Unidirectional isothermal compression deformation mechanism and microstructural evolution of semi-solid CuSn10P1 alloy

2019 ◽  
Vol 6 (8) ◽  
pp. 0865i5
Author(s):  
Jingbo Wang ◽  
Qiuping Wang ◽  
Lu Li ◽  
Rongfeng Zhou ◽  
Yongkun Li ◽  
...  
Materials ◽  
2021 ◽  
Vol 14 (1) ◽  
pp. 194
Author(s):  
Yongfei Wang ◽  
Shengdun Zhao ◽  
Yi Guo ◽  
Kuanxin Liu ◽  
Shunqi Zheng

Al-Mg-Si based alloys are popular alloys used in the automotive industry. However, limited studies have been performed to investigate the microstructure, deformation characteristics, and deformation mechanism for the semi-solid 6063 alloys. In this study, the cold radial forging method and semi-solid isothermal treatment (SSIT) are proposed in the semi-solid isothermal compression (SSIC) process to fabricate high-quality semi-solid 6063 billets. The effects of deformation temperature, strain rate, and strain on the microstructure, deformation characteristics, and deformation mechanism of the SSIC of cold radial forged 6063 alloys were investigated experimentally. Constitutive equations were established based on the measured data in experiments to predict the flow stress. Results show that an average grain size in the range from 59.22 to 73.02 μm and an average shape factor in the range from 071 to 078 can be obtained in the microstructure after the cold radial forged 6063 alloys were treated with SSIT process. Four stages (i.e., sharp increase, decrease, steady state, and slow increase) were observed in the true stress- true strain curve. The correlation coefficient of the constitutive equation was obtained as 0.9796 while the average relative error was 5.01%. The deformation mechanism for SSIC of cold radial forged aluminum alloy 6063 mainly included four modes: The liquid phase flow, grain slide or grain rotation along with the liquid film, slide among solid grains, and the plastic deformation of solid grains.


2009 ◽  
Vol 506 (1-2) ◽  
pp. 8-15 ◽  
Author(s):  
Zude Zhao ◽  
Qiang Chen ◽  
Yanbin Wang ◽  
Dayu Shu

2022 ◽  
Vol 327 ◽  
pp. 11-25
Author(s):  
Guan Fei Xiao ◽  
Ju Fu Jiang ◽  
Ying Wang ◽  
Ying Zhe Liu ◽  
Ying Zhang ◽  
...  

Semi-solid processing combines the advantages of traditional forging and casting methods, so it has received much attention recently. However, the research on semi-solid behaviors of Nickel-based superalloys has been rarely reported. In order to investigate the behaviors of Nickel-based superalloy at solid and semi-solid states, oxidation experiments, isothermal treatment experiments and deformation experiments of GH4037 alloy were studied. Short-term oxidation experiments of GH4037 alloy were carried out at a solid temperature (1200 °C) and a semi-solid temperature (1360 °C). The results indicated that the oxides formed at 1200 °C were mainly composed of TiO2, Cr2O3 and a small amount of spinels NiCr2O4, while the oxides formed at 1360 °C consisted of the spinels of NiCr2O4, NiWO4 and NiMoO4 besides TiO2 and Cr2O3. Microstructure evolution of GH4037 alloy after semi-solid isothermal treatment at 1370 °C and 1380 °C was studied. The results indicated that semi-solid microstructures consisted of equiaxed solid grains and liquid phases. The average grains size and shape factor of solid grains were affected by melting mechanism and grain growth mechanism. Compression behaviors of GH4037 alloy after compressed at 1200 °C and 1360 °C were investigated. The results indicated that the flow stress of 1360 °C decreased significantly compared to that of 1200 °C. The deformation zones in the specimens were divided into three parts: the difficult deformation zone, the large deformation zone, and the free deformation zone. At 1200 °C, the deformation mechanism was plastic deformation mechanism. At 1360 °C, sliding between solid particles (SS), liquid flow (LF), flow of liquid incorporating solid particles (FLS), plastic deformation of solid particles (PDS) coexisted in the compression specimen.


2012 ◽  
Vol 192-193 ◽  
pp. 238-245 ◽  
Author(s):  
Hong Yu Xu ◽  
Ze Sheng Ji ◽  
Zhen Yu Wang

In this paper, chip recycling technology combined with SIMA method which is called CR-SIMA method was adopted to prepare semi-solid billets. AZ91D magnesium alloy was refined by Er and its microstructural evolution was investigated during semi-solid isothermal treatment. The results show that Er can improve the feature of cast structure and decrease the grain size. Moreover, the γ-Mg17Al12 phase is well refined and disperses in the α-Mg matrix. A semisolid microstructure with small and spheroidal primary particles can be obtained after partially remelting. With increasing heating temperature, the dissolution of eutectic Mg17Al12 phase first took place, resulting in the primary dendritic grains coarsening into interconnected non-dendritic grains. With heating continuously, the residual interdendritic γ-Mg17Al12 at the edges of the primary grains melted in succession and the primary grains separated into small polygon grains. During the semi-solid isothermal treatment, the amount of liquid increased until the solid-liquid system reached its equilibrium state. At the same time, owing to the decreasing of interfacial energy, the grains gradually spheroidized and began to grow with a further increasing of the holding time.