A SiO2/pHEMA-Based Polymer-Infiltrated Ceramic Network Composite for Dental Restorative Materials

SiO2-poly(2-hydroxyethyl methacrylate) (pHEMA)-based composites have been widely used as biomaterials owing to their biocompatibility. However, they have not yet been applied as tooth restorative materials because of their poor mechanical properties. In the present paper, we develop a novel SiO2/pHEMA-based composite with a polymer-infiltrated network (PICN) structure for use in dental restorative materials. A mixture of SiO2 nanoparticles and a poly(vinyl alcohol) binder was sintered at 950 °C to fabricate a porous SiO2 block. A monomer mixture containing 70 wt%-HEMA/30 wt%-ethylene glycol dimethacrylate and a benzoyl peroxide initiator was infiltrated into the porous SiO2 block and heat-polymerized to fabricate the SiO2/pHEMA-based composite with a PICN structure. The composite was characterized according to its mechanical properties, surface free energy, and bonding properties with a dental adhesive. The flexural strength was 112.5 ± 18.7 MPa, the flexural modulus was 13.6 ± 3.4 GPa, and the Vickers hardness was 168.2 ± 16.1, which are similar values to human teeth. The surface free energy of the polar component of the composite was 19.6 ± 2.5 mN/m, suggesting that this composite has an active surface for bonding with the adhesive. The composite bonded well to the adhesive, in the presence of a silane coupling agent. The SiO2/pHEMA-based composite was demonstrated to be a potential candidate for dental restorative materials.

A Nanoindentation Approach for Time-Dependent Evaluation of Surface Free Energy in Micro- and Nano-Structured Titanium

Surface free energy (SFE) of titanium surfaces plays a significant role in tissue engineering, as it affects the effectiveness and long-term stability of both active coatings and functionalization and the establishment of strong bonds to the newly growing bone. A new contact–mechanics methodology based on high-resolution non-destructive elastic contacting nanoindentation is applied here to study SFE of micro- and nano-structured titanium surfaces, right after their preparation and as a function of exposure to air. The effectiveness of different surface treatments in enhancing SFE is assessed. A time-dependent decay of SFE within a few hours is observed, with kinetics related to the sample preparation. The fast, non-destructive method adopted allowed for SFE measurements in very hydrophilic conditions, establishing a reliable comparison between surfaces with different properties.

Benefits of Residual Aluminum Oxide for Sand Blasting Titanium Dental Implants: Osseointegration and Bactericidal Effects

Objectives. The purpose of this work was to determine the influence of residual alumina after sand blasting treatment in titanium dental implants. This paper studied the effect of alumina on physico-chemical surface properties, such as: surface wettability, surface energy. Osseointegration and bacteria adhesion were determined in order to determine the effect of the abrasive particles. Materials and Methods. Three surfaces were studied: (1) as-received, (2) rough surface with residual alumina from sand blasting on the surface and (3) with the same roughness but without residual alumina. Roughness was determined by white light interferometer microscopy. Surface wettability was evaluated with a contact angle video-based system and the surface free energy by means of Owens and Wendt equation. Scanning electron microscopy equipped with microanalysis was used to study the morphology and determine the chemical composition of the surfaces. Bacteria (Lactobacillus salivarius and Streptococcus sanguinis) were cultured in each surface. In total, 110 dental implants were placed into the bone of eight minipigs in order to compare the osseointegration. The percentage of bone-to-implant contact was determined after 4 and 6 weeks of implantation with histometric analysis. Results. The surfaces with residual alumina presented a lower surface free energy than clean surfaces. The in vivo studies demonstrated that the residual alumina accelerated bone tissue growth at different implantation times, in relation to clean dental implants. In addition, residual alumina showed a bactericidal effect by decreasing the quantity of bacteria adhering to the titanium. Conclusions. It is possible to verify the benefits that the alumina (percentages around 8% in weight) produces on the surface of titanium dental implants. Clinical relevance. Clinicians should be aware of the benefits of sand-blasted alumina due to the physico-chemical surface changes demonstrated in in vivo tests.

Epoxyorganosilane Finishing Compositions for Fibrous Fillers of Thermosetting and Thermoplastic Binders

The development of universal finishing compositions for fibers of various natures is an urgent task for polymer composite materials science. The developed finishes can be used for the fiber reinforcement of polymer matrices with a wide range of surface free energy characteristics. Epoxy systems modified with diaminesilane in a wide concentration range were examined by optical interferometry, FTIR spectroscopy, DSC and the sessile drop technique. It was shown that the partial curing of epoxy resin by diaminesilane at room temperature under an inert atmosphere, followed by contact with air, leads to a significant increase of the surface free energy of the system. Varying the concentration of diaminesilane allows us to effectively regulate the surface free energy of the composition. This makes it possible to use fibers finished with epoxyaminosilane compositions in composite materials based on a various thermosetting and thermoplastic binders with a surface tension of up to 75 mJ/m2.