scholarly journals High-Strength and Low-Cost Biobased Polyurethane Foam Composites Enhanced by Poplar Wood Powder Liquefaction

Polymers ◽  
2021 ◽  
Vol 13 (17) ◽  
pp. 2999
Author(s):  
Wanjia Yang ◽  
Yanming Han ◽  
Wei Zhang ◽  
Derong Zhang
Keyword(s):  
Molecular Weight ◽  
Polyurethane Foam ◽  
Apparent Density ◽  
Low Cost ◽  
Average Molecular Weight ◽  
High Strength ◽  
Acid Number ◽  
Process Time ◽  
Poplar Wood ◽  
Wood Powder

An environmentally friendly liquefaction of wood powder was prepared by atmospheric pressure liquefaction technology to replace the non-renewable petroleum polyols in the preparation of polyurethane foam composites. The liquefaction time varied from 0 min to 140 min. The composition of liquefied products and the effects of liquefaction time on the morphology, apparent density and mechanical properties of polyurethane foam composites were investigated. The results showed that the optimal process time for the preparation of wood powder liquefaction products, which could replace traditional petroleum polyols, was 110 min. At this time, polyether polyols are the main liquefaction products, with an average molecular weight in Mn reaching 237 and average molecular weight in Mw reaching 246. The functional group of the liquefied product consisted mainly of hydroxyl, with the highest content of 1042 mg KOH/g and the lowest acid number of 1.6 mg KOH/g. In addition, the surface of the polyurethane foam based on poplar wood is dominated by closed cell foam; thus its foam has good heat insulation and heat preservation properties. At 110 min liquefaction time, the apparent density of polyurethane foam is 0.164 g/cm3 and the compression strength is 850 kPa, which is higher than that of traditional polyurethane foam (768 kPa), which is without wood powder modification. Replacing petroleum polyol with renewable wood powder liquefaction products to prepare biomass-based polyurethane foam composite materials, researching complex chemical changes in different liquefaction stages, and finding the best liquefaction conditions are of great significance to optimize the performance of polyurethane, address the shortage of resources and reduce environmental pollution.

scholarly journals Towards regenerated cellulose fibers with high toughness

Cellulose ◽  
2021 ◽  
Vol 28 (15) ◽  
pp. 9547-9566 ◽  
Author(s):  
Kaniz Moriam ◽  
Daisuke Sawada ◽  
Kaarlo Nieminen ◽  
Michael Hummel ◽  
Yibo Ma ◽  
...  
Keyword(s):  
Molecular Weight ◽  
Tensile Strength ◽  
Structural Parameters ◽  
Average Molecular Weight ◽  
High Strength ◽  
Cellulose Fibers ◽  
Simultaneous Increase ◽  
Regenerated Cellulose ◽  
Synthetic Fibers ◽  
Strength And Toughness

AbstractThe production of sustainable and high-performance fabrics requires high mechanical strength of the individual (staple) fibers. Although Ioncell fibers already exhibit higher fiber strength than commercial man-made cellulose fibers or cotton fibers, we further aimed to increase both strength and toughness to gradually approach synthetic fibers in these properties. Decisive factors for the achievable mechanical properties of the fibers were the pulp purity, the cellulose concentration in the spinning solution and length-to-diameter (L/D) ratio of the cylindrical part of the spinneret. The absence of low molecular weight fractions in combination with an increased average molecular weight had the highest impact on the achievement of both high strength and toughness. Using a spinneret with a high L/D ratio, it was possible to spin Ioncell fibers with a tensile strength of 925 MPa (61.5 cN/tex) and a modulus of toughness of 83.3 MPa (55.5 J/g). According to a fluid dynamic simulation, uniformly longer molecular cellulose chains in combination with a longer cylindrical capillary promoted an effective alignment of the cellulose molecules inside the spinneret capillary before entering the airgap, thus creating the conditions for a simultaneous increase in tensile strength and elongation i.e. toughness of the fiber. Mechanistically, high fiber toughness is caused by the structural parameters in longitudinal direction, in particular by a higher tilt angle, a longer periodicity of the lamellar plane and lower micro void orientation. In summary, we have developed lyocell-type fibers with high strength and toughness, which can potentially be used as a surrogate for synthetic fibers. Graphic abstract

Decomposition of the metastable beta titanium alloy Ti-15-3

1983 ◽  
Vol 41 ◽  
pp. 264-265
Author(s):  
Y. L. Chen ◽  
S. Fujlshiro
Keyword(s):  
Low Cost ◽  
High Strength ◽  
Alpha Phase ◽  
Thick Sheet ◽  
Omega Phase ◽  
Beta Titanium Alloy ◽  
Beta Titanium ◽  
Beta Matrix ◽  
Metastable Beta ◽  
Very High

Metastable beta titanium alloys have been known to have numerous advantages such as cold formability, high strength, good fracture resistance, deep hardenability, and cost effectiveness. Very high strength is obtainable by precipitation of the hexagonal alpha phase in a bcc beta matrix in these alloys. Precipitation hardening in the metastable beta alloys may also result from the formation of transition phases such as omega phase. Ti-15-3 (Ti-15V- 3Cr-3Al-3Sn) has been developed recently by TIMET and USAF for low cost sheet metal applications. The purpose of the present study was to examine the aging characteristics in this alloy.The composition of the as-received material is: 14.7 V, 3.14 Cr, 3.05 Al, 2.26 Sn, and 0.145 Fe. The beta transus temperature as determined by optical metallographic method was about 770°C. Specimen coupons were prepared from a mill-annealed 1.2 mm thick sheet, and solution treated at 827°C for 2 hr in argon, then water quenched. Aging was also done in argon at temperatures ranging from 316 to 616°C for various times.

The Structure of Radiation Cross-Linked Poly (ethylene oxide) Gels

1971 ◽  
Vol 29 ◽  
pp. 76-77
Author(s):  
C. E. Cluthe ◽  
G. G. Cocks
Keyword(s):  
Molecular Weight ◽  
Ethylene Oxide ◽  
Parallel Plate ◽  
Average Molecular Weight ◽  
Radical Reaction ◽  
Free Radical Reaction ◽  
Nitrogen Gas ◽  
Poly Ethylene Oxide ◽  
Poly Ethylene ◽  
Initial Viscosity

Aqueous solutions of a 1 weight-per cent poly (ethylene oxide) (PEO) were degassed under vacuum, transferred to a parallel plate viscometer under a nitrogen gas blanket, and exposed to Co60 gamma radiation. The Co60 source was rated at 4000 curies, and the dose ratewas 3.8x105 rads/hr. The poly (ethylene oxide) employed in the irradiations had an initial viscosity average molecular weight of 2.1 x 106.The solutions were gelled by a free radical reaction with dosages ranging from 5x104 rads to 4.8x106 rads.

INCONEL ALLOY X-750

Alloy Digest ◽  
1966 ◽  
Vol 15 (7) ◽  
Keyword(s):  
Gas Turbines ◽  
Rupture Strength ◽  
Low Cost ◽  
High Strength ◽  
Heat Treating ◽  
Chromium Alloy ◽  
Cryogenic Temperatures ◽  
Inconel Alloy ◽  
Nickel Chromium ◽  
Corrosion And Oxidation

Abstract INCONEL alloy X-750 is an age-hardenable, nickel-chromium alloy used for its corrosion and oxidation resistance and high creep rupture strength at temperature up to 1500 F. It also has excellent properties at cryogenic temperatures. It was originally developed for use in gas turbines, but because of its low cost, high strength and weldability it has become the standards choice for a wide variety of applications. This datasheet provides information on composition, physical properties, elasticity, and tensile properties as well as creep and fatigue. It also includes information on forming, heat treating, machining, joining, and surface treatment. Filing Code: Ni-115. Producer or source: Huntington Alloy Products Division, An INCO Company.

Sign in / Sign up

Export Citation Format

Share Document