Fabrication of Li0.06(K0.5,Na0.5)0.94NbO3 Nanofibers by Electrospinning Technique

2019 ◽  
Vol 798 ◽  
pp. 218-222
Author(s):  
Supattra Wongsaenmai ◽  
Tawat Soitong
Keyword(s):  
Calcination Temperature ◽  
Single Phase ◽  
Sol Gel ◽  
Structural Phase ◽  
Orthorhombic Symmetry ◽  
X Ray Diffraction ◽  
Fiber Morphology ◽  
Electrospinning Technique ◽  
X Ray ◽  
Sol Gel Process

In this work, Li0.06(K0.5,Na0.5)0.94NbO3(KNNL) nanofibers were synthesized by sol–gel process and electrospinning technique. The thermal behaviour ofelectrospun fibers was characterized by thermogravimetric analysis (TG) to obtain the calcination temperature range. The structural phase formation and microstructure were characterized by X-ray diffraction technique (XRD) and scanning electron microscopy (SEM), respectively. The crystal structure was identified by XRD as a single-phase perovskite structure, with orthorhombic symmetry. The microstructure shows that the diameters are in the range of 80–160 nm. The electrospun fibers were calcined from 500°C to 900°C and observed the fiber morphology. With increasing calcination temperature, the fiber diameters decreased until the temperature up to 900 °C the morphology change from cylinder to square or rectangular shape grains.

The Structure and Ferromagnetic Properties of the Single Phase Bi0.95Eu0.05Fe0.95Co0.05O3 Nanoparticles Prepared by Sol-Gel

2012 ◽  
Vol 512-515 ◽  
pp. 1434-1437
Author(s):  
Xing Ao Li ◽  
Peng Li ◽  
Yong Tao Li ◽  
Jian Ping Yang ◽  
Qiu Fei Bai ◽  
...  
Keyword(s):  
Single Phase ◽  
Sol Gel ◽  
Mixed Valence ◽  
Magnetic Characteristics ◽  
X Ray Diffraction ◽  
X Ray ◽  
Valence States ◽  
Sol Gel Process ◽  
X Ray Absorption ◽  
Fe Ions

Bi0.95Eu0.05Fe0.95Co0.05O3 Nanoparticles sample was prepared by sol-gel process. The microstructure of samples was analysised by X-ray diffraction(XRD), the result indicated that it was the single phase rhombohedral perovskite structure. The morphology of samples was measured by scanning electron microsopy(SEM), the SEM photograph of samples indicated that the nanoparticles of Bi0.95Eu0.05Fe0.95Co0.05O3 sample were small than that of BiFeO3. The valence states of Fe ions in the samples was analysised by the X-ray absorption spectroscopy（XAS）. The XAS of Fe2p showed that it was the mixed valence states (Fe2+ and Fe3+) of Fe ions in samples, and the binding energy of Bi0.95Eu0.05Fe0.95Co0.05O3 was bigger than that of BiFeO3.The magnetic characteristics of the samples were measured by vibrating sample magnetometer (VSM)，the results showed that the weak metamagnetism were obtained from clear hysteresis loop and the magnetic saturation reached 0.408emu/g，compared with BiFeO3 sample, the magnetic properties were significantly enhanced.

Preparation and Characterization of Pr2Ti2O7 by Sol-Gel Process

2017 ◽  
Vol 748 ◽  
pp. 413-417
Author(s):  
Chun Yu Long ◽  
Fang Fang Peng ◽  
Min Min Jin ◽  
Pei Song Tang ◽  
Hai Feng Chen
Keyword(s):  
Methyl Orange ◽  
Single Phase ◽  
Raw Materials ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
Illumination Time ◽  
X Ray ◽  
Sol Gel Process ◽  
Ft Ir

Using Pr (NO3)3, butyl titanate, ethylene glycol and citric acid as main raw materials, praseodymium titanate (Pr2Ti2O7) was prepared by the sol-gel process. The samples were characterized by means of X-ray diffraction (XRD), scanning electron microscope (SEM), thermal gravity-differential thermal analysis (TG-DTA), diffuse-reflection spectra (DRS) and Fourier transform infrared (FT-IR). The effect of different calcination temperature and illumination time on the photocatalytic properties of Pr2Ti2O7 was investigated. It was found that the single phase Pr2Ti2O7 could be obtained through sol-gel process and calcination at 1000 °C. The Pr2Ti2O7 samples calcination at 1000 °C were uniform , and the resulting product had a particle size of 200 nm and an optical band gap of 3.26 eV. Under ultraviolet light, the degradation of methyl orange arrived to 80.11% after 180 min of photocatalytic reaction. The Pr2Ti2O7 samples showed good photocatalytic activity for decomposition of methyl orange.

Luminescent Properties of Zn2SiO4:Eu3+,Dy3+ Phosphors via Sol-Gel Process

2012 ◽  
Vol 217-219 ◽  
pp. 733-736
Author(s):  
Xiu Mei Han ◽  
Shu Ai Hao ◽  
Ying Ling Wang ◽  
Gui Fang Sun ◽  
Xi Wei Qi
Keyword(s):  
Thermal Analysis ◽  
Ir Spectra ◽  
Sol Gel ◽  
Luminescent Properties ◽  
Photoluminescence Spectra ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process ◽  
Ft Ir

Zn2SiO4:Eu3+, Dy3+ phosphors have been prepared through the sol-gel process. X-ray diffraction (XRD), thermogravimetric and ddifferential thermal analysis (TG-DTA), FT-IR spectra and photoluminescence spectra were used to characterize the resulting phosphors. The results of XRD indicated that the phosphors crystallized completely at 1000oC. In Zn2SiO4:Eu3+,Dy3+ phosphors, the Eu3+ and Dy3+ show their characteristic red(613nm, 5D0-7F2), blue (481nm, 4F9/2–6H15/2) and yellow (577nm, 4F9/2–6H13/2) emissions.

Impedance Spectroscopy Study of LiTaO3 Powder Synthesized via Sol-Gel Method

2012 ◽  
Vol 545 ◽  
pp. 275-278 ◽  
Author(s):  
Lili Widarti Zainuddin ◽  
Norlida Kamarulzaman
Keyword(s):  
Room Temperature ◽  
Single Phase ◽  
Sol Gel ◽  
Rhombohedral Structure ◽  
Spectroscopy Study ◽  
X Ray Diffraction ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Impedance Spectroscopy Study

A ceramics sample of LiTaO3 was prepared using a sol-gel method. The sample is annealed at 750 °C for 48 hours. X-ray diffraction analysis indicate the formation of single phase, rhombohedral structure. An ac impedance study was used to analyse the conductivity of LiTaO3 at room temperature and at various temperatures.

Sol-Gel derived Bi4-xNdxTi3O12 Thin Films and Their Characterization

2002 ◽  
Vol 737 ◽  
Author(s):  
R.E. Melgarejo ◽  
M.S. Tomar ◽  
A. Hidalgo ◽  
R.S. Katiyar
Keyword(s):  
Thin Films ◽  
Spin Coating ◽  
Bismuth Titanate ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
X Ray ◽  
Complete Solid Solution ◽  
Sol Gel Process ◽  
Ferroelectric Memory ◽  
Initial Results

ABSTRACTNd substituted bismuth titanate Bi4-xNdxTi3O12 were synthesized by sol-gel process and thin films were deposited on Pt substrate (Pt/TiO2/SiO2/Si) by spin coating. Thin films, characterized by X-ray diffraction and Raman spectroscopy, shows complete solid solution up to the composition x < 1. Initial results indicate that the ferroelectric polarization increases with increasing Nd content in the film with 2Pr = 50μC/cm2 for x = 0.46, which may have application in non-volatile ferroelectric memory devices.

Study on optical and magnetic properties of FexNi1-xMn2O4 materials

2021 ◽  
Vol 66 (1) ◽  
pp. 57-64
Author(s):  
Hang Pham Vu Bich ◽  
Yen Nguyen Hai ◽  
Mai Phung Thi Thanh ◽  
Dung Dang Duc ◽  
Hung Nguyen Manh ◽  
...  
Keyword(s):  
Single Phase ◽  
Sol Gel ◽  
Vibrating Sample Magnetometer ◽  
Raman Scattering Spectrum ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scattering Spectrum ◽  
Diffraction Diagram ◽  
Optical And Magnetic Properties ◽  
Scanning Electron

In this study, we present the process of synthesis FexNi1-xMn2O4 (x = 0; 0.1; 0.3; 0.5; 0.7; 0.9; 1) by method sol-gel. Scanning electron microscope results shows that the particle size is about 50 nm. The X-ray diffraction diagram shows that the samples are single phase, changing structure clearly as the x ratio increases from 0 to 1. The lattice constant, the bond length also changes with x-value as shown on the Raman scattering spectrum. The results of the vibrating sample magnetometer show that the magnetism of the material FexNi1-xMn2O4 changes with the value of x and reaches a maximum in the range x from 0.5 to 0.7.

Synthesis and Characterizations of Strontium Substituted Hydroxyapatite Thin Films

2010 ◽  
Vol 93-94 ◽  
pp. 231-234
Author(s):  
B. Hongthong ◽  
Satreerat K. Hodak ◽  
Sukkaneste Tungasmita
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Composition ◽  
Spin Coating ◽  
Phase Structure ◽  
Sol Gel ◽  
Cross Linking ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process

Strontium substituted hydroxyapatite(SrHAp) were fabricated both in the form of powder as reference and thin film by using inorganic precursor reaction. The sol-gel process has been used for the deposition of SrHAp layer on stainless steal 316L substrate by spin coating technique, after that the films were annealed in air at various temperatures. The chemical composition of SrHAp is represented (SrxCa1-x)5(PO4)3OH, where x is equal to 0, 0.5 and 1.0. Investigations of the phase structure of SrHAp were carried out by using X-ray diffraction technique (XRD). The results showed that strontium is incorporated into hydroxyapatite where its substitution for calcium increases in the lattice parameters, and Sr3(PO4)2 can be detected at 900°C. The SEM micrographs showed that SrHAp films exhibited porous structure before develop to a cross-linking structure.

Low-Temperature Synthesis of Nano-Crystalline ZnTiO3 Powders by Aqueous Sol-Gel Process

2014 ◽  
Vol 543-547 ◽  
pp. 3741-3744
Author(s):  
Quan Jing Mei ◽  
Cong Ying Li ◽  
Jing Dong Guo ◽  
Gui Wang ◽  
Hai Tao Wu
Keyword(s):  
Sol Gel ◽  
Zinc Nitrate ◽  
X Ray Diffraction ◽  
Low Temperature Synthesis ◽  
Temperature Synthesis ◽  
Calcination Process ◽  
X Ray ◽  
Nano Crystalline ◽  
Transmission Electron ◽  
Sol Gel Process

The ecandrewsite-type ZnTiO3was successfully synthesized by the aqueous sol-gel method using TiO2dioxide and zinc nitrate as starting materials instead of expensive organic solvent and metal alkoxides. The as-prepared nanopowders were characterized by X-ray diffraction (XRD), differential thermal analysis (DTA) and transmission electron microscopy (TEM), respectively. The results showed that the calcination process of gel consisted of a series of oxidation and combustion reactions, accompanied by significantly exothermal effects. Highly reactive nanosized ZnTiO3powders were successfully obtained at 850 °C with particle size ~50 nm. By comparison, the aqueous sol-gel process was the most effective and least expensive technique used for the preparation of ZnTiO3nanopowders.

Preparation of YBCO Superconducting Films by Sol-Gel Process

2007 ◽  
Vol 546-549 ◽  
pp. 2007-2010
Author(s):  
Gao Yang Zhao ◽  
Huang Li Zhang ◽  
Ren Zhong Xue ◽  
Yuan Qing Chen ◽  
Li Lei
Keyword(s):  
Sol Gel ◽  
Precursor Solution ◽  
Superconducting Films ◽  
Superconducting Transition ◽  
X Ray Diffraction ◽  
Organic Salts ◽  
Ybco Films ◽  
X Ray ◽  
Sol Gel Process ◽  
Ybco Superconducting Films

precursor solution was prepared using barium trifluoroacetae (Ba-TFA) and non-fluorine yttrium (Y) and copper (Cu) organic salts. The precursor solution was modified by benzalacetone (BzAcH), in which the Cu2+ were chelated with BzAcH, which preventing the loss of Cu in the pyrolysis process. Dense YBCO superconducting films with smooth surface, which confirmed by scanning electron microscopy (SEM), were repeatedly obtained through sol-gel process. X-ray diffraction (XRD) 2θ scanning and φ scanning indicated that the as-prepared YBCO films had good c-axis texture. YBCO films with superconducting transition temperature (TC) above 89K were obtained.

scholarly journals Dielectric and Raman studies of Ba0.06(Na1/2Bi1/2)0.94TiO3–NaNbO3 ceramics

2016 ◽  
Vol 34 (2) ◽  
pp. 437-445 ◽  
Author(s):  
Sumit K. Roy ◽  
S. Chaudhuri ◽  
R.K. Kotnala ◽  
D.K. Singh ◽  
B.P. Singh ◽  
...  
Keyword(s):  
Single Phase ◽  
Solid State Reaction Method ◽  
Lead Free ◽  
Orthorhombic Symmetry ◽  
Dielectric Studies ◽  
X Ray Diffraction ◽  
Reaction Method ◽  
X Ray ◽  
New Phase ◽  
Diffusivity Parameter

AbstractIn this work the X-ray diffraction, scanning electron microscopy, Raman and dielectric studies of lead free perovskite (1 – x)Ba0.06(Na1/2Bi1/2)0.94TiO3–xNaNbO3 (0 ⩽ x ⩽ 1.0) ceramics, prepared using a standard solid state reaction method, were investigated. X-ray diffraction studies of all the ceramics suggested the formation of single phase with crystal structure transforming from rhombohedral-tetragonal to orthorhombic symmetry with the increase in NaNbO3 content. Raman spectra also confirmed the formation of solid solution without any new phase. Dielectric studies showed that the phase transition is of diffusive character and diffusivity parameter decreases with increasing NaNbO3 content. The compositional fluctuation was considered to be the main cause of diffusivity.

Sign in / Sign up

Export Citation Format

Share Document