Designing Advanced Biomedical Biodegradable Mg Alloys: A Review

The increased demand for alloys that can serve as implantation devices with outstanding bio-properties has led to the development of numerous biomedical Mg-based alloys. These alloys have been extensively investigated for their performance in living tissue with mixed results. Hence, there are still major concerns regarding the use of magnesium alloys for such applications. Among the issues raised are elevated corrosion rates, hydrogen generation, and the maintenance of mechanical integrity for designated healing times. In addition, toxicity can arise from the addition of alloying elements that are intended to improve the mechanical integrity and corrosion resistance of Mg alloys. The current work reviews the recent advances in the development of Mg alloys for applications as bio-absorbable materials in living organic environments. In particular, it attempts to develop a roadmap of effective factors that can be utilized when designing Mg alloys. Among the factors reviewed are the effects of alloying additions and processing methods on the exhibited mechanical properties and corrosion rates in simulated bio-fluids used in biomedical applications.

Effect of Alloying Additions on Microstructure, Mechanical and Magnetic Properties of Rapidly Cooled Bulk Fe-B-M-Cu (M = Ti, Mo and Mn) Alloys

The influence of alloying additions on the microstructure, mechanical, and magnetic properties of bulk Fe79B20Cu1, Fe79B16Ti4Cu1, Fe79B16Mo4Cu1 and Fe79B16Mn4Cu1 (at. pct) alloys was investigated. Nanocrystalline samples in the form of 3 mm rods were prepared directly by suction casting without additional heat treatment. Mössbauer spectroscopy, transmission electron microscopy and scanning electron microscopy studies confirmed that the investigated alloys consist α-Fe and Fe2B nanograins embedded in an amorphous matrix. The addition of alloying elements, such as Ti, Mo and Mn to Fe79B20Cu1 alloy increases the amount of amorphous phase and decreases the presence of Fe2B phase in all examined alloys. The mechanical properties of the samples, such as hardness, elastic modulus, and elastic energy ratio, were analysed by an instrumented indentation technique performed on a 12 × 12 nanoindentation grid. These tests allowed to characterise the mechanical properties of the regions observed in the same material. For the Fe79B20Cu1 alloy, the hardness of 1508 and 1999 HV, as well as Young’s modulus of 287 and 308 GPa, were estimated for the amorphous- and nanocrystalline-rich phase, respectively. The addition of Ti, Mo, and Mn atoms leads to a decrease in both hardness and elastic modulus for all regions in the investigated samples. Investigations of thermomagnetic characteristics show the soft magnetic properties of the studied materials. More detailed studies of magnetisation versus magnetic field curves for the Fe79B20−xMxCu1 (where x = 0 or 4; M = Ti, Mo, Mn) alloy, recorded in a wide range of temperatures, followed by the law of approach to magnetic saturation revealed the relationship between microstructure and magneto-mechanical properties.

Experimental Investigation and Thermodynamic Modeling of Influence of Nickel and Titanium Content on the Structure and Selected Properties of Tin Bronzes

Investigations are conducted in order to maintain or to improve the selected properties of the group of foundry copper-tin alloys with nickel and titanium additions, at a limited fraction of the critical (deficit) element such as tin. The crystallisation process, as well as changes of the microstructure and selected mechanical properties of the CuSn8 alloy—occurring due to introducing alloying additions—were analysed. Investigations of the macro and microstructure were performed using optical and scanning electron microscopy. Based on the thermal analysis and thermodynamic modelling using the CALPHAD (CALculations of PHAse Diagrams) method, the crystallisation process was analysed. The identification of phases was performed by XRD (X-ray diffraction). In addition, such parameters as tensile strength-UTS, elongation-A and hardness-HBS were tested. Under the influence of the introduced titanium, the columnar crystals are reduced due to the crystallisation of the alloy at the walls of the mould. Precipitations (intermetallic phases) crystallize first (primary). The intermetallic phases associated with the presence of the alloying elements nickel and titanium are located in the interdendritic regions. In tin bronzes with titanium additions, hardness (HBS) increases, tensile strength (UTS) negligibly decreases, while elongation (A) significantly decreases. In the case of CuSnNi bronze, the addition of 0.2 wt.% Ti increases the hardness and increases ultimate tensile strength (UTS), while reducing the elongation (A). Higher Ti additions increase HBS, slightly decrease the tensile strength, and significantly reduce the elongation.

Tensile Creep Properties of Cr-Si Alloys at 980 °C in Air—Influence of Ge and Mo Addition

The tensile creep behavior of Cr-Si alloys with Cr ≥ 91 at.% was investigated in air at 980 °C with a constant load of 50–100 MPa. Additionally, the influence of substitutional alloying additions of 2 at.% Ge and Mo, leading to ternary alloys was studied. The addition of Ge or Mo results in an improvement in creep strength, with the highest strength achieved with addition of Mo. For longer creep exposure times a strong effect is observed, because of severe nitrogen uptake from the air, depending on alloy composition. Based on the results a novel mechanism for the impact of chromium nitride formation on the creep behavior is proposed.