Effects of Fineness on Activity Character of Fly Ash

2011 ◽  
Vol 266 ◽  
pp. 114-117
Author(s):  
Zhong Tao Luo ◽  
Bao Guo Ma ◽  
Jiu Jun Yang ◽  
Jun Xia Liu
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Cement Hydration ◽  
Chemical Activation ◽  
Cement Pastes ◽  
Starting Point ◽  
Aggregate Effect ◽  
Granule Morphology ◽  
Morphology Effect ◽  
Micro Analysis

The hydrated character of cement paste with fly ash was studied, through the methods of compressive strength, non-evaporable water content, reaction degree of fly ash and micro-analysis. The results indicated that the chemical activity of fly ash was an accumulative change process under this test condition. The starting point of chemical reaction of fly ash was nearby 28 days. In front of 28 days, the chemical activation of fly ash was not wakened, and the compressive strength of cement pastes with fly ash at this age was mainly from multiplex effects of cement hydration and the micro-aggregate effect, granule morphology effect and pozzolanic effect of fly ash.

scholarly journals Effect of Morphologically Controlled Hematite Nanoparticles on the Properties of Fly Ash Blended Cement

Nanomaterials ◽  
2021 ◽  
Vol 11 (4) ◽  
pp. 1003
Author(s):  
Pantharee Kongsat ◽  
Sakprayut Sinthupinyo ◽  
Edgar A. O’Rear ◽  
Thirawudh Pongprayoon
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Size Distribution ◽  
Cement Hydration ◽  
Blended Cement ◽  
Spherical Shape ◽  
Particle Sizes ◽  
Fe2o3 Nanoparticles ◽  
Structure And Properties ◽  
Hematite Nanoparticles

Several types of hematite nanoparticles (α-Fe2O3) have been investigated for their effects on the structure and properties of fly ash (FA) blended cement. All synthesized nanoparticles were found to be of spherical shape, but of different particle sizes ranging from 10 to 195 nm depending on the surfactant used in their preparation. The cement hydration with time showed 1.0% α-Fe2O3 nanoparticles are effective accelerators for FA blended cement. Moreover, adding α-Fe2O3 nanoparticles in FA blended cement enhanced the compressive strength and workability of cement. Nanoparticle size and size distribution were important for optimal filling of various size of pores within the cement structure.

Assessment of Hydration Degree of Cement in the Fly Ash-Cement Pastes Based on the Calcium Hydroxide Content

2014 ◽  
Vol 875-877 ◽  
pp. 177-182 ◽  
Author(s):  
Xiang Li ◽  
Hua Quan Yang ◽  
Ming Xia Li
Keyword(s):  
Fly Ash ◽  
Calcium Hydroxide ◽  
Cement Hydration ◽  
Ash Content ◽  
Content Increase ◽  
Hydration Degree ◽  
Equilibrium Calculation ◽  
Cement Pastes ◽  
Cement Ratio ◽  
Water Cement Ratio

The hydration degree of fly ash and the calcium hydroxide (CH) content were measured. Combined with the equilibrium calculation of cement hydration, a new method for assessment of the hydration degree of cement in the fly ash-cement (FC) pastes based on the CH content was developed. The results reveal that as the fly ash content increase, the hydration degree of fly ash and the CH content decrease gradually; at the same time, the hydration degree of cement increase. The hydration degree of cement in the FC pastes containing a high content of fly ash (more than 35%) at 360 days is as high as 80%, even some of which hydrates nearly completely. The effect of water-cement ratio to the hydration degree of cement in the FC pastes is far less distinct than that of the content of fly ash.

scholarly journals Hydration study of mechanically activated mixtures of Portland cement and fly ash

2007 ◽  
Vol 72 (6) ◽  
pp. 591-604 ◽  
Author(s):  
Gordana Stefanovic ◽  
Ljubica Cojbasic ◽  
Zivko Sekulic ◽  
Srdjan Matijasevic
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Mechanical Activation ◽  
Early Period ◽  
Negative Effects ◽  
Early Hydration ◽  
Cement Pastes ◽  
Dta And Tg ◽  
Low Activity

Fly ash (FA) can be used in cement mixtures with certain limitations. The problem of the mentioned mixtures lies in the insufficient activity of the particles of FA in the reactions which are important for the establishment of the mechanical characteristics of cement. This is particularly true for the hydration reactions. As a result of this, cement pastes formed by mixing ash and clinker have worse characteristics compared to those of pure Portland cement (PC), especially in the early period of setting. As is well known, FA can be a good solution for the neutralization of the negative effects generated due to the creation of free Ca(OH)2 during the hydration of PC, provided that the problems with the low activity of FAare overcome. For the experiments in this study, a mixture of Portland cement and fly ash was used, the content of ash in the mixture being 30 % and 50 %. Mechanical activation was performed in a vibrating ring mill. The goal of this study was to demonstrate, through experimental results, that during the mechanical activation of a PC and FA mixture, the components in the mixture which mostly affect the direction, rate and range of hydration reactions occurring in the mixture had been activated. The values of the compressive strength of the activated and non-activated mixtures and the changes of their specific surface area proved that during the grinding process, the mixture PC+FA had been mechanically activated. The highest increase of compressive strength was achieved in the early period of setting, which indicates an improvement in the early hydration of the mixture. XRD, DTA and TG analyses showed that the alite (C3S) and belite (C2S) from the PC and a part of the fly ash were activated. .

High Volume Slag and Slag-Fly Ash Blended Cement Pastes Containing Nano Silica

2019 ◽  
Vol 967 ◽  
pp. 205-213
Author(s):  
Faiz U.A. Shaikh ◽  
Anwar Hosan
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Cement Paste ◽  
Ordinary Portland Cement ◽  
Blended Cement ◽  
High Volume ◽  
Ash Content ◽  
Partial Replacement ◽  
Nano Silica ◽  
Cement Pastes

This paper presents the effect of nanosilica (NS) on compressive strength and microstructure of cement paste containing high volume slag and high volume slag-fly ash blend as partial replacement of ordinary Portland cement (OPC). Results show that high volume slag (HVS) cement paste containing 60% slag exhibited about 4% higher compressive strength than control cement paste, while the HVS cement paste containing 70% slag maintained the similar compressive strength to control cement paste. However, about 9% and 37% reduction in compressive strength in HVS cement pastes is observed due to use of 80% and 90% slag, respectively. The high volume slag-fly ash (HVSFA) cement pastes containing total slag and fly ash content of 60% exhibited about 5%-16% higher compressive strength than control cement paste. However, significant reduction in compressive strength is observed in higher slag-fly ash blends with increasing in fly ash contents. Results also show that the addition of 1-4% NS improves the compressive strength of HVS cement paste containing 70% slag by about 9-24%. However, at higher slag contents of 80% and 90% this improvement is even higher e.g. 11-29% and 17-41%, respectively. The NS addition also improves the compressive strength by about 1-59% and 5-21% in high volume slag-fly ash cement pastes containing 21% fly ash+49%slag and 24% fly ash+56%slag, respectively. The thermogravimetric analysis (TGA) results confirm the reduction of calcium hydroxide (CH) in HVS/HVSFA pastes containing NS indicating the formation of additional calcium silicate hydrate (CSH) gels in the system. By combining slag, fly ash and NS in high volumes e.g. 70-80%, the carbon footprint of cement paste is reduced by 66-76% while maintains the similar compressive strength of control cement paste. Keywords: high volume slag, nanosilica, compressive strength, TGA, high volume slag-fly ash blend, CO2 emission.

Determination of cement hydration and pozzolanic reaction extents for fly-ash cement pastes

2012 ◽  
Vol 27 (1) ◽  
pp. 560-569 ◽  
Author(s):  
Qiang Zeng ◽  
Kefei Li ◽  
Teddy Fen-chong ◽  
Patrick Dangla
Keyword(s):  
Fly Ash ◽  
Cement Hydration ◽  
Pozzolanic Reaction ◽  
Cement Pastes

Effect of Mechanical Activation of Fluidized Bed Fly Ash on Geopolymer Properties

2019 ◽  
Vol 288 ◽  
pp. 51-58
Author(s):  
Gendenjamts Oyun-Erdene ◽  
Jadambaa Temuujin
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Mechanical Activation ◽  
Sodium Hydroxide ◽  
Fluidized Bed ◽  
Sodium Silicate ◽  
Sodium Hydroxide Solution ◽  
Chemical Activation ◽  
Weight Ratio ◽  
Particle Size Reduction

This paper is focused on the elucidation of mechanical activation effect of circulating fluidized bed combustion fly ash (Amgalan Thermal Station, Mongolia) on mechanical properties of geopolymers. Fluidized bed fly ash was mechanically activated for 15-120 minutes with a vibratory mill. The effect of mechanical activation was quite visible on the particle size reduction and on the degree of amorphization.Geopolymer samples were prepared from the raw and milled fluidized bed fly ashes by alkaline activation. Chemical activation was performed with 10M sodium hydroxide solution, as well as solutions containing a mixture of sodium silicate and sodium hydroxide with a weight ratio of 2:1. The geopolymer cubic specimens were cured at 70°C for 24 hrs and their 7 days uniaxial compressive strength was measured. After curing and drying, the bulk density, water absorption and apparent porosity of geopolymer samples were evaluated.X-ray powder diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and thermogravimetry-differential thermal analysis (TGA-DTA) have been used for the structural characterization of the CFA and the resulting geopolymers. The highest compressive strength of 32.4 MPa was achieved for the fly ash milled for 30 minutes and activated with the solution containing the sodium silicate and 10M sodium hydroxide at a weight ratio of 2:1. Non-milled CFA based geopolymers showed the compressive strength of 16.2 MPa after activation with the same solution. Mechanical activation resulted in an increase in the reactivity of the fluidized bed fly ash and that enhances the geopolymerization reactions.

Effects of Packing Density of Micropowders on the Compressive Strength of Cement Pastes

2007 ◽  
Vol 353-358 ◽  
pp. 1394-1397
Author(s):  
Jian Qing Gong ◽  
Han Ning Xiao ◽  
Zheng Yu Huang ◽  
Jiu Su Li ◽  
Rong Kui Cao ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Silica Fume ◽  
Packing Density ◽  
Cement Pastes

This study was performed to evaluate the effects of micropowders content on the compressive strength of cement-based composite pastes. Granular ground blast slag (GGBS), grade I fly ash (FAI), ultra fine fly ash (UFA) and silica fume (SF) were selected as the micropowders. The compressive strength was tested after 3d, 7d and 28d curing. Results show that the paste containing both UFA and SF has the highest packing density and corresponding excellent compressive strength. The higher the packing density is, the better the compacting and filling effect of micropowders will be, which contributes to developing higher compressive strength of cement-based pastes.

Dry Shrinkage and Compressive Strength of Blended Cement Pastes with Fly Ash and Silica Fume

2012 ◽  
Vol 535-537 ◽  
pp. 1735-1738 ◽  
Author(s):  
Yan Li ◽  
Dao Sheng Sun ◽  
Xiu Sheng Wu ◽  
Ai Guo Wang ◽  
Wei Xu ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Silica Fume ◽  
Cement Paste ◽  
Blended Cement ◽  
Drying Shrinkage ◽  
Cementitious Material ◽  
Strength Increase ◽  
Cement Pastes ◽  
Dry Shrinkage

This paper reports the drying shrinkage and compressive strength results of cement pastes with fly ash and silica fume. In this study, Portland cement (PC) was used as the basic cementitious material. Fly ash (FA) and silica fume (SF) were used as cement replacement materials at levels of 0%, 5%, 10%, and 15% , 40%, 35%, 25%, and 15% by weight of the total cementitious material, respectively. The water/cement (PC + FA + SF) ratios (w/c) was 0.28 by weight. The samples produced from fresh pastes were demoulded after a day; then they were cured at 20 ±1°C with 50 ± 3% relative humidity (RH) until the samples were used for drying shrinkage and compressive strength measurement at various ages. The results show that drying shrinkage and compressive strength increase with increasing SF content, and the optimum composition of blended cement pastes is the cement paste with 30% fly ash and 10% silica fume, which possesses lower drying shrinkage values than that of plain cement paste and higher early age strength than that of blended cement pastes with fly ash. Furthermore, a linear relationship is established between compressive strength and drying shrinkage. By comparing the development of compressive strength and the drying shrinkage deformations, it appears possible to predict the drying shrinkage according to the acquired compressive strength.

Sign in / Sign up

Export Citation Format

Share Document