Synergistic Flame-Retardant Effect of Aluminum Diethyl Phosphinate in PP/IFR System and the Flame-Retardant Mechanism

Synergistic flame-retardant effect of aluminum diethyl phosphinate (AlPi) in intumescent flame retardant polypropylene (PP/IFR) system and the flame-retardant mechanism were investigated. The flame retardancy of PP/IFR/AlPi (the mass ratio of IFR to AlPi is 2 : 1) was the best, which was proved by the results of the limiting oxygen index (LOI) test, UL-94 test, and cone calorimeter test ( CCT) test. Here, the LOI value of the sample was as high as 34% and passed the V–0 rating in UL–94 test. The peak heat release rate (PHRR) decreased by 92.57%, the total heat release (THR) reduced by 90.52%. Thermogravimetric (TGA) data showed that the introduction of AlPi improved thermal stability and changed the thermal degradation behavior of PP/IFR composites. Interestingly, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDXS) and laser Raman spectroscopy (LRS) proved that PP/IFR/AlPi had formed more residual carbon, but the flame retardancy was worse than PP/IFR/AlPi. This is because when the mass ratio of IFR to AlPi is 2 : 1, the synergy between IFR and AlPi was significant, gas-phase flame retardant and condensed-phase flame retardant reached a balance and obtained the best flame retardant effect.

A Novel Synergistic Flame Retardant of Hexaphenoxycyclotriphosphazene for Epoxy Resin

Hexaphenoxycyclotriphosphazene (HPCP) is a common flame retardant for epoxy resin (EP). To improve the thermostability and fire safety of HPCP-containing EP, we combined UiO66-NH2 (a kind of metal-organic frame, MOF) with halloysite nanotubes (HNTs) by hydrothermal reaction to create a novel synergistic flame retardant (H-U) of HPCP for EP. For the EP containing HPCP and H-U, the initial decomposition temperature (T5%) and the temperature of maximum decomposition rate (Tmax) increased by 11 and 17 °C under nitrogen atmosphere compared with those of the EP containing only HPCP. Meanwhile, the EP containing HPCP and H-U exhibited better tensile and flexural properties due to the addition of rigid nanoparticles. Notably, the EP containing HPCP and H-U reached a V-0 rating in UL-94 test and a limited oxygen index (LOI) of 35.2%. However, with the introduction of H-U, the flame retardant performances of EP composites were weakened in the cone calorimeter test, which was probably due to the decreased height of intumescent residual char.

Synergistic Flame Retardant Effect of Barium Phytate and Intumescent Flame Retardant for Epoxy Resin

Recently, widespread concern has been aroused on environmentally friendly materials. In this article, barium phytate (Pa-Ba) was prepared by the reaction of phytic acid with barium carbonate in deionized water, which was used to blend with intumescent flame retardant (IFR) as a flame retardant and was added to epoxy resin (EP). Afterward, the chemical structure and thermal stability of Pa-Ba were characterized by Fourier transform infrared (FTIR) spectroscopy and thermogravimetric analysis (TGA), respectively. On this basis, the flammability and flame retardancy of EP composites were researched. It is shown that EP/14IFR/2Ba composite has the highest limiting oxygen index (LOI) value of 30.7%. Moreover, the peak heat release rate (PHRR) of EP/14IFR/2Ba decreases by 69.13% compared with pure EP. SEM and Raman spectra reveal the carbonization quality of EP/14IFR/2Ba is better than that of other composites. The results prove that Pa-Ba can cooperate with IFR to improve the flame retardancy of EP, reducing the addition amount of IFR in EP, thus expanding the application range of EP. In conclusion, adding Pa-Ba to IFR is a more environmentally friendly and efficient method compared with others.

A Synergistic Flame Retardant System Based on Expandable Graphite, Aluminum (Diethyl-)Polyphospinate and Melamine Polyphosphate for Polyamide 6

Expandable graphite (EG), aluminum (diethyl)polyphosphinate (AlPi) and melamine polyphophate (MPP) was used as flame retardant multi-material additive in a polyamide 6 (PA6) matrix. Flame inhabitation performances were conducted by cone calorimeter, LOI and UL-94 tests, synergisms identified analyzed by TGA-FTIR and TGA-GC/MS and effects found were comprehensively discussed. SEM images were used for char residue characterization. For PA6 containing 20 wt.% EG and 5 wt.% AlPi/MPP (3:2), a well working synergism in limiting oxygen indices could be identified exhibiting the highest oxygen index (OI) measured: 46%. The study shows that the synergism due to the partial substitution of EG by AlPi/MPP can be attributed to two effects: (1) When PA6/AlPi/MPP mixtures decompose predominantly CO2 evaporates in early decomposition stages. CO2 evaporations was found to be sensitive to the heating rate applied, whereas specifically high heating rates increased the CO2 yield measured. (2) Solid decomposition products of AlPi/MPP act as “glue” between expanded graphite and thus increase the mechanical residue stability.

Comparative Study of Fire Resistance and Anti-Ageing Properties of Intumescent Fire-Retardant Coatings Reinforced with Conch Shell Bio-Filler

Conch shell bio-filler (CSBF) was prepared by washing, ultrasonicating, and pulverizing of conch shells and then was applied in waterborne intumescent fire-retardant coatings. The influence of CSBF on fire resistance and anti-ageing properties of intumescent fire-retardant coatings were studied by using different analytical methods. The fire protection and smoke density tests showed that when the mass fraction of CSBF was 3%, the resulting FRC3 coating had the optimum synergistic flame-retardant and smoke-suppression effects concomitant with a flame-spread rating of 10.7, equilibrium backside temperature of 152.4 °C at 900 s, and smoke-density rating value of 10.4%, which were attributed to the establishment of a more dense and stable intumescent char layer against heat and mass transfer. Thermogravimetric analysis indicated that the presence of CSBF increased the thermal stability and char-forming performance of the coatings, and the char residue of FRC3 rose to 34.6% at 800 °C from 28.6% of FRC0 without CSBF. The accelerated ageing test suggested that the incorporation of CSBF reduced the migration and decomposition of the flame retardants and the yellowing, blistering, and powdering phenomenon, thus improving the structural stability of the coating, resulting in better durability of flame retardancy and smoke-suppression performance.