Mechanical Properties of Aluminium Processed by ECAP

2006 ◽  
Vol 114 ◽  
pp. 39-44
Author(s):  
Rafal M. Molak ◽  
Zbigniew Pakiela
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Plastic Strain ◽  
Room Temperature ◽  
Tensile Tests ◽  
Large Plastic Strain ◽  
Angular Pressing ◽  
Purity Aluminium ◽  
High Purity Aluminium ◽  
The Relationship

The aim of this study was to investigate the influence of large plastic strain on the microstructure and mechanical properties of aluminium processed by severe plastic deformation (SPD) by the Equal Channel Angular Pressing (ECAP) method. Polycrystalline high purity aluminium (99,99%) was pressed at room temperature to produce samples subjected to 4, 8 and 12 ECAP passes. The microstructure of aluminium was examined using a light polarized microscope. Microhardness measurements and tensile tests were undertaken to determine the mechanical properties of the material processed by ECAP. The results obtained show the relationship between the microstructure and the mechanical properties of the material.

Activities of Non-Basal Slips in Rolled Mg-Li and Mg-Ce Alloys Sheets

2021 ◽  
Vol 1016 ◽  
pp. 917-921
Author(s):  
Haruka Miyano ◽  
Keisuke Takemoto ◽  
Hiromoto Kitahara ◽  
Shinji Ando
Keyword(s):  
Mechanical Properties ◽  
Room Temperature ◽  
Tensile Tests ◽  
Lithium Content ◽  
Slip Systems ◽  
Alloying Additions ◽  
Alloy Strength ◽  
Critical Resolved Shear Stress ◽  
The Relationship ◽  
Strength And Ductility

In this study, tensile tests of rolled Mg-Li alloy and Mg-Ce alloy sheets were carried out at room temperature to investigate effects of alloying additions on the relationship between mechanical properties and activities of slip systems in magnesium polycrystals. In Mg-Li alloy, ductility increased while strength decreased by lithium addition. Frequency of non-basal slips increased with increasing lithium content. In Mg-Ce alloy, strength and ductility were similar pure magnesium, and non-basal slips were hardly activated. Since critical resolved shear stress of non-basal slips were decreased by lithium addition, ductility of magnesium was increased while its strength was decreased.

Dislocation study of ARMCO iron processed by ECAP

2016 ◽  
Vol 1818 ◽  
Author(s):  
Jairo Alberto Muñoz ◽  
Oscar Fabián Higuera ◽  
José María Cabrera
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Grain Size ◽  
Dislocation Density ◽  
Deformation Behavior ◽  
Armco Iron ◽  
Tensile Tests ◽  
Grain Sizes ◽  
Angular Pressing ◽  
Cylindrical Samples

ABSTRACTThe aim of this work was to study the deformation behavior of an Armco iron after severe plastic deformation by equal channel angular pressing (ECAP). Particular attention was paid to predict the dislocation density by different approaches like the model proposed by Bergström. Experimental measures of dislocation density by different techniques are used in the discussion. Cylindrical samples of ARMCO iron (8mm of diameter, 60mm of length) were subjected to ECAP deformation using a die with an intersecting channel of Φ=90° and outer arc of curvature of ψ= 37° die. Samples were deformed for up to 16 ECAP passes following route Bc. The mechanical properties of the material were measured after each pass by tensile tests. The original grain size of the annealed iron (70 μm) was drastically reduced after ECAP reaching grain sizes close to 300nm after 16 passes.

scholarly journals Influence of Hydrostatic Extrusion on the Mechanical Properties of the Model Al-Mg Alloys

2021 ◽  
Author(s):  
Aleksandra Towarek ◽  
Wojciech Jurczak ◽  
Joanna Zdunek ◽  
Mariusz Kulczyk ◽  
Jarosław Mizera
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Tensile Strength ◽  
Microstructural Analysis ◽  
Tensile Tests ◽  
Hydrostatic Extrusion ◽  
Microstructure Formation ◽  
Initial State ◽  
Degree Of Deformation ◽  
Al Mg Alloys

AbstractTwo model aluminium-magnesium alloys, containing 3 and 7.5 wt.% of Mg, were subjected to plastic deformation by means of hydrostatic extrusion (HE). Two degrees of deformation were imposed by two subsequent reductions of the diameter. Microstructural analysis and tensile tests of the materials in the initial state and after deformation were performed. For both materials, HE extrusion resulted in the deformation of the microstructure—formation of the un-equilibrium grain boundaries and partition of the grains. What is more, HE resulted in a significant increase of tensile strength and decrease of the elongation, mostly after the first degree of deformation.

Recrystallization of high-purity aluminium during equal channel angular pressing

2007 ◽  
Vol 55 (7) ◽  
pp. 2211-2218 ◽  
Author(s):  
W. Skrotzki ◽  
N. Scheerbaum ◽  
C.-G. Oertel ◽  
H.-G. Brokmeier ◽  
S. Suwas ◽  
...  
Keyword(s):  
Equal Channel Angular Pressing ◽  
High Purity ◽  
Angular Pressing ◽  
Purity Aluminium ◽  
High Purity Aluminium

Local Investigations of the Mechanical Properties of Ultrafine Grained Metals by Nanoindentations

2006 ◽  
Vol 503-504 ◽  
pp. 31-36 ◽  
Author(s):  
Johannes Mueller ◽  
Karsten Durst ◽  
Dorothea Amberger ◽  
Matthias Göken
Keyword(s):  
Mechanical Properties ◽  
Strain Rate ◽  
Strain Rate Sensitivity ◽  
Room Temperature ◽  
Rate Sensitivity ◽  
Strain Rates ◽  
Fcc Metals ◽  
Angular Pressing ◽  
Ultrafine Grained ◽  
Indentation Strain

The mechanical properties of ultrafine-grained metals processed by equal channel angular pressing is investigated by nanoindentations in comparison with measurements on nanocrystalline nickel with a grain size between 20 and 400 nm produced by pulsed electrodeposition. Besides hardness and Young’s modulus measurements, the nanoindentation method allows also controlled experiments on the strain rate sensitivity, which are discussed in detail in this paper. Nanoindentation measurements can be performed at indentation strain rates between 10-3 s-1 and 0.1 s-1. Nanocrystalline and ultrafine-grained fcc metals as Al and Ni show a significant strain rate sensitivity at room temperature in comparison with conventional grain sized materials. In ultrafine-grained bcc Fe the strain rate sensitivity does not change significantly after severe plastic deformation. Inelastic effects are found during repeated unloading-loading experiments in nanoindentations.

Influence of Heat Treatment on Microstructure and Mechanical Properties of Selective Laser Melted TiAl6V4 Alloy

2018 ◽  
Vol 284 ◽  
pp. 615-620 ◽  
Author(s):  
R.M. Baitimerov ◽  
P.A. Lykov ◽  
L.V. Radionova
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Selective Laser Melting ◽  
Room Temperature ◽  
Base Alloy ◽  
Tensile Tests ◽  
Heat Treatments ◽  
Laser Melting ◽  
Microstructure And Mechanical Properties ◽  
Treatment Procedures

TiAl6V4 titanium base alloy is widely used in aerospace and medical industries. Specimens for tensile tests from TiAl6V4 with porosity less than 0.5% was fabricated by selective laser melting (SLM). Specimens were treated using two heat treatment procedures, third batch of specimens was tested in as-fabricated statement after machining. Tensile tests were carried out at room temperature. Microstructure and mechanical properties of SLM fabricated TiAl6V4 after different heat treatments were investigated.

Strength of Commercial Aluminum Alloys after Equal Channel Angular Pressing and Post-ECAP Processing

2006 ◽  
Vol 114 ◽  
pp. 91-96 ◽  
Author(s):  
Maxim Yu. Murashkin ◽  
M.V. Markushev ◽  
Julia Ivanisenko ◽  
Ruslan Valiev
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Aluminum Alloys ◽  
Ultimate Tensile Strength ◽  
Equal Channel Angular Pressing ◽  
Room Temperature ◽  
Solution Treatment ◽  
Ecap Processing ◽  
Angular Pressing

The effects of equal channel angular pressing (ECAP), further heat treatment and rolling on the structure and room temperature mechanical properties of the commercial aluminum alloys 6061 (Al-0.9Mg-0.7Si) and 1560 (Al-6.5Mg-0.6Mn) were investigated. It has been shown that the strength of the alloys after ECAP is higher than that achieved after conventional processing. Prior ECAP solution treatment and post-ECAP ageing can additionally increase the strength of the 6061 alloy. Under optimal ageing conditions a yield strength (YS) of 434 MPa and am ultimate tensile strength (UTS) of 470 MPa were obtained for the alloy. Additional cold rolling leads to a YS and UTS of 475 and 500 MPa with 8% elongation. It was found that the post-ECAP isothermal rolling of the 1560 alloy resulted in the formation of a nano-fibred structure and a tensile strength (YS = 540 MPa and UTS = 635 MPa) that has never previously been observed in commercial non-heat treatable alloys.

Influence of Severe Plastic Deformation on the PLC Effect and Mechanical Properties in Al 5XXX Alloy

2006 ◽  
Vol 114 ◽  
pp. 171-176 ◽  
Author(s):  
Joanna Zdunek ◽  
Pawel Widlicki ◽  
Halina Garbacz ◽  
Jaroslaw Mizera ◽  
Krzysztof Jan Kurzydlowski
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Grain Size ◽  
Severe Plastic Deformation ◽  
True Strain ◽  
Tensile Tests ◽  
Size Reduction ◽  
Hydrostatic Extrusion ◽  
Stress Strain ◽  
Chatelier Effect

In this work, Al-Mg-Mn-Si alloy (5483) in the as-received and severe plastically deformed states was used. Plastic deformation was carried out by hydrostatic extrusion, and three different true strain values were applied 1.4, 2.8 and 3.8. All specimens were subjected to tensile tests and microhardness measurements. The investigated material revealed an instability during plastic deformation in the form of serration on the stress-strain curves, the so called Portevin-Le Chatelier effect It was shown that grain size reduction effected the character of the instability.

scholarly journals Microstructural and Mechanical Characterization of Al-0.80Mg-0.85Si-0.3Zr Alloy

2017 ◽  
Vol 17 (4) ◽  
pp. 73-78 ◽  
Author(s):  
F. Kahrıman ◽  
M. Zeren
Keyword(s):  
Mechanical Properties ◽  
Automotive Industry ◽  
Room Temperature ◽  
Tensile Tests ◽  
Direct Chill ◽  
Peak Hardness ◽  
Casting Method ◽  
Industry Standard ◽  
Three Stages

Abstract In this study, Al-0.80Mg-0.85Si alloy was modified with the addition of 0.3 wt.-% zirconium and the variation of microstructural features and mechanical properties were investigated. In order to produce the billets, vertical direct chill casting method was used and billets were homogenized at 580 °C for 6 h. Homogenized billets were subjected to aging practice following three stages: (i) solution annealing at 550 °C for 3 h, (ii) quenching in water, (iii) aging at 180 °C between 0 and 20 h. The hardness measurements were performed for the alloys following the aging process. It was observed that peak hardness value of Al-0.80Mg-0.85Si alloy increased with the addition of zirconium. This finding was very useful to obtain aging parameters for the extruded hollow profiles which are commonly used in automotive industry. Standard tensile tests were applied to aged profiles at room temperature and the results showed that modified alloy had higher mechanical properties compared to the non-modified alloy.

Sign in / Sign up

Export Citation Format

Share Document