Shear Bond Strength of Porcelain Veneers Rebonded to Enamel

2015 ◽  
Vol 40 (3) ◽  
pp. E112-E121 ◽  
Author(s):  
HA St Germain ◽  
TH St Germain
Keyword(s):  
Phosphoric Acid ◽  
Bond Strength ◽  
Aluminum Oxide ◽  
Shear Bond Strength ◽  
Resin Cement ◽  
Enamel Surface ◽  
Control Group ◽  
Significant Difference ◽  
Mode Of Failure ◽  
Group A

SUMMARY In this laboratory research, shear bond strength (SBS) and mode of failure of veneers rebonded to enamel in shear compression were determined. Three groups (A, B, and C; n=10 each) of mounted molar teeth were finished flat using wet 600-grit silicon carbide paper, and 30 leucite-reinforced porcelain veneers (5.0 × 0.75 mm) were air abraded on the internal surface with 50 μm aluminum oxide, etched with 9.5% hydrofluoric acid, and silanated. The control group (A) veneer specimens were bonded to enamel after etching with 37% phosphoric acid using bonding resin and a dual cure resin composite cement. Groups B and C were prepared similarly to group A with the exception that a release agent was placed before the veneer was positioned on the prepared enamel surface and the resin cement was subsequently light activated. The debonded veneers from groups B and C were placed in a casting burnout oven and heated to 454°C/850°F for 10 minutes to completely carbonize the resin cement and stay below the glass transition temperature (Tg) of the leucite-reinforced porcelain. The recovered veneers were then prepared for bonding. The previously bonded enamel surfaces in group B were air abraded using 50 μm aluminum oxide followed by 37% phosphoric acid etching, while group C enamel specimens were acid etched only. All specimens were thermocycled between 5°C and 55°C for 2000 cycles using a 30-second dwell time and stored in 37°C deionized water for 2 weeks. SBS was determined at a crosshead speed of 1.0 mm/min. SBS results in MPa for the groups were (A) = 20.6±5.1, (B) = 18.1±5.5, and (C) = 17.2±6.1. One-way analysis of variance indicated that there were no significant interactions (α=0.05), and Tukey-Kramer post hoc comparisons (α=0.05) detected no significant pairwise differences. An adhesive mode of failure at the enamel interface was observed to occur more often in the experimental groups (B = 40%, C = 50%). Rebonding the veneers produced SBS values that were not significantly different from the control group. Also, no significant difference in SBS values were observed whether the debonded enamel surface was air abraded and acid etched or acid etched only.

scholarly journals Shear bond strength of enamel surface treated with air-abrasive system

2002 ◽  
Vol 13 (3) ◽  
pp. 175-178 ◽  
Author(s):  
Maria Cristina Borsatto ◽  
Alma Blásida Elisaur Benitez Catirse ◽  
Regina Guenka Palma Dibb ◽  
Telma Nunes do Nascimento ◽  
Renata Andréa Salvitti de Sá Rocha ◽  
...  
Keyword(s):  
Phosphoric Acid ◽  
Bond Strength ◽  
Aluminum Oxide ◽  
Shear Bond Strength ◽  
Composite Resin ◽  
Enamel Surface ◽  
Acid Etching ◽  
Air Abrasion ◽  
Group Iii ◽  
Group I

The aim of this study was to evaluate the shear bond strength of a composite resin to dental enamel, using three different surface treatments. Fifteen sound third molars were randomly assigned to three groups. The mesial and distal surfaces were flattened and covered using adhesive tape with a central orifice delimiting the adhesion area (7.07 mm²). Group I, the enamel surface was conditioned with 37% phosphoric acid for 15 s; group II, the surface was treated using air abrasion with aluminum oxide; group III, the enamel surface was treated using an association of air abrasion with aluminum oxide and 37% phosphoric acid. The Single Bond (3M) adhesive system was applied and a Teflon matrix was placed and filled with composite resin Z-100 (3M) and light-cured. The shear bond strength test was performed with a universal testing machine. The acid etching technique and air abrasion with aluminum oxide associated with acid etching had the highest shear bond strength values. Data were subjected to statistical analysis using ANOVA and the Tukey test, and no statistically significant difference in shear bond strength was observed between group I (12.49 ± 2.85 MPa) and group III (12.59 ± 2.68 MPa). In contrast, both groups had statistically better shear bond strengths compared to group II (0.29 ± 0.56 MPa; p<0.05). Air abrasion with aluminum oxide does not substitute acid etching. The association of these methods to obtain adequate adhesion to the substrate is necessary.

scholarly journals Effect of Different Surface Treatments for Ceramic Bracket Base on Bond Strength of Rebonded Brackets

2015 ◽  
Vol 26 (1) ◽  
pp. 61-65 ◽  
Author(s):  
Monique Kruger Guarita ◽  
Alexa Helena Köhler Moresca ◽  
Estela Maris Losso ◽  
Alexandre Moro ◽  
Ricardo Cesar Moresca ◽  
...  
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Silica Coating ◽  
Surface Treatments ◽  
Enamel Surface ◽  
Control Group ◽  
Significant Difference ◽  
Ceramic Brackets ◽  
Ceramic Bracket ◽  
Bracket Base

The aim of this study was to evaluate the shear bond strength of rebonded ceramic brackets after subjecting the bracket base to different treatments. Seventy-five premolars were selected and randomly distributed into five groups (n=15), according to the type of the bracket surface treatment: I, no treatment, first bonding (control); II, sandblasting with aluminum oxide; III, sandblasting + silane; IV, silica coating + silane; and V, silicatization performed in a laboratory (Rocatec system). The brackets were fixed on an enamel surface with Transbond XT resin without acid etching. The brackets were then removed and their bases were subjected to different treatments. Thereafter, the brackets were fixed again to the enamel surface and the specimens were subjected to shear bond strength (SBS) test. The adhesive remnant index (ARI) was then evaluated for each specimen. Data were subjected to ANOVA and Tukey's tests (α=0.05). A statistically significant difference was observed only between Rocatec and the other groups; the Rocatec group showed the lowest SBS values. The highest SBS values were observed for group 1, without any significant difference from the values for groups II, III and IV. Most groups had a higher percentage of failures at the enamel-resin interface (score 1). It was concluded that the surface treatments of rebonded ceramic brackets were effective, with SBS values similar to that of the control group, except Rocatec group.

scholarly journals The effect of aluminum oxide sandblasting and discs on shear bond strength of metal brackets rebonded in eroded enamel

2021 ◽  
Vol 10 (13) ◽  
pp. e34101320132
Author(s):  
Luciana de Vasconcelos Leão ◽  
Adriana Oliveira ◽  
Jefferson Chaves Moreira ◽  
Luiz Renato Paranhos ◽  
Sigmar de Mello Rode ◽  
...  
Keyword(s):  
Shear Strength ◽  
Bond Strength ◽  
Aluminum Oxide ◽  
Shear Bond Strength ◽  
Artificial Saliva ◽  
Testing Machine ◽  
Control Group ◽  
Adhesive Remnant Index ◽  
Significant Difference ◽  
Kolmogorov Smirnov

This research aimed to assess the effect of aluminum oxide sandblasting and discs on the bond strength of metal brackets rebonded on artificially eroded enamel. Fifty-four bovine incisors were divided into groups: Control (Artificial Saliva), AlOx (Aluminum oxide sandblasting), and SL (Aluminum oxide discs). They had their enamel surface flattened with Al2O3 discs and a metallographic polisher, then Knoop microhardness was assessed. AlOx and SL specimens were eroded with Coca-Cola™ for 1 minute, 3 times a day for 7 days. Metal brackets were bonded to the tooth. Shear strength was measured by an EMIC universal testing machine (0.5 mm/min). The Adhesive Remnant Index (ARI) was performed after shearing through magnifying glass (10X). Kolmogorov-Smirnov, Levene, homoscedasticity and ANOVA tests were applied to assess microhardness and shear strength (p=0.163). All groups presented shear bond strength with no significant differences. The ARI showed statistically significant difference between the groups. The prevalence for the control group was ARI 3. However for AlOx and SL, ARI 1 and 2 prevailed. The aluminum oxide sandblasting and aluminum oxide discs did not positively increase the bond strength of brackets when bonded to artificially eroded enamel. The ARI indicated that eroded teeth present higher resin adhesion to enamel.

scholarly journals Micro-shear bond strength of bioactive cement to translucent zirconia after thermocycyling: a comparative in-vitro study

2020 ◽  
Vol 23 (1) ◽  
Author(s):  
Menna Ahmed ElGendy ◽  
Ihab Mosleh ◽  
Hanaa Zaghloul
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Testing Machine ◽  
In Vitro Study ◽  
Resin Cement ◽  
Zirconia Ceramic ◽  
Control Group ◽  
Significant Difference ◽  
Before And After

Objective: the purpose of the study was to evaluate the micro-shear bond strength of different cements to translucent zirconia before and after thermocycling aging. Material and methods: Twelve translucent zirconia ceramic discs were used in the study. Specimens were sandblasted using 50 ‎μm aluminum oxide (Al2O3) particles. The specimens were divided into three groups (n = 4) according to the cement type: Panavia resin cement (control group), resin modified glass ionomer (RMGI), and Activa bioactive cement. Each group was further sub-divided into two equal subgroups (n = 2) according to whether the specimens were subjected to thermocycling or not. Thermocycling was performed in distilled water at 5000 cycles between 5 oC - 55 oC. The micro-shear bond strength test (μSBS) was measured using universal testing machine. Kruskal-Wallis test was used to compare between the three cements. Dunn’s test was used for pair-wise comparisons when Kruskal-Wallis test is significant. Mann-Whitney U test was used to compare between micro-shear bond strength before and after thermocycling P ≤ 0.05. Results: In non-aged subgroups, there was no significant difference between Panavia and Activa; both showed significantly the highest mean μSBS values (22.9 MPa, 31.3 MPa respectively). While, RMGI showed the lowest μSBS values (4.7 MPa).  In thermocycled subgroups, Panavia showed significantly the highest mean μSBS values (32.2 MPa). There was no significant difference between RMGI and Activa; both showed the lowest significant mean μSBS values (3.2 MPa and 8.7 MPa respectively). Conclusions: RMGI and Activa couldn’t be considered long-term reliable materials for cementing zirconia. However, Panavia provided the most durable bond to zirconia.KEYWORDSBioactive cement; Micro-shear bond strength; Resin cement; Translucent zirconia.

scholarly journals Effects of Self-Etching Primer on Shear Bond Strength of Orthodontic Brackets at Different Debond Times

2007 ◽  
Vol 77 (1) ◽  
pp. 108-112 ◽  
Author(s):  
Tamer Turk ◽  
Selma Elekdag-Turk ◽  
Devrim Isci
Keyword(s):  
Phosphoric Acid ◽  
Bond Strength ◽  
Conventional Method ◽  
Shear Bond Strength ◽  
Orthodontic Brackets ◽  
Control Group ◽  
Study Group ◽  
Group A ◽  
Bond Strengths

Abstract Objective: To evaluate the effect of a self-etching primer on shear bond strengths (SBS) at the different debond times of 5, 15, 30, and 60 minutes and 24 hours. Materials and Methods: Brackets were bonded to human premolars with different etching protocols. In the control group (conventional method [CM]) teeth were etched with 37% phosphoric acid. In the study group, a self-etching primer (SEP; Transbond Plus Self Etching Primer; 3M Unitek, Monrovia, Calif) was applied as recommended by the manufacturer. Brackets were bonded with light-cure adhesive paste (Transbond XT; 3M Unitek) and light-cured for 20 seconds in both groups. The shear bond test was performed at the different debond times of 5, 15, 30 and 60 minutes and 24 hours. Results: Lowest SBS was attained with a debond time of 5 minutes for the CM group (9.51 MPa) and the SEP group (8.97 MPa). Highest SBS was obtained with a debond time of 24 hours for the CM group (16.82 MPa) and the SEP group (19.11 MPa). Statistically significant differences between the two groups were not observed for debond times of 5, 15, 30, or 60 minutes. However, the SBS values obtained at 24 hours were significantly different (P &lt; .001). Conclusions: Adequate SBS was obtained with self-etching primer during the first 60 minutes (5, 15, 30 and 60 minutes) when compared with the conventional method. It is reliable to load the bracket 5 minutes after bonding using self-etching primer (Transbond Plus) with the light-cure adhesive (Transbond XT).

scholarly journals Effect of saliva contamination and re-etching time on the shear bond strength of a pit and fissure sealant

2004 ◽  
Vol 12 (3) ◽  
pp. 200-204 ◽  
Author(s):  
Gisele Maria Correr ◽  
Angela S. Caldo-Teixeira ◽  
Roberta Caroline Bruschi Alonso ◽  
Regina Maria Puppin-Rontani ◽  
Mário Alexandre Coelho Sinhoreti ◽  
...  
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Etching Time ◽  
Control Group ◽  
Distilled Water ◽  
Third Molars ◽  
Fissure Sealant ◽  
Significant Difference ◽  
Pit And Fissure Sealant ◽  
Saliva Contamination

The aim of this study was to evaluate the effect of saliva contamination (SCT) and re-etching time (RET) on the shear bond strength (SBS) of the Fluroshield sealant. Forty-five extracted third molars were sectioned and flattened until reach an enamel surface area. Then, all samples were etched for 30 sec with 35% phosphoric acid and then they were distributed into 9 groups (n=10) according to SCT and RET (seconds), respectively: G1- control (no SCT and no RET); G2- 30s and 0s; G3- 60s and 0s; G4-30s and 2s; G5- 30s and 5s; G6- 30s and 15s; G7-60s and 2s; G8- 60s and 5s; G9- 60s and 15s. The sealant was applied according to the manufacturer's instructions. The samples were stored in distilled water at 37ºC for 72h and subjected to the SBS test. The results indicated that there was no statistically significant difference between the groups (p>0.05). However, it could be noticed that: 1- the longer the SCT, the lower the SBS values; 2 - the longer the RET, the higher the SBS values. It could be concluded that there was a tendency to the shortest SCT (30s) associated to the longest RET (5 and 15s) to reach similar SBS values for the control group.

scholarly journals The Impact of Chlorhexidine Mouth Rinse on the Bond Strength of Polycarbonate Orthodontic Brackets

2014 ◽  
Vol 15 (6) ◽  
pp. 688-692 ◽  
Author(s):  
Sukumaran Anil ◽  
Farouk Ahmed Hussein ◽  
Mohammed Ibrahim Hashem ◽  
Elna P Chalisserry
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Testing Machine ◽  
Test Group ◽  
Orthodontic Brackets ◽  
Control Group ◽  
Mouth Rinse ◽  
Significant Difference ◽  
Bond Strengths ◽  
The Impact

ABSTRACT Objective The purpose of the current in-vivo study was to assess the effect of using 0.12% chlorhexidine (CHX) mouth rinse, before bonding, on shear bond strength of polycarbonate brackets bonded with composite adhesive. Subjects and methods Eighteen orthodontic patients with a mean age 21.41 ± 1.2 years, who were scheduled to have 2 or more first premolars extracted, were included in this study. Patients were referred for an oral prophylaxis program which included, in part, the use of a mouth rinse. Patients were divided into 2 groups, a test group of 9 patients who used 0.12% CHX gluconate mouth rinse twice daily and a control group of 9 patients who used a mouth rinse without CHX, but with same color. After 1 week, polycarbonate brackets were bonded to first premolars with Transbond XT composite adhesive. Premolars were extracted after 28 days and tested for shear bond strength on a universal testing machine. Student's t-test was used to compare shear bond strengths of both groups. Results No statistically significant difference was found in bond strengths’ values between both groups. The test group (with CHX) has mean shear bond strength of 14.21 ± 2.42 MPa whereas the control group (without CHX) revealed a mean strength of 14.52 ± 2.31 MPa. Conclusion The use of 0.12% CHX mouth rinse, for one week before bonding, did not affect the shear bond strength of polycarbonate brackets bonded with Transbond composite. Furthermore, these brackets showed clinically acceptable bond strength. How to cite this article Hussein FA, Hashem MI, Chalisserry EP, Anil S. The Impact of Chlorhexidine Mouth Rinse on the Bond Strength of Polycarbonate Orthodontic Brackets. J Contemp Dent Pract 2014;15(6):688-692.

scholarly journals Effect of Surface Treatments on the Bond Strength to Turkom-Cera All-ceramic Material

2016 ◽  
Vol 17 (11) ◽  
pp. 920-925 ◽  
Author(s):  
Bandar MA Al-Makramani ◽  
Fuad A Al-Sanabani ◽  
Abdul AA Razak ◽  
Mohamed I Abu-Hassan ◽  
Ibrahim Z AL-Shami ◽  
...  
Keyword(s):  
Bond Strength ◽  
Ceramic Material ◽  
Failure Modes ◽  
Testing Machine ◽  
Surface Treatments ◽  
Resin Cement ◽  
Control Group ◽  
Significant Difference ◽  
All Ceramic ◽  
Effect Of Surface

ABSTRACT Aim The aim of this study was to evaluate the effect of surface treatments on shear bond strength (SBS) of Turkom-Cera (Turkom-Ceramic (M) Sdn. Bhd., Puchong, Malaysia) all-ceramic material cemented with resin cement Panavia-F (Kuraray Medical Inc., Okayama, Japan). Materials and methods Forty Turkom-Cera ceramic disks (10 mm × 3 mm) were prepared and randomly divided into four groups. The disks were wet ground to 1000-grit and subjected to four surface treatments: (1) No treatment (Control), (2) sandblasting, (3) silane application, and (4) sandblasting + silane. The four groups of 10 specimens each were bonded with Panavia-F resin cement according to manufacturer's recommendations. The SBS was determined using the universal testing machine (Instron) at 0.5 mm/min crosshead speed. Failure modes were recorded and a qualitative micromorphologic examination of different surface treatments was performed. The data were analyzed using the one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests. Results The SBS of the control, sandblasting, silane, and sandblasting + silane groups were: 10.8 ± 1.5, 16.4 ± 3.4, 16.2 ± 2.5, and 19.1 ± 2.4 MPa respectively. According to the Tukey HSD test, only the mean SBS of the control group was significantly different from the other three groups. There was no significant difference between sandblasting, silane, and sandblasting + silane groups. Conclusion In this study, the three surface treatments used improved the bond strength of resin cement to Turkom-Cera disks. Clinical significance The surface treatments used in this study appeared to be suitable methods for the cementation of glass infiltrated all-ceramic restorations. How to cite this article Razak AAA, Abu-Hassan MI, AL-Makramani BMA, AL-Sanabani FA, AL-Shami IZ, Almansour HM. Effect of Surface Treatments on the Bond Strength to Turkom-Cera All-Ceramic Material. J Contemp Dent Pract 2016;17(11):920-925.

scholarly journals Influence of curing mode of resin luting cements on bond strength to dentin

2017 ◽  
Vol 15 (4) ◽  
pp. 258
Author(s):  
Marcelo Giannini ◽  
Andreia Assis Carvalho ◽  
Ariovaldo Stefani ◽  
Wladimir Franco de Sá Barbosa ◽  
Lawrence Gonzaga Lopes
Keyword(s):  
Bond Strength ◽  
Testing Machine ◽  
Resin Cement ◽  
Control Group ◽  
Resin Cements ◽  
Luting Cements ◽  
Halogen Light ◽  
Significant Difference ◽  
Tooth Surfaces ◽  
Light Curing

Self-adhesive, dual-polymerizing resin cements require no treatment to the prepared tooth surfaces before cementation. Aim: The aim of this study was to evaluate the influence of curing mode on bond strength (BS) of three cementing systems to bovine dentin. Methods: The buccal enamel surfaces of 50 bovine incisors were removed to expose dentin and to flat the surface. The teeth were divided into five groups (n=10), which consisted of two resin cements (Multilink and Clearfil SA Cement) that were tested in dual- (halogen light for 40 s) and self-cured modes, and a control (RelyX ARC). Two cylinders of resin cements (1.0 mm X 0.75 mm) were prepared on each bonded dentin surface. After 24h at 37oC, resin cylinders were subjected to micro-shear testing in a universal testing machine (4411/Instron - 0.5 mm/min). Data were statistically analyzed by two-way ANOVA, Tukey and Dunnett`s test (5%). Results: Multilink showed higher BS than those observed on Clearfil SA. Light-curing resulted in higher BS for both Multilink and Clearfil SA. When Multilink was light-cured, no significant difference on BS was demonstrated between it and RelyX ARC. Conclusions: The highest BS values were obtained in control group and light-cured Multilink resin cement.

scholarly journals Reinforcement of bond strength of self-etching orthodontic adhesive

2011 ◽  
Vol 82 (1) ◽  
pp. 30-35
Author(s):  
Shinya Horiuchi ◽  
Shingo Kuroda ◽  
Masahiro Hiasa ◽  
Toshiyuki Suge ◽  
Seitaro Saku ◽  
...  
Keyword(s):  
Citric Acid ◽  
Phosphoric Acid ◽  
Bond Strength ◽  
Polyacrylic Acid ◽  
Shear Bond Strength ◽  
Adhesive System ◽  
Control Group ◽  
Bonding System ◽  
Adhesive Remnant Index ◽  
Debonding Process

Abstract Objective: To determine the reinforcement of bond strength of a self-etching system by applying a pretreatment agent. Materials and Methods: Sixty extracted human premolars were used in this study. The enamel surfaces were treated with four pretreatment agents—phosphoric acid, polyacrylic acid, citric acid, and ammonium hexafluorosilicate (SiF)—and were examined under a scanning electron microscope. Afterward, orthodontic brackets were bonded with a self-etching adhesive system (n  =  10 for each agent), and shear bond strength was measured through a debonding process. The adhesive remnant index (ARI) was also assessed. Results: Enamel surfaces treated with polyacrylic acid seemed almost the same as intact enamel. Treatment with SiF induced slight shallow depressions compared with the intact enamel. On the other hand, enamel surfaces treated with citric acid and phosphoric acid showed severe etching patterns. All pretreatments increased the bond strength, but SiF-treated specimens revealed the greatest strength (12.201 ± 1.048 MPa), followed by polyacrylic acid (12.030 ± 2.103 MPa). The control group with no pretreatment showed the least strength (9.078 ± 1.678 MPa). All pretreatments increased ARI score compared with the control group. Conclusions: Surface conditioning before bracket adhesion could reinforce the bond strength of the self-etching adhesive system, resulting in a more reliable bonding system.

Sign in / Sign up

Export Citation Format

Share Document