scholarly journals Assessment of Adhesion of Geopolymer and Varnished Coatings by the Pull-Off Method

Eng ◽  
2022 ◽  
Vol 3 (1) ◽  
pp. 42-59
Author(s):  
Michał Łach ◽  
Gabriela Róg ◽  
Karolina Ochman ◽  
Kinga Pławecka ◽  
Agnieszka Bąk ◽  
...  
Keyword(s):  
Adhesion Strength ◽  
Metal Surfaces ◽  
Measurement Method ◽  
Conventional Concrete ◽  
Peel Stress ◽  
Steel Substrates ◽  
Quick Determination

This paper presents the results of testing the adhesion of geopolymer coatings and varnishes with ceramic additives to concrete and steel substrates. The measurement method used and described in this article was the pull-off method. The pull-off method test provides an easy way to evaluate the degree of adhesion of coatings to metal surfaces. The pull-off device provides values for the peel stress, which not only allows a quick determination of the adhesion of the coating to the substrate, but also makes it easier to compare the adhesion of several coatings to each other. However, this method requires appropriate preparation, so an attempt was made to determine its suitability for geopolymer layers. The results of testing the adhesion of a geopolymer layer to a geopolymer substrate and a concrete substrate are presented. As a result of this study, a higher adhesion strength of the geopolymer layer to the geopolymer substrate was found in comparison to geopolymer coatings applied on conventional concrete. Adhesion tests were also conducted for steel substrates to which both geopolymer and acrylic lacquer were applied.

Diagnostics of the location of damage to tubing oil well pipes

2019 ◽  
Vol 5 (4) ◽  
pp. 115-128
Author(s):  
Timur A. Ishmuratov ◽  
Rif G. Sultanov ◽  
Milyausha N. Khusnutdinova
Keyword(s):  
Fluid Motion ◽  
Oil Well ◽  
General Belief ◽  
Oil Flow ◽  
Specialized Equipment ◽  
Improving Accuracy ◽  
Analytical Expressions ◽  
Technical Measures ◽  
Quick Determination

The study is devoted to the mathematical description of the process of oil outflow in places of leakage of the tubing string, which allows a computer to locate a leakage in the tubing. The authors propose methodology for identifying defects in the tubing and determining the location of the leak. The uniqueness of this methodology lies in quick determination of the place of leakage without the use of specialists, sophisticated and specialized equipment. Mathematical modeling of oil flow in the tubing requires the apparatus of continuum mechanics. It is a general belief that the movement of oil in the pipe flows at low speeds due to its outflow from the hole. Using the general equations of mass and energy balance, the authors have obtained differential equations of fluid motion in a vertical pipe in the process of its outflow from the tubing and in the process of injection. Analytical expressions are the solution to these equations, as they can help in estimating the degree of damage and its location, as well as the feasibility of its eliminating. The results show that an increase in the leakage and injection times leads to improving accuracy of locating damage. Thus, when conducting various geological and technical measures (GTM) at the well, it is possible to assess the presence of leakage and its intensity when deciding on the repair of tubing.

Effect of styrene–butadiene–styrene content on the adhesion properties of bitumen before and after heat aging

2008 ◽  
Vol 35 (5) ◽  
pp. 454-460 ◽  
Author(s):  
Krzysztof Zieliński
Keyword(s):  
Adhesion Strength ◽  
Test Results ◽  
Adhesion Properties ◽  
Before And After ◽  
Styrene Content ◽  
Styrene Butadiene Styrene ◽  
Styrene Butadiene ◽  
Steel Substrates ◽  
Butadiene Styrene

This article describes the effect of heat aging and styrene–butadiene–styrene (SBS) content in bitumen on the adhesion properties of mastics (bitumen-filler mix) to concrete and steel substrates. Test results showed that the adhesion strength of bituminous mastics to concrete and steel substrates decreased as the SBS content increased. Bitumen types modified with 9%–12% of SBS, commonly used in waterproofing materials, showed an approximately three times weaker bond with concrete and steel substrates than the nonmodified equivalents. Results also showed that after heat aging, the adhesion strength of the nonmodified bitumen was always higher than that of the unheated bitumen modified with 9%–12% of SBS.

Sign in / Sign up

Export Citation Format

Share Document