On the Possible Nature of Armchair-Zigzag Structure Formation and Heat Capacity Decrease in MWCNTs

Structural disorder and temperature behavior of specific heat in multi walled carbon nanotubes (MWCNTs) have been investigated. The results of X-ray diffractometry, Raman spectroscopy, and transmission electron microscopy (TEM) images are analyzed. The thermodynamic theory of the zigzag-armchair domain structure formation during nanotube synthesis is developed. The influence of structural disorder on the temperature behavior of specific heat is investigated. The size of domains was estimated at ~40 nm. A decrease in heat capacity is due to this size effect. The revealed dependence of the heat capacity of MWCNTs on the structural disorder allows control over thermal properties of nanotubes and can be useful for the development of thermoelectric, thermal interface materials and nanofluids based on them.

Active thermal interface graphene nanocomposites for thermal control of electronic and power devices

New experimental and calculated data are presented for active thermal interface materials, in which heat is removed not only due to high thermal conductivity, but also due to the evaporation of liquids, for example, water, inside a nanoporous graphene structure. It is shown that such active thermal interfaces may be new systems of active thermal control.

Ultrafast self-healing and self-adhesive polysiloxane towards reconfigurable on-skin electronics

While polysiloxanes are the most widely used interface materials for on-skin electronics, they usually do not exhibit mechanical robustness and fast healing speed simultaneously due to the inherent contradiction of...

Design of biointerfaces composed of soft materials using controlled radical polymerization

Soft interface materials have an immense potential for the improvement of biointerfaces, which are the interface of biological and artificially designed materials. Controlling the chemical and physical structures of the...

Silicone Elastomer Composites Fabricated with MgO and MgO-Multi-Wall Carbon Nanotubes with Improved Thermal Conductivity

The effect of multiwall carbon nanotubes (MWCNTs) and magnesium oxide (MgO) on the thermal conductivity of MWCNTs and MgO-reinforced silicone rubber was studied. The increment of thermal conductivity was found to be linear with respect to increased loading of MgO. In order to improve the thermal transportation of phonons 0.3 wt % and 0.5 wt % of MWCNTs were added as filler to MgO-reinforced silicone rubber. The MWCNTs were functionalized by hydrogen peroxide (H2O2) to activate organic groups onto the surface of MWCNTs. These functional groups improved the compatibility and adhesion and act as bridging agents between MWCNTs and silicone elastomer, resulting in the formation of active conductive pathways between MgO and MWCNTs in the silicone elastomer. The surface functionalization was confirmed with XRD and FTIR spectroscopy. Raman spectroscopy confirms the pristine structure of MWCNTs after oxidation with H2O2. The thermal conductivity is improved to 1 W/m·K with the addition of 20 vol % with 0.5 wt % of MWCNTs, which is an ~8-fold increment in comparison to neat elastomer. Improved thermal conductive properties of MgO-MWCNTs elastomer composite will be a potential replacement for conventional thermal interface materials.