Significant Improvement of Electrochemical Performance of Ni-rich Cathode Material by Polyethylene Coating
2016 ◽
Vol 19
(3)
◽
pp. 157-161
Keyword(s):
We attempted to use polyethylene (PE) to coat the surface of the cathode material in order to suppress these unnecessary reac-tion, and the results obtained via electrochemical impedance spectroscopy (EIS) suggest the growth of the SEI resistance and charge trans-fer resistance was suppressed in the samples consisting of 0.1 wt% PE-coated Li[(Ni0.6Co0.1Mn0.3)0.36(Ni0.80Co0.15Al0.05)0.64)]O2 (NCS). The initial discharge capacity of the coated material was of 190.56 mAhg-1 at 0.1 C between 3.0 and 4.3 V, and 94.6 % of this capacity was retained after 30 cycles. A notable of effect of the PE coating, is that the resulting exothermic temperature appears at approximately 258.1 °C, which is higher than that for bare NCS at 249.3 °C.
2017 ◽
Vol 4
(11)
◽
pp. 1806-1812
◽
2019 ◽
2010 ◽
Vol 157
(3)
◽
pp. B357
◽
2015 ◽
Vol 3
(15)
◽
pp. 7870-7876
◽
2011 ◽
Vol 287-290
◽
pp. 1416-1419