Activities of Non-Basal Slips in Rolled Mg-Li and Mg-Ce Alloys Sheets

2021 ◽  
Vol 1016 ◽  
pp. 917-921
Author(s):  
Haruka Miyano ◽  
Keisuke Takemoto ◽  
Hiromoto Kitahara ◽  
Shinji Ando

In this study, tensile tests of rolled Mg-Li alloy and Mg-Ce alloy sheets were carried out at room temperature to investigate effects of alloying additions on the relationship between mechanical properties and activities of slip systems in magnesium polycrystals. In Mg-Li alloy, ductility increased while strength decreased by lithium addition. Frequency of non-basal slips increased with increasing lithium content. In Mg-Ce alloy, strength and ductility were similar pure magnesium, and non-basal slips were hardly activated. Since critical resolved shear stress of non-basal slips were decreased by lithium addition, ductility of magnesium was increased while its strength was decreased.

2010 ◽  
Vol 638-642 ◽  
pp. 3128-3133 ◽  
Author(s):  
Felix Peñalba ◽  
Xabier Gómez ◽  
R. Allende ◽  
Manuel Carsí ◽  
Oscar A. Ruano

The possibilities to improve the properties of steels for tubes exposed at high temperatures are explored. The mechanical properties and forming behavior of an experimental casting of type 9Cr-ferritic steels, P92, containing 2%W, are studied. The hardenability was determined by means of continuous cooling diagrams associated with hardness measurements and microstructure observations. Tensile tests from room temperature to 650°C were carried out to determine the variation of the strength and ductility in this temperature range. In addition, Charpy impact tests were conducted to characterize the toughness of the steel and the ductile-brittle transition temperature. Finally, hot torsion tests at various temperatures and strain rates were carried out and the generalized stresses and strains to rupture for each test are determined. With these data forming stability maps were generated to characterize the best forming conditions.


2009 ◽  
Vol 23 (06n07) ◽  
pp. 783-789 ◽  
Author(s):  
C. J. BETTLES ◽  
T. PUEHRINGER ◽  
A. J. MORTON ◽  
D. TOMUS ◽  
M. A. GIBSON

Alloys in the dilute Ti - Al - Mn system, which are considered to be near-α alloys, possess an attractive combination of strength and ductility, with the room temperature properties being intermediate between CP Ti and Ti -6 Al -4 V . Low levels of Fe are often tolerated in such alloys, but rarely introduced as deliberate alloying additions (with the exception of CP Ti grades), and from a processing perspective, it may indeed be desirable to have higher tolerances for Fe as it is often a common contaminant which must be controlled. In this presentation, the effect of 0.3 wt .% Fe on the microstructure and behavior of a Ti -0.75 wt .% Al -0.75 wt .% Mn is reported. It was found that annealing in the (α+β) phase field can lead to an increase in the ductility of the alloy without having a detrimental effect on the tensile strength.


2006 ◽  
Vol 114 ◽  
pp. 39-44
Author(s):  
Rafal M. Molak ◽  
Zbigniew Pakiela

The aim of this study was to investigate the influence of large plastic strain on the microstructure and mechanical properties of aluminium processed by severe plastic deformation (SPD) by the Equal Channel Angular Pressing (ECAP) method. Polycrystalline high purity aluminium (99,99%) was pressed at room temperature to produce samples subjected to 4, 8 and 12 ECAP passes. The microstructure of aluminium was examined using a light polarized microscope. Microhardness measurements and tensile tests were undertaken to determine the mechanical properties of the material processed by ECAP. The results obtained show the relationship between the microstructure and the mechanical properties of the material.


2007 ◽  
Vol 23 ◽  
pp. 123-126
Author(s):  
Radu L. Orban ◽  
Mariana Lucaci

This paper investigates the effect of Fe, Cr and B additions, in small proportions, as alloying elements in Ni3Al with the purpose to reduce its intrinsic fragility and extrinsic embrittlement and to enhance, in the same time, its mechanical properties. It represents a development of some previous research works of the authors, proving that Ni3Al-Fe-Cr-B alloys obtained by reactive synthesis (SHS) starting from Mechanically Alloyed powder mixtures have superior both room temperature tensile strength and ductility, and compression ones at temperatures up to 800 °C, than pure Ni3Al. These create premises for their using as superalloys substitutes.


2018 ◽  
Vol 284 ◽  
pp. 615-620 ◽  
Author(s):  
R.M. Baitimerov ◽  
P.A. Lykov ◽  
L.V. Radionova

TiAl6V4 titanium base alloy is widely used in aerospace and medical industries. Specimens for tensile tests from TiAl6V4 with porosity less than 0.5% was fabricated by selective laser melting (SLM). Specimens were treated using two heat treatment procedures, third batch of specimens was tested in as-fabricated statement after machining. Tensile tests were carried out at room temperature. Microstructure and mechanical properties of SLM fabricated TiAl6V4 after different heat treatments were investigated.


2017 ◽  
Vol 17 (4) ◽  
pp. 73-78 ◽  
Author(s):  
F. Kahrıman ◽  
M. Zeren

Abstract In this study, Al-0.80Mg-0.85Si alloy was modified with the addition of 0.3 wt.-% zirconium and the variation of microstructural features and mechanical properties were investigated. In order to produce the billets, vertical direct chill casting method was used and billets were homogenized at 580 °C for 6 h. Homogenized billets were subjected to aging practice following three stages: (i) solution annealing at 550 °C for 3 h, (ii) quenching in water, (iii) aging at 180 °C between 0 and 20 h. The hardness measurements were performed for the alloys following the aging process. It was observed that peak hardness value of Al-0.80Mg-0.85Si alloy increased with the addition of zirconium. This finding was very useful to obtain aging parameters for the extruded hollow profiles which are commonly used in automotive industry. Standard tensile tests were applied to aged profiles at room temperature and the results showed that modified alloy had higher mechanical properties compared to the non-modified alloy.


2012 ◽  
Vol 736 ◽  
pp. 307-315 ◽  
Author(s):  
Murugavel Suresh ◽  
Satyam Suwas

Mg alloys show limited room temperature formability compared to its lightweight counterpart aluminium alloys, which is a main obstacle in using this metal for most of the structural applications. However, it is known that grain refinement and texture control are the two possibilities for the improvement of formability of magnesium alloys. Amongst the approaches attempted for the texture weakening, additions through of rare-earth (RE) elements have been found most effective. The relationship between the texture and ductility is well established. In this paper, the effect of rare earth addition on texture weakening has been summarized for various magnesium alloys under the two most common modes of deformation methods.


Materials ◽  
2021 ◽  
Vol 14 (19) ◽  
pp. 5856
Author(s):  
Pragya Mishra ◽  
Pia Åkerfeldt ◽  
Farnoosh Forouzan ◽  
Fredrik Svahn ◽  
Yuan Zhong ◽  
...  

Laser powder bed fusion (L-PBF) has attracted great interest in the aerospace and medical sectors because it can produce complex and lightweight parts with high accuracy. Austenitic stainless steel alloy 316 L is widely used in many applications due to its good mechanical properties and high corrosion resistance over a wide temperature range. In this study, L-PBF-processed 316 L was investigated for its suitability in aerospace applications at cryogenic service temperatures and the behavior at cryogenic temperature was compared with room temperature to understand the properties and microstructural changes within this temperature range. Tensile tests were performed at room temperature and at −196 °C to study the mechanical performance and phase changes. The microstructure and fracture surfaces were characterized using scanning electron microscopy, and the phases were analyzed by X-ray diffraction. The results showed a significant increase in the strength of 316 L at −196 °C, while its ductility remained at an acceptable level. The results indicated the formation of ε and α martensite during cryogenic testing, which explained the increase in strength. Nanoindentation revealed different hardness values, indicating the different mechanical properties of austenite (γ), strained austenite, body-centered cubic martensite (α), and hexagonal close-packed martensite (ε) formed during the tensile tests due to mechanical deformation.


2010 ◽  
Vol 654-656 ◽  
pp. 2126-2129 ◽  
Author(s):  
Yuichi Nakahira ◽  
Tomonari Inamura ◽  
Hiroyasu Kanetaka ◽  
Shuichi Miyazaki ◽  
Hideki Hosoda

Effect of nitrogen (N) addition on mechanical properties of Ti-Cr-Sn alloy was investigated in this study. Ti-7mol%Cr-3mol%Sn was selected and less than 0.5wt% of N were systematically added. The alloys were characterized by optical microscopy, X-ray diffraction analysis and tensile tests at room temperature. The apparent phase was β (bcc) phase, whereas the presence of precipitates was confirmed in 0.5wt%N-added alloy only which did not exhibit sufficient cold workability. The grain size was not largely affected by N addition being less than 0.5wt%. Tensile tests revealed that less than 0.5wt%N addition improves the strength which is due to the solution hardening by interstitial N atoms.


1996 ◽  
Vol 460 ◽  
Author(s):  
M. Moriwaki ◽  
K. Ito ◽  
H. Inui ◽  
M. Yamaguchi

ABSTRACTThe deformation behavior of single crystals of Mo(Si,Al)2 with the C40 structure has been studied as a function of crystal orientation and Al content in the temperature range from room temperature to 1500°C in compression. Plastic flow is possible only above 1100°C for orientations where slip along <1120> on (0001) is operative and no other slip systems are observed over whole temperature range investigated. The critical resolved shear stress for basal slip decreases rapidly with increasing temperature and the Schmid law is valid. Basal slip appears to occur through a synchroshear mechanism, in which a-dislocations (b=1/3<1120>) dissociate into two synchro-partial dislocations with the identical Burgers vector(b*1/6<1120>) and each synchro-partial further dissociates into two partials on two adjacent planes.