On the mechanism of nanoparticle coagulation

The article presents the results of an in situ study of the final stage of coagulation — the fusion of gold nanoparticles on an amorphous carbon film under the influence of highenergy electrons. It is shown that the nature of the fusion of interacting particles is affected by their orientation ratio at the moment of contact formation.

Evaluation of Anti-Adhesion Characteristics of Diamond-Like Carbon Film by Combining Friction and Wear Test with Step Loading and Weibull Analysis

Anti-adhesion characteristics are important requirements for diamond-like carbon (DLC) films. The failure load corresponding to the anti-adhesion capacity varies greatly on three types of DLC film (hydrogen-free amorphous carbon film (a-C), hydrogenated amorphous carbon film (a-C:H), and tetrahedral hydrogen-free amorphous carbon film (ta-C)) in the friction and wear test with step loading using a high-frequency, linear-oscillation tribometer. Therefore, a new method that estimates a representative value of the failure load was developed in this study by performing a statistical analysis based on the Weibull distribution based on the assumption that the mechanism of delamination of a DLC film obeys the weakest link model. The failure load at the cumulative failure probabilities of 10% and 50% increased in the order ta-C < a-C:H < a-C and ta-C < a-C < a-C:H, respectively. The variation of the failure load, represented by the Weibull slope, was minimum on ta-C and maximum on a-C:H. The rank of the anti-adhesion capacity of each DLC film with respect to the load obtained by a constant load test agreed with the rank of the failure load on each DLC film at the cumulative failure probability of 10% obtained by Weibull analysis. It was found to be possible to evaluate the anti-adhesion capacity of a DLC film under more practical conditions by combining the step loading test and Weibull analysis.