The effect of modification with dispersed compositions on the grain structure and mechanical properties of industrial aluminum alloys has been studied. Aluminum alloys of the Al-Si, Al-Mg-Sc, Al-Cu-Mn systems were modified with dispersed Mg2Si powder with a particle size of up to 200 nm. The amount of modifier to be added to the melt is calculated. The physicochemical properties of dispersed Mg2Si have been studied. Melting of the AMg6, 1570, 2219, AK9ch alloys in the initial state and with the treatment of Mg2Si melts have been carried out. The action of insoluble applications, isomorphic to aluminum, the similarity of the influence of soluble elements holds only when the amount of insoluble addition exceeds the number of crystals formed arbitrarily under the same conditions. Thus, with an increase in the amount of insoluble addition, in particular silicon carbide particles, the grain size first decreases and then remains constant. The mechanism of the influence of dispersed particles of magnesium silicide on the formation of the structure of hypoeutectic aluminum alloys during crystallization is that their bulk is pushed out by the crystallization front into the liquid phase and participates in the refinement of the structural components of the alloy. To determine the optimal amount of silicon carbide modifier, industrial melting and testing were performed on specimens that underwent heat treatment according to the T6 mode (quenching and artificial aging). The quality of cast aluminum alloys during modification depends on many factors: the nature of the dispersed phase, the temperature of the melt, and the modes of its mixing with the introduction of particles. Dependences of the particle size and the amount of the modifier on the mechanical properties of the alloys have been established. The mechanism of interaction of the modifier with aluminum melt during crystallization has been established. In industrial experiments, the most effective size of SiC particles for increasing the σm of the AK9ch alloy from 115 to 260 MPa in the as-cast state has been established. The optimal content of Mg2Si (0.10 %) for increasing the σm of aluminum alloys has been determined.