Optimization of Cellulose-Based Hydrogel Synthesis Using Response Surface Methodology

Synthesis parameters have a significant effect on the properties of cellulose hydrogel. This study aimed to investigate the effects of synthesis parameters, e.g., the cellulose and crosslinkers concentration, on the hydrogels' swelling ratio under both heating and freezing gelation conditions, respectively. Cellulose hydrogels were prepared from wastepaper by the chemical crosslinking method by using epichlorohydrin ECH as a crosslinker. The effects of the synthesis parameters were compared and optimized by response surface methodology (RSM). Synthesized cellulose-based hydrogels under optimized conditions demonstrated an excellent swelling ratio of around 2800%. The optimum swelling ratio of 2467.72% was achieved from the experiment under the heating gelation condition. Thus the synthesized cellulose hydrogels are promising water-saving materials or controlled-release fertilizer carriers for sustainable horticultural and agricultural applications.

Bioprinting Scaffolds for Vascular Tissues and Tissue Vascularization

In recent years, tissue engineering has achieved significant advancements towards the repair of damaged tissues. Until this day, the vascularization of engineered tissues remains a challenge to the development of large-scale artificial tissue. Recent breakthroughs in biomaterials and three-dimensional (3D) printing have made it possible to manipulate two or more biomaterials with complementary mechanical and/or biological properties to create hybrid scaffolds that imitate natural tissues. Hydrogels have become essential biomaterials due to their tissue-like physical properties and their ability to include living cells and/or biological molecules. Furthermore, 3D printing, such as dispensing-based bioprinting, has progressed to the point where it can now be utilized to construct hybrid scaffolds with intricate structures. Current bioprinting approaches are still challenged by the need for the necessary biomimetic nano-resolution in combination with bioactive spatiotemporal signals. Moreover, the intricacies of multi-material bioprinting and hydrogel synthesis also pose a challenge to the construction of hybrid scaffolds. This manuscript presents a brief review of scaffold bioprinting to create vascularized tissues, covering the key features of vascular systems, scaffold-based bioprinting methods, and the materials and cell sources used. We will also present examples and discuss current limitations and potential future directions of the technology.

Biopolymer Hydrogel Based on Acid Whey and Cellulose Derivatives for Enhancement Water Retention Capacity of Soil and Slow Release of Fertilizers

This study describes the development of a renewable and biodegradable biopolymer-based hydrogel for application in agriculture and horticulture as a soil conditioning agent and for release of a nutrient or fertilizer. The novel product is based on a combination of cellulose derivatives (carboxymethylcellulose and hydroxyethylcellulose) cross-linked with citric acid, as tested at various concentrations, with acid whey as a medium for hydrogel synthesis in order to utilize the almost unusable by-product of the dairy industry. The water uptake of the hydrogel was evaluated by swelling tests under variations in pH, temperature and ion concentration. Its swelling capacity, water retention and biodegradability were investigated in soil to simulate real-world conditions, the latter being monitored by the production of carbon dioxide during the biodegradation process by gas chromatography. Changes in the chemical structure and morphology of the hydrogels during biodegradation were assessed using Fourier transform infrared spectroscopy and scanning electron microscopy. The ability of the hydrogel to hold and release fertilizers was studied with urea and KNO3 as model substances. The results not only demonstrate the potential of the hydrogel to enhance the quality of soil, but also how acid whey can be employed in the development of a soil conditioning agent and nutrient release products.

Responsive Calcium (Ca2+) Alginate-Chitosan Based Hydrogel: A Promising Biomaterial for Spinal Cord Injury

Spinal cord injury is damage to the spinal cord which causes lesions in the spinal cord and leads to an increase in extracellular Ca2+. It results in additional neuronal loss which causes temporary/permanent disability or even death. The aim of this study was to determine characteristics and the best composition of alginate – chitosan hydrogel responsive to Calcium (Ca2+) for spinal cord injury. Hydrogel synthesis with its compositions, namely chitosan was dissolved in 0.4% acetic acid, neutralized in pH 7 with 0.5 M NaOH, added some 0.85% NaCl in it, and added 5 alginate variations which were dissolved in 0.85% NaCl, next will centrifugation method. Based on the FTIR test, hydrogel showed stretching vibrations of Chitosan’s O–H bonds appeared in 3415.93cm-1 wavenumber, while Na groups of alginate isomer appeared in 1413.82 cm-1 wavenumber. The results of the cytotoxicity test using the MTT Assay method showed live cell percentage from less than 50% to 52.61% in Sample B and 83.83% in Sample C. The results of the injectability test showed that all samples were injectable with the highest percentage of injectability at 98.283%. The results of the UV-Vis spectrophotometric test showed that all hydrogel samples were able to absorb Ca2+. Hydrogels can be degraded at more than 90% within 14 days. The results of the morphology test (SEM) obtained 84.7-99.6 μm pore sizes.

Smart Hydrogel Bilayers Prepared by Irradiation

Environment-responsive hydrogel actuators have attracted tremendous attention due to their intriguing properties. Gamma radiation has been considered as a green cross-linking process for hydrogel synthesis, as toxic cross-linking agents and initiators were not required. In this work, chitosan/agar/P(N-isopropyl acrylamide-co-acrylamide) (CS/agar/P(NIPAM-co-AM)) and CS/agar/Montmorillonite (MMT)/PNIPAM temperature-sensitive hydrogel bilayers were synthesized via gamma radiation at room temperature. The mechanical properties and temperature sensitivity of hydrogels under different agar content and irradiation doses were explored. The enhancement of the mechanical properties of the composite hydrogel can be attributed to the presence of agar and MMT. Due to the different temperature sensitivities provided by the two layers of hydrogel, they can move autonomously and act as a flexible gripper as the temperature changes. Thanks to the antibacterial properties of the hydrogel, their storage time and service life may be improved. The as prepared hydrogel bilayers have potential applications in control devices, soft robots, artificial muscles and other fields.