—Revisited

Batteries ◽  
2021 ◽  
Vol 7 (4) ◽  
pp. 87
Author(s):  
Emil Holm Kirk ◽  
Filippo Fenini ◽  
Sara Noriega Oreiro ◽  
Anders Bentien
Keyword(s):  
Temperature Stability ◽  
Time Lapse ◽  
High Temperature Stability ◽  
Ambient Temperatures ◽  
Operation Temperature ◽  
Batch Tests ◽  
External Oxidation ◽  
Flow Batteries ◽  
In Operando ◽  
Comprehensive Study

The maximum operation temperature of the vanadium solution in vanadium flow batteries is typically limited to 40 °C to prevent the damaging thermal precipitation of V2O5. Therefore, the operation of batteries at high ambient temperatures is an important aspect to tackle for stationary storage. In the present work, a comprehensive study of the high temperature stability of redox solutions for vanadium flow batteries was performed. In particular, focus was placed on a comparison between batch and in operando precipitation experiments. It was found that, despite being a widely used method in the literature, caution should be taken when assessing the precipitation through capacity fade due to the large influence of external oxidation and cycling parameters, plausibly leading to an incorrect interpretation of the results. The in operando experiments consistently show a precipitation temperature almost 10–20 °C higher than in the batch tests at a 100% state of charge for the same time lapse.

UNS N06455

Alloy Digest ◽  
1989 ◽  
Vol 38 (1) ◽  
Keyword(s):  
Corrosion Resistance ◽  
High Temperature ◽  
Stress Corrosion Cracking ◽  
Temperature Stability ◽  
Heat Treating ◽  
High Ductility ◽  
High Temperature Stability ◽  
Nickel Chromium ◽  
Long Time ◽  
Resistance To Stress

Abstract UNS NO6455 is a nickel-chromium-molybdenum alloy with outstanding high-temperature stability as shown by high ductility and corrosion resistance even after long-time aging in the range 1200-1900 F. The alloy also has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900 F. This datasheet provides information on composition, physical properties, hardness, elasticity, and tensile properties. It also includes information on corrosion resistance as well as forming, heat treating, machining, and joining. Filing Code: Ni-367. Producer or source: Nickel and nickel alloy producers.

UNS R54620

Alloy Digest ◽  
1987 ◽  
Vol 36 (7) ◽  
Keyword(s):  
Titanium Alloy ◽  
High Temperature ◽  
Time Use ◽  
Temperature Stability ◽  
High Strength ◽  
Heat Treating ◽  
High Temperature Stability ◽  
Beta Titanium Alloy ◽  
Beta Titanium ◽  
Long Time

Abstract UNS No. R54620 is an alpha-beta titanium alloy. It has an excellent combination of tensile strength, creep strength, toughness and high-temperature stability that makes it suitable for service to 1050 F. It is recommended for use where high strength is required. It has outstanding advantages for long-time use at temperatures to 800 F. This datasheet provides information on composition, physical properties, elasticity, tensile properties, and bend strength as well as creep. It also includes information on high temperature performance and corrosion resistance as well as forming, heat treating, machining, joining, and surface treatment. Filing Code: Ti-86. Producer or source: Titanium alloy mills.

Comparative Assessment of Sporophyte and Gametophyte Thermal Resistance of Winter Rape

2019 ◽  
pp. 15-22
Keyword(s):  
Elevated Temperatures ◽  
Rapid Assessment ◽  
Temperature Stability ◽  
Temperature Factor ◽  
Plant Genome ◽  
Limiting Factors ◽  
Initial Assessment ◽  
High Temperature Stability ◽  
Winter Rape ◽  
High Yields

The temperature factor is one of the limiting factors for obtaining high yields of crops, so one of the main tasks of selection is to search for temperature-resistant genotypes and to create on their basis the banks of crops with high temperature stability. The first step to solving this problem is to conduct a rapid assessment of the temperature plasticity of large populations and to isolate breeding-valuable genotypes from them. There are numerous methods that allow, in the short term with minimal technical and material costs, to carry out an initial assessment of a large number of genotypes at sporophytic level and differentiate them by resistance to the temperature factor. These methods include the method of estimating pollen populations. These studies have repeatedly been conducted on many cultures, their correctness is due to the expression of a large part of the plant genome, both at the diploid and haploid levels of development and demonstrated by many studies in this direction. The aim of our study was to study the stability of gametophyte and sporophyte of collecting varieties and varieties of winter rape to elevated temperatures, to study the correlation between the heat resistance of sporophyte and gametophyte.

scholarly journals Progress and perspectives in dielectric energy storage ceramics

2021 ◽  
Vol 10 (4) ◽  
pp. 675-703
Author(s):  
Dongxu Li ◽  
Xiaojun Zeng ◽  
Zhipeng Li ◽  
Zong-Yang Shen ◽  
Hua Hao ◽  
...  
Keyword(s):  
Energy Storage ◽  
Power Systems ◽  
Temperature Stability ◽  
Pulse Power ◽  
Research Progress ◽  
High Temperature Stability ◽  
Dielectric Ceramic ◽  
Microstructural Design ◽  
Pulse Power Systems ◽  
Fatigue Endurance

AbstractDielectric ceramic capacitors, with the advantages of high power density, fast charge-discharge capability, excellent fatigue endurance, and good high temperature stability, have been acknowledged to be promising candidates for solid-state pulse power systems. This review investigates the energy storage performances of linear dielectric, relaxor ferroelectric, and antiferroelectric from the viewpoint of chemical modification, macro/microstructural design, and electrical property optimization. Research progress of ceramic bulks and films for Pb-based and/or Pb-free systems is summarized. Finally, we propose the perspectives on the development of energy storage ceramics for pulse power capacitors in the future.

scholarly journals Performance and Microstructure of Cold Recycled Mixes Using Asphalt Emulsion with Different Contents of Cement

Materials ◽  
2019 ◽  
Vol 12 (16) ◽  
pp. 2548 ◽  
Author(s):  
Yanhai Yang ◽  
Ye Yang ◽  
Baitong Qian
Keyword(s):  
Low Temperature ◽  
Temperature Stability ◽  
Hydration Products ◽  
High Temperature Stability ◽  
Asphalt Emulsion ◽  
Moisture Susceptibility ◽  
Pavement Maintenance ◽  
Maintenance And Rehabilitation ◽  
Low Temperature Cracking ◽  
Temperature Crack

Cold recycled mixes using asphalt emulsion (CRME) is an economical and environmentally-friendly technology for asphalt pavement maintenance and rehabilitation. In order to determine the optimum range of cement contents, the complex interaction between cement and asphalt emulsion and the effects of cement on performance of CRME were investigated with different contents of cement. The microstructure and chemical composition of the fracture surface of CRME with different contents of cement were analyzed in this paper as well. Results show that the high-temperature stability and moisture susceptibility of CRME increased with the contents of cement increasing. The low-temperature crack resistance ability gradually increased when the content of cement is increased from 0% to 1.5%. However, it gradually decreased when the content of cement is increased from 1.5% to 4%. Cold recycled mixes had better low-temperature cracking resistance when the contents of cement were in the range from 1% to 2%. The results of microstructure and energy spectrum analysis show that the composite structure is formed by hydration products and asphalt emulsion. The study will be significant to better know the effects of cement and promote the development of CRME.

Sign in / Sign up

Export Citation Format

Share Document