Development of ultrafine grained high strength age hardenable Al 7075 alloy by cryorolling

2011 ◽  
Vol 32 (6) ◽  
pp. 3150-3160 ◽  
Author(s):  
Sushanta Kumar Panigrahi ◽  
R. Jayaganthan
2008 ◽  
Vol 584-586 ◽  
pp. 911-916 ◽  
Author(s):  
R. Jayaganthan ◽  
Sushanta Kumar Panigrahi

The effect of rolling strain on precipitation kinetics of Al 7075 alloy processed at liquid nitrogen temperature has been investigated in the present work. The Al 7075 alloy plates were solutionized and cryorolled with thickness reduction of 35% and 90%. The microstructural characterizations of the bulk and cryorolled Al alloy samples were carried out by electron backscatter diffraction analysis (EBSD) and transmission electron microscopy (TEM), respectively. The cryorolled Al alloys upon 90% thickness reduction exhibit ultrafine grained microstructure. The DSC results of cryorolled Al 7075 alloys obtained at different heating rates are used to calculate activation energies for the evolution of precipitates. The influence of different reduction rates on activation energy of precipitate formation in the cryorolled Al 7075 alloys was analyzed. The present study has shown that an ultrafine-grained Al 7075 alloy exhibits a higher driving force for the precipitation formation when compared to that of its bulk Al alloys.


Alloy Digest ◽  
1998 ◽  
Vol 47 (7) ◽  

Abstract Alcoa 7075 alloy has very high strength and is used for highly stressed structural parts. The T7351 temper offers improved stress-corrosion cracking resistance. The alloy’s strength level equals or exceeds mild steels. This datasheet provides information on composition, physical properties, and tensile properties. It also includes information on corrosion resistance as well as machining and surface treatment. Filing Code: AL-350. Producer or source: ALCOA Wire, Rod & Bar Division.


2014 ◽  
Vol 794-796 ◽  
pp. 851-856
Author(s):  
Tadashiege Nagae ◽  
Nobuhiro Tsuji ◽  
Daisuke Terada

Accumulative roll-bonding (ARB) process is one of the severe plastic deformation processes for fabricating ultrafine grained materials that exhibit high strength. In aluminum alloys, aging heat treatment has been an important process for hardening materials. In order to achieve good mechanical properties through the combination of grain refinement hardening and precipitation hardening, an Al-4.2wt%Ag binary alloy was used in the present study. After a solution treatment at 550°C for 1.5hr, the alloy was severely deformed by the ARB process at room temperature (RT) up to 6 cycles (equivalent strain of 4.8). The specimens ARB-processed by various cycles (various strains) were subsequently aged at 100, 150, 200, 250°C, and RT. The hardness of the solution treated (ST) specimen increased by aging. On the other hand, hardness of the ARB processed specimen decreased after aging at high temperatures such as 250°C. This was probably due to coarsening of precipitates or/and matrix grains. The specimen aged at lower temperature showed higher hardness. The maximum harnesses achieved by aging for the ST specimen, the specimens ARB processed by 2 cycles, 4 cycles and 6 cycles were 55HV, 71HV, 69HV and 65HV, respectively. By tensile tests it was shown that the strength increased by the ARB process though the elongation decreased significantly. However, it was found that the tensile elongation of the ARB processed specimens was improved by aging without sacrificing the strength. The results suggest that the Al-Ag alloy having large elongation as well as high strength can be realized by the combination of the ARB process for grain refinement and the subsequent aging for precipitation hardening.


2015 ◽  
Vol 112 (47) ◽  
pp. 14501-14505 ◽  
Author(s):  
Xiaolei Wu ◽  
Muxin Yang ◽  
Fuping Yuan ◽  
Guilin Wu ◽  
Yujie Wei ◽  
...  

Grain refinement can make conventional metals several times stronger, but this comes at dramatic loss of ductility. Here we report a heterogeneous lamella structure in Ti produced by asymmetric rolling and partial recrystallization that can produce an unprecedented property combination: as strong as ultrafine-grained metal and at the same time as ductile as conventional coarse-grained metal. It also has higher strain hardening than coarse-grained Ti, which was hitherto believed impossible. The heterogeneous lamella structure is characterized with soft micrograined lamellae embedded in hard ultrafine-grained lamella matrix. The unusual high strength is obtained with the assistance of high back stress developed from heterogeneous yielding, whereas the high ductility is attributed to back-stress hardening and dislocation hardening. The process discovered here is amenable to large-scale industrial production at low cost, and might be applicable to other metal systems.