Dislocation Structures in Ni3(Al, Hf)

1996 ◽  
Vol 460 ◽  
Author(s):  
T. Kruml ◽  
B. Viguier ◽  
J. Bonneville ◽  
P. Spätig ◽  
J. L. Martin
Keyword(s):  
Electron Microscopy ◽  
Antiphase Boundary ◽  
Image Simulation ◽  
Compression Tests ◽  
Simulation Techniques ◽  
Weak Beam ◽  
Thin Foils ◽  
Transmission Electron ◽  
Different Temperatures

ABSTRACTSingle crystalline specimens of Ni74.8Al21.9Hf3.3 were subjected to compression tests at different temperatures. Thin foils for transmission electron microscopy observations were prepared from several specimens deformed within and above the yield stress anomaly domain. The dislocation microstructure was studied. The weak beam imaging and image simulation techniques followed by anisotropie elasticity calculations were used for the determination of antiphase boundary energies in both cube and octahedral planes, resulting in values of 237 mJm-2 and 252 mJm-2 respectively. The comparison of the present results with data taken from literature shows the influence of Hf on mechanical properties, dislocation microstructures and APB energies.

Experimental Tem and Image Simulation of Dislocations in Ti3A1

1994 ◽  
Vol 364 ◽  
Author(s):  
JÖrg M.K. Wiezorek ◽  
S. A. Court ◽  
C.J. Humphreys
Keyword(s):  
Fine Structure ◽  
Room Temperature ◽  
Stacking Faults ◽  
Antiphase Boundary ◽  
Computational Techniques ◽  
Image Simulation ◽  
Prism Plane ◽  
Weak Beam ◽  
Transmission Electron ◽  
Beam Technique

AbstractThe fine structure and the character of a dislocations on prism planes have been determined for room-temperature deformed polycrystalline Ti3Al using a combination of experimental and computational techniques of transmission electron microscopy (TEM). Within the resolution limits of the weak-beam technique the fine structure of prism plane a dislocations in Ti3Al is found to be planar and to comprise only a single ribbon of antiphase boundary and no experimentally observable stacking faults.

Structure Determination of Clusters Formed in Ultra-Low Energy High-Dose Implanted Silicon

2005 ◽  
Vol 108-109 ◽  
pp. 303-308 ◽  
Author(s):  
N. Cherkashin ◽  
Martin J. Hÿtch ◽  
Fuccio Cristiano ◽  
A. Claverie
Keyword(s):  
Electron Microscopy ◽  
Geometric Phase ◽  
Low Energy ◽  
High Dose ◽  
Dislocation Loops ◽  
Weak Beam ◽  
Transmission Electron ◽  
Geometric Phase Analysis

In this work, we present a detailed structural characterization of the defects formed after 0.5 keV B+ implantation into Si to a dose of 1x1015 ions/cm2 and annealed at 650°C and 750°C during different times up to 160 s. The clusters were characterized by making use of Weak Beam and High Resolution Transmission Electron Microscopy (HRTEM) imaging. They are found to be platelets of several nanometer size with (001) habit plane. Conventional TEM procedure based on defect contrast behavior was applied to determine the directions of their Burger’s vectors. Geometric Phase Analysis of HRTEM images was used to measure the displacement field around these objects and, thus, to unambiguously determine their Burger’s vectors. Finally five types of dislocation loops lying on (001) plane are marked out: with ] 001 [1/3 ≅ b and b ∝ [1 0 1], [-1 0 1], [0 1 1], [0 -1 1].

Phenomena Associated with Oxygen in Titanium

1967 ◽  
Vol 25 ◽  
pp. 310-311
Author(s):  
E. U. Lee ◽  
P. A. Garner ◽  
J. S. Owens
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Electron Microscope ◽  
Microstructural Changes ◽  
Electrolytic Polishing ◽  
Interstitial Impurities ◽  
Thin Foils ◽  
Transmission Electron ◽  
Iodide Titanium ◽  
Alpha Titanium

Evidence for ordering (1-6) of interstitial impurities (O and C) has been obtained in b.c.c. metals, such as niobium and tantalum. In this paper we report the atomic and microstructural changes in an oxygenated c.p.h. metal (alpha titanium) as observed by transmission electron microscopy and diffraction.Oxygen was introduced into zone-refined iodide titanium sheets of 0.005 in. thickness in an atmosphere of oxygen and argon at 650°C, homogenized at 800°C and furnace-cooled in argon. Subsequently, thin foils were prepared by electrolytic polishing and examined in a JEM-7 electron microscope, operated at 100 KV.

Dislocations in alumina deformed by prismatic slip

1978 ◽  
Vol 36 (1) ◽  
pp. 606-607
Author(s):  
J. Cadoz ◽  
J. Castaing ◽  
J. Philibert
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Basal Slip ◽  
Prismatic Slip ◽  
Compression Tests ◽  
Thin Sections ◽  
Burgers Vector ◽  
Maximum Deformation ◽  
Transmission Electron ◽  
Mechanical Thinning

Plastic deformation of alumina has been much studied; basal slip occurs and dislocation structures have been investigated by transmission electron microscopy (T.E.M.) (1). Non basal slip has been observed (2); the prismatic glide system <1010> {1210} has been obtained by compression tests between 1400°C and 1800°C (3). Dislocations with <0110> burgers vector were identified using a 100 kV microscope(4).We describe the dislocation structures after prismatic slip, using high voltage T.E.M. which gives much information.Compression tests were performed at constant strainrate (∿10-4s-1); the maximum deformation reached was 0.03. Thin sections were cut from specimens deformed at 1450°C, either parallel to the glide plane or perpendicular to the glide direction. After mechanical thinning, foils were produced by ion bombardment. Details on experimental techniques can be obtained through reference (3).

Simulation of three Dimensional Defect Images in Transmission Electron Microscopy

1976 ◽  
Vol 34 ◽  
pp. 470-471
Author(s):  
W. D. Cooper ◽  
C. S. Hartley ◽  
J. J. Hren
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Three Dimensional ◽  
Crystalline Lattice ◽  
Continuum Models ◽  
Thin Foils ◽  
Transmission Electron ◽  
Microscope Images ◽  
General Computer Program ◽  
General Computer

Interpretation of electron microscope images of crystalline lattice defects can be greatly aided by computer simulation of theoretical contrast from continuum models of such defects in thin foils. Several computer programs exist at the present time, but none are sufficiently general to permit their use as an aid in the identification of the range of defect types encountered in electron microscopy. This paper presents progress in the development of a more general computer program for this purpose which eliminates a number of restrictions contained in other programs. In particular, the program permits a variety of foil geometries and defect types to be simulated.The conventional approximation of non-interacting columns is employed for evaluation of the two-beam dynamical scattering equations by a piecewise solution of the Howie-Whelan equations.

Determination of the Burgers vector of a dislocation in a Fe-Mn alloy by weak-beam image in HVEM

1978 ◽  
Vol 36 (1) ◽  
pp. 330-331
Author(s):  
Y. Ishida ◽  
H. Ishida ◽  
K. Kohra ◽  
H. Ichinose
Keyword(s):  
High Order ◽  
Simulation Technique ◽  
The Other ◽  
Image Simulation ◽  
Diffraction Vector ◽  
Burgers Vector ◽  
Weak Beam ◽  
Beam Image ◽  
Edge Component

IntroductionA simple and accurate technique to determine the Burgers vector of a dislocation has become feasible with the advent of HVEM. The conventional image vanishing technique(1) using Bragg conditions with the diffraction vector perpendicular to the Burgers vector suffers from various drawbacks; The dislocation image appears even when the g.b = 0 criterion is satisfied, if the edge component of the dislocation is large. On the other hand, the image disappears for certain high order diffractions even when g.b ≠ 0. Furthermore, the determination of the magnitude of the Burgers vector is not easy with the criterion. Recent image simulation technique is free from the ambiguities but require too many parameters for the computation. The weak-beam “fringe counting” technique investigated in the present study is immune from the problems. Even the magnitude of the Burgers vector is determined from the number of the terminating thickness fringes at the exit of the dislocation in wedge shaped foil surfaces.

Enhanced information from biological materials through technological improvements in cryo-electron microscopy

1992 ◽  
Vol 50 (1) ◽  
pp. 788-789
Author(s):  
Marc J.C. de Jong ◽  
Wim M. Busing ◽  
Max T. Otten
Keyword(s):  
Electron Microscopy ◽  
Electron Beam ◽  
Biological Materials ◽  
Electron Crystallography ◽  
Cryo Electron Microscopy ◽  
Transmission Electron ◽  
The Many ◽  
Technological Improvements ◽  
Beam Damage

Biological materials damage rapidly in the electron beam, limiting the amount of information that can be obtained in the transmission electron microscope. The discovery that observation at cryo temperatures strongly reduces beam damage (in addition to making it unnecessaiy to use chemical fixatives, dehydration agents and stains, which introduce artefacts) has given an important step forward to preserving the ‘live’ situation and makes it possible to study the relation between function, chemical composition and morphology.Among the many cryo-applications, the most challenging is perhaps the determination of the atomic structure. Henderson and co-workers were able to determine the structure of the purple membrane by electron crystallography, providing an understanding of the membrane's working as a proton pump. As far as understood at present, the main stumbling block in achieving high resolution appears to be a random movement of atoms or molecules in the specimen within a fraction of a second after exposure to the electron beam, which destroys the highest-resolution detail sought.

scholarly journals Electron Microscopy Investigation of Magnetization Process in Thin Foils and Nanostructures

2007 ◽  
Vol 1026 ◽  
Author(s):  
Pascale Bayle-Guillemaud ◽  
Aurelien Masseboeuf ◽  
Fabien Cheynis ◽  
Jean-Christophe Toussaint ◽  
Olivier Fruchart ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Magnetic Anisotropy ◽  
Magnetic Induction ◽  
Perpendicular Magnetic Anisotropy ◽  
In Situ Observation ◽  
Magnetic Imaging ◽  
Thin Foils ◽  
Transmission Electron

AbstractThis paper presents investigations of magnetization configuration evolution during in-situ magnetic processes in materials exhibiting planar and perpendicular magnetic anisotropy. Transmission electron microscopy has been used to perform magnetic imaging. Fresnel contrasts in Lorentz Transmission Electron Microscopy (LTEM) and phase retrieval methods such as Transport of Intensity Equation (TIE) solving or electron holography have been implemented. These techniques are sensitive to magnetic induction perpendicular to the electron beam and can give access to a spatially resolved (resolution better than 10 nm) mapping of magnetic induction distribution and could be extended to dynamical studies during in-situ observation. Thin foils of FePd alloys with a strong perpendicular magnetic anisotropy (PMA) and self-assembled Fe dots are presented. Both are studied during magnetization processes exhibiting the capacities of in-situ magnetic imaging in a TEM.