Bi-Functional Catalyst/Sorbent for a H2-Rich Gas from Biomass Gasification

The aim of this work is to identify the effect of the CaO phase as a CO2 sorbent and mayenite (Ca12Al14O33) as a stabilizing phase in a bi-functional material for CO2 capture in biomass syngas conditioning and cleaning at high temperature. The effect of different CaO weight contents is studied (0, 56, 85, 100 wt%) in sorbents synthesized by the wet mixing method. These high temperature solid sorbents are upgraded to bi-functional compounds by the addition of 3 or 6 wt% of nickel chosen as the metal active phase. N2 adsorption, X-ray diffraction, scanning electronic microscopy, temperature-programmed reduction analyses and CO2 sorption study were performed to characterize structural, textural, reducibility and sorption properties of bi-functional materials. Finally, sorption-enhanced reforming of toluene (chosen as tar model), of methane then of methane and toluene with bi-functional compounds were performed to study the best material to improve H2 content in a syngas, provided by steam biomass gasification. If the catalytic activity on the sorption enhanced reforming of methane exhibits a fast fall-down after 10–15 min of experimental test, the reforming of toluene reaches a constant conversion of 99.9% by using bi-functional materials.

Size Analysis Based on Sorption Study Data for Hydroxyapatite Nanoparticles

This work is devoted to the study on the possibility of applying the method of analyzing the particle size of hydroxyapatite at various stages of synthesis. A series of hydroxyapatite powders obtained by chemical deposition using microwave radiation is considered. Determination of the size of hydroxyapatite nanorods is carried out on the basis of data on the density and specific surface area. The specific surface area is analyzed by the sorption method. Determination of the ratio "length / diameter" of nanorods is based on the analysis of images obtained by scanning electron microscopy.

Antimonate sequestration from aqueous solution using zirconium, iron and zirconium-iron modified biochars

Antimony (Sb) is increasingly being recognized as an important contaminant due to its various industrial applications and mining operations. Environmental remediation approaches for Sb are still lacking, as is the understanding of Sb environmental chemistry. In this study, biosolid biochar (BSBC) was produced and utilized to remove antimonate (Sb(V)) from aqueous solution. Zirconium (Zr), Zirconium-iron (Zr–Fe) and Fe–O coated BSBC were synthesized for enhancing Sb(V) sorption capacities of BSBC. The combined results of specific surface area, FTIR, SEM–EDS, TEM–EDS, and XPS confirmed that Zr and/or Zr–Fe were successfully coated onto BSBC. The effects of reaction time, pH, initial Sb(V) concentration, adsorbate doses, ionic strength, temperature, and the influence of major competitive co-existing anions and cations on the adsorption of Sb(V) were investigated. The maximum sorption capacity of Zr–O, Zr–Fe, Zr–FeCl3, Fe–O, and FeCl3 coated BSBC were 66.67, 98.04, 85.47, 39.68, and 31.54 mg/g respectively under acidic conditions. The XPS results revealed redox transformation of Sb(V) species to Sb(III) occurred under oxic conditions, demonstrating the biochar’s ability to behave as an electron shuttle during sorption. The sorption study suggests that Zr–O and Zr–O–Fe coated BSBC could perform as favourable adsorbents for mitigating Sb(V) contaminated waters.

Antimonate Sequestration from Aqueous Solution Using Zirconium, Iron and Zirconium-iron Modified Biochars

Antimony (Sb) is increasingly being recognized as an important contaminant due to its various industrial applications and mining operations. Environmental remediation approaches for Sb are still lacking, as is the understanding of Sb environmental chemistry. In this study, biosolid biochar (BSBC) was produced and utilized to remove antimonate (Sb(V)) from aqueous solution. Zirconium (Zr), Zirconium-iron (Zr-Fe) and Fe-O coated BSBC were synthesized for enhancing Sb(V) sorption capacities of BSBC. The combined results of specific surface area, FTIR, SEM-EDS, TEM-EDS, and XPS confirmed that Zr and/or Zr-Fe were successfully coated onto BSBC. The effects of reaction time, pH, initial Sb(V) concentration, adsorbate doses, ionic strength, temperature, and the influence of major competitive co-existing anions and cations on the adsorption of Sb(V) were investigated. The maximum sorption capacity of Zr-O, Zr-Fe, Zr-FeCl3, Fe-O, and FeCl3 coated BSBC were 66.67, 98.04, 85.47, 39.68, and 31.54 mg/g respectively under acidic conditions. The XPS results revealed redox transformation of Sb(V) species to Sb(III) occurred under oxic conditions, demonstrating the biochar’s ability to behave as an electron shuttle during sorption. The sorption study suggest that Zr-O and Zr-O-Fe coated BSBC could perform as favourable adsorbents for mitigating Sb(V) contaminated waters.

Adsorption of Heavy Metal on Active Carbon Derived from Coconut Leaves Agro-Waste

In this paper activated carbon is prepared from coconut leaves by chemical activation during slow pyrolysis at 673 K in an inert atmosphere. Activated carbon is prepared in the stiochiometric ratio of 1:1 (CL1), 2:1 (CL2) and 3:1 (CL3). Optimized 3:1 ratio is preferable for further study. BET surface area of CL3 activated carbon was found 1060.57 m2/g. It is greater than those of CL1 and CL2. The batch sorption study experiments were conducted with respect to solute concentration of 2.5–122.8 mg/l and solution temperature of 313–343 K. The Langmuir, Freundlich and Temkin isotherm studies were conducted. The experimental data fitted very well for the pseudo-first order and pseudo-second-order. The results have established good potentiality for the CL3 activated carbon to be used as a sorbent for the removal of lead from wastewater.