Characterization of Machining Damages Generated by a Piercing Process in CFRP Laminates

2015 ◽  
Vol 656-657 ◽  
pp. 185-190 ◽  
Author(s):  
Shingo Ueshiba ◽  
Keiji Ogi ◽  
Yutaka Shigematsu ◽  
Kei Saito
Keyword(s):  
Elevated Temperature ◽  
Optical Microscopy ◽  
Fiber Direction ◽  
Cross Sectional ◽  
X Ray ◽  
Cfrp Laminates

This paper presents experimental examples of machining damages resulting from a piercing process in CFRP laminates. A circular perforation was formed in CFRP cross-ply specimen with a punch jig using different blade angles and two distinct dimensional conditions. Surface, cross-sectional, and internal changes to the CFRP specimens after the hole-punching were observed using optical microscopy and X-ray analysis to quantitatively evaluate damage, including delamination, around the perforation area. Results indicate that the optimum piercing is achieved when the blades are parallel to fiber direction at an elevated temperature with blade angles essentially irrelevant.

Dislocations, Ordering and Antiferromagnetic Domains in MnO

1970 ◽  
Vol 28 ◽  
pp. 522-523
Author(s):  
D. J. Barber ◽  
R. G. Evans
Keyword(s):  
Electron Diffraction ◽  
Single Crystal ◽  
Optical Microscopy ◽  
Defect Chemistry ◽  
Magnetic Structures ◽  
Optically Transparent ◽  
Magnetic Features ◽  
Antiferromagnetic Domains

Manganese (II) oxide, MnO, in common with CoO, NiO and FeO, possesses the NaCl structure and shows antiferromagnetism below its Neel point, Tn∼ 122 K. However, the defect chemistry of the four oxides is different and the magnetic structures are not identical. The non-stoichiometry in MnO2 small (∼2%) and below the Tn the spins lie in (111) planes. Previous work reported observations of magnetic features in CoO and NiO. The aim of our work was to find explanations for certain resonance results on antiferromagnetic MnO.Foils of single crystal MnO were prepared from shaped discs by dissolution in a mixture of HCl and HNO3. Optical microscopy revealed that the etch-pitted foils contained cruciform-shaped precipitates, often thick and proud of the surface but red-colored when optically transparent (MnO is green). Electron diffraction and probe microanalysis indicated that the precipitates were Mn2O3, in contrast with recent findings of Co3O4 in CoO.

A method to measure pores and fissures in geologic materials under S.E.M. by digital image processing

1978 ◽  
Vol 36 (1) ◽  
pp. 212-213
Author(s):  
L. Montoto ◽  
M. Montoto ◽  
A. Bel-Lan
Keyword(s):  
Image Processing ◽  
Optical Microscopy ◽  
Digital Image Processing ◽  
Digital Image ◽  
Digital Processing ◽  
Free Surfaces ◽  
Geologic Materials ◽  
Automatic Information ◽  
Detector Output ◽  
Rock Specimens

INTRODUCTION.- The physical properties of rock masses are greatly influenced by their internal discontinuities, like pores and fissures. So, these need to be measured as a basis for interpretation. To avoid the basic difficulties of measurement under optical microscopy and analogic image systems, the authors use S.E.M. and multiband digital image processing. In S.E.M., analog signal processing has been used to further image enhancement (1), but automatic information extraction can be achieved by simple digital processing of S.E.M. images (2). The use of multiband image would overcome difficulties such as artifacts introduced by the relative positions of sample and detector or the typicals encountered in optical microscopy.DIGITAL IMAGE PROCESSING.- The studied rock specimens were in the form of flat deformation-free surfaces observed under a Phillips SEM model 500. The SEM detector output signal was recorded in picture form in b&w negatives and digitized using a Perkin Elmer 1010 MP flat microdensitometer.

Evidence for a shear mechanism for the precipitation of γ-zirconium hydride in zirconium

1978 ◽  
Vol 36 (1) ◽  
pp. 658-659
Author(s):  
G.J.C. Carpenter
Keyword(s):  
Elevated Temperature ◽  
Strain Field ◽  
Zirconium Hydride ◽  
Zirconium Atom ◽  
Atom Diffusion ◽  
Solvus Temperature ◽  
Hexagonal Close Packed ◽  
Partial Dislocations ◽  
The Face

In zirconium-hydrogen alloys, rapid cooling from an elevated temperature causes precipitation of the face-centred tetragonal (fct) phase, γZrH, in the form of needles, parallel to the close-packed <1120>zr directions (1). With low hydrogen concentrations, the hydride solvus is sufficiently low that zirconium atom diffusion cannot occur. For example, with 6 μg/g hydrogen, the solvus temperature is approximately 370 K (2), at which only the hydrogen diffuses readily. Shears are therefore necessary to produce the crystallographic transformation from hexagonal close-packed (hep) zirconium to fct hydride.The simplest mechanism for the transformation is the passage of Shockley partial dislocations having Burgers vectors (b) of the type 1/3<0110> on every second (0001)Zr plane. If the partial dislocations are in the form of loops with the same b, the crosssection of a hydride precipitate will be as shown in fig.1. A consequence of this type of transformation is that a cumulative shear, S, is produced that leads to a strain field in the surrounding zirconium matrix, as illustrated in fig.2a.

Microstructural characterization of a rapidly solidified Al-Fe-V-Si alloy for elevated temperature applications

1988 ◽  
Vol 46 ◽  
pp. 550-551
Author(s):  
R. E. Franck ◽  
J. A. Hawk ◽  
G. J. Shiflet
Keyword(s):  
High Temperature ◽  
Elevated Temperature ◽  
Grain Growth ◽  
Volume Fraction ◽  
Microstructural Characterization ◽  
Second Phase ◽  
Microstructural Stability ◽  
Elevated Temperature Strength ◽  
Temperature Applications

Rapid solidification processing (RSP) is one method of producing high strength aluminum alloys for elevated temperature applications. Allied-Signal, Inc. has produced an Al-12.4 Fe-1.2 V-2.3 Si (composition in wt pct) alloy which possesses good microstructural stability up to 425°C. This alloy contains a high volume fraction (37 v/o) of fine nearly spherical, α-Al12(Fe, V)3Si dispersoids. The improved elevated temperature strength and stability of this alloy is due to the slower dispersoid coarsening rate of the silicide particles. Additionally, the high v/o of second phase particles should inhibit recrystallization and grain growth, and thus reduce any loss in strength due to long term, high temperature annealing.The focus of this research is to investigate microstructural changes induced by long term, high temperature static annealing heat-treatments. Annealing treatments for up to 1000 hours were carried out on this alloy at 500°C, 550°C and 600°C. Particle coarsening and/or recrystallization and grain growth would be accelerated in these temperature regimes.

Digital imaging: When should one take the plunge?

1996 ◽  
Vol 54 ◽  
pp. 602-603
Author(s):  
John F. Mansfield
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Optical Microscopy ◽  
Digital Imaging ◽  
Storage Devices ◽  
Major Benefit ◽  
Transmission Electron ◽  
New Instrument ◽  
Scanning Electron

The current imaging trend in optical microscopy, scanning electron microscopy (SEM) or transmission electron microscopy (TEM) is to record all data digitally. Most manufacturers currently market digital acquisition systems with their microscope packages. The advantages of digital acquisition include: almost instant viewing of the data as a high-quaity positive image (a major benefit when compared to TEM images recorded onto film, where one must wait until after the microscope session to develop the images); the ability to readily quantify features in the images and measure intensities; and extremely compact storage (removable 5.25” storage devices which now can hold up to several gigabytes of data).The problem for many researchers, however, is that they have perfectly serviceable microscopes that they routinely use that have no digital imaging capabilities with little hope of purchasing a new instrument.

Improved Autoadhesion Measurement Method for Micromachined Polysilicon Beams

1996 ◽  
Vol 444 ◽  
Author(s):  
Maarten P. de Boer ◽  
Terry A. Michalske
Keyword(s):  
Surface Chemistry ◽  
Optical Microscopy ◽  
Measurement Method ◽  
Current Practice ◽  
Cantilever Beams ◽  
Beam Length ◽  
Substrate Adhesion

AbstractWe have measured autoadhesion (e.g. stiction) of individual polysilicon beams by interferometric optical microscopy. Untreated cantilever beams were dried from water in air, while treated beams were coated with a hydrophobic molecular coating of octadecyltrichlorosilane (ODTS). Adhesion values obtained for beams adhered to the substrate over a long length (large d) are independent of beam length with values of 16.7 and 4.4 mJ/m2 for untreated and treated samples respectively. These values can be understood in terms of differences in surface chemistry and polysilicon roughness. Using the shortest length beam which remains attached to the substrate, adhesion values were 280 and 16 mJ/m2 respectively. These higher values may be a result of capillarity effects. We recommend that measurements be made on beams in which d is large, in contrast to the current practice of noting the shortest beam adhered.

Sign in / Sign up

Export Citation Format

Share Document