Mechanical Property Performance of Polymer-Modified Calcium Sulfoaluminate Cement Mortar Systems

2013 ◽  
Vol 2 (1) ◽  
pp. 20120036 ◽  
Author(s):  
Joshua V. Brien ◽  
Kamyar C. Mahboub ◽  
Thomas L. Robl
Keyword(s):  
Mechanical Property ◽  
Cement Mortar ◽  
Calcium Sulfoaluminate Cement ◽  
Calcium Sulfoaluminate ◽  
Property Performance

scholarly journals Properties of Calcium Sulfoaluminate Cement Mortar Modified by Hydroxyethyl Methyl Celluloses with Different Degrees of Substitution

Molecules ◽  
2021 ◽  
Vol 26 (8) ◽  
pp. 2136
Author(s):  
Shaokang Zhang ◽  
Ru Wang ◽  
Linglin Xu ◽  
Andreas Hecker ◽  
Horst-Michael Ludwig ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Flexural Strength ◽  
Bond Strength ◽  
Cement Mortar ◽  
Retention Rate ◽  
Methyl Cellulose ◽  
Tensile Bond Strength ◽  
Calcium Sulfoaluminate Cement ◽  
Calcium Sulfoaluminate ◽  
Cement Mortars

This paper studies the influence of hydroxyethyl methyl cellulose (HEMC) on the properties of calcium sulfoaluminate (CSA) cement mortar. In order to explore the applicability of different HEMCs in CSA cement mortars, HEMCs with higher and lower molar substitution (MS)/degree of substitution (DS) and polyacrylamide (PAAm) modification were used. At the same time, two kinds of CSA cements with different contents of ye’elimite were selected. Properties of cement mortar in fresh and hardened states were investigated, including the fluidity, consistency and water-retention rate of fresh mortar and the compressive strength, flexural strength, tensile bond strength and dry shrinkage rate of hardened mortar. The porosity and pore size distribution were also analyzed by mercury intrusion porosimetry (MIP). Results show that HEMCs improve the fresh state properties and tensile bond strength of both types of CSA cement mortars. However, the compressive strength of CSA cement mortars is greatly decreased by the addition of HEMCs, and the flexural strength is decreased slightly. The MIP measurement shows that HEMCs increase the amount of micron-level pores and the porosity. The HEMCs with different MS/DS have different effects on the improvement of tensile bond strength in different CSA cement mortars. PAAm modification can improve the tensile bond strength of HEMC-modified CSA cement mortar.

scholarly journals Strength Performance and Microstructure of Calcium Sulfoaluminate Cement-Stabilized Soft Soil

2021 ◽  
Vol 13 (4) ◽  
pp. 2295
Author(s):  
Hailong Liu ◽  
Jiuye Zhao ◽  
Yu Wang ◽  
Nangai Yi ◽  
Chunyi Cui
Keyword(s):  
Soft Soil ◽  
Hydration Product ◽  
X Ray Diffraction ◽  
Calcium Sulfoaluminate Cement ◽  
Strength Performance ◽  
X Ray ◽  
Calcium Sulfoaluminate ◽  
Stabilized Soil ◽  
Calcium Silicates ◽  
Hydrated Calcium

Calcium sulfoaluminate cement (CSA) was used to stabilize a type of marine soft soil in Dalian China. Unconfined compressive strength (UCS) of CSA-stabilized soil was tested and compared to ordinary Portland cement (OPC); meanwhile the influence of amounts of gypsum in CSA and cement contents in stabilized soils on the strength of stabilized soils were investigated. X-ray diffraction (XRD) tests were employed to detect generated hydration products, and scanning electron microscopy (SEM) was conducted to analyze microstructures of CSA-stabilized soils. The results showed that UCS of CSA-stabilized soils at 1, 3, and 28 d firstly increased and then decreased with contents of gypsum increasing from 0 to 40 wt.%, and CSA-stabilized soils exhibited the highest UCS when the content of gypsum equaled 25 wt.%. When the mixing amounts of OPC and CSA were the same, CSA-stabilized soils had a significantly higher early strength (1 and 3 d) than OPC. For CSA-stabilized soil with 0 wt.% gypsum, monosulfate (AFm) was detected as a major hydration product. As for CSA-stabilized soil with certain amounts of gypsum, the intensity of ettringite (Aft) was significantly higher than that in the sample hydrating without gypsum, but a tiny peak of AFm also could be detected in the sample with 15 wt.% gypsum at 28 d. Additionally, the intensity of AFt increased with the contents of gypsum increasing from 0 to 25 wt.%. When contents of gypsum increased from 25 to 40 wt.%, the intensity of AFt tended to decrease slightly, and residual gypsum could be detected in the sample with 40 wt.% gypsum at 28 d. In the microstructure of OPC-stabilized soils, hexagonal plate-shaped calcium hydroxide (CH) constituted skeleton structures, and clusters of hydrated calcium silicates (C-S-H) gel adhered to particles of soils. In the microstructure of CSA-stabilized soils, AFt constituted skeleton structures, and the crystalline sizes of ettringite increased with contents of gypsum increasing; meanwhile, clusters of the aluminum hydroxide (AH3) phase could be observed to adhere to particles of soils and strengthen the interaction.

scholarly journals Effect of Flue Gas Desulfurization Gypsum on the Properties of Calcium Sulfoaluminate Cement Blended with Ground Granulated Blast Furnace Slag

Materials ◽  
2021 ◽  
Vol 14 (2) ◽  
pp. 382 ◽  
Author(s):  
Danying Gao ◽  
Zhenqing Zhang ◽  
Yang Meng ◽  
Jiyu Tang ◽  
Lin Yang
Keyword(s):  
Blast Furnace ◽  
Mechanical Strength ◽  
Flue Gas ◽  
Blast Furnace Slag ◽  
Setting Time ◽  
Flue Gas Desulfurization ◽  
Calcium Sulfoaluminate Cement ◽  
Calcium Sulfoaluminate ◽  
Granulated Blast Furnace Slag ◽  
Furnace Slag

This work aims to investigate the effect of additional flue gas desulfurization gypsum (FGDG) on the properties of calcium sulfoaluminate cement (CSAC) blended with ground granulated blast furnace slag (GGBFS). The hydration rate, setting time, mechanical strength, pore structure and hydration products of the CSAC-GGBFS mixture containing FGDG were investigated systematically. The results show that the addition of FGDG promotes the hydration of the CSAC-GGBFS mixture and improves its mechanical strength; however, the FGDG content should not exceed 6%.

scholarly journals Printability and Setting Time of CSA Cement with Na2SiO3 and Gypsum for Binder Jetting 3D Printing

Materials ◽  
2021 ◽  
Vol 14 (11) ◽  
pp. 2811
Author(s):  
Okpin Na ◽  
Kangmin Kim ◽  
Hyunjoo Lee ◽  
Hyunseung Lee
Keyword(s):  
3D Printing ◽  
Sodium Silicate ◽  
Setting Time ◽  
Sodium Silicate Solution ◽  
Preliminary Test ◽  
Silicate Solution ◽  
Calcium Sulfoaluminate Cement ◽  
Calcium Sulfoaluminate ◽  
Parametric Studies ◽  
Binder Jetting

The purpose of this study is to optimize the composition of CSA (calcium sulfoaluminate) cement with sodium silicate (Na2SiO3) and gypsum for binder jetting 3D printing. The preliminary test was carried out with an applicator to decide the proper thickness of one layer before using the 3D printer. A liquid binder was then selected to maintain the shape of the particles. Based on the results, the optimal mixture of dry materials and a liquid activator was derived through various parametric studies. For dry materials, the optimum composition of CSA cement, gypsum, and sand was suggested, and the liquid activator made with sodium silicate solution and VMA (viscosity modified agent) were selected. The setting time with gypsum and sodium silicate was controlled within 30 s. In case of the delayed setting time and the rapid setting mixture, the jetting line was printed thicker or thinner and the accuracy of the printout was degraded. In order to adjust the viscosity of the liquid activator, 10% of the VMA was used in 35% of sodium silicate solution and the viscosity of 200–400 cP was suitable to be sprayed from the nozzle. With this optimal mixture, a prototype of atypical decorative wall was printed, and the compressive strength was measured at about 7 MPa.