COMPARISON OF THE CORROSION PROPERTIES OF CoCrMo DENTAL ALLOYS IN ARTIFICIAL SALIVA

CoCrMo alloys are known for their biocompatible properties, which, together with their favorable mechanical properties, mean they can be efficiently used in dentistry. With the development of selective laser melting for the fabrication of 3D printed objects, interest in the corrosion properties of this alloy has risen in the field of prosthodontics. In the study, CoCrMoW dental alloys were studied in artificial saliva at body temperature i.e. 37 °C. Different forms of CoCrMoW alloy were selected: a reference sample, i.e. original material as-received from the supplier, a casted sample acquired from an ordinary procedure in a dental laboratory, and two 3D printed samples made from CoCrMoW powder using the selective laser melting method (SLM). Electrochemical, spectroscopic and hardness measurements were conducted. It was shown that the reference and cast samples have similar microstructural and electrochemical properties, while the electrochemical properties of the 3D printed samples differ, most probably due to the effect of the higher micro porosity and chemical composition of the alloys.

Additively Manufactured Commercial Co-Cr Dental Alloys: Comparison of Microstructure and Mechanical Properties

Laser-powder bed fusion (LPBF) is one of the preferred techniques for producing Co-Cr metal structures for dental prosthodontic appliances. However, there is generally insufficient information about material properties related to the production process and parameters. This study was conducted on samples produced from three different commercially available Co-Cr dental alloys produced on three different LPBF machines. Identically prepared samples were used for tensile, three-point bending, and toughness tests. Light microscopy (LM), scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD) analyses of microstructure were performed after testing. Differences were observed in microstructures, which reflected statistically significant differences in mechanical properties (one-way analysis of variance (ANOVA) and Scheffé post hoc test (α = 0.05)). The material produced on the 3D Systems DMP Dental 100 had 24 times greater elongation ε than the material produced on the Sysma MySint 100 device and the EOS M100 machine. On the other hand, the material produced on the EOS M100 had significantly higher hardness (HV0.2) than the other two produced materials. However, the microstructure of the Sysma specimens with its morphology deviates considerably from the studied group. LPBF-prepared Co-Cr dental alloys demonstrated significant differences in their microstructures and, consequently, mechanical properties.

Analysis and Comparison of the Corrosive Behavior of Nickel-Based and Cobalt-Based Dental Alloys

Nickel-based and cobalt-based metal alloys are frequently used in dentistry. The introduction of various elements in the alloy changes its characteristics, and a thorough study of each alloy should be completed to determine its appropriate corrosion resistance and biocompatibility in contact with physiological fluids. There are scarce investigations on these widely used dental alloys in Ringer solution, and findings in this research bring new experimental data and information. The present study evaluated and compared the corrosion behavior of six NiCr- and two CoCr-based dental materials in Ringer solution, using the following techniques: potentiostatic polarization curves (chronoamperometry), microstructural analysis, and EIS (electrochemical impedance spectroscopy). The results obtained in this investigation showed that in the NiCr-based specimens Ni4, Ni5, and Ni6 the stability of the passive layer was destroyed after polarization and a development and growth of stable pits was found in the microstructural analysis after electrochemical treatment. In terms of susceptibility to corrosion, two different groups of specimens were derived from this investigation. A first group which included the two CoCr (Co1 and Co2) and three of the six NiCr alloys studied (Ni1, Ni2, and Ni3). A second group with the other NiCr alloys investigated Ni4, Ni5, and Ni6.

Experimental Study Regarding the Behavior at Different pH of Two Types of Co-Cr Alloys Used for Prosthetic Restorations

Cobalt-chromium (Co-Cr) alloys are widely utilized in dentistry. The salivary pH is a significant factor, which affects the characteristics and the behavior of dental alloys through corrosion. This study aimed to evaluate the corrosion behavior in artificial saliva with different pH values (3, 5.7, and 7.6) of two commercial Co-Cr dental alloys manufactured by casting and by milling. Corrosion resistance was determined by the polarization resistance technique, and the tests were carried out at 37 ± 1 °C, in Carter Brugirard artificial saliva. After the electrochemical parameters, it can be stated that the cast Co-Cr alloy has the lowest corrosion current density, the highest polarization resistance, and the lowest speed of corrosion in artificial saliva with pH = 7.6. In the case of milled Co-Cr alloy, the same behavior was observed, but in artificial saliva with pH = 5.7, it recorded the most electropositive values of open circuit potential and corrosion potential. Although both cast and milled Co-Cr alloys presented a poorer corrosion resistance in artificial saliva with a more acidic pH value, the milled Co-Cr alloy had better corrosion behavior, making this alloy a better option for the prosthetic treatment of patients suffering from GERD.