Influence of Cold Weather on Compressive Strength in High Performance with Silica Fume

2014 ◽  
Vol 627 ◽  
pp. 445-448 ◽  
Author(s):  
Young Il Jang ◽  
Wan Shin Park ◽  
Sun Woong Kim ◽  
Song Hui Yun ◽  
Hyun Do Yun ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Silica Fume ◽  
High Performance ◽  
Mechanical Performance ◽  
High Performance Concrete ◽  
Weather Condition ◽  
Weather Conditions ◽  
Cold Weather ◽  
Binder Ratio ◽  
Hot Weather

This paper addresses the influence of cold weather on the compressive strength of high performance concrete with silica fume under different curing days. Test variables of this study are weather condition (5°C, -5°C and-15°C) and different curing days (7days and 28 days). In this work, the specimen was designed a water-binder ratio of 0.34. One batches of concrete were prepared for each mixing hour, and the compressive strength of cylindrical concrete specimens was measured after 7 and 28 days. Test results for concrete compressive strength show that the concrete’s best mechanical performance occurred when there was the least difference between ambient temperature and concrete temperature, that is, during the later hours of the day in hot weather conditions.

Influence of Curing Temperature on the Compressive Strength of High Performance Concrete

2014 ◽  
Vol 597 ◽  
pp. 316-319
Author(s):  
Sun Woong Kim ◽  
Wan Shin Park ◽  
Nam Yong Eom ◽  
Yong Il Jang ◽  
Hyun Do Yun ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
High Performance ◽  
High Performance Concrete ◽  
Weather Conditions ◽  
Curing Temperature ◽  
Cold Weather ◽  
Binder Ratio ◽  
Strength Improvement ◽  
Water Binder Ratio

The supposition that curing at cold weather conditions leads to the loss of compressive strength of the high performance concrete was investigated. This paper addresses the results of an extensive experimental study on the compressive strength under cold weather conditions. The specimen was prepared as it’s inside 100-mm diameter and 200-mm heights cylindrical were used. In this work, high performance concrete was designed a water-binder ratio of 0.40. These tests were carried out to investigate the mechanical properties of HPC for 7 and 28 days. The results properties of HPC with silica fume were effective for compressive strength improvement between 7 to 28 curing days at 5°C, -5°C and-15°C.

Influence of Silica Fume on High-Performance Concrete

2014 ◽  
Vol 670-671 ◽  
pp. 437-440 ◽  
Author(s):  
Fan Wang ◽  
Shan Suo Zheng ◽  
Xiao Fei Wang
Keyword(s):  
Tensile Strength ◽  
Compressive Strength ◽  
Flexural Strength ◽  
Silica Fume ◽  
High Performance ◽  
Mechanical Performance ◽  
High Performance Concrete ◽  
Split Tensile Strength ◽  
Binder Ratio ◽  
Water Binder Ratio

With the improvement of concrete materials and the emergence of new materials, adding silica fume to high-performance concrete (HPC) has been one of the important ways in concrete technology. In this paper, through experimental study on the mechanical performance of HPC with 5%, 10%, 15% and 20% silica fume replacing cement for different water-binder ratio, along with polycarboxylates high performance water-reducing admixture, silica fume has large effects on 28d compressive strength, split tensile strength and flexural strength of the HPC. Meanwhile, due to the different level of water-binder ratio, the relationship between split tensile strength, flexural strength and compressive strength is also obvious linear.

An Experimental Study on Evaluation of Mechanical Properties in High Performance Concrete Using Admixture

2013 ◽  
Vol 372 ◽  
pp. 231-234
Author(s):  
Jeong Eun Kim ◽  
Wan Shin Park ◽  
Nam Yong Eom ◽  
Sun Woong Kim ◽  
Do Gyeum Kim ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Silica Fume ◽  
Modulus Of Elasticity ◽  
High Performance ◽  
High Performance Concrete ◽  
Splitting Tensile Strength ◽  
Experimental Investigations ◽  
Binder Ratio

In this study, some experimental investigations on the development of mechanical properties with age of high performance concrete (HPC) incorporated with blast furnace slag with fly ash or silica fume have been reported. Four different blended HPC were prepared in 0.40 water-binder ratio. At every four mixtures, the compressive strength, splitting tensile strength and modulus of elasticity at 7 and 28 days have been observed for HPC developments. Consequently, only replacement of silica fume significantly increases the mechanical properties in terms of compressive strength, splitting tensile strength and modulus of elasticity.

Effect of Mineral Admixture on Modulus of Elasticity in High Performance Concrete under Hot Weather Condition

2014 ◽  
Vol 627 ◽  
pp. 401-404
Author(s):  
Nam Yong Eom ◽  
Wan Shin Park ◽  
Song Hui Yun ◽  
Yong Il Jang ◽  
Hyun Do Yun ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Modulus Of Elasticity ◽  
High Performance ◽  
High Performance Concrete ◽  
Weather Condition ◽  
Mineral Admixture ◽  
Curing Temperature ◽  
Hot Weather ◽  
Paper Address

This paper address the mechanical properties of high performance concrete exposed to hot weather in terms of compressive strength and the modulus of elasticity. The variable of this study is curing temperature of 35 °C and 50°C under hot weather condition.

High Performance Concrete with Ternary Binders

2018 ◽  
Vol 761 ◽  
pp. 120-123 ◽  
Author(s):  
Vlastimil Bílek ◽  
David Pytlík ◽  
Marketa Bambuchova
Keyword(s):  
Fly Ash ◽  
Portland Cement ◽  
Silica Fume ◽  
High Performance ◽  
Ordinary Portland Cement ◽  
High Performance Concrete ◽  
Fresh Concrete ◽  
Binder Ratio ◽  
Water To Binder Ratio ◽  
Condensed Silica Fume

Use a ternary binder for production of a high performance concrete with a compressive strengths between 120 and 170 MPa is presented. The water to binder ratio of the concrete is 0.225 and the binder is composed of Ordinary Portland Cement (OPC), condensed silica fume (CSF), ground limestone (L), fly ash (FA) and metakaoline (MK). The dosage of (M + CSF) is kept at a constant level for a better workability of fresh concrete. Different workability, flexural and compressive strengths were obtained for concretes with a constant cement and a metakaoline dosage, and for a constant dosage (FA + L) but a different ratio FA / L. An optimum composition was found and concretes for other tests were designed using this composition.

scholarly journals Mechanical Properties and Environmental Evaluation of Ultra-High-Performance Concrete with Aeolian Sand

Materials ◽  
2020 ◽  
Vol 13 (14) ◽  
pp. 3148 ◽  
Author(s):  
Hongyan Chu ◽  
Fengjuan Wang ◽  
Liguo Wang ◽  
Taotao Feng ◽  
Danqian Wang
Keyword(s):  
Compressive Strength ◽  
Environmental Impact ◽  
Young’S Modulus ◽  
High Performance ◽  
High Performance Concrete ◽  
Young's Modulus ◽  
Ultra High Performance Concrete ◽  
Aeolian Sand ◽  
Binder Ratio ◽  
Water Binder Ratio

Ultra-high-performance concrete (UHPC) has received increasing attention in recent years due to its remarkable ductility, durability, and mechanical properties. However, the manufacture of UHPC can cause serious environmental issues. This work addresses the feasibility of using aeolian sand to produce UHPC, and the mix design, environmental impact, and mechanical characterization of UHPC are investigated. We designed the mix proportions of the UHPC according to the modified Andreasen and Andersen particle packing model. We studied the workability, microstructure, porosity, mechanical performance, and environmental impact of UHPC with three different water/binder ratios. The following findings were noted: (1) the compressive strength, flexural strength, and Young’s modulus of the designed UHPC samples were in the ranges of 163.9–207.0 MPa, 18.0–32.2 MPa, and 49.3–58.9 GPa, respectively; (2) the compressive strength, flexural strength, and Young’s modulus of the UHPC increased with a decrease in water/binder ratio and an increase in the steel fibre content; (3) the compressive strength–Young’s modulus correlation of the UHPC could be described by an exponential formula; (4) the environmental impact of UHPC can be improved by decreasing its water/binder ratio. These findings suggest that it is possible to use aeolian sand to manufacture UHPC, and this study promotes the application of aeolian sand for this purpose.

scholarly journals The Compressive Strength of High-Performance Concrete and Ultrahigh-Performance

2012 ◽  
Vol 2012 ◽  
pp. 1-7 ◽  
Author(s):  
E. H. Kadri ◽  
S. Aggoun ◽  
S. Kenai ◽  
A. Kaci
Keyword(s):  
Experimental Data ◽  
Compressive Strength ◽  
Silica Fume ◽  
High Performance ◽  
High Performance Concrete ◽  
Cementitious Materials ◽  
Strength Gain ◽  
Proposed Model ◽  
Partial Cement Replacement ◽  
Better Than

The compressive strength of silica fume concretes was investigated at low water-cementitious materials ratios with a naphthalene sulphonate superplasticizer. The results show that partial cement replacement up to 20% produce, higher compressive strengths than control concretes, nevertheless the strength gain is less than 15%. In this paper we propose a model to evaluate the compressive strength of silica fume concrete at any time. The model is related to the water-cementitious materials and silica-cement ratios. Taking into account the author's and other researchers’ experimental data, the accuracy of the proposed model is better than 5%.