Experimental Study on Engineering Properties of Cement Concrete Reinforced with Nylon and Jute Fibers

The use of synthetic fiber and natural fiber for concrete production has been continuously investigated. Most of the materials have become popular for their higher flexibility, durability, and strength. However, the current study explores the engineering properties of cement concrete reinforced with nylon and jute fibers together. Varying proportions and lengths of nylon and jute fibers were utilized in the concrete mixture. Hence, the combined effects of nylon and jute fibers on workability, density, water absorption, compressive, tensile, flexural strength, and drying shrinkage of concrete were investigated. Results showed that concrete with 1% of nylon and jute fibers together by the volume fraction showed a maximum enhancement of the compressive strength, split tensile strength, and flexural strength by 11.71%, 14.10%, and 11.04%, respectively, compared to the control mix of concrete at 90 days. However, the water absorption of concrete increased with increasing nylon and jute fiber contents. The drying shrinkage of concrete decreased with the addition of nylon and jute fibers together after 90 days. Thus, the sparing application of both nylon and jute fiber as discussed in this study can be adopted for concrete production.

Characterization of Mechanical Properties of Jute/PLA Composites Containing Nano SiO2 Modified By Coupling Agents

Although jute fibers-reinforced PLA composites shows strong application prospects, their low mechanical properties limit their applications to some extent. In this paper, nano-SiO2 particles as well as modified nano SiO2 by coupling agents which can efficiently improve the strength and toughness of composite materials are introduced into the PLA matrix. The bending, stretching and thermal properties of designed jute/PLA nonwoven composites were studied. The study shows that the nano-SiO2 particles are beneficial to the interface performance between the PLA matrix and jute leading to improvement in the mechanical property and thermal stability. Moreover, thermomechanical properties indicate that the addition of SiO2 can improve the jute/PLA interfacial adhesion and increase the glass transition temperature of the material. Finally, toughening mechanism of nano-SiO2 particles in the jute/PLA composite was analyzed.

Study on Thermal, Thermo-Mechanical, and Flexural Properties of Jute Fiber Surface Modification and Its Reinforced Composite

In recent years, reinforced composites from biodegradable and natural fibers have a worldwide scope for advanced applications. However, the core limitation of natural fiber reinforced composites are poor consistency among supporting fibers and the matrix. Therefore, optimal structural performance of fibers and matrix is desirable. In this study, chemical treatments (i.e., alkali pretreatment, acid pretreatment, and scouring) were applied to jute fibers for improvement of composite properties. Thermal, thermo-mechanical, and flexural properties, and surface morphology, of untreated and treated jute fibers were studied on the treated fibers. Jute fiber/epoxy composite properties were analyzed by thermogravimetric analysis (TGA), flexural strength and modulus, and dynamic mechanical analysis (DMA). The chemical treatments had a significant impact on the properties of jute fiber composites.

JUTE AND COTTON COMPOSITES REINFORCED UNSATURATED POLYESTER

In this study, the effect of adding two different types of reinforcing natural fibers (jute and cotton) singly and in combination as a hybrid to unsaturated polyester resin was investigated. At the first discontinuous random fibers used in (5)mm length are added separately with different weight fraction as (3, 4.5, 6, and 7.5 wt.%) for both types fibers, then these fibers were mixed at (3.75 wt.% jute, 3.75 wt.% cotton) in (5)mm long. and The mechanical tests (hardness, Impact, and compression), as well as moisture absorption, are performed. The results show an increase in these properties with increasing weight fraction of fibers (jute & cotton) and reach the maximum amount at the addition of weight fraction of (7.5 wt.%) of both fibers (jute and cotton) separately. All composite specimens reinforced with jute fibers showed the highest hardness, Impact, compression, and moisture absorption among the composite specimen reinforced by cotton fibers and higher than in combination as a hybrid it was (93.1, 28.81 KJ/m2, 205 Mpa., and 1.4%) respectively.