Analytical Model Formulation of Steel Plate Reinforced Concrete Walls against Hard Projectile Impact

Steel plate reinforced concrete (SC) walls can effectively resist projectile impact by preventing the rear concrete fragments flying away, thus attracting much attention in defence technology. This work numerically and analytically investigated the hard projectile perforation of steel plate reinforced concrete walls. Impact resistance theories, including cavity expansion analysis as well as the petaling theory of thin steel plates were used to describe the cratering, tunneling and plugging phases of SC walls perforation. Numerical modeling of SC walls perforation was performed to estimate projectile residual velocity and target destructive form, which were validated against the test results. An analytical model for SC wall perforation was established to describe the penetration resistance featuring five stages, i.e., cratering, tunneling and plugging, petaling with plugging and solely petaling. Analytical model predictions matched numerical results well with respect to projectile deceleration evolution as well as residual velocity. From a structural absorbed energy perspective, the effect of front concrete panel and rear steel plate thickness combinations was also studied and analyzed. Finally, equivalent concrete slab thickness was derived with respect to the ballistic limit of SC walls, which may be helpful in the design of a protective strategy.

Comparison of Numerical Simulation Techniques of Ballistic Ceramics under Projectile Impact Conditions

This article presents an analysis of the effectiveness of available numerical techniques in mapping the characteristic behavior of ballistic ceramics under projectile impact conditions. As part of the work, the ballistic tests were performed on the layered ceramic/steel composite armor and tested with the 7.62 × 39 mm, armor-piercing incendiary (API) BZ projectile. The experimental tests were then mapped using computer simulations. In numerical analyses, four different techniques were used to describe cubic ceramic tiles Al2O3 placed on the ARMOX 500T steel backing plate, i.e.,: the Finite Element Method without Erosion (FEM), Finite Element with erosion (FEM + Erosion), Smoothed Particles Hydrodynamics (SPH) and a hybrid method that converts finite elements to SPH particles after exceeding the defined failure criteria (FEM to SPH conversion). The effectiveness of the individual methods was compared in terms of quality (mapping of characteristic phenomena occurring during the penetration process), quantity (bulge height of the backing plate) and time needed to complete the calculations. On the basis of the results of the experiments and numerical simulations, it was noticed that the most accurate reproduction of the phenomenon of ballistic impact of AP projectiles on ceramic/steel composite armor can be obtained by using a hybrid method, incorporating the conversion of finite elements into SPH particles. This method should be used in cases where accuracy of the results is more important than the time required to complete the calculations. In other situations where the purpose of the calculation is not to determine, for example, the exact value of penetration depth but only to observe a certain trend, the FEM method with defined erosion criteria (variant 2), which is more than 10 times faster, can be successfully used.

Effect of Needle Type, Number of Layers on FPAFC Composite against Low-Velocity Projectile Impact

Protective structures subjected to intensive loads that may benefit from the use of multilayer composite structures with excellent hardness and impact resistance represent an emerging research field in recent times. In this study, low-velocity projectile impact tests were performed on Functionally-graded Preplaced Aggregate Fibrous Concrete (FPAFC) mixtures to evaluate their performance. The effects of projectile needle type, fibre type and hybridization in addition to the number of layers in the composites on projectile impact were investigated. The bioinspiration of the excellent impact strength of turtle shells was used to design an FPAFC comprising a higher amount of steel and polypropylene fibres at the outer layers. In parallel, one and two-layered concretes were also cast to assess the effectiveness of three-layered FPAFC. The tests were performed on disc specimens using non-deformable compound bevel, convex edge and hollow edge projectiles. The damage severity was quantified by the top damage area, bottom damage area and depth of penetration. In addition, a simple analytical model for predicting the composite mass expulsion was developed and implemented. Findings indicated that regardless of fiber type and distribution, the compound bevel projectile needle produced the lowest impact numbers for all single, double and triple-layer specimens compared to the convex edge and hollow edge projectiles. Repeated projectile impacts increased the penetration depth and damaged area at the top and bottom surfaces of all targets. Targets were more resistant to convex edge and hollow edge projectile penetration than the compound bevel. The experimental and analytical model results for mass expelled from the top surface are reasonably acceptable. This research gives an idea of developing advanced fibrous composite with superior impact resistance for the promising protective structures.

A scanning electron microscopy study of projectile entry fractures in cortical bone; genesis and microarchitectural features

The present paper presents a scanning electron microscope (SEM) analysis of the genesis and microarchitecture of experimentally induced cortical entry fractures in porcine scapulae impacted at velocities ranging from 54 to 897 m/s. SEM observation was conducted on polyurethane replicas cast from negative silicone moulds. Analysis of the sequence of fracture processes operative during projectile impact revealed the presence of ring cracks at the site of impact, confirming that penetration in sandwich bones is achieved by cone crack propagation. Despite impulsive loading, two forms of plastic deformation were identified in the cortical bone surrounding the entry fracture up to a maximum velocity of 871 m/s. Microscopic radial and concentric cracks were associated with projectile impact, and the role of pores and pits as stress concentrators was captured. Possible underlying mechanisms for the observed plastic deformation are described, and the diagnostic utility of SEM analysis is presented.

Influence of Calcined Bauxite Aggregate on the Resistance of Cement Composites Subjected to Small Caliber Deformable Projectile Impact

This paper presents an experimental investigation on the influence of calcined bauxite aggregate (CBA) on the resistance of cement composites subjected to small caliber deformable projectile impact at a designed velocity of 400 m/s. The deformable projectile was made from copper with a purity of 99.5% and a diameter of 8.0 mm. Compared to mixtures with conventional coarse granite aggregate and/or siliceous fine aggregate, the incorporation of either fine or coarse CBA or their combination is beneficial in reducing the depth of penetration (DOP), equivalent crater diameter (CD), and crater volume (CV) caused by deformable projectile impact. CBA is found to be more effective in controlling the DOP and CV in comparison to the CD. Replacing of conventional aggregate with CBA leads to more severe damage to the projectiles (e.g., projectile length reduction, diameter increase, and mass loss). Relative effective hardness is an effective indicator to the deformation potential and penetration capacity of a deformable projectile to impact cement composites incorporating CBA.