Energy Absorption Mechanism of Thermoplastic Fiber-Reinforced Plastics under Impact Loading Using Split-Hopkinson Pressure-Bar Method
The energy absorbing performance in the progressive failure of glass long-fiber-reinforced polyamide was evaluated by using the split Hopkinson pressure-bar method. An impact compression test of glass long-fiber-reinforced polyamide was performed from –30 °C to 90 °C, and the temperature-independent energy absorbing performance was confirmed only for the progressive failure mode. To clarify this phenomenon, compression tests, interlaminar compressive shear tests and mode-I fracture-toughness tests were conducted under static and impact conditions. The compression strength and the shear strength of all specimens decreased with an increase in temperature. The toughness improved with temperature. In addition to the mechanical tests, failure-mode analysis was performed by using a three-dimensional X-ray microscope to clarify the absorbing mechanism. From the above, it was concluded that the temperature-independent energy absorbing performance results from a balance of these mechanical properties against the temperature change.