CuO Microspheres Synthesized via the Easy Hydrothermal Method

2012 ◽  
Vol 159 ◽  
pp. 84-87
Author(s):  
Xiao Ming Fu
Keyword(s):  
Electron Microscope ◽  
Reaction Time ◽  
Scanning Electron Microscope ◽  
Hydrothermal Method ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Cuo Microspheres ◽  
Scanning Electron

CuO microspheres are successfully synthesized with CuCl2 as copper source and Na2CO3 as auxiliary salt at 240 °C for 24 h via the easy hydrothermal method. The phase and the morphologies of the samples have been characterized and analyzed by XRD (X-ray diffraction) and SEM (Scanning electron microscope), respectively. XRD analysis shows that the phase of as obtained samples is CuO. SEM analysis confirms that the increase of the reaction time, the reaction temperature and the auxiliary salt is propitious to synthesize CuO microspheres.

Synthesis of CuO Flower-Nanostructure via the Hydrothermal Method

2013 ◽  
Vol 873 ◽  
pp. 131-134
Author(s):  
Xiao Ming Fu ◽  
Jie Ren
Keyword(s):  
Electron Microscope ◽  
Reaction Time ◽  
Scanning Electron Microscope ◽  
Hydrothermal Method ◽  
Reaction Temperature ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

CuO flower-nanostructures are successfully synthesized with CuCl2 as copper source and Na2CO3 as auxiliary salt at 180 °C for 24 h via the simple hydrothermal method. The phase and the morphologies of the samples have been characterized and analyzed by XRD (X-ray diffraction) and SEM (Scanning electron microscope), respectively. XRD analysis shows that the phase of as obtained samples is CuO. SEM analysis confirms that the increase of the reaction temperature is propitious to synthesize CuO flower-nanostructures while the increase of the reaction time is not in favor of their synthesis. The influence of the increase of the auxiliary salt on the morphology of CuO flower-nanostructures is not remarkable. The mechanism of the formation of CuO flower-nanostructure is discussed.

The Effect of CaCO3 Addition on Physical Properties of ZnO-Based Crystal Glaze

2012 ◽  
Vol 620 ◽  
pp. 12-16 ◽  
Author(s):  
Abdul Rashid Jamaludin ◽  
Shah Rizal Kasim ◽  
Zainal Arifin Ahmad
Keyword(s):  
Electron Microscope ◽  
Calcium Carbonate ◽  
Scanning Electron Microscope ◽  
Physical Properties ◽  
Crystallization Temperature ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

The effects of calcium carbonate (CaCO3) addition on the physical properties of ZnO-based crystal glaze batches were investigated. Samples were fired at different gloss firing temperatures ranging from 1180-1220°C with 3 hours soaking at 1060°C crystallization temperature. X-ray diffraction (XRD) analysis identifiedthe crystal phase occurred as willemite (Zn2SiO4) and the scanning electron microscope (SEM) analysis indicated that willemite crystals are in the acicular needle like shape that formed spherulite. The intensities of willemite peaks decreased with CaCO3 addition and completely vanished at 5.0 wt% CaCO3. Varied formation of spherulites developed of the surface of crystal glaze as the flows of the glaze stretched further as the amount of CaCO3 increased.

The Influence of the Hydrothermal Temperature on the Morphologies of β-Ni(OH)2 Nanospheres and Nanoflakes

2012 ◽  
Vol 159 ◽  
pp. 376-379 ◽  
Author(s):  
Xiao Ming Fu
Keyword(s):  
Electron Microscope ◽  
High Temperature ◽  
Scanning Electron Microscope ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
Hydrothermal Temperature ◽  
X Ray ◽  
Low Reaction Temperature ◽  
Scanning Electron

β-Ni(OH)2 nanospheres and nanoflakes have been successfully synthesized with nickel nitrate as nickel source and stronger ammonia water as precipitant via the hydrothermal method. The phase and the morphologies of the samples have been characterized and analyzed by XRD (X-ray diffraction) and SEM (Scanning electron microscope), respectively. XRD analysis shows that the phase of the samples is β-Ni(OH)2. SEM analysis confirms that the low reaction temperature is propitious to the synthesis of β-Ni(OH)2 nanospheres. However, The high temperature is in favor of the synthesis of β-Ni(OH)2 nanosflakes.

The Influence of the Hydrothermal Conditions on the Morphologies of β-Ni(OH)2

2012 ◽  
Vol 562-564 ◽  
pp. 494-497
Author(s):  
Xiao Ming Fu
Keyword(s):  
Electron Microscope ◽  
High Temperature ◽  
Reaction Time ◽  
Scanning Electron Microscope ◽  
Reaction Temperature ◽  
X Ray Diffraction ◽  
Hydrothermal Conditions ◽  
X Ray ◽  
Low Reaction Temperature ◽  
Scanning Electron

Flower-like β-Ni(OH)2 and nanoflakes have been successfully synthesized with nickel nitrate as nickel source and stronger ammonia water as precipitant via the hydrothermal method. The phase and the morphologies of the samples have been characterized and analyzed by XRD (X-ray diffraction) and SEM (Scanning electron microscope), respectively. XRD shows that the phase of the samples is β-Ni(OH)2. SEM confirms that The low reaction temperature is propitious to the synthesis of flower-like β-Ni(OH)2, and with the increase of the reaction time the nanoflakes of flower-like β-Ni(OH)2 become much thinner. However, The high temperature is in favor of the synthesis of β-Ni(OH)2 nanosflakes, and with the further increase of the reaction temperature.

scholarly journals Characterization of Fe Doped AC/TiO2

2019 ◽  
Vol 8 (12S) ◽  
pp. 1146-1147
Keyword(s):  
Activated Carbon ◽  
Electron Microscope ◽  
Scanning Electron Microscope ◽  
Anatase Phase ◽  
Sol Gel ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

Abstract: The photocatalytic composite Fe doped AC/TiO2 has been prepared by sol-gel method. The prepared Fe doped AC/TiO2 composite were characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD).The SEM analysis showed that Fe and TiO2 were attached to the Activated Carbon surfaces. The X-Ray Diffraction data showed that Fe doped AC/TiO2 composite mostly contained anatase phase.

β-Ni(OH)2 Nanospheres Synthesized via the Easy Hydrothermal Method

2012 ◽  
Vol 510 ◽  
pp. 575-578
Author(s):  
Xiao Ming Fu
Keyword(s):  
Electron Microscope ◽  
Scanning Electron Microscope ◽  
Hydrothermal Method ◽  
Reaction Temperature ◽  
Nickel Nitrate ◽  
X Ray Diffraction ◽  
Ammonia Water ◽  
X Ray ◽  
Scanning Electron

β-Ni (OH)2nanospheres have been successfully synthesized with nickel nitrate as nickel source and stronger ammonia water as precipitant by the hydrothermal method. The phase and the morphologies of the samples have been characterized and analyzed by X-ray diffraction (XRD) and Scanning electron microscope (SEM). XRD shows that the phase of the samples isβ-Ni (OH)2. SEM confirms that the increase of the reaction temperature is propitious to the synthesis ofβ-Ni (OH)2nanospheres, which are synthesized at at 180 °C for 48 h with pH=9 by the hydrothermal method.

Synthesis of CuO Microspheres by the Simple Hydrothermal Method and their Optical Absorption Properties

2012 ◽  
Vol 562-564 ◽  
pp. 490-493
Author(s):  
Xiao Ming Fu
Keyword(s):  
Optical Absorption ◽  
Hydrothermal Method ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
Absorption Properties ◽  
Visible Absorption ◽  
X Ray ◽  
Cuo Microspheres ◽  
Visible Absorption Spectroscopy

CuO microspheres with a diameter range of 1~3 μm are successfully synthesized with 1 m mol CuCl2 as copper source and 3 m mol Na2CO3 as auxiliary salt at 180 °C for 24 h via the easy hydrothermal method. The phase, the morphologies and optical absorption properties of the samples have been characterized and analyzed by XRD (X-ray diffraction), SEM (Scanning electron microscope) and ultraviolet-visible absorption spectroscopy (UV-VIS), respectively. XRD analysis shows that the phase of as obtained samples is CuO. SEM analysis confirms that the increase of the the auxiliary salt is in favor of the synthesis of CuO microrods. And UV-VIS measurements show that CuO microspheres have a good optical absorption property.

scholarly journals REVO4 (RE=La, Pr, Nd) nanocrystals: Synthesis and investigation of photocatalytic degradation of some dyes

2021 ◽  
Vol 10 (3) ◽  
pp. 82-86
Author(s):  
Hai Nguyen Van ◽  
Huong Nguyen Thi
Keyword(s):  
Electron Microscope ◽  
Scanning Electron Microscope ◽  
Visible Light ◽  
Photocatalytic Degradation ◽  
Hydrothermal Method ◽  
Organic Dyes ◽  
X Ray Diffraction ◽  
X Ray ◽  
Photocatalytic Activities ◽  
Scanning Electron

In this, work, a series of REVO4 (RE = La, Pr, Nd) nanoparticles were successfully fabricated by the hydrothermal method. The as-synthesized REVO4 nanoparticles were characterized by various techniques of X-ray diffraction (XRD), scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDX). The photocatalytic activities of obtained products were investigated by photodegradation of moderacid red RS and direct yellow GX under visible light. The NdVO4 photocatalyst showed higher discoloration of organic dyes than LaVO4 and PrVO4. About 64% moderacid red RS was degraded within 150 minutes catalyzed by the catalyst NdVO4.

Studies on the Catalyzing Transesterification of Soybean Oil with Methanol for Biodiesel Using a Novel Porous CaO Microsphere Catalyst

2011 ◽  
Vol 197-198 ◽  
pp. 1057-1063
Author(s):  
Xiao Hua Liu ◽  
Hai Xin Bai ◽  
Lin Zhou
Keyword(s):  
Catalytic Activity ◽  
Electron Microscope ◽  
Reaction Time ◽  
Scanning Electron Microscope ◽  
Soybean Oil ◽  
Diffraction Analysis ◽  
Temperature Reaction ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

A novel porous CaO microsphere catalyst was synthesized by calcining spherical CaCO3 precursor which was prepared easily by mixing CaCl2 with Na2CO3. After characterized by scanning electron microscope and X-ray diffraction analysis, the synthesized CaO was studied on Studies on the catalyzing transesterification of soybean oil with methanol for biodiesel. The effects of calcining temperature, reaction time and temperature, amounts of catalyst and methanol on the catalytic activity of CaO microsphere had been evaluated by catalyzing transesterification of soybean oil with methanol for biodiesel. It expressed excellent catalytic activity with a transesterification yield of more than 98% at 65 °C in one hour with 3 wt% of CaO microsphere calcined at 800 °C.

PENGGUNAAN TiO2 PARTIKEL NANO HASIL SINTESIS BERBASIS AIR MENGGUNAKAN METODA SOL-GEL PADA BAHAN KAPAS SEBAGAI APLIKASI UNTUK TEKSTIL ANTI UV

Arena Tekstil ◽  
2013 ◽  
Vol 28 (1) ◽  
Author(s):  
Maya Komalasari ◽  
Bambang Sunendar
Keyword(s):  
Fourier Transform ◽  
Electron Microscope ◽  
Scanning Electron Microscope ◽  
Sol Gel ◽  
Crosslinking Agent ◽  
X Ray Diffraction ◽  
Nano Tio2 ◽  
X Ray ◽  
Infra Red ◽  
Scanning Electron

Partikel nano TiO2 berbasis air dengan pH basa telah berhasil disintesis dengan menggunakan metode sol-gel dan diimobilisasi pada kain kapas dengan menggunakan kitosan sebagai zat pengikat silang. Sintesis dilakukan  dengan prekursor TiCl4 pada konsentrasi 0,3 M, 0,5 M dan 1 M, dan menggunakan templat kanji dengan proses kalsinasi pada suhu 500˚C selama 2 jam. Partikel nano TiO2 diaplikasikan ke kain kapas dengan metoda pad-dry-cure dan menggunakan kitosan sebagai crosslinking agent. Berdasarkan hasil Scanning Electron Microscope (SEM),diketahui bahwa morfologi partikel TiO2 berbentuk spherical dengan ukuran nano (kurang dari 100 nm). Karakterisasi X-Ray Diffraction (XRD) menunjukkan adanya tiga tipe struktur kristal utama, yaitu (100), (101) dan (102) dengan fasa kristal yang terbentuk adalah anatase dan rutile. Pada karakterisasi menggunakan SEM terhadap serbuk dari TiO2 yang telah diaplikasikan ke permukaan kain kapas, terlihat adanya imobilisasi partikel nano TiO2 melalui ikatan hidrogen silang dengan kitosan pada kain kapas. Hasil analisa tersebut kemudian dikonfirmasi dengan FTIR (Fourier Transform Infra Red) yang hasilnya memperlihatkan puncak serapan pada bilangan gelombang 3495 cm-1, 2546 cm-1, dan 511 cm-1,  yang masing-masing diasumsikan sebagai adanya vibrasi gugus fungsi O-H, N-H dan Ti-O-Ti. Hasil SEM menunjukkan pula bahwa kristal nano yang terbentuk diantaranya adalah fasa rutile , yang berdasarkan literatur terbukti dapatberfungsi sebagai anti UV.

Sign in / Sign up

Export Citation Format

Share Document