Magnetic CuFe2O4 Nanoparticles for Adsorpstion of Cr(VI) from Aqueous Solution

2014 ◽  
Vol 896 ◽  
pp. 104-107 ◽  
Author(s):  
Poedji Loekitowati Hariani ◽  
Fahma Riyanti
Keyword(s):  
Aqueous Solution ◽  
Precipitation Method ◽  
Alkaline Condition ◽  
Batch Adsorption ◽  
X Ray Diffraction ◽  
Transmission Electron ◽  
Adsorption Condition ◽  
Co Precipitation ◽  
20 Nm

CuFe2O4 nanoparticles were synthesized by co-precipitation method from the solution of CuCl2 and FeCl3 in alkaline condition. The prepared magnetic CuFe2O4 can be used to adsorb Cr (VI) ions from aqueous solution and separated from medium by magnetic technique. The characterization of CuFe2O4 with X-Ray diffraction (XRD) showed cubic units shells with diameter in the range 15-20 nm which obtained by Transmission Electron Microscope (TEM). The saturation of magnetization is around 13 emu g-1 measured with Vibrating Sample Magnetometer (VSM). Batch adsorption studies were carried out to optimize adsorption condition. Effective conditions for adsorption of Cr (VI) were found at the weight of CuFe2O4 was 1.0 g with contact time of 60 minutes and pH 3 with adsorption capacity 9.20 mg g-1.

Microstructure Characterization of Metal Mixed Oxides

MRS Advances ◽  
2017 ◽  
Vol 2 (64) ◽  
pp. 4025-4030 ◽  
Author(s):  
T. Kryshtab ◽  
H. A. Calderon ◽  
A. Kryvko
Keyword(s):  
Mixed Oxides ◽  
Profile Analysis ◽  
Atomic Resolution ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
Reconstruction Procedure ◽  
Transmission Electron ◽  
Xrd Patterns ◽  
Co Precipitation

ABSTRACTThe microstructure of Ni-Mg-Al mixed oxides obtained by thermal decomposition of hydrotalcite-like compounds synthesized by a co-precipitation method has been studied by using X-ray diffraction (XRD) and atomic resolution transmission electron microscopy (TEM). XRD patterns revealed the formation of NixMg1-xO (x=0÷1), α-Al2O3 and traces of MgAl2O4 and NiAl2O4 phases. The peaks profile analysis indicated a small grain size, microdeformations and partial overlapping of peaks due to phases with different, but similar interplanar spacings. The microdeformations point out the presence of dislocations and the peaks shift associated with the presence of excess vacancies. The use of atomic resolution TEM made it possible to identify the phases, directly observe dislocations and demonstrate the vacancies excess. Atomic resolution TEM is achieved by applying an Exit Wave Reconstruction procedure with 40 low dose images taken at different defocus. The current results suggest that vacancies of metals are predominant in MgO (NiO) crystals and that vacancies of Oxygen are predominant in Al2O3 crystals.

Preparation and characterization of iron oxide nanoparticles coated with chitosan for removal of Cd(II) and Cr(VI) from aqueous solution

2014 ◽  
Vol 70 (6) ◽  
pp. 1004-1010 ◽  
Author(s):  
Th. I. Shalaby ◽  
N. M. Fikrt ◽  
M. M. Mohamed ◽  
M. F. El Kady
Keyword(s):  
Electron Microscope ◽  
Magnetic Nanoparticles ◽  
Magnetic Nanomaterials ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
Toxic Heavy Metals ◽  
Transmission Electron ◽  
Magnetite Fe3o4 ◽  
Co Precipitation

This study investigated the applicability of magnetite Fe3O4 nanoparticles coated with chitosan (CMNs) for the removal of some toxic heavy metals from simulated wastewater. Magnetic nanomaterials were synthesized using the co-precipitation method and characterized by transmission electron microscope, scanning electron microscope, X-ray diffraction, and Fourier transformer infrared spectroscopy. The magnetic properties of the prepared magnetic nanoparticles were determined by a vibrating-sample magnetometer. Batch experiments were carried out to determine the adsorption kinetics of Cr(VI) and Cd(II) by magnetic nanoparticles. It is noteworthy that CMNs show a highly efficient adsorption capacity for low concentration Cr(VI) and Cd(II) ions solution, which can reach 98% within 10 min.

Synthesis and Characterization of Structure of Fe3O4@Graphene Oxide Nanocomposites

2016 ◽  
Vol 25 (6) ◽  
pp. 096369351602500 ◽  
Author(s):  
Ruimin Fu ◽  
Mingfu Zhu
Keyword(s):  
Graphene Oxide ◽  
Drug Carrier ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Ft Ir ◽  
Co Precipitation ◽  
Ft Ir Spectroscopy

Nowadays, the hummers method for preparation of graphene oxide (GO) was improved. The grapheme oxide @ Fe3O4 magnetic nanocomposites were synthesized by co-precipitation method. After analysing the morphology and structure of obtained nanocomposites by X-ray diffraction (XRD), transmission electron microscope (TEM) and Fourier transform infrared (FT-IR) spectroscopy, the result was shown as follows. The particle size of Fe3O4 in nanocomposites is 30 nm. Many functional groups are found in grapheme oxide, and such groups could be used to bind with the drug. In the test for magnetic properties, the nanocomposites gathered rapidly in the vicinity of the permanent magnet. The nanocomposites, with high superparamagnetism, can be used in the following applications: drug targeting transports, drug carrier, and diagnosis assistant system.

Preparation and Characterization of a New Type of Magnetic Polymer Micro Spheres

2011 ◽  
Vol 80-81 ◽  
pp. 405-408
Author(s):  
Li Li Zhang ◽  
Hong Wei Zhang ◽  
Xiang Hua Yao ◽  
Can Bang Zhang ◽  
Jia Jin Tian ◽  
...  
Keyword(s):  
Precipitation Method ◽  
Average Particle ◽  
X Ray Diffraction ◽  
Transmission Electron ◽  
Fe Content ◽  
New Type ◽  
Co Precipitation ◽  
Micro Morphology ◽  
Paramagnetic Properties

A new type of magnetic polymer microspheres with super paramagnetic properties were prepared by a co-precipitation method. Atomic absorption spectroscopy (AAS), X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscopy (SEM) were used to analyze Fe content, micro morphology, particle size and phase structure of the products. Results indicate that the content of Fe in the microspheres is up to 5.25 *105ug/g. The main phase of the product is Fe3O4. The average particle sizes of the products are ~30nm.

Characterization of Al2(WO4)3 Synthesized by Co-Precipitation Method

2014 ◽  
Vol 798-799 ◽  
pp. 85-89 ◽  
Author(s):  
E.S.G. Junior ◽  
P.M . Jardim
Keyword(s):  
Precipitation Method ◽  
X Ray Diffraction ◽  
Scanning Calorimetry ◽  
Tem Analysis ◽  
X Ray ◽  
Transmission Electron ◽  
Different Temperatures ◽  
Co Precipitation ◽  
Alpha Alumina

Al2(WO4)3was synthesized by co-precipitation using Na2WO4and Al (NO3)3as precursors. After drying the precipitate, it was calcined at different temperatures between 500°C and 800°C. The crystallization and degradation temperatures of the samples were evaluated by means of Differential Scanning Calorimetry (DSC), Thermogravimetry (TG) and X-Ray Diffraction (XRD). It was observed that the crystallization starts at around 600°C, however Transmission Electron Microscopy (TEM) analysis showed that at this temperature the sample is partially amorphous. The degradation of the material starts at around 1200°C and at 1400°C the tungsten oxide has almost completely evaporated and the material is transformed mainly in alpha-alumina.

Magnetic and dielectric properties of BiFeO3 nanoparticles

2015 ◽  
Vol 7 (2) ◽  
pp. 1393-1403
Author(s):  
Dr R.P VIJAYALAKSHMI ◽  
N. Manjula ◽  
S. Ramu ◽  
Amaranatha Reddy
Keyword(s):  
Diffuse Reflectance Spectrum ◽  
Precipitation Method ◽  
Secondary Phases ◽  
X Ray Diffraction ◽  
Bifeo3 Nanoparticles ◽  
Transmission Electron ◽  
Multiferroic Bifeo3 ◽  
Pure Phase ◽  
Simple Chemical ◽  
Co Precipitation

Single crystalline nano-sized multiferroic BiFeO3 (BFO) powders were synthesized through simple chemical co-precipitation method using polyethylene glycol (PEG) as capping agent. We obtained pure phase BiFeO3 powder by controlling pHand calcination temperature. From X-ray diffraction studies the nanoparticles were unambiguously identified to have a rhombohedrally distorted perovskite structure belonging to the space group of R3c. No secondary phases were detected. It indicates single phase structure. EDX spectra indicated the appearance of three elements Bi, Fe, O in 1:1:3. From the UV-Vis diffuse reflectance spectrum, the absorption cut-off wavelength of the BFO sample is around 558nm corresponding to the energy band gap of 2.2 eV. The size (60-70 nm) and morphology of the nanoparticles have been analyzed using transmission electron microscopy (TEM).   Linear M−H behaviour and slight hysteresis at lower magnetic field is observed for BiFeO3 nanoparticles from Vibrating sample magnetometer studies. It indicates weak ferromagnetic behaviour at room temperature. From dielectric studies, the conductivity value is calculated from the relation s = L/RbA Sm-1 and it is around 7.2 x 10-9 S/m.

Template Induced Synthesis of Nano-Hydroxyapatite by Co-Precipitation Method

2011 ◽  
Vol 311-313 ◽  
pp. 1713-1716 ◽  
Author(s):  
Yan Rong Sun ◽  
Tao Fan ◽  
Chang An Wang ◽  
Li Guo Ma ◽  
Feng Liu
Keyword(s):  
Electron Microscope ◽  
Chondroitin Sulfate ◽  
Aspartic Acid ◽  
Transmission Electron Microscope ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Structure And Morphology ◽  
Transmission Electron ◽  
Co Precipitation

Nano-hydroxyapatite with different morphology was synthesized by the co-precipitation method coupled with biomineralization using Ca(NO3)2•4H2O and (NH4)2HPO4 as reagents, adding chondroitin sulfate, agarose and aspartic acid as template. The structure and morphology of the prepared powders were characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM).

scholarly journals Synthesis of Co3O4 Nano Aggregates by Co-precipitation Method and its Catalytic and Fuel Additive Applications

2019 ◽  
Vol 17 (1) ◽  
pp. 865-873 ◽  
Author(s):  
Muhammad Ramzan Saeed Ashraf Janjua
Keyword(s):  
Electron Microscopy ◽  
Precipitation Method ◽  
Fuel Additive ◽  
X Ray Diffraction ◽  
Efficient Catalyst ◽  
Calcination Process ◽  
Electron Microscopies ◽  
Transmission Electron ◽  
Co Precipitation ◽  
Individual Particles

AbstractThe nano aggregates of cobalt oxide (Co3O4) are synthesized successfully by adopting simple a co precipitation approach. The product obtained was further subjected to the calcination process that not only changed it morphology but also reduces the size of individual particles of aggregates. The prepared nano aggregates are subjected to different characterization techniques such as electron microscopies (scanning electron microscopy and transmission electron microscopy) and X-ray diffraction and results obtained by these instruments are analyzed by different software. The characterization results show that, although the arrangement of particles is compact, several intrinsic spaces and small holes/ pores can also be seen in any aggregate of the product. The as synthesized product is further tested for catalytic properties in thermal decomposition of ammonium perchlorate and proved to be an efficient catalyst.

Synthesis Conditions of Nano-Hydroxyapatite Using Chondroitin Sulfate by Co-Precipitation Method

2011 ◽  
Vol 236-238 ◽  
pp. 2076-2079
Author(s):  
Yan Rong Sun ◽  
Tao Fan ◽  
Yong Huang ◽  
Li Guo Ma ◽  
Feng Liu
Keyword(s):  
Chondroitin Sulfate ◽  
Ph Value ◽  
Orthogonal Design ◽  
Precipitation Method ◽  
Synthesis Process ◽  
X Ray Diffraction ◽  
Powder Morphology ◽  
Synthesis Conditions ◽  
Transmission Electron ◽  
Co Precipitation

The introduction of biomineralization was coupled with the co-precipitation synthesis process of nano-hydroxyapatite with the addition of chondroitin sulfate as a template agent. The effect of a variety of processing conditions on the properties of final hydroxyapatite (HA) product was investigated by orthogonal design. The ratio of calcium to phosphorus was detected by chemical analysis, the phase composition was evaluated by X-ray diffraction (XRD), and the powder morphology was characterized by transmission electron microscope (TEM). The process scheme, moreover, was optimized by the analysis of four aspects which may have different extent of influence on product properties. It can be concluded from the results that product properties can be affected remarkably by the content of chondroitin sulfate and the pH value of reactant, less remarkably by the reaction temperature and slightly by the reaction time.

The Preparation and Characterization of LiFe0.98Mn0.02PO4/C by Spray-Drying and Low Temperature Reduction Route

2012 ◽  
Vol 581-582 ◽  
pp. 525-528
Author(s):  
Jia Feng Zhang ◽  
Bao Zhang ◽  
Xue Yi Guo ◽  
He Zhang Chen ◽  
Jian Long Wang ◽  
...  
Keyword(s):  
Low Temperature ◽  
Spray Drying ◽  
Xrd Analysis ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
Sem Images ◽  
Temperature Reduction ◽  
Co Precipitation ◽  
Low Temperature Reduction

The LiFe0.98Mn0.02PO4/C was synthesized by spray-drying and low temperature reduction route using FePO4•2H2O as precursor, which was prepared by a simple co-precipitation method. The LiFe0.98Mn0.02PO4/C sample was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and electrochemical measurements. The XRD analysis and SEM images show that sample has the good ordered structure and spherical particle. The charge-discharge tests demonstrate that the powder has the better electrochemical properties, with an initial discharge capacity of 162.1 mAh•g−1 and 155.8 mAh•g−1 at current density of 0.1 C and 1C, respectively. The capacity retention reaches 99.4% after 100 cycles at 1C.

Sign in / Sign up

Export Citation Format

Share Document