CW Argon-ion laser initiated aluminum induced crystallization of amorphous silicon thin films

ABSTRACTCW Argon-ion laser initiated aluminum induced crystallization (AIC) of RF magnetron sputtered amorphous silicon (a-Si) thin films has been investigated. It was found that lasers could be effectively used to initiate AIC process at very low threshold power densities. An argon-ion laser (λ=514.5 nm) was used to anneal Al/a-Si/glass structures with varying power densities ranging between 55 and 125 W/cm2 and exposure times ranging from 10 to 120 s. X-ray diffraction analysis showed the resulting films to be polycrystalline. The crystallization rate increased both with power density and exposure time. Environmental scanning electron microscopy (ESEM) analysis showed that the surface features change with increasing power density and irradiation time. A dendritic growth pattern was observed in the initial stages of interaction between the films. A strong crystalline Raman peak at around 520 cm-1 was observed in the Raman spectra of the crystallized samples.