scholarly journals Elastic and Anelastic Behavior of Microwave Sintered BCT-BST Ceramics

2019 ◽  
Vol 9 (1S3) ◽  
pp. 392-396
Keyword(s):  
Piezoelectric Coefficient ◽  
Sol Gel ◽  
Ultrasonic Waves ◽  
Molten Salt Method ◽  
Solid State Method ◽  
Cubic Crystal ◽  
X Ray ◽  
Transmission Electron ◽  
Anelastic Behavior ◽  
Bst Ceramics

Lead free 0.55(Ba0.9Ca0.1) TiO3-0.45Ba (Sn0.2Ti0.8) O3 (BCT-BST) ceramic is synthesized by three different techniques viz solid state method, sol-gel method and molten-salt method. The prepared BCT-BST ceramic samples exhibited cubic crystal structure on X-ray powder diffraction analysis. The morphology of the samples is analyzed using transmission electron microscope. The lattice interactions with ultrasonic waves and morphotropic phase boundary at 70oC is confirmed from elastic and anelastic studies of the ceramic. High piezoelectric coefficient d33 of 623 pC/N is achieved in the prepared BCT-BST ceramics.

scholarly journals Synthesis, characterization and in vitro cytotoxicity study of Co and Ni ferrite nanoparticles prepared by sol-gel method

2021 ◽  
Vol 3 (7) ◽  
Author(s):  
Alexandre Pancotti ◽  
Dener Pereira Santos ◽  
Dielly Oliveira Morais ◽  
Mauro Vinícius de Barros Souza ◽  
Débora R. Lima ◽  
...  
Keyword(s):  
Photoelectron Spectroscopy ◽  
Sol Gel ◽  
Test Sample ◽  
In Vitro Cytotoxicity ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Transmission Electron ◽  
Crystallite Sizes

AbstractIn this study, we report the synthesis and characterization of NiFe2O4 and CoFe2O4 nanoparticles (NPs) which are widely used in the biomedical area. There is still limited knowledge how the properties of these materials are influenced by different chemical routes. In this work, we investigated the effect of heat treatment over cytotoxicity of cobalt and niquel ferrites NPs synthesized by sol-gel method. Then the samples were studied using transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), vibrating sample magnetometer (VSM), Fourier Transform Infrared Spectroscopy Analysis (FTIR), and X-ray fluorescence (XRF). The average crystallite sizes of the particles were found to be in the range of 20–35 nm. The hemocompatibility (erythrocytes and leukocytes) was checked. Cytotoxicity results were similar to those of the control test sample, therefore suggesting hemocompatibility of the tested materials.

Effect of Calcinations on Characterizations of Fabricated Nano Manganese Ferrite

2013 ◽  
Vol 634-638 ◽  
pp. 2150-2154 ◽  
Author(s):  
Rita Sundari ◽  
Tang Ing Hua ◽  
M. Rusli Yosfiah
Keyword(s):  
Sol Gel ◽  
Volatile Components ◽  
Manganese Ferrite ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Reflectance Analysis ◽  
Transmission Electron Microscope Analysis ◽  
Electron Microscope Analysis ◽  
Nano Size

A citric acid anionic surfactant has been applied for nano manganese ferrite (MnFeO3) fabrication using sol gel method. The calcinations have been varied for 300, 600 and 800oC. The UVDR (UV-Vis Diffused Reflectance) analysis shows a high absorptive band gap after 400 nm for the 600oC calcinated MnFeO3. The DTA (Differential Thermal Analysis) profiles exhibit remarkably trapped volatile matters (H2O, CO2, and NO2) in the fabricated MnFeO3 under sol gel heat treatment at 100oC and the peaks disappeared as the calcination increased to 600oC. As the temperature elevated from 100 to 300oC, the absorption peaks of volatile components are disappeared as demonstrated clearly by the FTIR (Fourier Transform Infrared) spectra of the fabricated material, which 3393 cm-1 corresponded to OH group, 1624 cm-1 to CO group, and 1384 cm-1 to NO group. The XRD (X-Ray Diffraction) spectra show clearly the alteration process from amorphous to crystalline structure as the calcinations increased from 300 to 600oC. In addition, the TEM (Transmission Electron Microscope) analysis exhibits parts of the fabricated MnFeO3 found in cubic nano size of 15-40 nm under interested calcinations and the result is in agreement with that obtained by XRD investigation.

Characterization of ordered mesoporous films on silicon (001) surface using X-ray and electron diffraction

2005 ◽  
Vol 38 (1) ◽  
pp. 211-216 ◽  
Author(s):  
Pang-Hung Liu ◽  
Kuei-Jung Chao ◽  
Xing-Jian Guo ◽  
Kuo-Ying Huang ◽  
Yen-Ru Lee ◽  
...  
Keyword(s):  
Electron Diffraction ◽  
Sol Gel ◽  
Dip Coating ◽  
Silica Film ◽  
Continuous Film ◽  
X Ray ◽  
Transmission Electron ◽  
Ordered Mesoporous ◽  
Direction Dependence

A continuous silica film with well aligned mesochannels parallel to the Si(001) surface was found to be formed through sol–gel dip-coating of a silica precursor with nonionic ethylene oxide surfactant. Two two-dimensional mesoporous structures in centered and non-centered rectangular symmetries and with the short axes of elongated ellipsoidal pores normal to the surface were observed by X-ray and electron diffraction. Detailed transmission electron microscopy investigations were employed to view the direction dependence of the channel or pore packing in the continuous film.

Evaluation Humidity Sensing Properties of Graphene/HS-TiO2 Nanocomposites

2021 ◽  
Vol 21 (10) ◽  
pp. 5143-5149
Author(s):  
Zhen Zhu ◽  
Wang-De Lin
Keyword(s):  
Room Temperature ◽  
Response Times ◽  
Sol Gel ◽  
Hollow Spheres ◽  
High Sensitivity ◽  
Humidity Sensing ◽  
X Ray ◽  
Transmission Electron ◽  
Recovery Times ◽  
Relative Humidity Range

This paper reports on a nanocomposite synthesized by sol–gel procedure comprising graphene sheets with hollow spheres of titanium dioxide (G/HS-TiO2) with varying weight percentages of graphene for the purpose of humidity sensors. The surface morphology of the nanocomposite was characterized using transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDX). The structural properties were examined using X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR). The response to 12–80% RH at room temperature exhibited sensitivity (S = 135). However, the relative humidity range of 12–90% at room temperature exhibited higher sensitivity (S = 557). Sensors fabricated using the proposed nanocomposite exhibited high sensitivity to humidity, high stability, rapid response times, and rapid recovery times with hysteresis error of less than 1.79%. These results demonstrate the outstanding potential of his material for the monitoring of atmospheric humidity. This study also sought to elucidate the mechanisms underlying humidity sensing performance.

FeYO3@rGO nanocomposites: Synthesis, characterization and application in photooxidative degradation of atrazine under visible light

2021 ◽  
Vol 11 (5) ◽  
pp. 706-716
Author(s):  
Nada D. Al-Khthami ◽  
Tariq Altalhi ◽  
Mohammed Alsawat ◽  
Mohamed S. Amin ◽  
Yousef G. Alghamdi ◽  
...  
Keyword(s):  
Visible Light ◽  
Photoelectron Spectroscopy ◽  
Sol Gel ◽  
Bandgap Energy ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Reduced Graphene ◽  
Structural Surface ◽  
Adsorption Desorption

Different organic pollutants have been remediated photo catalytically by applying perovskite photocatalysts. Atrazine (ATR) is a pesticide commonly detected as a pollutant in drinking, surface and ground water. Herein, FeYO3@rGO heterojunction was synthesized and applied for photooxidation decomposition of ATR. First, FeYO 3nanoparticles (NPs) were prepared via routine sol-gel. After that, FeYO3 NPs were successfully incorporated with different percentages (5, 10, 15 and 20 wt.%) of reduced graphene oxide (rGO) in the synthesis of novel FeYO3@rGO photocatalyst. Morphological, structural, surface, optoelectrical and optical characteristics of constructed materials were identified via X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Transmission electron microscopy (TEM), adsorption/desorption isotherms, diffusive reflectance (DR) spectra, and photoluminescence response (PL). Furthermore, photocatalytic achievement of the constructed materials was evaluated via photooxidative degradation of ATR. Various investigations affirmed the usefulness of rGO incorporation on the advancement of formed photocatalysts. Actually, novel nanocomposite containing rGO (15 wt.%) possessed diminished bandgap energy, as well as magnified visible light absorption. Furthermore, such nanocomposite presented exceptional photocatalytic achievement when exposed to visible light as ATR was perfectly photooxidized over finite amount (1.6 g · L-1) from the optimized photocatalyst when illuminated for 30 min. The advanced photocatalytic performance of constructed heterojunctions could be accredited mainly to depressed recombination amid induced charges. The constructed FeYO3@rGO nanocomposite is labelled as efficient photocatalyst for remediation of herbicides from aquatic environments.

scholarly journals Effect of Preheating Temperature on Synthesis of Pure BiFeO3 via Sol–Gel Method

Nanopages ◽  
2019 ◽  
pp. 1-11
Author(s):  
G. M. Taha ◽  
M. N. Rashed ◽  
M. S. El-Sadek ◽  
M. A. Moghazy
Keyword(s):  
Electron Microscope ◽  
Transmission Electron Microscope ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
Pure Bifeo3 ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Transmission Electron ◽  
Preheating Temperature

Abstract BiFeO3 (BFO) nanopowder was synthesized in a pure form via a sol- gel method based on glycol gel reaction. Effect of drying and preheating temperature on preventing other phases was studied. Many parameters were studied as calcination temperature and time & stirring temperature as well. The prepared powder was characterized by X-Ray Diffraction of powder (XRD) and Transmission Electron Microscope (TEM). High pure BiFeO3 was obtained by preheated process at 400 °C for 0.5 h and calcination at 600 °C for 0.5 h without any impurities compared to dry at110 °C.

Synthesis of Nanosized HMS Mesoporous Molecular Sieve in an Ionic Liquid-Water Mixture

2011 ◽  
Vol 236-238 ◽  
pp. 2110-2113
Author(s):  
Hong Liu ◽  
Meng Yang Wang ◽  
Wei Ran Cao
Keyword(s):  
Electron Microscopy ◽  
Ionic Liquid ◽  
Sol Gel ◽  
Mesoporous Molecular Sieve ◽  
Nano Particles ◽  
Water Mixture ◽  
X Ray ◽  
Transmission Electron ◽  
Adsorption Desorption ◽  
Synthesized Materials

The hexagonal mesoporous silica (HMS) nano-particles were prepared in mixture of 1-butyl-3-methyl-imidazolium tetrafluoroborate (BMIM+BF4-) ionic liquid and water by a sol-gel method. The structure and morphology of obtained materials were characterized by X-ray powder diffraction (XRD), N2adsorption-desorption, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and dynamic light scattering (DLS). The influence of the amount of BMIM+BF4-was investigated. It was shown that the synthesized materials have discrete and uniform spherical morphology with the size in the range of 68-177 nm (obtained from DLS measurements), and the particle size of HMS can be controlled by varying the amount of BMIM+BF4-.

Low-Temperature Synthesis of Nano-Crystalline ZnTiO3 Powders by Aqueous Sol-Gel Process

2014 ◽  
Vol 543-547 ◽  
pp. 3741-3744
Author(s):  
Quan Jing Mei ◽  
Cong Ying Li ◽  
Jing Dong Guo ◽  
Gui Wang ◽  
Hai Tao Wu
Keyword(s):  
Sol Gel ◽  
Zinc Nitrate ◽  
X Ray Diffraction ◽  
Low Temperature Synthesis ◽  
Temperature Synthesis ◽  
Calcination Process ◽  
X Ray ◽  
Nano Crystalline ◽  
Transmission Electron ◽  
Sol Gel Process

The ecandrewsite-type ZnTiO3was successfully synthesized by the aqueous sol-gel method using TiO2dioxide and zinc nitrate as starting materials instead of expensive organic solvent and metal alkoxides. The as-prepared nanopowders were characterized by X-ray diffraction (XRD), differential thermal analysis (DTA) and transmission electron microscopy (TEM), respectively. The results showed that the calcination process of gel consisted of a series of oxidation and combustion reactions, accompanied by significantly exothermal effects. Highly reactive nanosized ZnTiO3powders were successfully obtained at 850 °C with particle size ~50 nm. By comparison, the aqueous sol-gel process was the most effective and least expensive technique used for the preparation of ZnTiO3nanopowders.

scholarly journals Ultrasound enhanced heterogeneous activation of peroxymonosulfate by a Co-NiOx catalyst

2017 ◽  
Vol 76 (6) ◽  
pp. 1436-1446 ◽  
Author(s):  
Chenmo Wei ◽  
Jing Zhang ◽  
Yongli Zhang ◽  
Gucheng Zhang ◽  
Peng Zhou ◽  
...  
Keyword(s):  
Photoelectron Spectroscopy ◽  
Sol Gel ◽  
Maximum Efficiency ◽  
Acid Orange 7 ◽  
X Ray Diffraction ◽  
X Ray ◽  
Surface Hydroxyl ◽  
Transmission Electron ◽  
Initial Ph ◽  
Reactive Oxidant

Sulfate radical-based advanced oxidation processes have had considerable attention due to the highly oxidizing function of sulfate radicals (SO4−·) resulting in acceleration of organic pollutants degradation in aqueous environments. A Co-Ni mixed oxide nanocatalyst, which was prepared by the sol-gel method, was employed to activate peroxymonosulfate (PMS, HSO5−) to produce SO4−· with Acid Orange 7 (AO7) selected as a radical probe. The catalyst was characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR) and transmission electron microscopy (TEM). The characterization results indicated that the ingredient of the catalyst had been changed and the amount of surface hydroxyl increased significantly with the addition of Ni. Therefore, it proved that Co-NiOx catalyst was more effective than CoOx to activate PMS. Moreover, ultrasound (US) can increase the degradation rate of AO7 and US/Co-NiOx/PMS system. This study also focused on some synthesis parameters and the system reached the maximum efficiency under the condition when [PMS] = 0.4 mM, [catalyst] = 0.28 g/L, Pus = 200 W. The AO7 removal in these systems follows first order kinetics. Last but not least, quenching studies was conducted which indicated that the amount of hydroxyl radicals (·OH) increases with the increase of initial pH and SO4−· was the primary reactive oxidant for AO7 degradation.

Sign in / Sign up

Export Citation Format

Share Document