Microstructure and wear resistance of CoCrNbNiW high-entropy alloy coating prepared by laser melting deposition

Rare Metals ◽  
2019 ◽  
Vol 38 (12) ◽  
pp. 1153-1159 ◽  
Author(s):  
Yan-Jun Jia ◽  
Han-Ning Chen ◽  
Xiao-Dan Liang
Keyword(s):  
Wear Resistance ◽  
Alloy Coating ◽  
High Entropy Alloy ◽  
Laser Melting ◽  
High Entropy ◽  
Laser Melting Deposition

scholarly journals Microstructure and tensile property of a BCC-structured high entropy alloy fabricated by laser melting deposition

2021 ◽  
Vol 1948 (1) ◽  
pp. 012194
Author(s):  
Min Yang ◽  
Shi-Hai Sun ◽  
Benpeng Wang ◽  
Yaojian Liang ◽  
Lu Wang ◽  
...  
Keyword(s):  
Tensile Property ◽  
High Entropy Alloy ◽  
Laser Melting ◽  
High Entropy ◽  
Laser Melting Deposition

Laser Assisted High Entropy Alloy Coating on Low Carbon Steel

2019 ◽  
Vol 813 ◽  
pp. 159-164
Author(s):  
Carlos Alberto Souto ◽  
Gustavo Faria Melo da Silva ◽  
Laura Angelica Ardila Rodriguez ◽  
Aline C. de Oliveira ◽  
Kátia Regina Cardoso
Keyword(s):  
Wear Resistance ◽  
Carbon Steel ◽  
Low Carbon Steel ◽  
High Hardness ◽  
Alloy Coating ◽  
High Entropy Alloy ◽  
Nominal Composition ◽  
Low Carbon ◽  
High Entropy ◽  
Scan Speed

Coatings with high entropy alloys of the AlCoCrFeNiV system were obtained by selective laser melting on low carbon steel substrates. The effect of the variation of the Fe and V contents as well as the laser processing parameters in the development of the coating were evaluated. The coatings were obtained from the simple powder mixtures of the high purity elemental components in a planetary ball mill. The coatings were obtained by using CO2 laser with a power of 100 W, diameter of 0.16 mm, and scan speed varying from 3 to 12 mm/s. Phase constituents, microstructure and hardness were investigated by XRD, SEM, and microhardness tester, respectively. Wear resistance measurements were carried out by the micro-abrasion method using ball-cratering tests. The coatings presented good adhesion to the substrate and high hardness, of the order of 480 to 650 HV. Most homogeneous coating with nominal composition was obtained by using the higher scan speed, 12 mm/s. Vanadium addition increased hardness and gave rise to a high entropy alloy coating composed by BCC solid solutions. Ball cratering tests conducted on HEA layer showing improvement of material wear resistance, when compared to base substrate, decreasing up to 88% its wear rate, from 1.91x10-6 mm3/Nmm to 0.23x10-6 mm3/Nmm.

Effects of Al Addition on Microstructure and Wear Resistance of High-Velocity-Oxygen-Fuel-Sprayed FeCoNiCrMn High Entropy Alloy Coating

2019 ◽  
Vol 11 (5) ◽  
pp. 685-693 ◽  
Author(s):  
Zhidan Zhou ◽  
Xiubing Liang ◽  
Yongxiong Chen ◽  
Baolong Shen ◽  
Junchao Shang ◽  
...  
Keyword(s):  
Wear Resistance ◽  
High Velocity ◽  
Alloy Coating ◽  
High Entropy Alloy ◽  
High Velocity Oxygen Fuel ◽  
High Entropy ◽  
Al Addition ◽  
Oxygen Fuel

scholarly journals Wear and Corrosion Resistance of Al0.5CoCrCuFeNi High-Entropy Alloy Coating Deposited on AZ91D Magnesium Alloy by Laser Cladding

Entropy ◽  
2018 ◽  
Vol 20 (12) ◽  
pp. 915 ◽  
Author(s):  
Kaijin Huang ◽  
Lin Chen ◽  
Xin Lin ◽  
Haisong Huang ◽  
Shihao Tang ◽  
...  
Keyword(s):  
Wear Resistance ◽  
Corrosion Resistance ◽  
Magnesium Alloy ◽  
Laser Cladding ◽  
Alloy Coating ◽  
High Entropy Alloy ◽  
High Entropy ◽  
Az91d Magnesium Alloy ◽  
Wear And Corrosion ◽  
Wear And Corrosion Resistance

In order to improve the wear and corrosion resistance of an AZ91D magnesium alloy substrate, an Al0.5CoCrCuFeNi high-entropy alloy coating was successfully prepared on an AZ91D magnesium alloy surface by laser cladding using mixed elemental powders. Optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction were used to characterize the microstructure of the coating. The wear resistance and corrosion resistance of the coating were evaluated by dry sliding wear and potentiodynamic polarization curve test methods, respectively. The results show that the coating was composed of a simple FCC solid solution phase with a microhardness about 3.7 times higher than that of the AZ91D matrix and even higher than that of the same high-entropy alloy prepared by an arc melting method. The coating had better wear resistance than the AZ91D matrix, and the wear rate was about 2.5 times lower than that of the AZ91D matrix. Moreover, the main wear mechanisms of the coating and the AZ91D matrix were different. The former was abrasive wear and the latter was adhesive wear. The corrosion resistance of the coating was also better than that of the AZ91D matrix because the corrosion potential of the former was more positive and the corrosion current was smaller.

Manufacturing of FeCoCrNi + FeCoCrNiAl laminated high-entropy alloy by laser melting deposition (LMD)

2021 ◽  
Vol 289 ◽  
pp. 129445
Author(s):  
Yangchuan Cai ◽  
Lisong Zhu ◽  
Yan Cui ◽  
Jian Han
Keyword(s):  
High Entropy Alloy ◽  
Laser Melting ◽  
High Entropy ◽  
Laser Melting Deposition

scholarly journals Effects of Annealing on the Microstructure and Wear Resistance of Laser Cladding CrFeMoNbTiW High-Entropy Alloy Coating

Crystals ◽  
2021 ◽  
Vol 11 (9) ◽  
pp. 1096
Author(s):  
Qiang Shen ◽  
Yan Li ◽  
Jing Zhao ◽  
Dezheng Liu ◽  
Yongsheng Yang
Keyword(s):  
Wear Resistance ◽  
Laser Cladding ◽  
Annealing Temperature ◽  
Annealing Treatment ◽  
Alloy Coating ◽  
Resistance Testing ◽  
High Entropy Alloy ◽  
Face Centered Cubic ◽  
High Entropy ◽  
Hardness Tester

In this study, a CrFeMoNbTiW high-entropy alloy (HEA) coating was prepared on a Q245R steel (American grade: SA515 Gr60) substrate by means of laser cladding. The effects of annealing temperature on the microstructure and wear resistance of the CrFeMoNbTiW coating were investigated using X-ray diffraction (XRD), a scanning electron microscope (SEM), a Vickers hardness tester and a roller friction wear tester. The results showed that the coating was mainly composed of body-centered cubic (BCC) solid solution and face-centered cubic (FCC) structural (Nb,Ti)C carbides prior to annealing, exhibiting an interdendritic structure and needlelike dendritic crystal structure with average microhardness of 682 HV0.2. The coarsening of the dendrite arms increased gradually after a 10-h long annealing treatment at 800 °C, 900 °C and 1000 °C, and a small amount of Laves phase was produced. After annealing, the highest microhardness value of the as-annealed coating reached 1176 HV0.2, which represents an increase of approximately 72.5% compared to that of the as-deposit coating. The wear resistance testing results imply that this type of coating retains good wear resistance following the annealing treatment and that its wear resistance increases in proportion to the annealing temperature in a range from 800 °C to 1000 °C.

scholarly journals Microstructure and Mechanical Properties Investigation of the CoCrFeNiNbx High Entropy Alloy Coatings

Crystals ◽  
2018 ◽  
Vol 8 (11) ◽  
pp. 409 ◽  
Author(s):  
Hui Jiang ◽  
Kaiming Han ◽  
Dayan Li ◽  
Zhiqiang Cao
Keyword(s):  
Wear Resistance ◽  
Steel Substrate ◽  
Alloy Coating ◽  
304 Stainless Steel ◽  
Molar Ratio ◽  
High Entropy Alloy ◽  
Solid Solution Phase ◽  
Face Centered Cubic ◽  
Laves Phases ◽  
High Entropy

In this work, the CoCrFeNiNbx (x: molar ratio, x = 0.45, 0.5, 0.75, and 1.0) high entropy alloy coatings were synthesized on a 304 stainless steel substrate by laser cladding to investigate the effect of Nb element on their microstructure, hardness, and wear resistance. The results indicated that in all of the CoCrFeNiNbx alloy coatings, two phases were found: One was a face-centered cubic (FCC) solid solution phase, the other was a Co1.92Nb1.08-type Laves phase. The microstructures of samples varied from hypoeutectic structure (x = 0.45 and 0.5) to hypereutectic structure (x = 0.75 and 1.0). The Vickers hardness of CoCrFeNiNbx alloy coatings was obviously improved compared with the substrate. The hardness value of the CoCrFeNiNb1.0 alloy coating reached to 590 HV, which was 2.8 times higher than that of the substrate. There was also a corresponding variation in wear properties with hardness evolutions. Wherein the hypereutectic CoCrFeNiNb1.0 alloy coating with the highest hardness exhibited the best wear resistance under the same wear condition, the dry wear test showed the wear mass loss of CoCrFeNiNb1.0 alloy coating was less than a third of the substrate. The high hardness and wear resistance properties were considered with the fine lamellar eutectic structure and proper combination of FCC and Laves phases.