In Situ TiB Reinforced Titanium Metal Matrix Composites Prepared by Spark Plasma Sintering

2005 ◽  
Vol 502 ◽  
pp. 189-194
Author(s):  
Yu Zhou ◽  
Hai Bo Feng ◽  
De Chang Jia

In situ synthesized TiB reinforced titanium matrix composites of Ti-B and Ti-TiB2 systems have been prepared by spark plasma sintering at 800-1200 °C under 20 MPa for 5 min. The effects of sintering temperature and reinforcement volume fraction on flexural strength, Young’s modulus and fracture toughness of the composites were investigated. The in situ synthesized TiB reinforcements are randomly and uniformly distributed in titanium matrix. The TiB whiskers are aligned along [010] direction, and the crystallographic planes of the TiB needles are always of the type (100), (101) and (10 1) . The parallel TiB were observed in β-Ti grains in both of the investigated composites. The in situ TiB needle is likely to grow along [010] direction which is parallel to [111] direction of cubic lattice of β-Ti phase.

2014 ◽  
Vol 881-883 ◽  
pp. 923-926
Author(s):  
Xiang Bo Shen ◽  
Zhao Hui Zhang ◽  
Mao Sheng Cao ◽  
Fu Chi Wang

The in-situ synthesized TiB reinforced titanium matrix composites have been prepared by spark plasma sintering technique at 950–1250°C, using mixtures of 10wt% TiB2 and 90wt% Ti powders. The effects of the sintering temperature on the mechanical properties (Vickers microhardness, yield strength and Young`s modulus) of the composites were investigated. SEM was used to analyze the reaction process and the microstructure of the compacts synthesized at different sintering temperatures. The results indicated that the in situ synthesized TiB grow rapidly with increasing sintering temperature. The composite sintered at 1250°C have the highest relative density of 99.2%. However, the composite sintered at 950°C exhibits the best Vickers microhardness of 4.64GPa and yield strength of 989MPa, respectively.


2007 ◽  
Vol 336-338 ◽  
pp. 1310-1312
Author(s):  
Hai Bo Feng ◽  
De Chang Jia ◽  
Yu Zhou ◽  
Qing Chang Meng

The in situ TiB whisker reinforced titanium matrix composites were prepared by mechanical alloying followed by spark plasma sintering. X-ray diffraction, scanning electron microscopy and transmission electron microscopy were used to characterize the microstructure of the TiB whiskers. The effect of sintering temperature on morphologies of in situ TiB whiskers was evaluated. With the increase of spark plasma sintering temperature, the average diameter of in situ TiB whiskers increased. The in situ TiB whiskers exhibited a hexagonal shape with (100), (101) and (10 1 ) planes at the transverse section and a growth orientation of [010]TiB direction.


2018 ◽  
Vol 875 ◽  
pp. 41-46 ◽  
Author(s):  
Yue Ying Li ◽  
Fu Wen Zhu ◽  
Zhen Liang Qiao

TiB2 particulate reinforced titanium matrix composites were prepared by mechanical alloying and spark plasma sintering. Volume fraction of TiB2 powders in the composites are 5%, 10%, 15%. The effect of milling time and the volume fraction of reinforcement on microstructure and properties of the composites were studied. The results show that with increasing milling time, the size of powder particles decreases, quantity of them increases, and microstructure of the sintered samples becomes finer and more uniform. When milling time reaches 30h, the trend of powder agglomeration increases, the downward trend of the particle size becomes slowly. With the milling time, the density of titanium matrix composites is on the rise. The density of 10vol%TiB2 particulate reinforced titanium matrix composites can reach 4.799 g/cm3, with 30h milling time and sintering at 900°C. The density and hardness of the composites increase with increasing the volume fraction of TiB2. When the volume fraction of TiB2 is 15%, after milling 10h and sintered at 800°C, the density and hardness of the composites can reach 4.713g/cm3 and HV851.58.


2006 ◽  
Vol 313 ◽  
pp. 105-108 ◽  
Author(s):  
Lian Meng Zhang ◽  
Mei Juan Li ◽  
Qiang Shen ◽  
T. Li ◽  
M.Q. Yu

Aluminum nitride-boron nitride (AlN/BN) composite ceramics were prepared by spark plasma sintering (SPS). The sintering behaviors of AlN/BN composites with 5~15% volume fraction of BN were studied. The influences of BN content, as well as the sintering temperature on the density, microstructure, mechanical strength, thermal conductivity and machinability of the composites were also investigated. The results showed that the full densification of AlN/BN composite ceramics could be realized by SPS technique at the temperature no higher than 1800°C for 3 minutes. The thermal conductivity of AlN/BN composites is in the range of 66~79W/mK, and AlN/BN composites can be cut or drilled by carbides or even steel tools when BN content is 15% volume fraction. The mechanical strength of AlN/BN composites is about 330MPa and is not remarkably affected by the addition of BN. The improvement of mechanical properties of AlN/BN composite ceramics is due to the fine and homogenous microstructure developed in the SPS process.


2013 ◽  
Vol 750 ◽  
pp. 92-95
Author(s):  
Zhong Chun Chen ◽  
Sri Nugroho ◽  
Akira Kawasaki

Al2O3 matrix composites reinforced with Ba-b-Al2O3 phase were synthesized through reactive sintering using Al2O3 and BaCO3 as starting powders. Dense Al2O3/Ba-b-Al2O3 composites can be obtained by spark plasma sintering from Al2O3/BaO•Al2O3 powder, which was prepared by calcining Al2O3/BaCO3 powder mixture. The Ba-b-Al2O3 reinforcing phase exhibited an elongated morphology due to preferred diffusion of Ba cations. The existence of Ba-b-Al2O3 phase as well as low sintering temperature and short holding time during reactive sintering inhibit grain growth and thus result in small grain sizes of the Al2O3 matrix.


Author(s):  
Zheng-Yang Hu ◽  
Hai-Chun Peng ◽  
Zhao-Hui Zhang ◽  
Peng Song ◽  
Ming Chen ◽  
...  

Abstract A hybrid of TiB whiskers and TiC particles reinforced TC4 matrix composites were in-situ synthesized by spark plasma sintering (SPS) using a TC4-0.6wt.% B4C powder mixture at temperatures range from 550°C to 1150°C. The effect of sintering temperature on microstructure, grain size, mechanical properties and densification process of the (TiB+TiC)/ TC4 matrix composites were investigated. The composite sintered at 1050℃ has the highest tensile strength (1129.0 MPa), yield strength (1077.8MPa) and plasticity (7.1%). The aspect ratio of TiB whiskers increases almost linearly below 1050°C and its highest value is 33.2. The grain size of TiC increases with the increase of sintering temperature, and rapid growth occurs in the range of 850°C to 950°C. The composite sintered body appears four shrinkage stages before applying sintering pressure. The corresponding peak temperatures are 663℃, 758℃, 840℃ and 994℃, respectively.


2021 ◽  
Vol 21 (4) ◽  
pp. 2687-2691
Author(s):  
Nguyen Thi ◽  
Hoang Oanh ◽  
Nguyen Hoang Viet

The present work is focused on the fabrication and the investigation of microstructures of copperbased TiC nanocomposites produced by mechanical milling in a high energy planetary ball mill. TiH2, carbon and copper powders were used as starting materials in which In-Situ reaction between carbon and TiH2 occurs to form TiC nanoparticles. The mixture powders of Cu–TiH2–C were milled for 12 h at 450 rpm in Argon gas. Annealing treatment process at 950 °C for 2 h was applied for as-milled composite powders to enhance In-Situ reaction. The consolidation of composite powders was conducted by spark plasma sintering under uniaxial pressing of 70 MPa. Sintering procedure was done at 950 and 1000 °C for 5 min. The results indicated that as TiC nanoparticles are formed after sintering at 950 °C and the TiC particles are increased up at higher sintering temperature of 1000 °C. Fracture surface of sintered samples shows ductile mode. HR-TEM image showed the crystal size of copper was about 10 nm for sample sintered at 1000 °C. The hardness and relative density of the nanocomposites increase when increasing sintering temperature.